Coating for tissue drag reduction
Assignee: Covidien AG
•
Filing: 1994-04-20
•
Granted: 1995-08-15
•
Expires: 2014-04-20
Abstract
Abstract This invention relates to materials for medical or veterinary use that possess considerably improved properties with regard to friction. The invention also relates to the production of such materials from existing materials that possess suitable bulk properties, but inappropriate frictional properties. This invention also relates to a hydrophilic coating material that provides improved frictional properties.
Inventors
- 👤 Peter K. Jarrett
- 👤 George Jessup
- 👤 Louis Rosati
- 👤 Chris Martin
- 👤 John W. Maney
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:46
CPC Classifications
A; A61; A61L; A61L17/00; A61L17/14; A61L17/145; A61L2/00; A61L2/02; A61L2/08; A61L2/081; A61L29/00; A61L29/08; A61L29/085; A61L31/00; A61L31/08; A61L31/10; C; C08; C08G; C08G63/00; C08G63/66; C08G63/664; A61L2103/00; A61L2103/15; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964; Y10T428/2967; Y10T428/2969; Y10T428/31504; Y10T428/31786
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
64 words
An ABA or AB block copolymer having a (B) block comprising a poly(alkylene oxide) having a number average molecular weight of about 5,000 to 20,000 and an A block comprising a biodegradable random copolymer of (1) the cyclic ester of an alpha-hydroxy acid and (2) ε-caprolactone, wherein the ABA or AB block polymer has a glass transition temperature at or less than 16° C.
Claim 2
Dependent Claim
64 words
An ABA or AB block copolymer having a (B) block comprising a poly(alkylene oxide) having a number average molecular weight of about 5,000 to 20,000 and an A block comprising a biodegradable random copolymer of (1) the cyclic ester of an alpha-hydroxy acid and (2) ε-caprolactone, wherein the ABA or AB block polymer has a glass transition temperature at or less than 16° C.
Claim 3
Dependent Claim
12 words
An ABA block polymer according to claim 1 wherein (1) is glycolide.
Claim 4
Dependent Claim
17 words
The polymer according to claim 2 wherein the B block is poly(ethylene oxide) or poly(ethylene oxide-co-propylene oxide).
Claim 5
Dependent Claim
51 words
The polymer according to claim 2 wherein the poly(alkylene oxide) comprises up to about 95 weight percent and the ratio of glycolide to ε-caprolactone components is within a range of about 5 weight percent glycolide and 95 weight percent ε-caprolactone to about 50 weight percent glycolide and 50 weight percent ε-caprolactone.
Claim 6
Dependent Claim
21 words
The polymer according to claim 4 wherein said ratio is within a range of about 60 to 90 weight percent ε-caprolactone.
Claim 7
Dependent Claim
21 words
The polymer according to claim 5 wherein said ratio is within a range of about 80 to 90 weight percent ε-caprolactone.
Claim 8
Dependent Claim
15 words
The polymer according to claim 6 wherein the ε-caprolactone component is about 85 weight percent.
Claim 9
Dependent Claim
21 words
The polymer according to claim 4 wherein said poly(alkylene oxide) comprises about 20 to 60 weight percent of the ABA polymer.
Claim 10
Dependent Claim
17 words
The polymer according to claim 8 wherein said polymer(alkylene oxide) comprises about 25 to 45 weight percent.
Claim 11
Dependent Claim
22 words
The polymer according to claim 4 wherein the number average molecular weight of said poly(alkylene oxide) is from about 6,000 to 20,000.
Claim 12
Dependent Claim
22 words
The polymer according to claim 10 wherein the said number average molecular weight of said poly(alkylene oxide) is up to about 14,000.
Claim 13
Dependent Claim
22 words
The polymer according to claim 11 wherein said number average molecular weight of said poly(alkylene oxide) is from about 8,000 to 14,000.
Claim 14
Dependent Claim
12 words
An AB block polymer according to claim 1 wherein (1) is glycolide.
Claim 15
Dependent Claim
20 words
The polymer according to claim 13 wherein the B block is a monomethyl ether of a hydroxyl ended polyethylene oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-08-14 | 1999-02-13 | 1999-08-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-08-14 | 2003-02-13 | 2003-08-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-08-14 | 2007-02-13 | 2007-08-15 | $7700.00 | Window Closed / Lapsed |