Aqueous crosslinkable resin dispersions, method of their production and use thereof
Assignee: Nippon Shokubai Co Ltd
•
Filing: 1991-05-31
•
Granted: 1994-02-08
•
Expires: 2011-05-31
Abstract
Abstract The present invention yields a coating film excellent in adhesion, water resistance, solvent resistance and durability. A compound having a carboxyl group and a long-chain alkylthio group or a salt thereof is used as an emulsifier and emulsion polymerization is carried out using a polymerizable monomer or monomers having, within their molecule, a group reactive with a carboxyl group as raw materials for emulsion polymerization, whereby the resin produced by emulsion polymerization and the emulsifier react with each other efficiently on the occasion of film formation and form a crosslinked structure. When a compound having a polymerizable unsaturated group in addition to the carboxyl group and long-chain alkylthio group or a salt thereof is used as the emulsifier, not only the above-mentioned crosslinked structure is formed but also the polymerizable unsaturated group in the emulsifier will react with the unsaturated group in the polymerizable monomer or monomers in the manner of grafting. As a result, the compatibility between the emulsifier and the emulsion-polymerized resin is improved.
Inventors
- 👤 Masuji Izubayashi
- 👤 Masatoshi Yoshida
- 👤 Toshiaki Matsunaga
- 👤 Kohei Hori
- 👤 Teruo Kikuta
- 👤 Shiro Nakano
- 👤 Hidetoshi Hatta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:53
CPC Classifications
B; B41; B41M; B41M5/00; B41M5/26; B41M5/40; B41M5/42; B41M5/44; C; C08; C08F; C08F2/00; C08F2/12; C08F2/16; C08F2/22; C08F2/24; C09; C09J; C09J7/00; C09J7/30; C09J7/38; C09J7/381; D; D06; D06M; D06M11/00; D06M11/77; D06M11/79; D06M15/00; D06M15/19; D06M15/21; D06M15/263; D21; D21H; D21H19/00; D21H19/36; D21H19/44; D21H19/56; B41M2205/00; B41M2205/04; B41M5/426
Claims Analysis
Total Claims: 47
Claim 1
Independent Claim
227 words
An aqueous crosslinkable resin dispersion characterized by its being obtained by emulsion-polymerizing in an aqueous medium a monomer composition I composed of 0.1-40% by weight of at least one polymerizable monomer (a) having, within its molecular structure, a polymerizable double bond and an epoxy, aziridine or oxazoline group and 60-99.9% by weight of one or more other polymerizable monomers (b) copolymerizable with the polymerizable monomer (a), the sum total of the polymerizable monomers (a) and (b) being 100% by weight, in the presence of a water-soluble or water-dispersible emulsifier or emulsifiers selected from either one or both of the groups (P) and (Q) below: (P) polymers IIa having a terminal alkylthio group and an acid value of not less than 200 obtained by polymerizing a polymerizable monomer composition A containing an unsaturated carboxylic acid as an essential component thereof, in the presence of an alkylmercaptan B having 6-18 carbon atoms, or salts thereof; (Q) polymers IIb having a terminal alkylthio group and an acid value of not less than 200 obtained by polymerizing a polymerizable monomer composition A containing an unsaturated carboxylic acid as an essential component thereof, in the presence of an alkylmercaptan B having 6-18 carbon atoms, and further reacting the resulting polymer with at least one polymerizable monomer (c) having, within its molecular structure, a group reactive with a carboxyl group, or salts thereof.
Claim 2
Dependent Claim
227 words
An aqueous crosslinkable resin dispersion characterized by its being obtained by emulsion-polymerizing in an aqueous medium a monomer composition I composed of 0.1-40% by weight of at least one polymerizable monomer (a) having, within its molecular structure, a polymerizable double bond and an epoxy, aziridine or oxazoline group and 60-99.9% by weight of one or more other polymerizable monomers (b) copolymerizable with the polymerizable monomer (a), the sum total of the polymerizable monomers (a) and (b) being 100% by weight, in the presence of a water-soluble or water-dispersible emulsifier or emulsifiers selected from either one or both of the groups (P) and (Q) below: (P) polymers IIa having a terminal alkylthio group and an acid value of not less than 200 obtained by polymerizing a polymerizable monomer composition A containing an unsaturated carboxylic acid as an essential component thereof, in the presence of an alkylmercaptan B having 6-18 carbon atoms, or salts thereof; (Q) polymers IIb having a terminal alkylthio group and an acid value of not less than 200 obtained by polymerizing a polymerizable monomer composition A containing an unsaturated carboxylic acid as an essential component thereof, in the presence of an alkylmercaptan B having 6-18 carbon atoms, and further reacting the resulting polymer with at least one polymerizable monomer (c) having, within its molecular structure, a group reactive with a carboxyl group, or salts thereof.
Claim 3
Dependent Claim
260 words
An aqueous crosslinkable resin dispersion as claimed in claim 1, wherein the emulsifier or emulsifiers have a R 1 S-- group, wherein R 1 is a C 6-18 alkyl group, at one end of the molecular structure and a --H at the other end of the molecular structure and wherein the emulsifier or emulsifiers comprise repeating units of the formulas ##STR5## wherein R 2 -R 8 are, independently in each repeating unit, hydrogen, halogen, methyl, carboxyl, alkoxycarbonyl or COO - M + , wherein M + is an ammonium cation, an amine cation, an alkali metal cation or 1/2M1 + , where M1 + is an alkaline earth metal cation, X + is, independently in each repeating unit, an ammonium cation, an amine cation, an alkali metal cation or 1/2M1 + , where M1 + is an alkaline earth metal cation, Y is a group having a polymerizable unsaturated bond, Z is cyano, phenyl, substituted phenyl, amido, N-mono- or N,N-disubstituted amido, alkoxycarbonyl or a group of the formula --COO--(R 9 --O--) n H, where R 9 is C 2-4 alkylene and n is an integer of 1-50, said repeating units T, U, V and W being arranged in an optional order provided that the following numerical conditions are satisfied: the number of occurrences of T and the number of occurrences of U are each, independently, 0 or 1-500, with the total number of T and U occurrences being 1-500, the number of occurrences of V is 0 or 1-100 and the number of occurrences of W is 0 or 1-250.
Claim 4
Dependent Claim
137 words
An aqueous crosslinkable resin dispersion as claimed in claim 2, wherein the emulsifier or emulsifiers used have R 1 S-- at one end of their molecule and --H at the other and comprises repeating units of the formulas ##STR6## in which R 1 to R 8 , X, Y and Z are as defined above, said repeating units T, U, V and W being arranged in an optional order provided that the following numerical conditions are satisfied: that the number of occurrences of T and the number of occurrences of U are each 1 to 499, with a total number of occurrences of T and U of 2 to 500, that the number of occurrences of V is 0 or 1 to 100 and that the number of occurrences of W is 0 or 1 to 250.
Claim 5
Dependent Claim
42 words
An aqueous crosslinkable resin dispersion as claimed in claim 1, wherein the other polymerizable monomers (b) comprise at least one organosilane monomer having, within its molecule, a polymerizable unsaturated group and at least one hydrolyzable group directly bound to the silicon atom.
Claim 6
Dependent Claim
23 words
An aqueous, crosslinkable resin dispersion as claimed in claim 1, wherein a polymer selected from the group (Q) is used as the emulsifier.
Claim 7
Dependent Claim
37 words
An aqueous crosslinkable resin dispersion as claimed in claim 1, wherein the emulsifier or emulsifiers are used in an amount of 0.5 to 20 parts by weight per 100 parts by weight of the monomer composition [I].
Claim 8
Dependent Claim
28 words
An aqueous crosslinkable resin dispersion as claimed in claim 1, wherein the polymerizable monomer or monomers (a) are used in an amount of 0.5 to 20% by weight.
Claim 9
Independent Claim
228 words
A method of producing aqueous crosslinkable resin dispersions which comprises emulsion-polymerizing in an aqueous medium a monomer composition I composed of 0.1-40% by weight of at least one polymerizable monomer (a) having, within its molecule, a polymerizable double bond and an epoxy, aziridine or oxazoline group and 60-99.9% by weight of one or more other polymerizable monomers (b) copolymerizable with the polymerizable monomer (a), the sum total of the polymerizable monomers (a) and (b) being 100% by weight, in the presence of a water-soluble or water-dispersible emulsifier or emulsifiers selected from either one or both of the groups (P) and (Q) mentioned below: (P) Polymers IIa having a terminal alkylthio group and an acid value of not less than 200 obtained by polymerizing a polymerizable monomer composition A containing an unsaturated carboxylic acid as an essential component thereof in the presence of an alkylmercaptan B having 6 to 18 carbon atoms, or salts thereof; (Q) Polymers IIb having a terminal alkylthio group and an acid value of not less 200 obtained by polymerizing a polymerizable monomer composition A containing an unsaturated carboxylic acid as an essential component thereof in the presence of an alkylmercaptan B having 6 to 18 carbon atoms and further reacting the resulting polymer with at least one polymerizable monomer (c) having, within its molecule, a group reactive with a carboxyl group, or salts thereof.
Claim 10
Independent Claim
228 words
A method of producing aqueous crosslinkable resin dispersions which comprises emulsion-polymerizing in an aqueous medium a monomer composition I composed of 0.1-40% by weight of at least one polymerizable monomer (a) having, within its molecule, a polymerizable double bond and an epoxy, aziridine or oxazoline group and 60-99.9% by weight of one or more other polymerizable monomers (b) copolymerizable with the polymerizable monomer (a), the sum total of the polymerizable monomers (a) and (b) being 100% by weight, in the presence of a water-soluble or water-dispersible emulsifier or emulsifiers selected from either one or both of the groups (P) and (Q) mentioned below: (P) Polymers IIa having a terminal alkylthio group and an acid value of not less than 200 obtained by polymerizing a polymerizable monomer composition A containing an unsaturated carboxylic acid as an essential component thereof in the presence of an alkylmercaptan B having 6 to 18 carbon atoms, or salts thereof; (Q) Polymers IIb having a terminal alkylthio group and an acid value of not less 200 obtained by polymerizing a polymerizable monomer composition A containing an unsaturated carboxylic acid as an essential component thereof in the presence of an alkylmercaptan B having 6 to 18 carbon atoms and further reacting the resulting polymer with at least one polymerizable monomer (c) having, within its molecule, a group reactive with a carboxyl group, or salts thereof.
Claim 11
Dependent Claim
255 words
A method of producing aqueous crosslinkable resin dispersions as claimed in claim 8, wherein the emulsifier or emulsifiers used have R 1 S-- at one end of their molecule and --H at the other and comprises repeating units of the formulas ##STR7## in which R 1 to R 8 are, independently in each repeating unit, hydrogen, halogen, methyl, carboxyl, alkoxycarbonyl or COO - M + , wherein M + is an ammonium cation, an amine cation, an alkali metal cation or 1/2M1 + , where M1 + is an alkaline earth metal cation, X + is, independently in each repeating unit, an ammonium cation, an amine cation, an alkali metal cation or 1/2M1 + , where M1 + is an alkaline earth metal cation, Y is a group having a polymerizable unsaturated bond, Z is cyano, phenyl, substituted phenyl, amido, N-mono- or N,N-disubstituted amido, alkoxycarbonyl or a group of the formula --COO--(R 9 --O--) n H, where R 9 is C 2-4 alkylene and n is an integer of 1-50, said repeating units T, U, V and W being arranged in an optional order provided that the following numerical conditions are satisfied: that the number of occurrences of T and the number of occurrences of U are each independently 0 or 1 to 500, with a total number of occurrences of T and U of 1 to 500, that the number of occurrences of V is 0 or 1 to 100 and that the number of occurrences of W is 0 or 1 to 250.
Claim 12
Dependent Claim
252 words
A method of producing aqueous crosslinkable resin dispersions as claimed in claim 8, wherein the emulsifier or emulsifiers used have R 1 S-- at one end of their molecule and --H at the other and comprises repeating units of the formulas ##STR8## in which R 1 to R 8 are, independently in each repeating unit, hydrogen, halogen, methyl, carboxyl, alkoxycarbonyl or COO - M + , wherein M + is an ammonium cation, an amine cation, an alkali metal cation or 1/2M1 + , where M1 + is an alkaline earth metal cation, X + is, independently in each repeating unit, an ammonium cation, an amine cation, an alkali metal cation or 1/2M1 + , where M1 + is an alkaline earth metal cation, Y is a group having a polymerizable unsaturated bond, Z is cyano, phenyl, substituted phenyl, amido, N-mono- or N,N-disubstituted amido, alkoxycarbonyl or a group of the formula --COO--(R 9 --O--) n H, where R 9 is C 2-4 alkylene and n is an integer of 1-50, said repeating units T, U, V and W being arranged in an optional order provided that the following numerical conditions are satisfied: that the number of occurrences of t and the number of occurrences of U are each 1 to 499, with a total number of occurrences of T and U of 2 to 500, that the number of occurrences of V is 0 or 1 to 100 and that the number of occurrences of W is 0 or 1 to 250.
Claim 13
Dependent Claim
51 words
A method of producing aqueous crosslinkable resin dispersions as claimed in claim 8, wherein the monomer composition I is divided into two or more portions differing in composition from one another and these portions are fed in sequence, so that the polymerization is carried out in the manner of multistep polymerization.
Claim 14
Dependent Claim
34 words
A method of producing aqueous crosslinkable resin dispersions as claimed in claim 1, wherein at least two of the divided portions differ in the content of polymerizable monomer or monomers (a) from each other.
Claim 15
Dependent Claim
28 words
A method of producing aqueous crosslinkable resin dispersions as claimed in claim 11, wherein at least one of the divided portions does not contain any polymerizable monomers (a).
Claim 16
Dependent Claim
33 words
A method of producing aqueous crosslinkable resin dispersions as claimed in claim 13, wherein the divided portion which does not contain any polymerizable monomers (a) is subjected to polymerization in the last step.
Claim 17
Dependent Claim
47 words
An aqueous composition which comprises 100 parts by weight (on the solids basis) of an aqueous crosslinkable resin dispersion as claimed in claim 1 and 1 to 200 parts by weight of a metal oxide or metal hydroxide or mixture thereof in the form of fine particles.
Claim 18
Dependent Claim
47 words
An aqueous composition which comprises 100 parts by weight (on the solids basis) of an aqueous crosslinkable resin dispersion as claimed in claim 4 and 1 to 200 parts by weight of a metal oxide or metal hydroxide or mixture thereof in the form of fine particles.
Claim 19
Dependent Claim
28 words
An aqueous composition as claimed in claim 16, wherein the metal oxide or metal hydroxide or mixture thereof in the form of fine particles is aqueous colloidal silica.
Claim 20
Dependent Claim
36 words
An aqueous resin composition which comprises 100 parts by weight (on the solids basis) of an aqueous crosslinkable resin dispersion as claimed in claim 1 and 0.001 to 100 parts by weight of a water-soluble resin.
Claim 21
Dependent Claim
16 words
An aqueous resin composition as claimed in claim 18, wherein the water-soluble resin is polyvinyl alcohol.
Claim 22
Dependent Claim
25 words
An aqueous resin composition as claimed in claim 19, wherein the aqueous resin dispersion is obtained by emulsion polymerization in the presence of polyvinyl alcohol.
Claim 23
Dependent Claim
29 words
An aqueous resin composition as claimed in claim 19 as obtained by reacting the aqueous crosslinkable resin dispersion and polyvinyl alcohol in the presence of a radical polymerization catalyst.
Claim 24
Dependent Claim
55 words
A water-dispersible composition which comprises 100 parts by weight (on the solids basis) of an aqueous crosslinkable resin dispersion as claimed in claim 1, 1-200 parts by weight, of a metal oxide or metal hydroxide or mixture thereof in the form of fine particles and 0.001 to 100 parts by weight of a water-soluble resin.
Claim 25
Dependent Claim
15 words
A coating composition which contains an aqueous crosslinkable resin dispersion as claimed in claim 1.
Claim 26
Dependent Claim
26 words
A coating composition as claimed in claim 23, which further contains a metal oxide or metal hydroxide or mixture thereof in the form of fine particles.
Claim 27
Dependent Claim
28 words
A coating composition as claimed in claim 24, wherein the metal oxide or metal hydroxide or mixture thereof in the form of fine particles is aqueous colloidal silica.
Claim 28
Dependent Claim
14 words
A coating composition as claimed in claim 25, which further contains a water-soluble resin.
Claim 29
Dependent Claim
15 words
A coating composition as claimed in claim 26, wherein the water-soluble resin is polyvinyl alcohol.
Claim 30
Dependent Claim
25 words
A coating composition as claimed in claim 26, which further contains a metal oxide or metal hydroxide or mixture in the form of fine particles.
Claim 31
Dependent Claim
15 words
A coating composition which comprises an aqueous crosslinkable resin dispersion as claimed in claim 4.
Claim 32
Dependent Claim
14 words
A coating composition as claimed in claim 29, which further contains a crosslinking agent.
Claim 33
Dependent Claim
13 words
A coating composition as claimed in claim 30, which further contains a filler.
Claim 34
Dependent Claim
14 words
An adhesive which contains an aqueous crosslinkable resin dispersion as claimed in claim 1.
Claim 35
Dependent Claim
25 words
An adhesive as claimed in claim 32, which further contains a metal oxide or metal hydroxide or mixture thereof in the form of fine particles.
Claim 36
Dependent Claim
24 words
An adhesive as claimed in claim 33, wherein the metal oxide and/or metal hydroxide in the form of fine particles is aqueous colloidal silica.
Claim 37
Dependent Claim
13 words
An adhesive as claimed in claim 34, which further contains a water-soluble resin.
Claim 38
Dependent Claim
14 words
An adhesive as claimed in claim 35, wherein the water-soluble resin is polyvinyl alcohol.
Claim 39
Dependent Claim
25 words
An adhesive as claimed in claim 35, which further contains a metal oxide or metal hydroxide or mixture thereof in the form of fine particles.
Claim 40
Dependent Claim
34 words
An adhesive as claimed in any one of claims 32-37, wherein the polymer obtained by polymerizing the monomer composition I has a glass transition temperature within the range of -80° C. to 0° C.
Claim 41
Dependent Claim
25 words
A coating composition for heat-sensitive color-developing layer formation which contains an aqueous crosslinkable resion dispersion as claimed in claim 1 together with heat-sensitive color-developing components.
Claim 42
Dependent Claim
31 words
A coating composition for heat-sensitive color-developing layer formation as claimed in claim 39, which further contains a metal oxide or metal hydroxide or mixture thereof in the form of fine particles.
Claim 43
Dependent Claim
33 words
A coating composition for heat-sensitive color-developing layer formation as claimed in claim 40, wherein the metal oxide or metal hydroxide or mixture thereof in the form of fine particles is aqueous colloidal silica.
Claim 44
Dependent Claim
18 words
coating composition for heat-sensitive color-developing layer formation as claimed in claim 41, which further contains a water-soluble resin.
Claim 45
Dependent Claim
20 words
A coating composition for heat-sensitive color-developing layer formation as claimed in claim 42, wherein the water-soluble resin is polyvinyl alcohol.
Claim 46
Dependent Claim
33 words
A coating composition for heat-sensitive color-developing layer formation as claimed in claim 42 or 43, which further contains a metal oxide or metal hydroxide or mixture thereof in the form of fine particles.
Claim 47
Dependent Claim
25 words
A coating composition for pressure-sensitive color-developing layer formation which contains an aqueous crosslinkable resin dispersion as claimed in claim 1 together with pressure-sensitive color-developing components.
References Cited (Backward Citations)
GB1146582A
Cited
JPS5310683A
Cited
US4427819A
Cited
US4431768A
Cited
US4617343A
Cited
US4885320A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-02-07 | 1997-08-09 | 1998-02-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-02-07 | 2001-08-09 | 2002-02-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-02-07 | 2005-08-09 | 2006-02-08 | $7700.00 | Window Closed / Lapsed |