Support for a photographic printing paper and a manufacturing process therefor
Assignee: Fujifilm Holdings Corp
•
Filing: 1994-04-28
•
Granted: 1995-11-14
•
Expires: 2014-04-28
Abstract
Abstract A support for a photographic printing paper comprising a substrate and a waterproof resin coating layers provided on the both sides of the substrate, wherein at least the waterproof resin-coating provided on the side of the substrate on which an emulsion for forming an image is coated comprises i) a lowermost waterproof resin coating layer contacting the substrate and ii) at least one upper coating layer containing a waterproof resin capable of melt-extruded at a temperature of from 170° to 290° C. and containing uniformly dispersed titanium dioxide, and a method for manufacturing the support by melt extrusion.
Inventors
- 👤 Yuji Shirakura
- 👤 Hisamasa Abe
- 👤 Teruo Yamashita
- 👤 Tatsuo Shimizu
- 👤 Sei Kawahara
- 👤 Takahito Miyoshi
- 👤 Yasuo Nishikawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 16:28
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/18; B32B27/20; B32B27/06; B32B27/10; B32B27/08; B32B27/32; G; G03; G03C; G03C1/00; G03C1/76; G03C1/775; G03C1/79; B32B2307/00; B32B2307/70; B32B2307/726; B32B2307/7265; B32B2309/00; B32B2309/02; B32B2323/00; B32B2323/04; B32B2323/043; B32B2323/046; B32B2323/10; B32B2367/00; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/31504; Y10T428/31855; Y10T428/3188; Y10T428/31895; Y10T428/31899; Y10T428/31902; Y10T428/31909
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
121 words
A support for a photographic printing paper comprising a substrate and waterproof resin coating layers provided on both sides of the substrate, wherein at least the waterproof resin coating provided on the side of the substrate on which an emulsion for forming an image is to be coated comprises i) a lowermost melt-extruded waterproof resin coating layer contacting the substrate and ii) at least one melt-extruded upper coating layer containing a waterproof resin capable of being melt-extruded at a temperature of from 170° to 290° C. and containing uniformly dispersed titanium dioxide wherein the lowermost melt-extruded waterproof resin coating layer contains at least one additive selected from the group consisting of a tackifier, an adhesive resin, talc, kaolin and calcium carbonate.
Claim 2
Dependent Claim
121 words
A support for a photographic printing paper comprising a substrate and waterproof resin coating layers provided on both sides of the substrate, wherein at least the waterproof resin coating provided on the side of the substrate on which an emulsion for forming an image is to be coated comprises i) a lowermost melt-extruded waterproof resin coating layer contacting the substrate and ii) at least one melt-extruded upper coating layer containing a waterproof resin capable of being melt-extruded at a temperature of from 170° to 290° C. and containing uniformly dispersed titanium dioxide wherein the lowermost melt-extruded waterproof resin coating layer contains at least one additive selected from the group consisting of a tackifier, an adhesive resin, talc, kaolin and calcium carbonate.
Claim 3
Dependent Claim
45 words
The support for a photographic printing paper as in claim 1, wherein the amount of the titanium dioxide in the at least one upper coating layer is from 5 to 60 weight % based on the weight of the composition of the waterproof resin layer.
Claim 4
Dependent Claim
41 words
The support for a photographic printing paper as in claim 1, wherein the waterproof resin contained in said at least one titanium dioxide-containing waterproof resin layer has a melt index falling within a range of from 1.2 to 100 g/10 minutes.
Claim 5
Dependent Claim
39 words
The support for a photographic printing paper as in claim 1, wherein said waterproof resin in a layer which does not contain titanium dioxide has a melt index falling within a range of from 1.2 to 100 g/10 minutes.
Claim 6
Dependent Claim
19 words
The support for a photographic printing paper as in claim 1, wherein said waterproof resin is a polyolefin resin.
Claim 7
Dependent Claim
41 words
The support for a photographic printing paper as in claim 5, wherein said polyolefin resin is at least one resin selected from the group consisting of low density polyethylene, linear low density polyethylene, high density polyethylene, polypropylene, and an ester copolymer.
Claim 8
Dependent Claim
38 words
The support for a photographic printing paper as in claim 1, wherein the at least one upper waterproof resin coating layer containing titanium dioxide is formed by melt-extrusion at a resin temperature of from 170° to 290° C.
Claim 9
Dependent Claim
40 words
The support for a photographic printing paper as in claim 1, wherein the amount of said tackifier in the lowermost waterproof resin layer is from 0.5 to 60 weight % based on the weight of the composition of the layer.
Claim 10
Dependent Claim
41 words
The support for a photographic printing paper as in claim 1, wherein the amount of said adhesive resin in the lowermost waterproof resin layer is from 5 to 500 weight % based on the weight of the composition of the layer.
Claim 11
Dependent Claim
40 words
The support for a photographic printing paper as in claim 1, wherein said tackifier is at least one resin selected from the group consisting of a rosin compound resin, a terpene resin, a coumarone-indene resin and a petroleum hydrocarbon resin.
Claim 12
Dependent Claim
31 words
The support for a photographic printing paper as in claim 1, wherein said adhesive resin is selected from the group consisting of an adhesive polyolefin resin and an ethylene copolymer resin.
Claim 13
Dependent Claim
67 words
The support for a photographic printing paper as in claim 12, wherein said ethylene copolymer resin is selected from the group consisting of an ionomer, an ethylene-vinyl acetate copolymer, an ethylene-methyl methacrylate copolymer, an ethylene-ethyl acrylate copolymer, an ethylene-methyl acrylate copolymer, an ethylene-acrylic acid copolymer, an ethylene-ethyl acrylate-maleic anhydride copolymer, an ethylene-methacrylic acid copolymer, and a graft-polymer of polyolefin with maleic anhydride and the metal salts thereof.
Claim 14
Dependent Claim
42 words
The support for a photographic printing paper as in claim 1, wherein said adhesive resin is at least one resin of an adhesive polyolefin resin, an ethylene-vinyl acetate copolymer, an ethylene-acrylic acid copolymer and metal salt thereof, and an ethylene-methyl methacrylate copolymer.
Claim 15
Dependent Claim
46 words
The support for a photographic printing paper as in claim 1, wherein the amount of at least one of talc, kaolin and calcium carbonate is from 0.1 to 30 weight % based on the weight of the layer composition containing at least one of these compounds.
Claim 16
Dependent Claim
29 words
The support for a photographic printing paper as in claim 1, wherein the average particle size of the talc, kaolin and calcium carbonate is from 0.01 to 1.0 μm.
Claim 17
Dependent Claim
72 words
The support for a photographic printing paper as in claim 1, wherein said coating, provided on the side of the substrate on which an emulsion for forming an image is coated consists of the lowermost waterproof layer and an upper waterproof resin layer, wherein the lowermost layer has a thickness of from 0.5 to 20 μm and the upper waterproof resin coating layer has a thickness of from 0.5 to 50 μm.
Claim 18
Dependent Claim
81 words
The support for a photographic printing paper as in claim 1, wherein said coating provided on the side of the substrate on which an emulsion for forming an image is coated consists of a lowermost waterproof layer, an intermediate waterproof layer and an upper most waterproof layer, wherein the lowermost waterproof layer has a thickness of from 0.5 to 10 μm and the uppermost waterproof layer and the intermediate waterproof layer each has a thickness of from 0.5 to 50 μm.
Claim 19
Dependent Claim
72 words
The support for a photographic printing paper as in claim 1, wherein said coating provided on the side of the substrate on which an emulsion for forming an image is coated consists of a lowermost waterproof layer, an intermediate waterproof layer and an upper most waterproof layer, wherein the intermediate waterproof layer comprises a waterproof resin and titanium dioxide and the uppermost layer comprises a waterproof resin and contains no titanium dioxide.
Claim 20
Dependent Claim
42 words
The support for a photographic printing paper as in claim 1, wherein said lowermost waterproof resin coating layer contains titanium dioxide in an amount of less than 20 weight % based on the weight of the composition of the waterproof resin layer.
Claim 21
Dependent Claim
20 words
The support for a photographic printing paper as in claim 1, wherein said emulsion is a light-sensitive silver halide emulsion.
Claim 22
Independent Claim
90 words
A method for manufacturing a support for a photographic material, which comprises forming a lowermost coating layer containing a waterproof resin and at least one upper coating layer containing a waterproof resin and titanium dioxide dispersed therein, by melt-extrusion coating on the side of a substrate to which an emulsion is to be coated, wherein the temperature of the extrusion of the upper layer containing titanium dioxide is from 170° to 290° C. and the temperature of the extrusion of the lowermost layer is from 290° C. to 345° C.
Claim 23
Independent Claim
90 words
A method for manufacturing a support for a photographic material, which comprises forming a lowermost coating layer containing a waterproof resin and at least one upper coating layer containing a waterproof resin and titanium dioxide dispersed therein, by melt-extrusion coating on the side of a substrate to which an emulsion is to be coated, wherein the temperature of the extrusion of the upper layer containing titanium dioxide is from 170° to 290° C. and the temperature of the extrusion of the lowermost layer is from 290° C. to 345° C.
Claim 24
Dependent Claim
36 words
The method for manufacturing a support for a photographic printing paper as in claim 21, wherein the waterproof resin in the layer containing titanium dioxide has a melt index of from 1.2 to 100 g/10 minutes.
Claim 25
Dependent Claim
45 words
The support for a photographic printing paper as in claim 21, wherein the amount of the titanium dioxide in the at least one upper coating layer is from 5 to 60 weight % based on the weight of the composition of the waterproof resin layer.
Claim 26
Dependent Claim
41 words
The support for a photographic printing paper as in claim 21, wherein tackifier is present in the lowermost waterproof resin layer in an amount of from 0.5 to 60 weight % based on the weight of the composition of the layer.
Claim 27
Dependent Claim
42 words
The support for a photographic printing paper as in claim 22, wherein adhesive resin is present in the lowermost waterproof resin layer in an amount of from 5 to 500 weight % based on the weight of the composition of the layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-11-13 | 1999-05-15 | 1999-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-11-13 | 2003-05-15 | 2003-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-11-13 | 2007-05-15 | 2007-11-14 | $7700.00 | Window Closed / Lapsed |