Coated plastic molded articles
Assignee: Nippon Sheet Glass Co Ltd
•
Filing: 1993-12-02
•
Granted: 1996-03-12
•
Expires: 2013-12-02
Abstract
Abstract A coated plastic molded article comprising a plastic molded article on the surface of which are laminated (a) a first layer comprising a cured composition containing a partially hydrolyzed product of at least one silicon compound, (b) a second layer comprising a cured, partially hydrolyzed product of a second silicon compound, and (c) a third layer comprising silicon dioxide from an aqueous hydrosilicofluoric acid solution supersaturated with silicon dioxide, the coating layers being applied to the plastic molded article in the order stated; and alternate embodiments of a process for preparing the coated plastic molded articles.
Inventors
- 👤 Akio Takigawa
- 👤 Naoto Hirayama
- 👤 Masaki Kitaoka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 04:36
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B05; B05D; B05D7/00; B05D7/02; B05D7/50; B05D7/56; B05D7/57; B05D7/576; B32B27/16; B32B27/28; B32B27/283; B32B27/30; B32B27/308; B32B7/00; B32B7/04; B32B7/12; B32B2305/00; B32B2305/72; B32B2307/00; B32B2307/50; B32B2307/554; B32B2307/70; B32B2307/712; B32B2307/714; B32B2307/726; B32B2307/7265; B32B2383/00; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/31504; Y10T428/31507; Y10T428/31652; Y10T428/31663; Y10T428/31667; Y10T428/31786; Y10T428/31797; Y10T428/31855; Y10T428/31909; Y10T428/31928
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
372 words
A coated plastic molded article consisting essentially of a plastic article onto at least one surface of which are laminated: (a) at least one first layer having a thickness ranging from 1 to 100 μm, and comprising a cured composition containing at least one hydrolyzate of at least one silicon compound which is represented by the formula: R.sup.1 Si(R.sup.2).sub.3 wherein R 1 is selected from the group consisting of a C 1 -C 4 hydrocarbon group, an epoxy group-containing organic group and a fluorine atom-containing organic group, and R 2 is selected from the group consisting of alkoxy, alkoxyalkoxy, and acetoxy groups and chlorine atoms, provided that said R 2 s are the same or different from each other; (b) at least one second layer, on a surface of said first layer, having a thickness ranging from about 1 to 100 nm, but less than 100 nm, and comprising at least one cured hydrolyzate of at least one silicon compound represented by the formula: (R.sup.3).sub.n Si(R.sup.4).sub.4-n wherein R 3 is selected from the group consisting of an acryloxy group-containing organic group, a methacryloxy group-containing organic group and a chlorine-containing organic group, and R 4 is selected from the group consisting of alkoxy, alkoxyalkoxy and acetoxy groups, and n is 0 or 1, said at least one second layer which makes said at least one second layer and said at least one third layer adhere uniformly together; and (c) at least one third layer, on a surface of said second layer, which is formed by immersing said plastic article, with said at least one first layer and said at least one second layer thereon, into an aqueous hydrosilicofluoric acid solution supersaturated with silicon dioxide, forming, on a surface of said at least one second layer, said at least one third layer which is abrasion resistant, weather resistant, chemical resistant and impervious to water; said at least one first layer, said at least one second layer and said at least one third layer being arranged on said at least one surface of said plastic article in the order of, initially, said at least one first layer, followed by said at least one second layer, and then followed by said at least one third layer.
Claim 2
Dependent Claim
372 words
A coated plastic molded article consisting essentially of a plastic article onto at least one surface of which are laminated: (a) at least one first layer having a thickness ranging from 1 to 100 μm, and comprising a cured composition containing at least one hydrolyzate of at least one silicon compound which is represented by the formula: R.sup.1 Si(R.sup.2).sub.3 wherein R 1 is selected from the group consisting of a C 1 -C 4 hydrocarbon group, an epoxy group-containing organic group and a fluorine atom-containing organic group, and R 2 is selected from the group consisting of alkoxy, alkoxyalkoxy, and acetoxy groups and chlorine atoms, provided that said R 2 s are the same or different from each other; (b) at least one second layer, on a surface of said first layer, having a thickness ranging from about 1 to 100 nm, but less than 100 nm, and comprising at least one cured hydrolyzate of at least one silicon compound represented by the formula: (R.sup.3).sub.n Si(R.sup.4).sub.4-n wherein R 3 is selected from the group consisting of an acryloxy group-containing organic group, a methacryloxy group-containing organic group and a chlorine-containing organic group, and R 4 is selected from the group consisting of alkoxy, alkoxyalkoxy and acetoxy groups, and n is 0 or 1, said at least one second layer which makes said at least one second layer and said at least one third layer adhere uniformly together; and (c) at least one third layer, on a surface of said second layer, which is formed by immersing said plastic article, with said at least one first layer and said at least one second layer thereon, into an aqueous hydrosilicofluoric acid solution supersaturated with silicon dioxide, forming, on a surface of said at least one second layer, said at least one third layer which is abrasion resistant, weather resistant, chemical resistant and impervious to water; said at least one first layer, said at least one second layer and said at least one third layer being arranged on said at least one surface of said plastic article in the order of, initially, said at least one first layer, followed by said at least one second layer, and then followed by said at least one third layer.
Claim 3
Dependent Claim
30 words
The invention of claim 1 further comprising an adhesive layer present between said at least one surface of said coated plastic molded article and said at least one first layer.
Claim 4
Dependent Claim
16 words
The invention of claim 2 in which said adhesive layer comprises at least one acrylic polymer.
Claim 5
Dependent Claim
16 words
The invention of claim 2 in which said adhesive layer comprises at least one methacrylic polymer.
Claim 6
Dependent Claim
22 words
The invention of claim 2 in which said adhesive layer comprises at least one acrylic polymer and at least one methacrylic polymer.
Claim 7
Dependent Claim
32 words
The invention of claim 1 wherein said plastic molded article is comprised of at least one material selected from the group consisting of polycarbonate, diethylene glycol-bis-allylcarbonate polymer, acrylic resin and polyester resin.
Claim 8
Dependent Claim
234 words
A coated plastic molded article comprising a plastic coated article having on at least one surface thereof: (a) a first polymer layer having a thickness ranging from 1 to 100 μm cured with irradiation of actinic rays; (b) a second layer, on a surface of said first polymer layer, having a thickness ranging from about 1 to 100 nm, but less than 100 nm, and consisting essentially of at least one cured hydrolyzate of at least one of the silicon compounds represented by the formula: (R.sup.3).sub.n Si(R.sup.4).sub.4-n wherein R 3 is selected from the group consisting of an acryloxy group-containing organic group, a methacryloxy group-containing organic group and a chlorine-containing organic group, and R 4 is selected from the group consisting of alkoxy, alkoxyalkoxy and acetoxy groups, and n is 0 or 1, said second layer which provides enhanced means for forming thereon at least one adhering and uniform third layer; and (c) a third layer, on a surface of said second layer, comprising silicon dioxide from an aqueous hydrosilicofluoric acid solution supersaturated with silicon dioxide; said first polymer layer, said second layer and said third layer being laminated together and onto said a least one surface of said plastic molded article in the order of initially said first polymer layer, followed by said second layer, followed by said third layer, said third layer which is abrasion resistant, chemical resistant and impervious to water.
Claim 9
Dependent Claim
234 words
A coated plastic molded article comprising a plastic coated article having on at least one surface thereof: (a) a first polymer layer having a thickness ranging from 1 to 100 μm cured with irradiation of actinic rays; (b) a second layer, on a surface of said first polymer layer, having a thickness ranging from about 1 to 100 nm, but less than 100 nm, and consisting essentially of at least one cured hydrolyzate of at least one of the silicon compounds represented by the formula: (R.sup.3).sub.n Si(R.sup.4).sub.4-n wherein R 3 is selected from the group consisting of an acryloxy group-containing organic group, a methacryloxy group-containing organic group and a chlorine-containing organic group, and R 4 is selected from the group consisting of alkoxy, alkoxyalkoxy and acetoxy groups, and n is 0 or 1, said second layer which provides enhanced means for forming thereon at least one adhering and uniform third layer; and (c) a third layer, on a surface of said second layer, comprising silicon dioxide from an aqueous hydrosilicofluoric acid solution supersaturated with silicon dioxide; said first polymer layer, said second layer and said third layer being laminated together and onto said a least one surface of said plastic molded article in the order of initially said first polymer layer, followed by said second layer, followed by said third layer, said third layer which is abrasion resistant, chemical resistant and impervious to water.
Claim 10
Dependent Claim
25 words
The invention of claim 7 wherein said first layer is formed by a method comprising curing a polyfunctional acrylate compound with irradiation of actinic rays.
Claim 11
Dependent Claim
33 words
The invention of claim 7 wherein said plastic molded article is comprised of at least one material selected from the group consisting of poly carbonate, diethylene glycol-bis-allylcarbonate polymer, acrylic resin and polyester resin.
References Cited (Backward Citations)
US4284685A
Cited
US5015523A
Cited
US4902724A
Cited
US4902725A
Cited
US4855180A
Cited
US4927704A
Cited
US5051308A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-03-12 | 1999-09-11 | 2000-03-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-03-12 | 2003-09-11 | 2004-03-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-03-12 | 2007-09-11 | 2008-03-12 | $7700.00 | Window Closed / Lapsed |