Manufacturing method for solid-electrolyte fuel cell
Assignee: Honda Motor Co Ltd
•
Filing: 1991-12-09
•
Granted: 1994-03-01
•
Expires: 2011-12-09
Abstract
Abstract This invention relates to a manufacturing method for a solid-electrolyte fuel cell having a three-layer structure and equipped with a fuel-electrode and an air-electrode for its electrodes with a solid-electrolyte sandwiched between them. A mold (4) comprising a material having a property to suck a specified solvent is used. A slurry is made up by mixing a solid-electrolyte powder and an electrode powder to the same solvent as the above specified solvent, and the slurry is poured in turn in the mold to form an electrolyte green body (5) and electrode green bodies (6) and (7). Thereby, a solid-electrolyte fuel cell including no crack and peeling-off in each layer can be obtained easily and inexpensively.
Inventors
- 👤 Ryoichi Okuyama
- 👤 Eiichi Nomura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 01:09
CPC Classifications
H; H01; H01M; H01M8/00; H01M8/10; H01M8/12; H01M8/1233; H01M8/1231; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y02P; Y02P70/00; Y02P70/50; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49108; Y10T29/49115
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
158 words
A method for manufacturing a solid-electrolyte fuel cell equipped with a fuel-electrode and an air-electrode for its electrodes with a solid-electrolyte sandwiched between said electrodes; said method comprising the steps of pouring a first slurry into a concave portion of a mold composed of a material having a property for sucking a specified liquid and forming an electrolyte green body, said first slurry being a mixture of a solid-electrolyte powder and said specified liquid, pouring a second slurry into said concave portion and forming an electrode green body on said electrolyte green body and forming a multi-layer green body integrated with said electrolyte green body, said second slurry being a mixture of an electrode powder and said specified liquid, and removing said multi-layer green body from said mold and sintering said removed multi-layer green body; said electrode green body formed in said concave portion being one or both of a fuel-electrode green body and an air-electrode green body.
Claim 2
Independent Claim
158 words
A method for manufacturing a solid-electrolyte fuel cell equipped with a fuel-electrode and an air-electrode for its electrodes with a solid-electrolyte sandwiched between said electrodes; said method comprising the steps of pouring a first slurry into a concave portion of a mold composed of a material having a property for sucking a specified liquid and forming an electrolyte green body, said first slurry being a mixture of a solid-electrolyte powder and said specified liquid, pouring a second slurry into said concave portion and forming an electrode green body on said electrolyte green body and forming a multi-layer green body integrated with said electrolyte green body, said second slurry being a mixture of an electrode powder and said specified liquid, and removing said multi-layer green body from said mold and sintering said removed multi-layer green body; said electrode green body formed in said concave portion being one or both of a fuel-electrode green body and an air-electrode green body.
Claim 3
Independent Claim
183 words
A method for manufacturing a solid-electrolyte fuel cell equipped with a fuel-electrode and an air-electrode for its electrodes with a solid-electrolyte sandwiched between said electrodes; said method comprising the steps of pouring a first slurry into a concave portion of a mold composed of a material having a property for sucking a specified liquid and forming an electrolyte green body, said first slurry being a mixture of a solid-electrolyte powder and said specified liquid, pouring a second slurry onto said electrolyte green body in said concave portion of said mold and forming a selected one of a fuel-electrode green body and an air-electrode green body and forming a double-layer green body integrated with said electrolyte green body, said second slurry being a mixture of said selected one of said fuel-electrode powder and said air-electrode powder with said specified liquid, and removing said double-layer green body from said mold and sintering said removed double-layer green body and forming an electrolyte-electrode composite, and forming a coating of the other of said selected said fuel-electrode and said air-electrode on the electrolyte side of said electrolyte-electrode composite.
Claim 4
Independent Claim
183 words
A method for manufacturing a solid-electrolyte fuel cell equipped with a fuel-electrode and an air-electrode for its electrodes with a solid-electrolyte sandwiched between said electrodes; said method comprising the steps of pouring a first slurry into a concave portion of a mold composed of a material having a property for sucking a specified liquid and forming an electrolyte green body, said first slurry being a mixture of a solid-electrolyte powder and said specified liquid, pouring a second slurry onto said electrolyte green body in said concave portion of said mold and forming a selected one of a fuel-electrode green body and an air-electrode green body and forming a double-layer green body integrated with said electrolyte green body, said second slurry being a mixture of said selected one of said fuel-electrode powder and said air-electrode powder with said specified liquid, and removing said double-layer green body from said mold and sintering said removed double-layer green body and forming an electrolyte-electrode composite, and forming a coating of the other of said selected said fuel-electrode and said air-electrode on the electrolyte side of said electrolyte-electrode composite.
Claim 5
Dependent Claim
35 words
A method for manufacturing solid-electrolyte fuel cell as set forth in claim 2, in which said fuel-electrode green body is formed in said second slurry pouring and said air-electrode is formed in forming said coating.
Claim 6
Dependent Claim
36 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2, in which said air-electrode green body is formed in said second slurry pouring and said fuel-electrode is formed in forming said coating.
Claim 7
Dependent Claim
131 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2, in which said first slurry is poured into said concave portion of said mold after a water resistant and water repellent member is installed on a part of an inside surface of said concave portion of said mold, said pouring of said slurry second is carried out after said water resistant and water repellent member is removed to expose a part of said selected one of said fuel-electrode green body and said air-electrode green body from the electrolyte green body and an interconnector port is formed on said exposed part when said electrolyte-electrode composite is formed an said other of said selected fuel-electrode and air-electrode is formed when said coating is formed, while avoiding said interconnector part.
Claim 8
Dependent Claim
136 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2, in which: prior to said pouring of said second slurry, an open mold having a through hole provided with the same shape as an opening of the concave portion of said mold and a size at least equal to a size of said opening, is positioned on said mold with said through hole in axial alignment with said concave portion, and said second slurry is poured up to the through hole to leave exposed a part of one of the fuel-electrode green body or the air-electrode green body from the electrolyte green body; thereafter said green body is removed from said mold; and said coating of said other of said selected fuel-electrode and said air-electrode is formed while avoiding said exposed part.
Claim 9
Dependent Claim
70 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 5, in which said interconnector part is formed so that a slurry including LaCrO 3 or CoCr 2 O 4 is applied onto the exposed part of said selected one of said fuel-electrode green body and said air-electrode green body exposed from the electrolyte green body, and said green body and said interconnector part are then sintered.
Claim 10
Independent Claim
192 words
A method for manufacturing a solid-electrolyte fuel cell equipped with a fuel-electrode and an air-electrode for its electrodes with a solid-electrolyte sandwiched between said electrodes; said method comprising the steps of pouring a first slurry into a concave portion of a mold composed of a material having a property for sucking a specified liquid for forming a selected one of a fuel-electrode green body and an air-electrode green body, said first slurry being a mixture of a selected one of a fuel-electrode powder and an air-electrode powder and said specified liquid, pouring a second slurry onto said green body made up in said pouring of said first slurry and forming an electrolyte green body integrated with said green body made up in said first slurry pouring and forming a double-layer green body, said second slurry being made up of a mixture of a solid-electrolyte powder and said specified liquid, removing said double-layer green body from said mold and sintered said removed double-layer green body and forming an electrolyte-electrode composite, and forming a coating of the other of said selected said fuel-electrode and said air-electrode on the electrolyte side of said electrolyte-electrode composite.
Claim 11
Independent Claim
192 words
A method for manufacturing a solid-electrolyte fuel cell equipped with a fuel-electrode and an air-electrode for its electrodes with a solid-electrolyte sandwiched between said electrodes; said method comprising the steps of pouring a first slurry into a concave portion of a mold composed of a material having a property for sucking a specified liquid for forming a selected one of a fuel-electrode green body and an air-electrode green body, said first slurry being a mixture of a selected one of a fuel-electrode powder and an air-electrode powder and said specified liquid, pouring a second slurry onto said green body made up in said pouring of said first slurry and forming an electrolyte green body integrated with said green body made up in said first slurry pouring and forming a double-layer green body, said second slurry being made up of a mixture of a solid-electrolyte powder and said specified liquid, removing said double-layer green body from said mold and sintered said removed double-layer green body and forming an electrolyte-electrode composite, and forming a coating of the other of said selected said fuel-electrode and said air-electrode on the electrolyte side of said electrolyte-electrode composite.
Claim 12
Dependent Claim
36 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 8, in which said fuel-electrode green body is formed in said first slurry pouring and said air-electrode is formed in forming said coating.
Claim 13
Dependent Claim
36 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 8, in which said air-electrode green body is formed in said first slurry pouring and said fuel-electrode is formed in forming said coating.
Claim 14
Dependent Claim
32 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2 or claim 8, in which said fuel-electrode is formed by using Ni-ZrO 2 cermet or Co-ZrO 2 cermet.
Claim 15
Independent Claim
207 words
A method for manufacturing a solid-electrolyte fuel cell equipped with a fuel-electrode and an air-electrode for its electrodes with a solid-electrolyte sandwiched between said electrodes; said method comprising the steps of pouring a first slurry into a concave portion of a mold composed of a material having a property for sucking a specified liquid and forming a first green body, said first slurry being a mixture of a powder selected from one of a fuel-electrode powder and an air-electrode powder with said specified liquid, pouring a second slurry onto said first green body formed in said concave portion of said mold and forming a second green body on said first green body in said mold, said second slurry being a mixture of a solid-electrolyte powder and said specified liquid, pouring a third slurry onto said second green body formed in said concave portion of said mold and forming a third green body on said first and second green bodies in said mold, said third slurry being a mixture of a powder selected from the other of said fuel-electrode powder and said air-electrode powder with said specified liquid, and removing said three-layer green body from said mold and sintering said three-layer green body and forming an electrolyte-electrode composite.
Claim 16
Independent Claim
207 words
A method for manufacturing a solid-electrolyte fuel cell equipped with a fuel-electrode and an air-electrode for its electrodes with a solid-electrolyte sandwiched between said electrodes; said method comprising the steps of pouring a first slurry into a concave portion of a mold composed of a material having a property for sucking a specified liquid and forming a first green body, said first slurry being a mixture of a powder selected from one of a fuel-electrode powder and an air-electrode powder with said specified liquid, pouring a second slurry onto said first green body formed in said concave portion of said mold and forming a second green body on said first green body in said mold, said second slurry being a mixture of a solid-electrolyte powder and said specified liquid, pouring a third slurry onto said second green body formed in said concave portion of said mold and forming a third green body on said first and second green bodies in said mold, said third slurry being a mixture of a powder selected from the other of said fuel-electrode powder and said air-electrode powder with said specified liquid, and removing said three-layer green body from said mold and sintering said three-layer green body and forming an electrolyte-electrode composite.
Claim 17
Dependent Claim
37 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 12, in which a fuel-electrode green body is formed with said first slurry, and an air-electrode green body is formed with said third slurry.
Claim 18
Dependent Claim
38 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 12, in which an air-electrode green body is formed with said first slurry, and a fuel-electrode green body is formed in with said third slurry.
Claim 19
Dependent Claim
36 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2, claim 8 or claim 12, in which said specified liquid is water, and said mold comprises a material having a water absorptivity.
Claim 20
Dependent Claim
47 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2, claim 8 or claim 12, in which said specified liquid is an organic solvent evaporated more quickly than water, and said mold comprises a material having a property for sucking said organic solvent.
Claim 21
Dependent Claim
22 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 16, in which said organic solvent is ethyl alcohol.
Claim 22
Dependent Claim
63 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2, claim 8 or claim 12, in which relative shrinkage factor of said electrolyte green body and shrinkage factors of said formed fuel-electrode green body and said air-electrode green body, are reversed midway and at the final sintering as sintering temperature is gradually raised to a specified value during sintering.
Claim 23
Dependent Claim
30 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 18, in which temperature at a final stage of sintering is from 1,200° C. to 1,600° C.
Claim 24
Dependent Claim
63 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2, claim 8 or claim 12, in which material selected from carbon powder and an organic powder, difficult to be dissolved in said specified liquid is mixed in the slurry including the fuel-electrode powder slurry and the air-electrode powder slurry, and sintering is carried out under an atmosphere including oxygen.
Claim 25
Dependent Claim
37 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 20, in which said organic powder is selected from one or more of teflon powder, vinyl chloride powder, nylon powder and an acrylic powder.
Claim 26
Dependent Claim
45 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2, claim 8 or claim 12, in which a porous high-molecular film is previously installed on an inside surface of said concave portion of said mold before said first slurry is poured.
Claim 27
Dependent Claim
37 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 22, in which said porous high-molecular film comprises a cellulose-based resin, a teflon-based resin, a polyvinyl-based resin, a nylon-based resin or a polyamide-based resin.
Claim 28
Dependent Claim
52 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2, claim 8 or claim 12, in which said solid-electrolyte powder is a zirconia powder containing a stabilizer and comprising one or a mixture of a stabilized zirconia, a cubic zirconia, a tetragonal zirconia or a partial stabilized zirconia.
Claim 29
Dependent Claim
32 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 24, in which said stabilizer is yttrium oxide, calcium oxide, scandium oxide, ytterbium oxide, neodymium oxide or gadolinium oxide.
Claim 30
Dependent Claim
50 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2, claim 8 or claim 12, in which said fuel-electrode powder is a powder of metal or metal oxide, said metal being nickel or cobalt, and said metal oxide being a nickel oxide or a cobalt oxide.
Claim 31
Dependent Claim
54 words
A method for manufacturing a solid-electrolyte fuel cell as set forth in claim 2, claim 8 or claim 12, in which said air-electrode powder is a powder of complex oxide of perovskite, and said complex oxide is LaMnO 3 , LaCoO 3 , or CaMnO 3 added with rare earth or alkaline earth metals.
References Cited (Backward Citations)
GB1048839A
Cited
US3377203A
Cited
JPS4976038A
Cited
US3843400A
Cited
EP0134136A2
Cited
US4782392A
Cited
JPS61216258A
Cited
JPS62268063A
Cited
JPS647475A
Cited
JPH0193065A
Cited
JPH01110904A
Cited
US4957673A
Cited
JPH0381972A
Cited
JPH03101065A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-02-28 | 1997-08-30 | 1998-03-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-02-28 | 2001-08-30 | 2002-03-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-02-28 | 2005-08-30 | 2006-03-01 | $7700.00 | Window Closed / Lapsed |