Heat sink and method of fabricating
Assignee: Iowa State University Research Foundation Inc
•
Filing: 1994-11-01
•
Granted: 1996-06-04
•
Expires: 2014-11-01
Abstract
Abstract A heat sink composed of thermally conductive particles dispersed in a monolithic structure having a continuous microstructure; and the method of forming a heat sink by molding the heat sink from a thermoplastic or epoxy material which has been filled with thermally conductive particles, debinding the molded heat sink and densifying the debound heat sink into a monolithic structure.
Inventors
- 👤 Robert L. Terpstra
- 👤 Barbara K. Lograsso
- 👤 Iver E. Anderson
- 👤 Jeffrey A. Moore
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 20:04
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/22; B22F3/225; B22F3/10; B22F3/1017; B22F3/1021; C; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B35/528; C04B35/532; C04B35/56; C04B35/565; C04B35/58; C04B35/581; C04B35/583; H; H10; H10W; H10W40/00; H10W40/20; H10W40/25; H10W40/257; H10W99/00; B22F2998/00
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
140 words
A method of fabricating a heat sink having a selected configuration comprising the steps of: mixing powder particles of at least one material having a relatively high thermal conductivity with a polymer binder to form a powder particle/binder mixture; molding the powder particle/binder mixture into a heat sink having the selected configuration; debinding the molded heat sink to remove said binder therefrom by positioning the molded heat sink in a controlled environment and heating the molded heat sink to a plurality of predetermined temperatures and retaining said heat sink at each of said predetermined temperatures for a predetermined period of time to evaporate said binder from the molded heat sink to provide a particulate body formed of said powder particles; and processing the particulate body to consolidate said powder particles into a monolithic heat sink having a substantially continuous microstructure.
Claim 2
Independent Claim
140 words
A method of fabricating a heat sink having a selected configuration comprising the steps of: mixing powder particles of at least one material having a relatively high thermal conductivity with a polymer binder to form a powder particle/binder mixture; molding the powder particle/binder mixture into a heat sink having the selected configuration; debinding the molded heat sink to remove said binder therefrom by positioning the molded heat sink in a controlled environment and heating the molded heat sink to a plurality of predetermined temperatures and retaining said heat sink at each of said predetermined temperatures for a predetermined period of time to evaporate said binder from the molded heat sink to provide a particulate body formed of said powder particles; and processing the particulate body to consolidate said powder particles into a monolithic heat sink having a substantially continuous microstructure.
Claim 3
Dependent Claim
40 words
The method of claim 1 in which the step of processing the debound heat sink includes processing the debound heat sink using a process selected from the group comprising sintering, liquid phase sintering, electro-consolidation processing, forging and hot isostatic pressing.
Claim 4
Dependent Claim
25 words
The method of claim 1 in which said step of mixing powder particles includes mixing particles of a copper and silver powder with said binder.
Claim 5
Dependent Claim
47 words
The method of claim 1 in which the thermally conductive material is selected from the group comprising copper, silver, boron nitride, aluminum, molybdenum, aluminum nitride, silicon carbide, silica, carbon, diamond and alloys of said materials having a thermal conductivity similar to the thermal conductivity of said materials.
Claim 6
Dependent Claim
44 words
A heat sink comprising an interconnected particulate body formed of particles of a thermally conductive material and having a base and extended surface means, said body being densified to form interparticle bonds between said particles and provide said body with a substantially continuous microstructure.
Claim 7
Dependent Claim
44 words
A heat sink comprising an interconnected particulate body formed of particles of a thermally conductive material and having a base and extended surface means, said body being densified to form interparticle bonds between said particles and provide said body with a substantially continuous microstructure.
Claim 8
Dependent Claim
20 words
The heat sink of claim 5 in which said particulate body is formed of particles of a copper silver alloy.
Claim 9
Dependent Claim
51 words
A heat sink as in claim 5 in which said thermally conductive material is selected from the group of materials comprising copper, silver, boron nitride, aluminum, molybdenum, aluminum nitride, silicon carbide, silica, carbon, diamond and alloys of said materials having a thermal conductivity similar to the thermal conductivity of said materials.
Claim 10
Dependent Claim
30 words
The heat sink of claim 5 in which said particles are densified by a process selected from the group comprising liquid phase sintering, electro-consolidation processing, forging and hot isostatic pressing.
Claim 11
Dependent Claim
29 words
The method of claim 1 in which said step of positioning the molded heat sink in a controlled environment includes positioning the molded heat sink in a vacuum environment.
Claim 12
Dependent Claim
27 words
The method of claim 1 in which said step of processing the particulate body includes heating the particulate body and applying pressure to the heated particulate body.
Claim 13
Dependent Claim
21 words
The method of claim 10 in which said step of applying pressure includes forging the particulate body in a forging press.
Claim 14
Dependent Claim
36 words
The method of claim 11 in which said step of forging the particulate body includes positioning the particulate body in a heated pressure transmitting medium, said transmitting medium transferring the applied pressure to the particulate body.
Claim 15
Dependent Claim
48 words
The method of claim 10 in which said step of applying pressure includes positioning the particulate body in a bed of graphite grains for uniformly distributing pressure across the particulate body and said step of heating the particulate body includes applying an electrical current to said graphite grains.
Claim 16
Dependent Claim
35 words
The method of claim 10 in which said step of applying pressure includes positioning the particulate body in a chamber filled with a gaseous substance, said gaseous substance applying pressure to the heated particulate body.
Claim 17
Dependent Claim
59 words
The method of claim 1 in which said step of processing the particulate body includes heating the particulate body to a temperature at which said particulate body is in a liquid phase and a solid phase for a predetermined period of time and rapidly cooling the heated particulate body to densify the heated particulate body into said monolithic structure.
Claim 18
Dependent Claim
32 words
The method of claim 15 in which in which said processing step includes heating the particulate body until the particulate body has a liquid content of about 20-30 percent liquid by volume.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-06-04 | 1999-12-04 | 2000-06-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-06-04 | 2003-12-04 | 2004-06-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-06-04 | 2007-12-04 | 2008-06-04 | $7700.00 | Window Closed / Lapsed |