Formation of vertical polysilicon resistor having a nitride sidewall for small static RAM cell
Assignee: GlobalFoundries Singapore Pte Ltd
•
Filing: 1992-12-31
•
Granted: 1994-07-19
•
Expires: 2012-12-31
Abstract
Abstract A new method of forming a polysilicon resistor is achieved. Polysilicon gate structures and source/drain regions are formed in and on a semiconductor substrate. A passivation layer is formed overlying the gate structures. A contact window is opened to the drain portion of the source/drain region. A resistor is formed within the contact window as follows. A nitride layer is deposited over the passivation layer and within the contact window. The nitride layer is etched back to form nitride sidewalls within the contact window. A layer of polysilicon is deposited over the passivation layer and within the contact window. The polysilicon layer is etched back to leave the polysilicon only within the contact opening completing formation of the resistor. A second contact window is opened to the source portion of the source/drain region. A barrier metal layer is deposited over the passivation layer, over the resistor, and within the second contact window. A metal layer is deposited over the barrier metal layer and the metal interconnection of the integrated circuit is completed.
Inventors
- 👤 Keh-Fei C. Chi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:37
CPC Classifications
H; H10; H10D; H10D1/00; H10D1/40; H10D1/47; H10B; H10B10/00; H10B10/15
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
227 words
A method for fabricating an integrated circuit having a vertical resistor directly connected to a drain region comprising: providing polysilicon gate structures and source/drain regions in and on a semiconductor substrate; forming a refractory metal silicide layer over said source/drain regions; forming a passivation layer overlying said gate structures; opening a contact window through said passivation layer to the drain portion of said source/drain region; forming a resistor within said contact window comprising: depositing a silicon nitride layer over said passivation layer and within said contact window; anisotropically etching back said nitride layer to form nitride sidewalls within said contact window to prevent migration of any impurities from said passivation layer into said planned vertical resistor; depositing a layer of polysilicon over said passivation layer and within said contact window; anisotropically etching back said polysilicon to leave said polysilicon only within said contact opening; and ion implanting said polysilicon layer within said contact window with sufficient ions to provide said resistor and completing formation of said resistor and simultaneously ion implanting impurities into said passivation layer; opening second contact window through said passivation layer to source portion of said source/drain region; depositing barrier metal layer electrically contacting and over said passivation layer, over said resistor, and within said second contact window; depositing metal layer over said barrier metal layer; and completing metal interconnection of said integrated circuit.
Claim 2
Independent Claim
227 words
A method for fabricating an integrated circuit having a vertical resistor directly connected to a drain region comprising: providing polysilicon gate structures and source/drain regions in and on a semiconductor substrate; forming a refractory metal silicide layer over said source/drain regions; forming a passivation layer overlying said gate structures; opening a contact window through said passivation layer to the drain portion of said source/drain region; forming a resistor within said contact window comprising: depositing a silicon nitride layer over said passivation layer and within said contact window; anisotropically etching back said nitride layer to form nitride sidewalls within said contact window to prevent migration of any impurities from said passivation layer into said planned vertical resistor; depositing a layer of polysilicon over said passivation layer and within said contact window; anisotropically etching back said polysilicon to leave said polysilicon only within said contact opening; and ion implanting said polysilicon layer within said contact window with sufficient ions to provide said resistor and completing formation of said resistor and simultaneously ion implanting impurities into said passivation layer; opening second contact window through said passivation layer to source portion of said source/drain region; depositing barrier metal layer electrically contacting and over said passivation layer, over said resistor, and within said second contact window; depositing metal layer over said barrier metal layer; and completing metal interconnection of said integrated circuit.
Claim 3
Dependent Claim
30 words
The method of claim 1 wherein said refractory metal silicide layer overlying said source/drain regions is composed of TiSi 2 and is between about 400 to 1000 Angstroms in thickness.
Claim 4
Dependent Claim
27 words
The method of claim 1 wherein said polysilicon layer is deposited by low pressure chemical vapor deposition to a thickness of between about 5000 to 7000 Angstroms.
Claim 5
Dependent Claim
37 words
The method of claim 1 wherein said polysilicon layer within said contact opening is ion implanted with boron ions with a dosage of between 5E12 and 5E13 ions/cm 2 and energy of between 80 and 150 KEV.
Claim 6
Dependent Claim
25 words
The method of claim 1 wherein said barrier metal layer is composed of TiW and has a thickness of between about 400 to 1200 Angstroms.
Claim 7
Dependent Claim
25 words
The method of claim 1 wherein said barrier metal layer is composed of TiN and has a thickness of between about 400 to 1200 Angstroms.
Claim 8
Independent Claim
222 words
A method for fabricating an integrated circuit having a vertical resistor directly connected to a drain region comprising: providing polysilicon gate structures and source/drain regions in and on a semiconductor substrate; forming a refractory metal silicide layer over said source/drain regions; forming a passivation layer having dopant impurity material therein overlying said gate structures; opening a contact window through said passivation layer to the drain portion of said source/drain region; forming a resistor within said contact window comprising: depositing a silicon nitride layer over said passivation layer and within said contact window; anisotropically etching back said nitride layer to form nitride sidewalls within said contact window to prevent migration of any impurities from said passivation layer into said planned vertical resistor; depositing a layer of polysilicon over said passivation layer and within said contact window; ion implanting said polysilicon layer with sufficient ions to provide said resistor within said contact window; and anisotropically etching back said polysilicon to leave said polysilicon only within said contact opening completing formation of said resistor; opening second contact window through said passivation layer to source portion of said source/drain region; depositing barrier metal layer electrically contacting and over said passivation layer, over said resistor, and within said second contact window; depositing metal layer over said barrier metal layer; and completing metal interconnection of said integrated circuit.
Claim 9
Independent Claim
222 words
A method for fabricating an integrated circuit having a vertical resistor directly connected to a drain region comprising: providing polysilicon gate structures and source/drain regions in and on a semiconductor substrate; forming a refractory metal silicide layer over said source/drain regions; forming a passivation layer having dopant impurity material therein overlying said gate structures; opening a contact window through said passivation layer to the drain portion of said source/drain region; forming a resistor within said contact window comprising: depositing a silicon nitride layer over said passivation layer and within said contact window; anisotropically etching back said nitride layer to form nitride sidewalls within said contact window to prevent migration of any impurities from said passivation layer into said planned vertical resistor; depositing a layer of polysilicon over said passivation layer and within said contact window; ion implanting said polysilicon layer with sufficient ions to provide said resistor within said contact window; and anisotropically etching back said polysilicon to leave said polysilicon only within said contact opening completing formation of said resistor; opening second contact window through said passivation layer to source portion of said source/drain region; depositing barrier metal layer electrically contacting and over said passivation layer, over said resistor, and within said second contact window; depositing metal layer over said barrier metal layer; and completing metal interconnection of said integrated circuit.
Claim 10
Dependent Claim
30 words
The method of claim 7 wherein said refractory metal silicide layer overlying said source/drain regions is composed of TiSi 2 and is between about 400 to 1000 Angstroms in thickness.
Claim 11
Dependent Claim
27 words
The method of claim 7 wherein said polysilicon layer is deposited by low pressure chemical vapor deposition to a thickness of between about 5000 to 7000 Angstroms.
Claim 12
Dependent Claim
33 words
The method of claim 7 wherein said polysilicon layer is ion implanted with boron ions with a dosage of between 5E12 and 5E13 ions/cm 2 and energy of between 80 and 150 KEV.
Claim 13
Dependent Claim
25 words
The method of claim 7 wherein said barrier metal layer is composed of TiW and has a thickness of between about 400 to 1200 Angstroms.
Claim 14
Dependent Claim
25 words
The method of claim 7 wherein said barrier metal layer is composed of TiN and has a thickness of between about 400 to 1200 Angstroms.
Claim 15
Independent Claim
126 words
The method of forming a vertical resistor within a contact window of an integrated circuit comprising: providing a contact window through a passivation layer to a device structure within a semiconductor substrate; depositing a silicon nitride layer within said contact window; anisotropically etching back said nitride layer to form nitride sidewalls within said contact window to prevent migration of any impurities from said passivation layer into said planned vertical resistor; depositing a layer of polysilicon within said contact window; anisotropically etching back said polysilicon to leave said polysilicon only within said contact opening; and ion implanting into said polysilicon layer remaining in said contact window sufficient ions and simultaneously into said passivation layer to provide for said planned vertical resistor thereby completing formation of said resistor.
Claim 16
Independent Claim
126 words
The method of forming a vertical resistor within a contact window of an integrated circuit comprising: providing a contact window through a passivation layer to a device structure within a semiconductor substrate; depositing a silicon nitride layer within said contact window; anisotropically etching back said nitride layer to form nitride sidewalls within said contact window to prevent migration of any impurities from said passivation layer into said planned vertical resistor; depositing a layer of polysilicon within said contact window; anisotropically etching back said polysilicon to leave said polysilicon only within said contact opening; and ion implanting into said polysilicon layer remaining in said contact window sufficient ions and simultaneously into said passivation layer to provide for said planned vertical resistor thereby completing formation of said resistor.
Claim 17
Dependent Claim
13 words
The method of claim 13 wherein said device structure is a source/drain region.
Claim 18
Dependent Claim
14 words
The method of claim 13 wherein said device structure is a conducting polysilicon layer.
Claim 19
Dependent Claim
27 words
The method of claim 13 wherein said polysilicon layer is deposited by low pressure chemical vapor deposition to a thickness of between about 5000 to 7000 Angstroms.
Claim 20
Dependent Claim
38 words
The method of claim 13, wherein said polysilicon layer remaining in said contact opening is ion implanted with boron ions with a dosage of between 5E12 and 5E13 ions/cm 2 and energy of between 80 and 150 KEV.
Claim 21
Dependent Claim
16 words
The method of claim 7 wherein said dopant impurity material in said passivation layer includes phosphorus.
References Cited (Backward Citations)
US4797717A
Cited
US4727045A
Cited
US5229311A
Cited
US5013677A
Cited
US5170233A
Cited
US5086017A
Cited
US5177030A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-07-18 | 1998-01-17 | 1998-07-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-07-18 | 2002-01-17 | 2002-07-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-07-18 | 2006-01-17 | 2006-07-19 | $7700.00 | Window Closed / Lapsed |