Method of forming a fibrous structure composite ceramic material and material thus obtained
Assignee: Airbus Group SAS
•
Filing: 1989-03-22
•
Granted: 1991-06-18
•
Expires: 2009-03-22
Abstract
Abstract A method is provided for forming a composite ceramic material, in which a fibrous structure is first of all formed which is then embedded in the material of a ceramic matrix. To introduce said matrix into said structure, the following succession of operations is carried out: (a) said fibrous support is impregnated with a polymerization catalyst for an organometallic precursor of said ceramic matrix; (b) said fibrous support impregnated with said polymerization catalyst is placed in contact with said organometallic precursor; (c) said organometallic precursor is polymerized, and (d) said organometallic precursor is pyrolysed so as to obtain said matrix.
Inventors
- 👤 Caroline Debaig-Valade
- 👤 Claude Filliatre
- 👤 Christian Servens
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 16:07
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B30/00; C04B30/02; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/571; C04B35/58; C04B35/581; C04B35/584; C04B35/589; C04B35/71; C04B35/78; C04B35/80; C04B41/45; C04B41/4505; C04B41/455; C04B41/4554; C08; C08G; C08G77/00; C08G77/60; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/48; C04B2235/483; C04B2235/486; C04B2235/50; C04B2235/52; C04B2235/5208; C04B2235/5216; C04B2235/522; C04B2235/5224; C04B2235/5228; C04B2235/524; C04B2235/5244; C04B2235/5252; C04B2235/526; C04B2235/60; C04B2235/616; C04B2235/70; C04B2235/96
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
107 words
A method for forming a composite ceramic material, in which a fibrous support is first of all formed which is then embedded in a material of a ceramic matrix, which method includes, in order to introduce said matrix into said structure, the following succession of operation: (a) said fibrous support is impregnated with a polymerization catalyst for polymerizing a polymerizable organometallic precursor capable of forming a ceramic matrix upon pyrolysis; (b) said fibrous support impregnated with said polymerization catalyst is placed in contact with said polymerizable organometallic precursor; (c) said organometallic precursor is polymerized, and (d) said organometallic precursor is pyrolyzed so as to obtain said matrix.
Claim 2
Independent Claim
107 words
A method for forming a composite ceramic material, in which a fibrous support is first of all formed which is then embedded in a material of a ceramic matrix, which method includes, in order to introduce said matrix into said structure, the following succession of operation: (a) said fibrous support is impregnated with a polymerization catalyst for polymerizing a polymerizable organometallic precursor capable of forming a ceramic matrix upon pyrolysis; (b) said fibrous support impregnated with said polymerization catalyst is placed in contact with said polymerizable organometallic precursor; (c) said organometallic precursor is polymerized, and (d) said organometallic precursor is pyrolyzed so as to obtain said matrix.
Claim 3
Dependent Claim
20 words
The method as claimed in claim 2, wherein said fibrous support is impregnated with a solution of said polymerization catalyst.
Claim 4
Dependent Claim
26 words
The method as claimed in claim 2, wherein said polymerization catalyst is selected from the group consisting of polyborodimethylsiloxane, polyborodiethylsiloxane, polyborodiphenylsiloxane, polyborodivinylsiloxane, trifluoromethanesulfonic acid and dodecacarbonyltriruthenium.
Claim 5
Dependent Claim
25 words
The method as claimed in claim 1, wherein the organometallic precursor is selected from the group consisting of carbosilanes, silazanes, carbolsilazanes, borazines, borazanes and aluminosilicate-silanes.
Claim 6
Dependent Claim
23 words
The method as claimed in claim 1, wherein the organometallic precursor used is a direct precursor of the desired material for the matrix.
Claim 7
Dependent Claim
19 words
The method as claimed in claim 5, for obtaining a silicon carbide matrix, wherein said direct precursor is carbosilane.
Claim 8
Dependent Claim
34 words
The method as claimed in claim 1, wherein the organometallic precursor used is an indirect precursor capable of giving rise, by heat treatment, to a direct precursor of the desired material for the matrix.
Claim 9
Dependent Claim
19 words
The method as claimed in claim 7, for obtaining a silicon carbide matrix, wherein said indirect precursor is polydimethylsilane.
Claim 10
Dependent Claim
20 words
The method as claimed in claim 7, for obtaining a boron nitride matrix, wherein said indirect precursor is B-triphenyl N-trimethylborazine.
Claim 11
Dependent Claim
20 words
The method as claimed in claim 7, for obtaining a silicon nitride matrix, wherein said indirect precursor is tetramethyl-1,1,3,3 disilazane.
Claim 12
Dependent Claim
60 words
The method as claimed in claim 7, wherein, in the above operation b) the fibrous support, impregnated with the catalyst, is placed in contact with the indirect precursor and the heat treatment for transforming the indirect precursor into a direct precursor, impregnation of the fibrous support with said direct precursor and polymerization of the latter are carried out substantially simultaneously.
Claim 13
Dependent Claim
145 words
The method as claimed in claim 1, wherein: (a) a1--a solution of the polymerization catalyst in a solvent is formed, a2--the fibrous support is plunged into said solution of the catalyst so that the catalyst is adsorbed by the support, a3--said support is dried so as to evaporate said solvent, (b) said support is covered with said direct precursor, (c) said support covered with said precursor is subjected to a heat treatment by heating between about 60° C. and 400° C. for a time between about 4 and 40 hours so that: c1--the direct precursor penetrates into said fibrous support, c2--the direct precursor polymerizes within the fibrous support, (d) d1 --said fibrous support impregnated with polymerized precursor is cooled, then d2--said fibrous support is subjected to heat treatment for pyrolyzing the polymerized precursor and transforming it into the desired ceramic material of the ceramic matrix.
Claim 14
Dependent Claim
40 words
The method as claimed in claim 1, wherein the cycle of operations a, b, c, and d are repeated several times until the desired density is obtained for the composite ceramic material, formed of said fibrous structure and said matrix.
Claim 15
Independent Claim
108 words
A method for forming a composite ceramic material having a fibrous structure embedded in a ceramic matrix, comprising the steps of: (a) impregnating said fibrous structure with a polymerization catalyst for polymerizing a polymerizable organometallic precursor of said ceramic matrix, said polymerizable catalyst selected from the group consisting of polyborodimethylsiloxane, polyborodiethylsiloxane, polyborodiphenylsiloxane, poyborodivinylsiloxane, trifluoromethanesulfonic acid, tribromomethanesulfonic acid, trifluoracetic acid and dodecacarbonyltriruthenium; (b) placing said fibrous structure impregnated with said polymerization catalyst in contact with said polymerizable organometallic precursor selected from the group consisting of carbosilanes, silazanes, carbosilazanes, borazines, borazanes and aluminosilicate-silanes; (c) polymerizing said organometallic precursor; and (d) pyrolyzing said organometallic precursor so as to obtain said matrix.
Claim 16
Independent Claim
108 words
A method for forming a composite ceramic material having a fibrous structure embedded in a ceramic matrix, comprising the steps of: (a) impregnating said fibrous structure with a polymerization catalyst for polymerizing a polymerizable organometallic precursor of said ceramic matrix, said polymerizable catalyst selected from the group consisting of polyborodimethylsiloxane, polyborodiethylsiloxane, polyborodiphenylsiloxane, poyborodivinylsiloxane, trifluoromethanesulfonic acid, tribromomethanesulfonic acid, trifluoracetic acid and dodecacarbonyltriruthenium; (b) placing said fibrous structure impregnated with said polymerization catalyst in contact with said polymerizable organometallic precursor selected from the group consisting of carbosilanes, silazanes, carbosilazanes, borazines, borazanes and aluminosilicate-silanes; (c) polymerizing said organometallic precursor; and (d) pyrolyzing said organometallic precursor so as to obtain said matrix.
Claim 17
Independent Claim
108 words
A method for forming a composite ceramic material having a fibrous structure embedded in a ceramic matrix, comprising the steps of: (a) impregnating said fibrous structure with a polymerization catalyst for polymerizing a polymerizable organometallic precursor capable of forming ceramic matrix upon pyrolysis; and (b) placing said fibrous structure impregnated with said polymerization catalyst in contact with said polymerizable organometallic precursor, wherein the organometallic precursor used is an indirect precursor capable of giving rise, by heat treatment, to a direct precursor, and wherein the indirect precursor is B-triphenyl N-trimethylborazine; (c) polymerizing said organometalic precursor; and (d) pyrolyzing said organometallic precursor so as to obtain a boron nitride matrix.
Claim 18
Independent Claim
108 words
A method for forming a composite ceramic material having a fibrous structure embedded in a ceramic matrix, comprising the steps of: (a) impregnating said fibrous structure with a polymerization catalyst for polymerizing a polymerizable organometallic precursor capable of forming ceramic matrix upon pyrolysis; and (b) placing said fibrous structure impregnated with said polymerization catalyst in contact with said polymerizable organometallic precursor, wherein the organometallic precursor used is an indirect precursor capable of giving rise, by heat treatment, to a direct precursor, and wherein the indirect precursor is B-triphenyl N-trimethylborazine; (c) polymerizing said organometalic precursor; and (d) pyrolyzing said organometallic precursor so as to obtain a boron nitride matrix.
Claim 19
Dependent Claim
153 words
The method as claimed in claim 7, wherein: (a) a1--a solution of the polymerization catalyst in a solvent is formed, a2--the fibrous support is plunged into said solution of the catalyst so that the catalyst is adsorbed by the support, a3--said support is dried so as to evaporate said solvent, (b) said support is covered with said indirect precursor, (c) said support covered with said precursor is subjected to a heat treatment by heating between about 60° C. and 400° C. for a time between about 4 and 40 hours so that: c1--the indirect precursor is transformed into a direct precursor, c2--the direct precursor penetrates into said fibrous support, c3--the direct precursor polymerizes within the fibrous support, (d) d1--said fibrous structure impregnated with polymerized precursor is cooled, then d2--said fibrous structure is subjected to heat treatment for pyrolyzing the polymerized precursor and transforming it into the desired ceramic material of the ceramic matrix.
References Cited (Backward Citations)
US4122139A
Cited
US4404153A
Cited
US4395460A
Cited
EP0078197A1
Cited
EP0130105A1
Cited
US4618591A
Cited
EP0179589A2
Cited
US4689252A
Cited
US4851491A
Cited
US4828774A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-06-17 | 1994-12-17 | 1995-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-06-17 | 1998-12-17 | 1999-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-06-17 | 2002-12-17 | 2003-06-18 | $7700.00 | Window Closed / Lapsed |