Method of making MOS transistor having improved oxynitride dielectric
Assignee: The University of Texas System
•
Filing: 1994-01-07
•
Granted: 1995-03-14
•
Expires: 2014-01-07
Abstract
Abstract High quality ultrathin gate oxides having nitrogen atoms therein with a profile having a peak at the silicon oxide-silicon interface are formed by oxidizing a surface of a monocrystalline silicon body in an atmosphere of nitrous oxide (N 2 O) at a temperature above 900° C. preferably in the range of 900°-1100° C., and then heating the silicon body and oxidized surface in an atmosphere of anhydrous ammonia to introduce additional nitrogen atoms into the oxide and increase resistance to boron penetration without degrading the oxide by charge trapping. The resulting oxynitride has less degradation under channel hot electron stress and approximately one order of magnitude longer lifetime than that of conventional silicon oxide in MIS applications.
Inventors
- 👤 Dim-Lee Kwong
- 👤 Giwan Yoon
- 👤 Jonghan Kim
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:40
CPC Classifications
H; H10; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01332; H10D64/01336; H10D64/0134; H10D64/01344; H10D64/60; H10D64/66; H10D64/68; H10D64/693; Y; Y10; Y10S; Y10S148/00; Y10S148/112
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
130 words
A method of fabricating an MIS transistor comprising the steps of a) providing a monocrystalline silicon substrate having a major surface, b) cleaning said major surface, c) placing said body in an atmosphere of nitrous oxide, d) heating said body and atmosphere at a temperature for the oxidation of said major surface thereby forming a oxynitride layer with nitrogen atoms therein, e) heating said silicon substrate and oxynitride layer in an atmosphere of anhydrous ammonia to introduce additional nitrogen atoms in said oxynitride layer, f) annealing said silicon substrate and oxynitride layer in an atmosphere of nitrogen, g) forming a gate electrode on said oxynitride layer, and h) forming a source region and a drain region in said silicon body abutting said major surface and aligned with said gate electrode.
Claim 2
Independent Claim
130 words
A method of fabricating an MIS transistor comprising the steps of a) providing a monocrystalline silicon substrate having a major surface, b) cleaning said major surface, c) placing said body in an atmosphere of nitrous oxide, d) heating said body and atmosphere at a temperature for the oxidation of said major surface thereby forming a oxynitride layer with nitrogen atoms therein, e) heating said silicon substrate and oxynitride layer in an atmosphere of anhydrous ammonia to introduce additional nitrogen atoms in said oxynitride layer, f) annealing said silicon substrate and oxynitride layer in an atmosphere of nitrogen, g) forming a gate electrode on said oxynitride layer, and h) forming a source region and a drain region in said silicon body abutting said major surface and aligned with said gate electrode.
Claim 3
Dependent Claim
47 words
The method as defined by claim 1 wherein step g) includes forming a layer of material on said oxynitride layer and etching said layer of material and said oxynitride layer to form said gate electrode with said oxynitride layer between said gate electrode and said major surface.
Claim 4
Dependent Claim
15 words
The method as defined by claim 2 wherein said layer of material comprises polycrystalline silicon.
Claim 5
Dependent Claim
13 words
The method as defined by claim 2 wherein said material comprises a metal.
Claim 6
Dependent Claim
22 words
The method as defined by claim 1 wherein step c) includes placing said substrate in an atmosphere of essentially pure nitrous oxide.
Claim 7
Dependent Claim
15 words
The method as defined by claim 5 wherein said nitrous oxide is approximately 99.998% pure.
Claim 8
Dependent Claim
22 words
The method as defined by claim 5 wherein step d) includes heating said substrate and atmosphere to a temperature above 900° C.
Claim 9
Dependent Claim
25 words
The method as defined by claim 7 wherein step d) includes heating said substrate and atmosphere to a temperature in the range of 900°-1100° C.
Claim 10
Dependent Claim
26 words
The method as defined by claim 1 wherein step e) includes heating said substrate and atmosphere to a temperature in the range of 800° C.-1100° C.
Claim 11
Dependent Claim
26 words
The method as defined by claim 1 wherein step e) includes heating said substrate and atmosphere to a temperature in the range of 850° C.-950° C.
Claim 12
Independent Claim
103 words
A method of fabricating a oxynitride layer on a surface of a silicon body with nitrogen atoms dispersed i said oxynitride layer and having a profile having a peak at the oxynitride-silicon interface comprising the steps of a) cleaning said surface, b) placing said body in an atmosphere of nitrous oxide, c) heating said body and said atmosphere at a temperature for the oxidation of said surface thereby forming a oxynitride layer on said major surface with nitrogen atoms therein, and d) heating said body and oxynitride layer in an atmosphere of anhydrous ammonia to introduce additional nitrogen atoms in said oxynitride layer.
Claim 13
Independent Claim
103 words
A method of fabricating a oxynitride layer on a surface of a silicon body with nitrogen atoms dispersed i said oxynitride layer and having a profile having a peak at the oxynitride-silicon interface comprising the steps of a) cleaning said surface, b) placing said body in an atmosphere of nitrous oxide, c) heating said body and said atmosphere at a temperature for the oxidation of said surface thereby forming a oxynitride layer on said major surface with nitrogen atoms therein, and d) heating said body and oxynitride layer in an atmosphere of anhydrous ammonia to introduce additional nitrogen atoms in said oxynitride layer.
Claim 14
Dependent Claim
22 words
The method as defined by claim 11 wherein step b) includes placing said substrate in an atmosphere of essentially pure nitrous oxide.
Claim 15
Dependent Claim
15 words
The method as defined by claim 12 wherein said nitrous oxide is approximately 99.998% pure.
Claim 16
Dependent Claim
22 words
The method as defined by claim 12 wherein step c) includes heating said body and atmosphere to a temperature above 900° C.
Claim 17
Dependent Claim
23 words
The method as defined by claim 11 and further including the step of a) annealing said oxynitride layer in an atmosphere of nitrogen.
Claim 18
Dependent Claim
25 words
The method as defined by claim 11 wherein step c) includes heating said body and atmosphere to a temperature in the range of 900°-1100° C.
Claim 19
Dependent Claim
26 words
The method as defined by claim 11 wherein step d) includes heating said body and atmosphere to a temperature in the range of 800° C.-1100° C.
Claim 20
Dependent Claim
26 words
The method as defined by claim 11 wherein step d) includes heating said body and atmosphere to a temperature in the range of 850° C.-950° C.
References Cited (Backward Citations)
US3422321A
Cited
US3629088A
Cited
US4188565A
Cited
US4980307A
Cited
JPS55113335A
Cited
US4581622A
Cited
US4438157A
Cited
WO1983002199A1
Cited
WO1984000852A1
Cited
JPS61172339A
Cited
US4702936A
Cited
US4620986A
Cited
US4721631A
Cited
WO1986005323A1
Cited
WO1987005439A1
Cited
US4901133A
Cited
EP0259826A1
Cited
EP0289246A1
Cited
EP0305741A2
Cited
JPS6469932A
Cited
JPH0218934A
Cited
WO1990003560A2
Cited
US5254506A
Cited
JPH03257828A
Cited
US5254489A
Cited
JPH05283679A
Cited
US5258333A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-03-13 | 1998-09-12 | 1999-03-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-03-13 | 2002-09-12 | 2003-03-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-03-13 | 2006-09-12 | 2007-03-14 | $7700.00 | Window Closed / Lapsed |