Laser CVD method for synthesizing diamond
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1993-07-08
•
Granted: 1995-02-07
•
Expires: 2013-07-08
Abstract
Abstract A method for synthesizing a diamond by vapor deposition permits selectively growing high quality diamond on any desired region of a base material at a lower temperature compared to respective conventional temperatures starting with a raw material gas which is prepared by diluting a compound containing carbon atoms such as methane with hydrogen gas. This diluted raw material gas is irradiated with a laser beam satisfying at least one of the following two conditions, namely a spread angle of 1×10 -1 mrad to 5×10 -1 mrad during oscillation or a half-power band width of 1×10 -4 nm to 1×10 -1 nm with respect to a band width of an oscillation having a wavelength of 190 nm to 360 nm. Diamond is deposited on the base material from a chemical species generated by such irradiation.
Inventors
- 👤 Nobuhiro Ota
- 👤 Naoji Fujimori
- 👤 Kenichi Watanabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 06:11
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/26; C23C16/27; C23C16/04; C23C16/047; C23C16/44; C23C16/48; C23C16/483
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
158 words
A laser CVD method for synthesizing diamond on a base material from a vapor phase comprising the following steps: (a) using a raw material gas prepared by diluting a compound consisting essentially of saturated hydrocarbon with gaseous hydrogen, (b) irradiating said raw material gas or said base material with a laser beam satisfying at least one of the following conditions: maintaining during oscillation a spread angle within a range of at least about 1×10 -2 mrad and not more than about 5×10 -1 mrad, or a half-power band width within a range of at least about 1×10 -4 nm and not more than about 1×10 -1 nm with respect to a band width of an oscillation having a wavelength within a range of about 190 nm to 360 nm for decomposing said compound and said gaseous hydrogen to form decomposed raw material gas; and (c) depositing the diamond on said base material from said decomposed raw material gas.
Claim 2
Dependent Claim
158 words
A laser CVD method for synthesizing diamond on a base material from a vapor phase comprising the following steps: (a) using a raw material gas prepared by diluting a compound consisting essentially of saturated hydrocarbon with gaseous hydrogen, (b) irradiating said raw material gas or said base material with a laser beam satisfying at least one of the following conditions: maintaining during oscillation a spread angle within a range of at least about 1×10 -2 mrad and not more than about 5×10 -1 mrad, or a half-power band width within a range of at least about 1×10 -4 nm and not more than about 1×10 -1 nm with respect to a band width of an oscillation having a wavelength within a range of about 190 nm to 360 nm for decomposing said compound and said gaseous hydrogen to form decomposed raw material gas; and (c) depositing the diamond on said base material from said decomposed raw material gas.
Claim 3
Dependent Claim
36 words
The method in accordance with claim 1, wherein a dispersion of an energy intensity in a plane perpendicular to an optical axis of said laser beam is at the most 10% of an average energy intensity.
Claim 4
Dependent Claim
30 words
The method in accordance with claim 1, wherein said raw material gas includes at least one gas selected from the group consisting of helium, argon, neon, krypton, xenon and radon.
Claim 5
Dependent Claim
13 words
The method in accordance with claim 1, wherein said saturated hydrocarbon is methane.
Claim 6
Dependent Claim
35 words
A method in accordance with claim 1, wherein said raw material gas consists essentially of methane, hydrogen, and at least one gas selected from the group consisting of helium, argon, neon, krypton, xenon and radon.
Claim 7
Dependent Claim
30 words
The method in accordance with claim 1, comprising moving said base material relative to said laser beam thereby moving a region for deposition of said diamond on said base material.
Claim 8
Dependent Claim
43 words
The method in accordance with claim 1, wherein said laser beam is linearly focused on said base material and said base material is translated for forming a flat diamond film on a region of said base material being irradiated by said laser beam.
Claim 9
Dependent Claim
42 words
The method in accordance with claim 1, comprising focussing said laser beam linearly on said base material and said base material is rotated for forming a flat diamond film on a region of said base material being irradiated by said laser beam.
Claim 10
Dependent Claim
22 words
The method in accordance with claim 1, comprising heating said base material to a temperature of not more than about 300° C.
Claim 11
Dependent Claim
44 words
The method in accordance with claim 1, wherein a laser source is selected from the group consisting of an ArF excimer laser, a KrCl excimer laser, a KrF excimer laser, an XeCl excimer laser, an N 2 excimer laser and an XeF excimer laser.
References Cited (Backward Citations)
SU339134A1
Cited
US3030187A
Cited
US3030188A
Cited
JPS61236691A
Cited
US4711790A
Cited
US4994301A
Cited
JPS63288991A
Cited
JPS63288992A
Cited
US4948629A
Cited
EP0382341A1
Cited
JPH0351675A
Cited
JPH03185956A
Cited
US5154945A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-02-06 | 1998-08-08 | 1999-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-02-06 | 2002-08-08 | 2003-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-02-06 | 2006-08-08 | 2007-02-07 | $7700.00 | Window Closed / Lapsed |