Assignee: Honeywell International Inc
•
Filing: 1993-12-21
•
Granted: 1995-03-28
•
Expires: 2013-12-21
Abstract
Abstract A process for the manufacture of a stain resistant melt colored carpet by melt mixing a polyamide copolymer, containing sulfonate groups with a coloring agent to form a homogeneous polymer melt into fibers, tufting the fibers in a backing to form a carpet, treating the carpet with polymethacrylic acid, copolymers of polymethacrylic acid, a mixture of polymethacrylic acid and a sulfonated aromatic formaldehyde condensation product, and a reaction product of the polymerization or copolymerization of methacrylic acid in the presence of a sulfonated aromatic formaldehyde condensation product.
Inventors
- 👤 Ardy Armen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 12:28
CPC Classifications
D; D01; D01F; D01F6/00; D01F6/58; D01F6/60; D01F1/00; D01F1/02; D01F1/04; D01F1/06; D06; D06M; D06M15/00; D06M15/19; D06M15/21; D06M15/263; D06M15/285; D06M15/37; D06M15/39; D06M15/41; D06M15/412; D06M23/00; D06M23/04; D06N; D06N7/00; D06N7/0063; D06N7/0065; D06N7/0071; D06N7/0073; D06M2101/00; D06M2101/16; D06M2101/30; D06M2101/34; D06N2203/00; D06N2203/04; D06N2203/041; D06N2203/06; D06N2203/065; D06N2205/00; D06N2205/04; D06N2205/06; D06N2209/00; D06N2209/08; D06N2209/0807; D06N2209/14; D06N2209/147; Y; Y10; Y10T; Y10T428/00; Y10T428/23907; Y10T428/23986; Y10T442/00; Y10T442/20; Y10T442/2041; Y10T442/2049; Y10T442/2057; Y10T442/2066; Y10T442/2279; Y10T442/2549; Y10T442/2574
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
158 words
A process for the manufacture of a acid stain-resistant, melt-colored carpet which retains its acid stain-resistance after shampooing with a high pH shampoo, said method comprising the steps of: a) melt mixing a cationically dyeable polyamide copolymer, containing sulfonate groups, with a coloring agent to form a homogeneous polymer melt; b) spinning the polymer melt into cationically dyeable fibers; c) tufting the fibers into a backing to form a carpet; and d) treating the carpet with a compound, selected from the group consisting of polymethacrylic acid, copolymers of polymethacrylic acid, a mixture of polymethacrylic acid and a sulfonated aromatic formaldehyde condensation product, and a reaction product of the polymerization or copolymerization of a methacrylic acid in the presence of a sulfonated aromatic formaldehyde condensation product in an amount sufficient to impart acid stain-resistance retention properties to said treated carpet such that said treated carpet retains its acid-stain resistance after being subjected to shampooing with a high pH shampoo.
Claim 2
Dependent Claim
158 words
A process for the manufacture of a acid stain-resistant, melt-colored carpet which retains its acid stain-resistance after shampooing with a high pH shampoo, said method comprising the steps of: a) melt mixing a cationically dyeable polyamide copolymer, containing sulfonate groups, with a coloring agent to form a homogeneous polymer melt; b) spinning the polymer melt into cationically dyeable fibers; c) tufting the fibers into a backing to form a carpet; and d) treating the carpet with a compound, selected from the group consisting of polymethacrylic acid, copolymers of polymethacrylic acid, a mixture of polymethacrylic acid and a sulfonated aromatic formaldehyde condensation product, and a reaction product of the polymerization or copolymerization of a methacrylic acid in the presence of a sulfonated aromatic formaldehyde condensation product in an amount sufficient to impart acid stain-resistance retention properties to said treated carpet such that said treated carpet retains its acid-stain resistance after being subjected to shampooing with a high pH shampoo.
Claim 3
Dependent Claim
17 words
The process according to claim 1, further comprising a drawing and texturing step after spinning step (b).
Claim 4
Dependent Claim
14 words
The process according to claim 1, further comprising coating the backing with a latex.
Claim 5
Dependent Claim
15 words
The process according to claim 3, further comprising applying a secondary backing on the latex.
Claim 6
Dependent Claim
32 words
The process according to claim 1, wherein polyamide copolymers, containing sulfonate groups, being formed by copolymerization of a sulfonated aromatic dicarboxylic acid or an alkali metal salt thereof with polyamide forming monomers.
Claim 7
Dependent Claim
38 words
The process according to claim 5, wherein the sulfonated aromatic dicarboxylic acid or an alkali metal salt thereof is selected from the group consisting of 5-sulfoisophthalic acid, a sodium salt, potassium salt and lithium salt of 5-sulfoisophthalic acid.
Claim 8
Dependent Claim
44 words
The process according to claim 5, wherein the polyamide copolymer, containing sulfonate groups, is a copolymer of a nylon, selected from the group consisting of nylon 6, nylon 6/6, nylon 6/9, nylon 6/10, nylon 6T, nylon 6/12, nylon 11, nylon 12, and copolymers thereof.
Claim 9
Dependent Claim
19 words
The process according to claim 7, wherein the polyamide copolymer, containing sulfonate groups, is a copolymer of nylon 6.
Claim 10
Dependent Claim
40 words
The process according to claim 1, wherein the polyamide copolymer contains from about 0.25 to about 4.0% by weight of the sulfonated aromatic dicarboxylic acid or an alkali metal salt thereof, based on the total amount of the polyamide copolymer.
Claim 11
Dependent Claim
27 words
The process according to claim 6, wherein the coloring agent is selected from the group consisting of water-soluble dyes, organic solvent--soluble dyes, polymer soluble dyes and pigments.
Claim 12
Dependent Claim
32 words
The process according to claim 1, wherein the coloring agent is used in an amount of from about 0.001 to about 5.0% by weight, based on the total amount of polyamide copolymer.
Claim 13
Dependent Claim
34 words
The process according to claim 1, wherein the copolymers of polymethacrylic acid are formed by copolymerization of methacrylic acid and monomers selected from the group consisting of monoolefinically unsaturated acids, esters, anhydrides and amides.
Claim 14
Dependent Claim
31 words
The process according to claim 1, wherein the monomers are selected from the group consisting of acrylic acid, maleic acid, maleic anhydride, fumaric acid, alkyl acrylate, cycloalkylacrylate, hydroxy-alkylacrylate, acrylamide and methacrylamide.
Claim 15
Dependent Claim
34 words
The process according to claim 1, wherein the sulfonated aromatic formaldehyde condensation product comprise condensation products of formaldehyde with sulfonated aromatic compound selected from the group consisting of 4,4'-dihydroxydiphenylsulfone, phenyl-4-sulfonic acid and mixtures thereof.
Claim 16
Dependent Claim
21 words
The process according to claim 1, wherein the carpet is treated with an aqueous solution of the compound in step (d).
Claim 17
Dependent Claim
23 words
The process according to claim 15, wherein the aqueous solution has a solid content of from about 0.1 to about 10.0% by weight.
Claim 18
Dependent Claim
21 words
The process according to claim 1, wherein in step (d) an exhaust application is used for the treatment of the carpet.
Claim 19
Dependent Claim
21 words
The process according to claim 1, wherein in step (d) a continuous application is used for the treatment of the carpet.
Claim 20
Dependent Claim
21 words
The process according to claim 1, wherein in step (d) a foam application is used for the treatment of the carpet.
Claim 21
Dependent Claim
12 words
Stain resistant melt colored carpet, obtained by the process of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-03-27 | 1998-09-26 | 1999-03-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-03-27 | 2002-09-26 | 2003-03-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-03-27 | 2006-09-26 | 2007-03-28 | $7700.00 | Window Closed / Lapsed |