US5088554A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Sintered metal sand screen
Assignee: Halliburton Co
•
Filing: 1990-10-22
•
Granted: 1992-02-18
•
Expires: 2010-10-22
Abstract
Abstract A tubular sand screen is made in one piece entirely of powdered metal slivers which are molded and sintered to form a metallurgically integral rigid tubular structure. Aggregate metal particles, for example, stainless steel slivers, are bonded together by interatomic diffusion as a result of sintering the compacted slivers under high temperature and pressure conditions. The sintered metal sand screen performs the function of the conventional prepack assembly as well as the screen function. In one aspect of the invention, the sintered metal screen is subjected to electropolishing to yield an effective porosity of 40-60 mesh, with an average pore size of 150 microns. Most of the surface irregularities are removed by electropolishing, and very few nucleation sites remain where particles in the size range of 74 microns-100 microns can become captured or otherwise lodged to cause plugging of the screen.
Inventors
- 👤 Bryant A. Arterbury
- 👤 James E. Spangler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:59
CPC Classifications
E; E21; E21B; E21B43/00; E21B43/02; E21B43/08; E21B43/082; B; B01; B01D; B01D29/00; B01D29/11; B01D29/111; B01D29/13; B01D29/15; B01D29/31; B01D29/33; B01D39/00; B01D39/14; B01D39/20; B01D39/2027; B01D39/2031; B01D39/2034; B22; B22F; B22F3/00; B22F3/10; B22F3/11; B22F8/00; B22F2998/00; Y; Y02; Y02P; Y02P10/00; Y02P10/20; Y02W; Y02W30/00; Y02W30/50; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/496; Y10T29/49604
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
61 words
A well screen assembly for separating particulated material from formation fluid comprising, in combination: a mandrel having a tubular sidewall and longitudinally spaced apertures formed radially therethrough; and, a well screen mounted on said mandrel, said well screen being a tubular body of sintered powdered metal, said tubular well screen body having an external surface which has been smoothed by electropolishing.
Claim 2
Dependent Claim
61 words
A well screen assembly for separating particulated material from formation fluid comprising, in combination: a mandrel having a tubular sidewall and longitudinally spaced apertures formed radially therethrough; and, a well screen mounted on said mandrel, said well screen being a tubular body of sintered powdered metal, said tubular well screen body having an external surface which has been smoothed by electropolishing.
Claim 3
Dependent Claim
16 words
A well screen assembly as defined in claim 1, wherein the powdered metal is stainless steel.
Claim 4
Dependent Claim
14 words
A well screen assembly as defined in claim wherein the powdered metal is nickel.
Claim 5
Dependent Claim
17 words
A well screen assembly as defined in claim 1, wherein the powdered metal comprises nickel chromium alloy.
Claim 6
Dependent Claim
36 words
A well screen assembly as defined in claim 1, wherein the powdered metal comprises metal slivers having an average length in the range of 0.001-0.002 inches, and having a diameter which is substantially less than length.
Claim 7
Dependent Claim
43 words
A well screen for separating unconsolidated material out of inflowing well fluid in water, oil, gas and recovery wells comprising a tubular, porous body of sintered powdered metal, said tubular well screen body having an external surface which has been smoothed by electropolishing.
Claim 8
Dependent Claim
43 words
A well screen for separating unconsolidated material out of inflowing well fluid in water, oil, gas and recovery wells comprising a tubular, porous body of sintered powdered metal, said tubular well screen body having an external surface which has been smoothed by electropolishing.
Claim 9
Dependent Claim
15 words
A well screen as defined in claim 6, wherein the powdered metal is stainless steel.
Claim 10
Dependent Claim
14 words
A well screen as defined in claim 6, wherein the powdered metal is nickel.
Claim 11
Dependent Claim
16 words
A well screen as defined in claim 6, wherein the powdered metal comprises nickel chromium alloy.
Claim 12
Dependent Claim
25 words
A well screen as defined in claim 6, wherein the powdered metal comprises metal slivers having an average length in the range of 0.001-0.002 inches.
Claim 13
Dependent Claim
27 words
A well screen as defined in claim 6, wherein said tubular, porous body has threaded fittings formed on opposite ends, respectively, for connection to threaded coupling collars.
Claim 14
Dependent Claim
45 words
A well screen as defined in claim 6, wherein said tubular, porous body has a central body portion disposed between first and second radially stepped end portions, said first and second radially stepped end portions each having threaded fittings for connection to threaded coupling collars.
Claim 15
Independent Claim
25 words
A method for making a well screen comprising the steps: forming a unitary, porous tubular body of sintered powdered metal; and, electropolishing said sintered body.
Claim 16
Independent Claim
25 words
A method for making a well screen comprising the steps: forming a unitary, porous tubular body of sintered powdered metal; and, electropolishing said sintered body.
Claim 17
Dependent Claim
54 words
The method for making a well screen as defined in claim 12, wherein the forming step is performed by: depositing metal slivers into a mold; compressing the slivers within the mold; and, baking the compressed slivers in an oven at a temperature sufficient to cause the slivers to become bonded together by interatomic diffusion.
Claim 18
Dependent Claim
74 words
The method for making a well screen as defined in claim 13, wherein the forming step is performed by: producing metal slivers in average lengths of 0.001-0.002 inches; compressing the slivers to approximately 60,000 to approximately 65,000 pounds per square inch within a mold; and, baking the compressed slivers in an oven at a temperature of from about 1,600 to about 1,800 degrees F until the slivers become tacky and bond to each other.
Claim 19
Dependent Claim
71 words
The method for making a well screen as defined in claim 13, wherein the forming step is performed by: depositing metal slivers into a mold; compressing the slivers within the mold until the slivers are united in an interlocking union; and, baking the compressed slivers in an oven at a temperature sufficient to cause the slivers to become tacky and bond to each other, thereby forming a metallurgically integral, porous structure.
Claim 20
Dependent Claim
124 words
An improved well screen of the type having a fluid porous, particulate restricting member for separating unconsolidated material out of formation fluid, characterized in that the particulate restricting member is a porous, tubular body of sintered powdered metal formed by the following steps: depositing metal slivers having an average length of from about 0.001 to about 0.002 inches into a mold; compressing the slivers within the mold until the slivers are interlocked in a structurally stable union; and baking the compressed slivers in an oven at a temperature sufficient to cause the slivers to become tacky and bonded to each other, thereby forming a metallurgically integral, porous structure having pore openings in the size range of from about 74 microns to about 100 microns.
Claim 21
Dependent Claim
124 words
An improved well screen of the type having a fluid porous, particulate restricting member for separating unconsolidated material out of formation fluid, characterized in that the particulate restricting member is a porous, tubular body of sintered powdered metal formed by the following steps: depositing metal slivers having an average length of from about 0.001 to about 0.002 inches into a mold; compressing the slivers within the mold until the slivers are interlocked in a structurally stable union; and baking the compressed slivers in an oven at a temperature sufficient to cause the slivers to become tacky and bonded to each other, thereby forming a metallurgically integral, porous structure having pore openings in the size range of from about 74 microns to about 100 microns.
Claim 22
Dependent Claim
18 words
A well screen as defined in claim 17, including the step of electropolishing said tubular well screen body.
Claim 23
Dependent Claim
62 words
A well screen as defined in claim 19, wherein said electropolishing step is performed until the average size of the pore openings in the tubular well screen body is increased to a value in the size range of from about 100 microns to about 200 microns, thereby yielding an effective porosity in the range of from about 40 to about 60 mesh.
References Cited (Backward Citations)
US1874035A
Cited
US2554343A
Cited
US2600150A
Cited
US2826805A
Cited
US2963163A
Cited
US3033783A
Cited
US3201858A
Cited
US3313621A
Cited
US3567437A
Cited
US3785038A
Cited
US3605245A
Cited
US3632243A
Cited
US3746642A
Cited
US3897531A
Cited
US4071937A
Cited
US4072616A
Cited
US4088580A
Cited
US4186100A
Cited
US4217141A
Cited
US4483820A
Cited
US4705611A
Cited
US4755265A
Cited
US4821800A
Cited
US4811790A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-02-17 | 1995-08-19 | 1996-02-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-02-17 | 1999-08-19 | 2000-02-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-02-17 | 2003-08-19 | 2004-02-18 | $7700.00 | Window Closed / Lapsed |