Electrical contacts and methods of manufacturing same
Assignee: Schott Solar CSP Inc
•
Filing: 1990-09-24
•
Granted: 1992-06-02
•
Expires: 2010-09-24
Abstract
Abstract Nickel is introduced into the construction of the rear electrical contacts on silicon solar cells to reduce contact resistance between the aluminum contact material and the silver pads. In one embodiment, the nickel is applied as an intermediate layer between the silicon substrate and each silver pad. In a second and preferred embodiment, the nickel is incorporated into the silver ink that is used to make the soldering pads. Specifically, the invention provides a "double-fired" process for forming a rear contact on a solar cell wherein (1) a windowed aluminum layer is first formed on the rear surface of a partially finished silicon solar cell by printing an aluminum ink or paste that contains a glass frit, (2) the aluminum ink or paste is fired without any intervening drying step, (3) soldering pads are formed by printing a silver/nickel/glass frit ink or paste so as to fill and overlap the windows, and (4) the silver/nickel/glass frit ink or paste is fired so as to cause the constituents thereof to make an ohmic bond with the silicon substrate. The foregoing procedure is integrated with the formation of a silver grid contact on the front side of the solar cell substrate in a conventional manner and firing that grid contact simultaneously with the silver soldering pads so as to form an ohmic contact with the front surface of the substrate.
Inventors
- 👤 David A. St. Angelo
- 👤 Frank J. Bottari
- 👤 Christopher E. Dube
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:22
CPC Classifications
H; H10; H10F; H10F71/00; H10F10/00; H10F10/10; H10F10/14; H10F77/00; H10F77/10; H10F77/16; H10F77/20; H10F77/206; H10F77/211; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/547
Claims Analysis
Total Claims: 45
Claim 1
Independent Claim
209 words
A method of making a solar cell, comprising the steps of: (a) providing a silicon substrate having first and second opposing surfaces and a P-N junction adjacent said first surface; (b) applying to said second surface a first composition comprising aluminum metal particles and a glass frit in a liquid vehicle so as to form a first aluminum-containing coating that covers all but at least one selected area of said second surface; (c) firing said substrate in a non-oxidizing atmosphere so as to effect removal of said liquid vehicle and alloying of said aluminum metal particles with silicon at said second surface; (d) applying a second composition comprising silver and nickel metal particles and glass frit in a liquid vehicle so that said second composition forms a second coating that covers said at least one selected area of said second surface and also overlaps the edges of the alloyed aluminum that surrounds said at least one selected area; and (e) firing said second composition in an oxygen-containing environment so as to effect removal of said liquid vehicle from said second composition and cause the silver and nickel particles in said second composition to fuse to said substrate and the alloyed aluminum that surrounds said at least one selected area.
Claim 2
Independent Claim
209 words
A method of making a solar cell, comprising the steps of: (a) providing a silicon substrate having first and second opposing surfaces and a P-N junction adjacent said first surface; (b) applying to said second surface a first composition comprising aluminum metal particles and a glass frit in a liquid vehicle so as to form a first aluminum-containing coating that covers all but at least one selected area of said second surface; (c) firing said substrate in a non-oxidizing atmosphere so as to effect removal of said liquid vehicle and alloying of said aluminum metal particles with silicon at said second surface; (d) applying a second composition comprising silver and nickel metal particles and glass frit in a liquid vehicle so that said second composition forms a second coating that covers said at least one selected area of said second surface and also overlaps the edges of the alloyed aluminum that surrounds said at least one selected area; and (e) firing said second composition in an oxygen-containing environment so as to effect removal of said liquid vehicle from said second composition and cause the silver and nickel particles in said second composition to fuse to said substrate and the alloyed aluminum that surrounds said at least one selected area.
Claim 3
Dependent Claim
30 words
A method according to claim 1 wherein step (e) is accomplished by heating said substrate to a temperature of at least 750 degrees C. for at least about 5 seconds.
Claim 4
Dependent Claim
29 words
A method according to claim 1 wherein said second composition is dried in air at a temperature of about 100-150 degrees C. before it is subjected to step (e).
Claim 5
Dependent Claim
32 words
A method according to claim 1 wherein in step (c) said substrate is heated to a temperature of 670 to 850 degrees C. in order to alloy said aluminum to said substrate.
Claim 6
Dependent Claim
18 words
A method according to claim 1 wherein said first composition is applied to said substrate by pad printing.
Claim 7
Dependent Claim
30 words
A method according to claim 1 wherein said first composition comprises aluminum particles and a glass frit suspended in a vehicle comprising a vaporizable organic solvent and an organic binder.
Claim 8
Dependent Claim
25 words
A method according to claim 1 wherein said first and second compositions are inks and said inks are applied to said substrate by pad printing.
Claim 9
Dependent Claim
19 words
A method according to claim 1 wherein said second composition contains between about 1.0 and 5.0 wt. % nickel.
Claim 10
Dependent Claim
24 words
A method according to claim 1 wherein said at least one selected area comprises at least two mutually spaced portions of said second surface.
Claim 11
Dependent Claim
58 words
A method according to claim 9 wherein step (b) is accomplished by pad printing, and further wherein at least one selected second area of said second surface of said substrate is masked prior to step (b) so as to prevent said first composition from being applied to said at least one second selected area of said second surface.
Claim 12
Dependent Claim
41 words
A method according to claim 10 wherein said second composition is applied to as to cover said at least two mutually spaced portions of said second surface and adjacent portions of the alloyed aluminum formed by firing of said first composition.
Claim 13
Dependent Claim
29 words
A method according claim 1 wherein said first surface of said substrate is covered by a layer of a dielectric material before application of said first and second compositions.
Claim 14
Dependent Claim
18 words
A method according to claim 12 wherein said dielectric material is silicon nitride, silicon dioxide or titanium dioxide.
Claim 15
Dependent Claim
86 words
A method according to claim 12 further including the following step: (f) after step (d) applying to selected portions of said layer of dielectric material a third composition comprising silver metal particles and a glass frit in a liquid vehicle so as to form a third silver-containing coating in the form of a grid electrode pattern, whereby when said substrate is fired according to step (e), said third composition will penetrate said dielectric layer and form an ohmic bond with said first surface of said substrate.
Claim 16
Dependent Claim
31 words
A method according to claim 14 wherein step (e) is conducted so that the substrate is heated to a temperature of 750-850 degrees C. for between about 5 and 10 seconds.
Claim 17
Independent Claim
264 words
A method of making a solar cell, comprising the steps of: (a) providing a silicon substrate having first and second opposite surfaces and a P-N junction adjacent said first surface; (b) applying a first composition comprising aluminum metal particles and a glass frit in a liquid vehicle so as to form a first aluminum-containing coating that covers all but at least one selected area of said second surface; (c) firing said substrate in a non-oxidizing atmosphere so as to effect removal of said liquid vehicle and alloying of said aluminum metal particles with silicon at said second surface; (d) applying to said second surface a second composition comprising nickel metal particles and a glass frit in a liquid vehicle so that said second composition forms a second coating that covers said at least one selected area of said second surface and also overlaps the edges of the alloyed aluminum that surrounds said at least one selected area; (e) applying a third composition comprising silver metal particles and a glass frit in a liquid vehicle so that said third composition forms a third coating that covers said second coating; and (f) firing said second and third compositions in an oxygen-containing environment so as to effect removal of said liquid vehicle from said second and third compositions and (a) cause the nickel in said second composition to bond to said substrate and the overlapped edges of the alloyed aluminum that surrounds said at least one selected area, and (b) cause the silver in said third composition to bond to the bonded nickel from said second coating.
Claim 18
Independent Claim
264 words
A method of making a solar cell, comprising the steps of: (a) providing a silicon substrate having first and second opposite surfaces and a P-N junction adjacent said first surface; (b) applying a first composition comprising aluminum metal particles and a glass frit in a liquid vehicle so as to form a first aluminum-containing coating that covers all but at least one selected area of said second surface; (c) firing said substrate in a non-oxidizing atmosphere so as to effect removal of said liquid vehicle and alloying of said aluminum metal particles with silicon at said second surface; (d) applying to said second surface a second composition comprising nickel metal particles and a glass frit in a liquid vehicle so that said second composition forms a second coating that covers said at least one selected area of said second surface and also overlaps the edges of the alloyed aluminum that surrounds said at least one selected area; (e) applying a third composition comprising silver metal particles and a glass frit in a liquid vehicle so that said third composition forms a third coating that covers said second coating; and (f) firing said second and third compositions in an oxygen-containing environment so as to effect removal of said liquid vehicle from said second and third compositions and (a) cause the nickel in said second composition to bond to said substrate and the overlapped edges of the alloyed aluminum that surrounds said at least one selected area, and (b) cause the silver in said third composition to bond to the bonded nickel from said second coating.
Claim 19
Dependent Claim
19 words
A method accord claim 16 wherein in step (e) said third composition further comprises about 3 wt. % aluminum.
Claim 20
Dependent Claim
29 words
A method according to claim 16 wherein said first surface of said substrate is covered by a layer of a dielectric material before the application of said first composition.
Claim 21
Dependent Claim
85 words
A method according to claim 18 wherein step (f) is preceded by the step of applying to selected portions of said layer of dielectric material a fourth composition comprising silver metal particles and a glass frit in a liquid vehicle so as to form a fourth coating in the form of a grid electrode pattern, whereby when said substrate is fired according to step (f) said fourth composition will penetrate said dielectric layer and form an ohmic bond with said first surface of said substrate.
Claim 22
Dependent Claim
13 words
A method according to claim 19 wherein said dielectric layer is silicon nitride.
Claim 23
Independent Claim
260 words
A method of making a solar cell, comprising the steps of: (a) providing a silicon substrate having first and second opposite surfaces and a P-N junction adjacent said first surface; (b) applying to said second surface a first composition comprising aluminum metal particles and a glass frit in a liquid vehicle so as to form a first aluminum-containing coating that covers all but at least one area of said second surface; (c) firing said substrate in a non-oxidizing atmosphere so as to effect removal of said vehicle and alloying of said aluminum metal particles with silicon at said second surface; (d) applying a second composition comprising silver and nickel metal particles and a glass frit in a liquid vehicle so that said second composition forms a second coating that covers said at least one area of said second surface and also overlaps the edges of the alloyed aluminum coating that surrounds said at least one area; (e) applying a third composition comprising silver metal particles and glass frit in a liquid vehicle so that said third composition forms a third coating that covers selected areas of said first surface so as to define a grid electrode pattern; and (f) firing said second and third compositions in air so as to effect removal of said liquid vehicle from said second and third compositions and cause the silver and nickel in said second composition to form an ohmic contact with said aluminum layer and the silver in said third composition to form an ohmic contact with said first surface of said substrate.
Claim 24
Independent Claim
260 words
A method of making a solar cell, comprising the steps of: (a) providing a silicon substrate having first and second opposite surfaces and a P-N junction adjacent said first surface; (b) applying to said second surface a first composition comprising aluminum metal particles and a glass frit in a liquid vehicle so as to form a first aluminum-containing coating that covers all but at least one area of said second surface; (c) firing said substrate in a non-oxidizing atmosphere so as to effect removal of said vehicle and alloying of said aluminum metal particles with silicon at said second surface; (d) applying a second composition comprising silver and nickel metal particles and a glass frit in a liquid vehicle so that said second composition forms a second coating that covers said at least one area of said second surface and also overlaps the edges of the alloyed aluminum coating that surrounds said at least one area; (e) applying a third composition comprising silver metal particles and glass frit in a liquid vehicle so that said third composition forms a third coating that covers selected areas of said first surface so as to define a grid electrode pattern; and (f) firing said second and third compositions in air so as to effect removal of said liquid vehicle from said second and third compositions and cause the silver and nickel in said second composition to form an ohmic contact with said aluminum layer and the silver in said third composition to form an ohmic contact with said first surface of said substrate.
Claim 25
Independent Claim
140 words
A method of forming an aluminum contact with silver soldering pads on a silicon semiconductor substrate, comprising the steps of: (a) providing a silicon substrate having first and second opposing surfaces; (b) applying to said second surface a first composition comprising aluminum metal particles and a glass frit in a liquid vehicle; (c) firing said substrate and said first composition in a non-oxidizing atmosphere so as to effect removal of said vehicle, and alloying of said aluminum metal particles with silicon at said second surface; (d) applying over said fired composition a second composition comprising silver and nickel particles and a glass frit in a liquid vehicle; and (f) firing said second composition in an air atmosphere so as to cause said silver and nickel particles to form an electrically conductive contact with the aluminum particles of said first composition.
Claim 26
Independent Claim
140 words
A method of forming an aluminum contact with silver soldering pads on a silicon semiconductor substrate, comprising the steps of: (a) providing a silicon substrate having first and second opposing surfaces; (b) applying to said second surface a first composition comprising aluminum metal particles and a glass frit in a liquid vehicle; (c) firing said substrate and said first composition in a non-oxidizing atmosphere so as to effect removal of said vehicle, and alloying of said aluminum metal particles with silicon at said second surface; (d) applying over said fired composition a second composition comprising silver and nickel particles and a glass frit in a liquid vehicle; and (f) firing said second composition in an air atmosphere so as to cause said silver and nickel particles to form an electrically conductive contact with the aluminum particles of said first composition.
Claim 27
Dependent Claim
16 words
A method according to claim 22 wherein said first composition if fired in a nitrogen atmosphere.
Claim 28
Dependent Claim
18 words
A method according to claim 22 wherein the glass in said second composition comprises a lead borosilicate glass.
Claim 29
Independent Claim
284 words
A method of making a solar cell, comprising the steps of: (a) providing a silicon substrate having first and second opposite surfaces, a P-N junction adjacent said first surface, and a dielectric layer covering said first surface; (b) applying to said second surface a first composition comprising aluminum metal particles in a liquid vehicle so as to form a first aluminum-containing coating that covers all but at least one area of said second surface; (c) firing said first coating in a non-oxidizing atmosphere so as to effect removal of said vehicle and alloying of said aluminum metal particles with silicon at said second surface; (d) applying to said second surface a second composition comprising particles of silver metal, particles of nickel metal, and particles of a borosilicate glass in a liquid vehicle so that said second composition forms a second coating that covers said at least one area of said second surface and also overlaps the edges of the alloyed aluminum coating that surrounds said at least one area; (e) drying said second composition; (f) applying to said dielectric layer a third composition comprising silver particles and a glass frit in a liquid vehicle so that said third composition forms a third coating that defines a grid electrode pattern; and (g) firing said second and third coatings in air so as to effect removal of the liquid vehicle from said second and third compositions and (a) cause the silver and nickel metal in said second composition to bond to said substrate and form an ohmic contact with the alloyed aluminum, and (b) cause the silver and glass frit components of said third composition to penetrate said dielectric layer and bond to said first surface.
Claim 30
Independent Claim
284 words
A method of making a solar cell, comprising the steps of: (a) providing a silicon substrate having first and second opposite surfaces, a P-N junction adjacent said first surface, and a dielectric layer covering said first surface; (b) applying to said second surface a first composition comprising aluminum metal particles in a liquid vehicle so as to form a first aluminum-containing coating that covers all but at least one area of said second surface; (c) firing said first coating in a non-oxidizing atmosphere so as to effect removal of said vehicle and alloying of said aluminum metal particles with silicon at said second surface; (d) applying to said second surface a second composition comprising particles of silver metal, particles of nickel metal, and particles of a borosilicate glass in a liquid vehicle so that said second composition forms a second coating that covers said at least one area of said second surface and also overlaps the edges of the alloyed aluminum coating that surrounds said at least one area; (e) drying said second composition; (f) applying to said dielectric layer a third composition comprising silver particles and a glass frit in a liquid vehicle so that said third composition forms a third coating that defines a grid electrode pattern; and (g) firing said second and third coatings in air so as to effect removal of the liquid vehicle from said second and third compositions and (a) cause the silver and nickel metal in said second composition to bond to said substrate and form an ohmic contact with the alloyed aluminum, and (b) cause the silver and glass frit components of said third composition to penetrate said dielectric layer and bond to said first surface.
Claim 31
Independent Claim
298 words
A method of making a solar cell, comprising the steps of: (a) providing a silicon substrate having first and second opposite surfaces, a P-N junction adjacent said first surface, and a dielectric layer covering said first surface; (b) applying to said second surface a first composition comprising aluminum metal particles in a liquid vehicle so as to form a first aluminum-containing coating that covers all but selected areas of said second surface; (c) firing said substrate in a non-oxidizing atmosphere so as to effect removal of said vehicle and alloying of said aluminum metal particles with silicon at said second surface; (d) applying to said selected areas of said second surface a second composition comprising particles of nickel metal and particles of a borosilicate glass in a liquid vehicle so that said second composition forms a second coating that covers said selected areas of said second surface and also overlaps the edges of the alloyed aluminum coating that surrounds said selected areas; (e) covering said second coating with a third coating of a third composition comprising particles of silver metal and frit of a borosilicate glass in a liquid vehicle; (f) applying to said dielectric layer a fourth composition comprising silver particles and a glass frit in a liquid vehicle so that said fourth composition forms a fourth coating that defines a grid electrode pattern; and (g) firing said second, third and fourth compositions in air so as to effect removal of the liquid vehicle from said compositions and (a) cause the silver and nickel metal in said second and third compositions to bond to said substrate and the adjacent alloyed aluminum, and (b) cause the silver and glass frit of the fourth composition to penetrate said dielectric layer and form an aluminum bond with said first surface.
Claim 32
Independent Claim
298 words
A method of making a solar cell, comprising the steps of: (a) providing a silicon substrate having first and second opposite surfaces, a P-N junction adjacent said first surface, and a dielectric layer covering said first surface; (b) applying to said second surface a first composition comprising aluminum metal particles in a liquid vehicle so as to form a first aluminum-containing coating that covers all but selected areas of said second surface; (c) firing said substrate in a non-oxidizing atmosphere so as to effect removal of said vehicle and alloying of said aluminum metal particles with silicon at said second surface; (d) applying to said selected areas of said second surface a second composition comprising particles of nickel metal and particles of a borosilicate glass in a liquid vehicle so that said second composition forms a second coating that covers said selected areas of said second surface and also overlaps the edges of the alloyed aluminum coating that surrounds said selected areas; (e) covering said second coating with a third coating of a third composition comprising particles of silver metal and frit of a borosilicate glass in a liquid vehicle; (f) applying to said dielectric layer a fourth composition comprising silver particles and a glass frit in a liquid vehicle so that said fourth composition forms a fourth coating that defines a grid electrode pattern; and (g) firing said second, third and fourth compositions in air so as to effect removal of the liquid vehicle from said compositions and (a) cause the silver and nickel metal in said second and third compositions to bond to said substrate and the adjacent alloyed aluminum, and (b) cause the silver and glass frit of the fourth composition to penetrate said dielectric layer and form an aluminum bond with said first surface.
Claim 33
Dependent Claim
129 words
A solar cell comprising a silicon substrate having first and second oppositely facing surfaces, a P-N junction formed adjacent said first surface, a layer of a dielectric overlying said first surface, said dielectric being a member of the class consisting of silicon nitride, titanium dioxide, and silicon dioxide, a first grid-shaped contact extending through portions of said layer of dielectric, said grid-shaped contact comprising silver and a glass frit bonded to said first surface, a second aluminum contact overlying said second surface, said second aluminum contact comprising aluminum alloyed with silicon at the interface of said substrate and said second contact, a plurality of silver-containing soldering pads bonded to said second contact, and nickel disposed so as to improve the contact resistance between said silver pads and said aluminum.
Claim 34
Dependent Claim
129 words
A solar cell comprising a silicon substrate having first and second oppositely facing surfaces, a P-N junction formed adjacent said first surface, a layer of a dielectric overlying said first surface, said dielectric being a member of the class consisting of silicon nitride, titanium dioxide, and silicon dioxide, a first grid-shaped contact extending through portions of said layer of dielectric, said grid-shaped contact comprising silver and a glass frit bonded to said first surface, a second aluminum contact overlying said second surface, said second aluminum contact comprising aluminum alloyed with silicon at the interface of said substrate and said second contact, a plurality of silver-containing soldering pads bonded to said second contact, and nickel disposed so as to improve the contact resistance between said silver pads and said aluminum.
Claim 35
Dependent Claim
16 words
A solar cell according to claim 27 wherein said nickel is disposed as a discrete layer.
Claim 36
Dependent Claim
20 words
A solar cell according to claim 27 wherein said nickel is incorporated as a constituent of said silver-containing soldering pads.
Claim 37
Dependent Claim
50 words
A solar cell according to claim 29 wherein said second contact is formed with a plurality of apertures exposing selected portions of said second surface, and further wherein said silver soldering pads fill said apertures and are bonded to said selected portions of said second surface and said second contact.
Claim 38
Dependent Claim
27 words
A solar cell according to claim 30 wherein said silver-containing soldering pads extend beyond the peripheries of said apertures so as to overlap said second aluminum contact.
Claim 39
Dependent Claim
13 words
A solar cell according to claim 31 wherein said dielectric is silicon nitride.
Claim 40
Dependent Claim
131 words
A solar cell comprising a silicon substrate having first and second oppositely facing surfaces, a P-N junction formed adjacent said first surface, a layer of a dielectric overlying said first surface, said dielectric being a member of the class consisting of silicon nitride, titanium dioxide, and silicon dioxide, a first grid-shaped contact extending through portions of said layer of dielectric, said grid-shaped contact comprising silver and a glass frit bonded to said first surface, a second aluminum contact overlying said second surface, said second aluminum contact comprising aluminum alloyed with silicon at the interface of said substrate and said second contact, a plurality of silver-containing soldering pads bonded to said second contact, and nickel fused in contact with the aluminum of said second contact and the silver of said soldering pads.
Claim 41
Dependent Claim
131 words
A solar cell comprising a silicon substrate having first and second oppositely facing surfaces, a P-N junction formed adjacent said first surface, a layer of a dielectric overlying said first surface, said dielectric being a member of the class consisting of silicon nitride, titanium dioxide, and silicon dioxide, a first grid-shaped contact extending through portions of said layer of dielectric, said grid-shaped contact comprising silver and a glass frit bonded to said first surface, a second aluminum contact overlying said second surface, said second aluminum contact comprising aluminum alloyed with silicon at the interface of said substrate and said second contact, a plurality of silver-containing soldering pads bonded to said second contact, and nickel fused in contact with the aluminum of said second contact and the silver of said soldering pads.
Claim 42
Dependent Claim
157 words
A solar cell comprising a silicon substrate having first and second oppositely facing surfaces, a P-N junction formed adjacent said first surface, a layer of silicon nitride overlying said first surface, a first grid-shaped silver contact extending through portions of said layer of silicon nitride and bonded to said first surface, a second contact overlying and bonded to said second surface, said second contact comprising aluminum and a glass frit with the aluminum being alloyed with silicon at said second surface, said second contact being formed with a plurality of apertures that expose portions of said second surface, a plurality of soldering pads comprising silver filling said apertures and bonded to said second surface and adjacent portions of said second contact, and nickel disposed in electrically conductive relation with the silver component of said soldering pads and the aluminum of said second contact, so as to improve the contact resistance between said silver pads and said aluminum.
Claim 43
Dependent Claim
157 words
A solar cell comprising a silicon substrate having first and second oppositely facing surfaces, a P-N junction formed adjacent said first surface, a layer of silicon nitride overlying said first surface, a first grid-shaped silver contact extending through portions of said layer of silicon nitride and bonded to said first surface, a second contact overlying and bonded to said second surface, said second contact comprising aluminum and a glass frit with the aluminum being alloyed with silicon at said second surface, said second contact being formed with a plurality of apertures that expose portions of said second surface, a plurality of soldering pads comprising silver filling said apertures and bonded to said second surface and adjacent portions of said second contact, and nickel disposed in electrically conductive relation with the silver component of said soldering pads and the aluminum of said second contact, so as to improve the contact resistance between said silver pads and said aluminum.
Claim 44
Dependent Claim
34 words
A solar cell according to claim 34 wherein said nickel is disposed as a discrete layer in each of said apertures, and said silver pads are bonded to said substrate by said nickel layers.
Claim 45
Dependent Claim
23 words
A solar cell according to claim 34 wherein said nickel is incorporated in said silver pads in admixture with the silver constituent thereof.
References Cited (Backward Citations)
JPS59117276A
Cited
JPS62237765A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-06-02 | 1995-12-02 | 1996-06-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-06-02 | 1999-12-02 | 2000-06-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-06-02 | 2003-12-02 | 2004-06-02 | $7700.00 | Window Closed / Lapsed |