Enhanced crystallization of amorphous films
Assignee: Penn State Research Foundation
•
Filing: 1995-03-29
•
Granted: 1997-04-29
•
Expires: 2015-03-29
Abstract
Abstract A fabrication process for rendering, for example, amorphous silicon (a-Si) films into polycrystalline silicon (poly-Si) films initially commences with the deposition of the a-Si film on a substrate such as glass. The a-Si film is then exposed to a particle flux (e.g. a plasma or a neutral beam). The resulting treatment apparently causes an action that enhances a subsequent crystallization process. The treatment occurs at a temperature well below any level which causes a change in the substrate. The particle flux treatment is followed by an anneal step that enables a rapid crystallization. By appropriate masking prior to the treatment, crystallization in non-treated areas is prevented while crystallization in treated areas occurs during the anneal procedure.
Inventors
- 👤 Stephen J. Fonash
- 👤 Aiguo Yin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:45
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/29; H10P14/2901; H10P14/2922; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/031; H10D30/0312; H10D30/0314; H10D30/0321; H10P14/32; H10P14/3202; H10P14/3238; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/38; H10P14/3802; H10P14/3806; H10P14/3808
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
121 words
A method exhibiting a reduced thermal budget for producing a polycrystalline film of a semiconducting material film on a substrate, comprising the steps of: (a) depositing an amorphous film of said semiconducting material on said substrate, said amorphous film having a thickness enabling fabrication of a semiconductor structure therein: (b) exposing said amorphous film to a particle flux to promote subsequent solid phase crystallization growth therein while maintaining said amorphous film below any melting point thereof, said particle flux bearing a constituent selected so as to not adversely react with or etch said amorphous film; (c) annealing said amorphous film for not more than about 10 hours to enable solid phase crystal growth therein; and (d) subsequently passivating said amorphous film.
Claim 2
Independent Claim
121 words
A method exhibiting a reduced thermal budget for producing a polycrystalline film of a semiconducting material film on a substrate, comprising the steps of: (a) depositing an amorphous film of said semiconducting material on said substrate, said amorphous film having a thickness enabling fabrication of a semiconductor structure therein: (b) exposing said amorphous film to a particle flux to promote subsequent solid phase crystallization growth therein while maintaining said amorphous film below any melting point thereof, said particle flux bearing a constituent selected so as to not adversely react with or etch said amorphous film; (c) annealing said amorphous film for not more than about 10 hours to enable solid phase crystal growth therein; and (d) subsequently passivating said amorphous film.
Claim 3
Dependent Claim
11 words
The method of claim 1 wherein said semiconducting material is silicon.
Claim 4
Dependent Claim
19 words
The method of claim 1 wherein step (b) exposes said amorphous film to a particle flux from a plasma.
Claim 5
Dependent Claim
27 words
The method of claim 1 wherein said annealing step (c) is accomplished by placing said substrate and plasma-exposed amorphous film into a furnace at an elevated temperature.
Claim 6
Dependent Claim
26 words
The method of claim 1 wherein said annealing step (c) is accomplished by rapid thermal annealing through exposure of said film to intense radiative light energy.
Claim 7
Dependent Claim
21 words
The method of claim 1 wherein said annealing step (c) is accomplished by exposure of said film to a laser beam.
Claim 8
Dependent Claim
12 words
The method of claim 1 wherein said substrate is a glass plate.
Claim 9
Dependent Claim
17 words
The method of claim 1 wherein said substrate is a glass plate having a diffusion barrier coating.
Claim 10
Dependent Claim
42 words
The method of claim 1 wherein step (b) exposes said amorphous film to said particle flux while said film is at a temperature in a range from ambient to approximately 650° C., for a time not in excess of approximately two hours.
Claim 11
Dependent Claim
20 words
The method of claim 1, wherein said constituent is selected from at least one of: oxygen, hydrogen, argon and helium.
Claim 12
Dependent Claim
22 words
The method of claim 1, wherein said annealing step (c) occurs after exposing step (b) and after removal of said particle flux.
Claim 13
Independent Claim
124 words
A method for producing a patterned polycrystalline film of a semiconducting material from an amorphous film of said semiconducting material that is resident on a substrate, said amorphous film having a thickness enabling fabrication therein of a semiconductor structure, said method comprising: (a) masking portions of said amorphous film; (b) exposing unmasked areas of said amorphous film to a particle flux to promote solid phase crystallization in unmasked areas while maintaining said amorphous film below any melting point thereof, said particle flux bearing a constituent selected so as to not adversely react with or etch said amorphous film; (c) annealing said amorphous film for not more than about 10 hours to enable solid phase crystal growth therein; and (d) subsequently passivating said amorphous film.
Claim 14
Independent Claim
124 words
A method for producing a patterned polycrystalline film of a semiconducting material from an amorphous film of said semiconducting material that is resident on a substrate, said amorphous film having a thickness enabling fabrication therein of a semiconductor structure, said method comprising: (a) masking portions of said amorphous film; (b) exposing unmasked areas of said amorphous film to a particle flux to promote solid phase crystallization in unmasked areas while maintaining said amorphous film below any melting point thereof, said particle flux bearing a constituent selected so as to not adversely react with or etch said amorphous film; (c) annealing said amorphous film for not more than about 10 hours to enable solid phase crystal growth therein; and (d) subsequently passivating said amorphous film.
Claim 15
Dependent Claim
19 words
The method of claim 12 wherein step (b) exposes said amorphous film to a particle flux from a plasma.
Claim 16
Dependent Claim
27 words
The method of claim 12 wherein said annealing step (c) is accomplished by placing said substrate and plasma-exposed amorphous film into a furnace at an elevated temperature.
Claim 17
Dependent Claim
26 words
The method of claim 12 wherein said annealing step (c) is accomplished by rapid thermal annealing through exposure of said film to intense radiative light energy.
Claim 18
Dependent Claim
21 words
The method of claim 12 wherein said annealing step (c) is accomplished by exposure of said film to a laser beam.
Claim 19
Dependent Claim
12 words
The method of claim 12 wherein said substrate is a glass plate.
Claim 20
Dependent Claim
17 words
The method of claim 12 wherein said substrate is a glass plate having a diffusion barrier coating.
Claim 21
Dependent Claim
42 words
The method of claim 12 wherein step (b) exposes said amorphous film to said particle flux while said film is at a temperature in a range from ambient to approximately 650° C., for a time not in excess of approximately two hours.
Claim 22
Dependent Claim
20 words
The method of claim 12, wherein said constituent is selected from at least one of: oxygen, hydrogen, argon and helium.
Claim 23
Dependent Claim
22 words
The method of claim 12, wherein said annealing step (c) occurs after exposing step (b) and after removal of said particle flux.
References Cited (Backward Citations)
US4151058A
Cited
JPS5515677A
Cited
JPS57102027A
Cited
US4727044A
Cited
JPS6231111A
Cited
JPS6276514A
Cited
JPH03139824A
Cited
JPH03250728A
Cited
US5147826A
Cited
US5254484A
Cited
JPH04252018A
Cited
US5288658A
Cited
JPH04372118A
Cited
US5246886A
Cited
WO1993010555A1
Cited
US5387542A
Cited
JPH06120152A
Cited
US5403772A
Cited
US5275851A
Cited
JPH06267861A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-04-28 | 2000-10-28 | 2001-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-04-28 | 2004-10-28 | 2005-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-04-28 | 2008-10-28 | 2009-04-29 | $7700.00 | Window Closed / Lapsed |