Resin composition for forming plated layer and use thereof
Assignee: Mitsui Chemicals Inc
•
Filing: 1993-10-20
•
Granted: 1994-06-28
•
Expires: 2013-10-20
Abstract
Abstract The resin composition for forming plated layer disclosed herein comprises a polyamide composed of a dicarboxylic acid component recuring unit and a recurring unit derived from a diamine component unit having an alkylene group of 4 to 25 carbon atoms and at least one inorganic filler. There are also disclosed the resin molded article having plated layer formed thereon, the electromagnetic wave shielding material, the decorative resin molded article and the connecting material produced by forming plated layer on the surfaces of the resin molded articles formed from said resin composition. Further, there is disclosed the printed circuit board produced by forming selectively metallized layer in wiring circuit portion on the surface of the resin molded article formed from said resin composition and the method for plating to form these articles having the layer plated thereon.
Inventors
- 👤 Fumitoshi Ikejiri
- 👤 Sanehiro Yamamoto
- 👤 Keiji Kawamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 11:34
CPC Classifications
H; H05; H05K; H05K9/00; H05K9/0073; H05K9/0081; H05K9/0083; C; C08; C08K; C08K3/00; C08K3/01; C08K3/013; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/032; H05K1/0346
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
179 words
A resin molded article for forming plated layer comprising a chromic acid surface etched resin molded article from a resin composition comprising (i) a polyamide comprising (a) a dicarboxylic acid component recurring unit comprising a dicarboxylic acid component unit consisting of 30 to 100 mole % of terephthalic acid component unit and 0 to 40 mole % of an aromatic dicarboxylic acid component unit other than terephthalic acid and/or 0 to 70 mole % of an aliphatic dicarboxylic acid component unit having an alkylene group of 4 to 20 carbon atoms and (b) a diamine component recurring unit comprising an alkylene diamine component unit having an alkylene group of 4 to 25 carbon atoms, said polyamide having a melting point of at least 280° C.; (ii) 5 to 100 parts by weight, per 100 parts by weight of said polyamide, of at least one material selected from the group consisting of alkaline earth metal carbonate and alkaline earth metal oxide; and (iii) 5 to 200 parts by weight, per 100 parts by weight of said polyamide, of glass fiber.
Claim 2
Dependent Claim
179 words
A resin molded article for forming plated layer comprising a chromic acid surface etched resin molded article from a resin composition comprising (i) a polyamide comprising (a) a dicarboxylic acid component recurring unit comprising a dicarboxylic acid component unit consisting of 30 to 100 mole % of terephthalic acid component unit and 0 to 40 mole % of an aromatic dicarboxylic acid component unit other than terephthalic acid and/or 0 to 70 mole % of an aliphatic dicarboxylic acid component unit having an alkylene group of 4 to 20 carbon atoms and (b) a diamine component recurring unit comprising an alkylene diamine component unit having an alkylene group of 4 to 25 carbon atoms, said polyamide having a melting point of at least 280° C.; (ii) 5 to 100 parts by weight, per 100 parts by weight of said polyamide, of at least one material selected from the group consisting of alkaline earth metal carbonate and alkaline earth metal oxide; and (iii) 5 to 200 parts by weight, per 100 parts by weight of said polyamide, of glass fiber.
Claim 3
Dependent Claim
25 words
The resin molded article according to claim 1, wherein said polyamide has a glass transition temperature in the amorphous portion of at least 70° C.
Claim 4
Dependent Claim
26 words
The resin molded article according to claim 1, wherein said polyamide has an intrinsic viscosity, as measured in concentrated sulfuric acid, of 0.5 to 3.0 dl/g.
Claim 5
Dependent Claim
24 words
The resin molded article according to claim 1, wherein said alkylene group of said aliphatic dicarboxylic acid component has 6 to 12 carbon atoms.
Claim 6
Dependent Claim
23 words
The resin molded article according to claim 1, wherein said alkylene group of said alkylene diamine component has 6 to 18 carbon atoms.
Claim 7
Dependent Claim
22 words
The resin molded article according to claim 1, wherein said alkylene group of said alkylene diamine component is a straight-chain aliphatic group.
Claim 8
Dependent Claim
22 words
The resin molded article according to claim 1, wherein said alkylene group of said alkylene diamine component is a cyclic aliphatic group.
Claim 9
Dependent Claim
20 words
The resin molded article according to claim 1, wherein said polyamide has a melting point of 290° to 340° C.
Claim 10
Dependent Claim
27 words
The resin molded article according to claim 1, wherein said at least one material (ii) is granular with an average particle diameter of 0.1 to 200 μm.
Claim 11
Dependent Claim
28 words
The resin molded article according to claim 1, wherein said glass fiber has a length of 0.1 to 20 mm and an aspect ratio of 10 to 2,000.
Claim 12
Dependent Claim
56 words
The resin molded article according to claim 1, wherein said dicarboxylic acid component unit consists of 60 to 100 mole % of said terephthalic acid component unit, 0 to 40 mole % of said aromatic dicarboxylic acid component unit other than terephthalic acid and 0 to 40 mole % of said aliphatic dicarboxylic acid component unit.
Claim 13
Dependent Claim
38 words
The resin molded article according to claim 1, wherein said dicarboxylic acid component recurring unit further comprises 0 to 5 mole % of a polycarboxylic acid component unit consisting of polycarboxylic acids having at least three carboxyl groups.
Claim 14
Dependent Claim
21 words
The resin molded article according to claim 1, wherein said polyamide comprises at least 50% by weight of said resin composition.
Claim 15
Dependent Claim
35 words
The resin molded article according to claim 1, wherein said at least one material (ii) is present in an amount of 5 to 40 parts by weight, per 100 parts by weight of said polyamide.
Claim 16
Dependent Claim
33 words
The resin molded article according to claim 1, wherein said glass fibers (iii) are present in an amount of 5 to 150 parts by weight, per 100 parts by weight of said polyamide.
Claim 17
Dependent Claim
18 words
The resin molded article according to claim 1, wherein said at least one material (ii) is magnesium oxide.
Claim 18
Dependent Claim
18 words
The resin molded article according to claim 1, wherein said at least one material (ii) is calcium carbonate.
Claim 19
Dependent Claim
202 words
A resin molded article for forming plated layer produced by the process comprising: providing a resin molded article from a resin composition comprising (i) a polyamide comprising (a) a dicarboxylic acid component recurring unit comprising a dicarboxylic acid component unit consisting of 30 to 100 mole % of terephthalic acid component unit and 0 to 40 mole % of an aromatic dicarboxylic acid component unit other than terephthalic acid and/or 0 to 70 mole % of an aliphatic dicarboxylic acid component unit having an alkylene group of 4 to 20 carbon atoms and (b) a diamine component recurring unit comprising an alkylene diamine component unit comprising an alkylene diamine component unit having an alkylene group of 4 to 25 carbon atoms, said polyamide having a melting point of at least 280° C., (ii) 5 to 100 parts by weight, per 100 parts by weight of said polyamide, of at least one material selected from the group consisting of alkaline earth metal carbonate and alkaline earth metal oxide and (iii) 5 to 200 parts by weight, per 100 parts by weight of said polyamide, of glass fiber; and etching a surface of said resin molded article with an acidic solution of chromic acid.
Claim 20
Dependent Claim
202 words
A resin molded article for forming plated layer produced by the process comprising: providing a resin molded article from a resin composition comprising (i) a polyamide comprising (a) a dicarboxylic acid component recurring unit comprising a dicarboxylic acid component unit consisting of 30 to 100 mole % of terephthalic acid component unit and 0 to 40 mole % of an aromatic dicarboxylic acid component unit other than terephthalic acid and/or 0 to 70 mole % of an aliphatic dicarboxylic acid component unit having an alkylene group of 4 to 20 carbon atoms and (b) a diamine component recurring unit comprising an alkylene diamine component unit comprising an alkylene diamine component unit having an alkylene group of 4 to 25 carbon atoms, said polyamide having a melting point of at least 280° C., (ii) 5 to 100 parts by weight, per 100 parts by weight of said polyamide, of at least one material selected from the group consisting of alkaline earth metal carbonate and alkaline earth metal oxide and (iii) 5 to 200 parts by weight, per 100 parts by weight of said polyamide, of glass fiber; and etching a surface of said resin molded article with an acidic solution of chromic acid.
References Cited (Backward Citations)
US3962524A
Cited
EP0121984A2
Cited
US4552626A
Cited
EP0291833A1
Cited
US4948868A
Cited
EP0394029A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-06-27 | 1997-12-27 | 1998-06-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-06-27 | 2001-12-27 | 2002-06-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-06-27 | 2005-12-27 | 2006-06-28 | $7700.00 | Window Closed / Lapsed |