Acidic palladium strike bath

Claim 2

An aqueous strike bath for producing a strike electrodeposit of palladium on an electrically conductive surface, which comprises from 0.1 to 30 grams per liter palladium, from 1 to 250 grams per liter of a complexing agent, from 10 to 200 grams per liter of a supporting electrolyte, from 20 to 350 grams per liter of a buffering agent, and from 0 to 50 ppm of a surfactant additive selected from non-ionic and cationic surfactants, which bath exhibits a pH value within a range of from 2.0 to about 4.3, in which said complexing agent comprises an organic diamine selected from the group consisting of 1,2-diaminobutane, 1,2-diaminopropane, 1,2-diamino-2-methylpropane, 1,2-diaminopentane, 1,2-diaminohexane, 2,3-diaminobutane, 2,3-diaminopentane, 2,3-diaminohexane, 3,4-diaminohexane, and higher aliphatic diamines with adjacent primary, secondary or tertiary amino groups, and in which said buffering agent is selected from the group consisting of acetic acid, citric acid, tartaric acid, tetraboric acid, acetoacetic acid, chloracetic acid, maleic acid, malic acid, itaconic acid, and their salts.

Claim 3

The bath of claim 1 in which said complexing agent is 1,2-diaminopropane.

Claim 4

The bath of claim 1 in which a source of palladium is selected from the group consisting of palladium dichloride, palladium dibromide, palladium sulfate, palladium nitrate, palladium monoxide hydrate, diamminepalladium(II) hydroxide, dichlorodiamminepalladium(II), dinitritodiamminepalladium(II), tetrammine palladium(II) chloride and tetramminepalladium tetrachloropalladate.

Claim 5

The bath of claim 1 in which said supporting electrolyte is chosen from the group consisting of chlorides, bromides, sulfates and nitrates of sodium, potassium and ammonia.

Claim 6

The bath of claim 3 in which said supporting electrolyte is chosen from the group consisting of chlorides of sodium, potassium and ammonia.

Claim 7

The bath of claim 1 in which said buffering agent comprises acetic acid.

Claim 8

The bath of claim 1 in which said strike bath, when used for a low-speed plating, comprises 0.1 to 5 grams per liter palladium, 10 to 100 grams per liter of the supporting electrolyte, 1 to 50 grams per liter of the complexing agent, 20 to 200 grams per liter of the buffering agent, 0 to 50 ppm of the surfactant additive, and water to volume, and which exhibits a pH value within a range of from 3.7 to 4.3.

Claim 9

The bath of claim 7 in which said strike bath comprises 3±1 grams per liter palladium, 60 grams per liter of the supporting electrolyte, 40 grams per liter of the complexing agent, 150 grams per liter of the buffering agent and 1 ppm of cationic surfactant additive, and which exhibits a pH value of 3.7 to 4.1.

Claim 10

The bath of claim 1 in which said strike bath, when used for a highspeed plating, comprises 5 to 30 grams per liter palladium, 20-200 grams per liter of the supporting electrolyte, 50-250 grams per liter of the complexing agent, 200-350 grams per liter of the buffering agent, and 0-50 ppm of the surfactant additive, and water to volume, and which exhibits a pH value within a range of 3.7 to 4.3.

Claim 11

The bath of claim 9 in which said strike bath comprises 10±2 grams per liter palladium, 60 grams per liter of the supporting electrolyte, 65 grams per liter of the complexing agent, 250 grams per liter of the buffering agent and 1 ppm of the cationic surfactant additive, and which exhibits a pH value of 3.7 to 4.1.

Claim 12

The bath of claim 1 in which said passivated surface is one chosen from the group consisting of nickel, chromium, bronze, and steels.

Claim 13

A process of plating an electrically conductive surface, which comprises electroplating on said surface at least two layers in succession comprising a palladium strike layer on said surface and a cover layer comprising a metal selected from the group consisting of palladium nickel alloy and palladium, gold, rhodium, ruthenium, platinum, silver and their alloys, wherein said palladium strike layer is deposited from an aqueous bath comprising from 0.1 to 30 grams per liter palladium, from 1 to 250 grams per liter of a complexing agent, from 10 to 200 grams per liter of a supporting electrolyte, from 50 to 350 grams per liter of a buffering agent, and from 0 to 50 ppm of an additive selected from non-ionic and cationic surfactants, which bath exhibits a pH value within a range of from 2 to about 4.3, in which said complexing agent comprises an organic diamine selected from the group consisting of 1,2-diaminobutane, 1,2-diaminopropane, 1,2-diamino-2-methylpropane, 1,2-diaminopentane, 1,2-diaminohexane, 2,3-diaminobutane, 2,3-diaminopentane, 2,3-diaminohexane, 3,4-diaminohexane, and higher aliphatic diamines with adjacent primary, secondary or tertiary amino groups, and in which said buffering agent is selected from the group consisting of acetic acid, citric acid, tartaric acid, tetraboric acid, acetoacetic acid, chloracetic acid, malic acid, malic acid, itaconic acid, and their salts.

Claim 14

A process of plating an electrically conductive surface, which comprises electroplating on said surface at least two layers in succession comprising a palladium strike layer on said surface and a cover layer comprising a metal selected from the group consisting of palladium nickel alloy and palladium, gold, rhodium, ruthenium, platinum, silver and their alloys, wherein said palladium strike layer is deposited from an aqueous bath comprising from 0.1 to 30 grams per liter palladium, from 1 to 250 grams per liter of a complexing agent, from 10 to 200 grams per liter of a supporting electrolyte, from 50 to 350 grams per liter of a buffering agent, and from 0 to 50 ppm of an additive selected from non-ionic and cationic surfactants, which bath exhibits a pH value within a range of from 2 to about 4.3, in which said complexing agent comprises an organic diamine selected from the group consisting of 1,2-diaminobutane, 1,2-diaminopropane, 1,2-diamino-2-methylpropane, 1,2-diaminopentane, 1,2-diaminohexane, 2,3-diaminobutane, 2,3-diaminopentane, 2,3-diaminohexane, 3,4-diaminohexane, and higher aliphatic diamines with adjacent primary, secondary or tertiary amino groups, and in which said buffering agent is selected from the group consisting of acetic acid, citric acid, tartaric acid, tetraboric acid, acetoacetic acid, chloracetic acid, malic acid, malic acid, itaconic acid, and their salts.

Claim 15

The process of claim 12 in which said complexing agent is 1,2-diaminopropane.

Claim 16

The process of claim 12 in which a source of palladium is selected from the group consisting of palladium dichloride, palladium dibromide, palladium sulfate, palladium nitrate, palladium monoxide hydrate, diamminepalladium(II) hydroxide, dichlorodiamminepalladium(II), dinitritodiamminepalladium(II), tetramminepalladium(II) chloride and tetramminepalladium tetrachloropalladate.

Claim 17

The process of claim 12 in which said supporting electrolyte is chosen from the group consisting of chlorides, bromides, sulfates and nitrates of sodium, potassium and ammonia.

Claim 18

The process of claim 15 in which said supporting electrolyte is chosen from the group consisting of chlorides of sodium, potassium and ammonia.

Claim 19

The process of claim 12 in which said buffering agent comprises acetic acid.

Claim 20

The process of claim 12 in which said strike bath, when used for a low-speed plating, comprises 0.1 to 5 grams per liter palladium, 10 to 100 grams per liter of the supporting electrolyte, 1 to 50 grams per liter of the complexing agent, 20 to 200 grams per liter of the buffering agent, 0 to 50 ppm of the surfactant additive, and water to volume, and which exhibits a pH value within a range of from 3.7 to 4.3.

Claim 21

The process of claim 18 in which said strike bath comprises 3±1 grams per liter palladium, 60 grams per liter of a supporting electrolyte, 40 grams per liter of a complexing agent, 150 grams per liter of a buffering agent and 1 ppm of cationic surfactant additive, and which exhibits a pH value of 3.7 to 4.1.

Claim 22

The process of claim 12 in which said strike bath, when used for a high-speed plating, comprises 5 to 30 grams per liter palladium, 20-200 grams per liter of the supporting electrolyte, 50-250 grams per liter of the complexing agent, 200-350 grams per liter of the buffering agent, 0 to 50 ppm of the surfactant additive, and water to volume, and which exhibits a pH value within a range of 3.7 to 4.3.

Claim 23

The process of claim 20 in which said strike bath comprises 10±2 grams per liter palladium, 60 grams per liter of the supporting electrolyte, 65 grams per liter of the complexing agent, 250 grams per liter of the buffering agent and 1 ppm of the cationic surfactant additive, and which exhibits a pH value of 3.7 to 4.1.

Claim 24

The process of claim 12 in which said electrically conductive surface is one chosen from the group consisting of nickel, chromium, bronze, and steels.

Claim 25

A process of plating palladium strike on an electrically conductive surface of an article comprising the step of passing current through an article acting as a cathode, an aqueous strike bath and an anode, wherein the pH of the strike bath ranges from 2 to about 4.3, the strike bath comprises from 0.1 to 30 grams per liter palladium, from 1 to 250 grams per liter of a complexing agent, from 10 to 200 grams per liter of a supporting electrolyte, from 20 to 350 grams per liter of a buffering agent, and from 0 to 50 ppm of a surfactant additive selected from non-ionic and cationic surfactants, said complexing agent comprises an organic diamine selected from 1,2-diaminobutane, 1,2-diaminopropane, 1,2-diamino-2-methylpropane, 1,2-diaminopentane, 1,2-diaminohexane, 2,3-diaminobutane, 2,3-diaminopentane, 2,3-diaminohexane, 3,4-diaminohexane and higher aliphatic diamines with adjacent primary, secondary or tertiary amino groups, and said buffering agent is selected from the group consisting of acetic acid, citric acid, tartaric acid, tetraboric acid, acetoacetic acid, chloracetic acid, malic acid, malic acid, itaconic acid, and their salts.

Claim 26

A process of plating palladium strike on an electrically conductive surface of an article comprising the step of passing current through an article acting as a cathode, an aqueous strike bath and an anode, wherein the pH of the strike bath ranges from 2 to about 4.3, the strike bath comprises from 0.1 to 30 grams per liter palladium, from 1 to 250 grams per liter of a complexing agent, from 10 to 200 grams per liter of a supporting electrolyte, from 20 to 350 grams per liter of a buffering agent, and from 0 to 50 ppm of a surfactant additive selected from non-ionic and cationic surfactants, said complexing agent comprises an organic diamine selected from 1,2-diaminobutane, 1,2-diaminopropane, 1,2-diamino-2-methylpropane, 1,2-diaminopentane, 1,2-diaminohexane, 2,3-diaminobutane, 2,3-diaminopentane, 2,3-diaminohexane, 3,4-diaminohexane and higher aliphatic diamines with adjacent primary, secondary or tertiary amino groups, and said buffering agent is selected from the group consisting of acetic acid, citric acid, tartaric acid, tetraboric acid, acetoacetic acid, chloracetic acid, malic acid, malic acid, itaconic acid, and their salts.