US5665202A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Multi-step planarization process using polishing at two different pad pressures
Assignee: NXP USA Inc
•
Filing: 1995-11-24
•
Granted: 1997-09-09
•
Expires: 2015-11-24
Abstract
Abstract A process for polish planarizing a fill material (40) overlying a semiconductor substrate (30) includes a multi-step polishing process. In one embodiment, a second planarization layer (42) is deposited over a fill material (40) and a portion of the fill material (40) is removed leaving a remaining portion (44). The pad pressure of a CMP apparatus (20) is adjusted such that a first pressure is generated during the polishing process. Then, the remaining portion (44) is removed, while operating the CMP apparatus (20) at a second pad pressure. The selectivity of the polishing process is maintained by reducing the pad pressure during the second polishing step. In a second embodiment, after the first polishing step is performed, the remaining portion (44) is removed by an etching process using a portion (46) of second planarization layer (42).
Inventors
- 👤 Chitra K. Subramanian
- 👤 Asanga H. Perera
- 👤 James D. Hayden
- 👤 Subramoney V. Iyer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 00:17
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/06; H10P95/062
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
126 words
A process for fabricating a semiconductor device comprising the steps of: providing a semiconductor substrate having elevated regions and recessed regions therein, wherein a first planarization layer overlies the elevated regions; depositing a fill material to overlie the first planarization layer and the recessed regions; forming a second planarization layer to overlie the fill material wherein the second planarization material is not lithographically patterned to expose any portion of the underlying fill material; chemical-mechanical-polishing a first portion of the fill material using a polishing apparatus having a polishing pad, wherein the first portion is planarized using a first pad pressure; and chemical-mechanical-polishing a second portion of the fill material using a second pad pressure, wherein the first pad pressure is greater than the second pad pressure.
Claim 2
Dependent Claim
126 words
A process for fabricating a semiconductor device comprising the steps of: providing a semiconductor substrate having elevated regions and recessed regions therein, wherein a first planarization layer overlies the elevated regions; depositing a fill material to overlie the first planarization layer and the recessed regions; forming a second planarization layer to overlie the fill material wherein the second planarization material is not lithographically patterned to expose any portion of the underlying fill material; chemical-mechanical-polishing a first portion of the fill material using a polishing apparatus having a polishing pad, wherein the first portion is planarized using a first pad pressure; and chemical-mechanical-polishing a second portion of the fill material using a second pad pressure, wherein the first pad pressure is greater than the second pad pressure.
Claim 3
Dependent Claim
20 words
The process of claim 1, wherein the step of depositing a fill material comprises chemical vapor deposition of silicon dioxide.
Claim 4
Dependent Claim
34 words
The process of claim 1, wherein the step of forming a second planarization layer comprises depositing a layer selected from the group consisting of silicon nitride, boron nitride, silicon-rich silicon nitride, and boron oxynitride.
Claim 5
Dependent Claim
32 words
The method of claim 1 wherein the first polishing pad pressure is substantially within a range of 7.0-15.0 psi and the second polishing pad pressure substantially within a range of 2.5-5.0 psi.
Claim 6
Dependent Claim
60 words
The method of claim 1 wherein the first polishing pad pressure is set so that a polishing selectively of fill material to second planarization layer is substantially 3:1 in the first time period and setting the second polishing pad pressure so that a polishing selectively of fill material to second planarization layer is substantially 10:1 in the second time period.
Claim 7
Dependent Claim
177 words
A process for fabricating a semiconductor device comprising the steps of: providing a semiconductor substrate having a plurality of elevated regions and a plurality of recessed regions therein, wherein a portion of the recessed regions are characterized by a first horizontal distance, and wherein a portion of the recessed regions are characterized by a second horizontal distance, and wherein the second horizontal distance is different from the first horizontal distance, and wherein a first planarization layer overlies the elevated regions; depositing a fill material to overlie the first planarization layer and the plurality of recessed regions; forming a second planarization layer to overlie the fill material wherein the second planarization material is not lithographically patterned to expose any portion of the underlying fill material; chemical-mechanical-polishing a first portion of the fill material using a polishing apparatus having a polishing pad, wherein the first portion is planarized at a first pad pressure; and chemical-mechanical-polishing a second portion of the fill material at a second pad pressure, wherein the first pad pressure is greater than the second pad pressure.
Claim 8
Dependent Claim
177 words
A process for fabricating a semiconductor device comprising the steps of: providing a semiconductor substrate having a plurality of elevated regions and a plurality of recessed regions therein, wherein a portion of the recessed regions are characterized by a first horizontal distance, and wherein a portion of the recessed regions are characterized by a second horizontal distance, and wherein the second horizontal distance is different from the first horizontal distance, and wherein a first planarization layer overlies the elevated regions; depositing a fill material to overlie the first planarization layer and the plurality of recessed regions; forming a second planarization layer to overlie the fill material wherein the second planarization material is not lithographically patterned to expose any portion of the underlying fill material; chemical-mechanical-polishing a first portion of the fill material using a polishing apparatus having a polishing pad, wherein the first portion is planarized at a first pad pressure; and chemical-mechanical-polishing a second portion of the fill material at a second pad pressure, wherein the first pad pressure is greater than the second pad pressure.
Claim 9
Dependent Claim
20 words
The process of claim 6, wherein the step of depositing a fill material comprises chemical vapor deposition of silicon dioxide.
Claim 10
Dependent Claim
34 words
The process of claim 6, wherein the step of forming a second planarization layer comprises depositing a layer selected from the group consisting of silicon nitride, boron nitride, silicon-rich silicon nitride, and boron oxynitride.
Claim 11
Dependent Claim
32 words
The method of claim 6 wherein the first polishing pad pressure is substantially within a range of 7.0-15.0 psi and the second polishing pad pressure substantially within a range of 2.5-5.0 psi.
Claim 12
Dependent Claim
60 words
The method of claim 6 wherein the first polishing pad pressure is set so that a polishing selectively of fill material to second planarization layer is substantially 3:1 in the first time period and setting the second polishing pad pressure so that a polishing selectively of fill material to second planarization layer is substantially 10:1 in the second time period.
Claim 13
Dependent Claim
200 words
A process for fabricating a semiconductor device comprising the steps of: providing a substrate having elevated regions vertically separated from recessed regions by a separation distance; forming a first planarization layer overlying the elevated regions; depositing a fill material on the substrate to a thickness greater than the separation distance; forming a second planarization layer to overlie the fill material; removing a first portion of the fill material and a first portion of the second planarization layer, and leaving a second portion of the fill material and a second portion of the second planarization layer, the step of removing being performed by polishing the wafer during a first time period at a first polishing pad pressure and polishing the wafer during a second time period at a second polishing pad pressure wherein the second time period follows the first time period and wherein the second polishing pad pressure is less than the first polishing pad pressure; etching the second portion of the fill material using the second portion of the second planarization layer as an etch mask; and removing the second portion of the second planarization layer whereby the second portion of the fill material remains overlying the recessed regions.
Claim 14
Dependent Claim
200 words
A process for fabricating a semiconductor device comprising the steps of: providing a substrate having elevated regions vertically separated from recessed regions by a separation distance; forming a first planarization layer overlying the elevated regions; depositing a fill material on the substrate to a thickness greater than the separation distance; forming a second planarization layer to overlie the fill material; removing a first portion of the fill material and a first portion of the second planarization layer, and leaving a second portion of the fill material and a second portion of the second planarization layer, the step of removing being performed by polishing the wafer during a first time period at a first polishing pad pressure and polishing the wafer during a second time period at a second polishing pad pressure wherein the second time period follows the first time period and wherein the second polishing pad pressure is less than the first polishing pad pressure; etching the second portion of the fill material using the second portion of the second planarization layer as an etch mask; and removing the second portion of the second planarization layer whereby the second portion of the fill material remains overlying the recessed regions.
Claim 15
Dependent Claim
20 words
The process of claim 11, wherein the step of depositing a fill material comprises chemical vapor deposition of silicon dioxide.
Claim 16
Dependent Claim
32 words
The process of claim 12, wherein the step of etching the second portion of the fill material comprises selectively etching the silicon dioxide in preference to the first and second planarization layers.
Claim 17
Dependent Claim
73 words
The method of claim 11 wherein the step of removing a first portion of the fill material and a first portion of the second planarization layer comprises: removing the first portion of the fill material and the first portion of the second planarization layer so that the second portion of the fill material which remains overlying the recessed regions defines a topographical pattern which is used to perform a subsequent lithographic alignment operation.
Claim 18
Dependent Claim
54 words
The method of claim 11 wherein the step of removing a first portion of the fill material and a first portion of the second planarization layer comprises: setting the first polishing pad pressure substantially within a range of 7.0-15.0 psi and setting the second polishing pad pressure substantially within a range of 2.5-5.0 psi.
Claim 19
Dependent Claim
80 words
The method of claim 11 wherein the step of removing a first portion of the fill material and a first portion of the second planarization layer comprises: setting the first polishing pad pressure so that a polishing selectively of fill material to second planarization layer is substantially 3:1 in the first time period and setting the second polishing pad pressure so that a polishing selectively of fill material to second planarization layer is substantially 10:1 in the second time period.
Claim 20
Dependent Claim
209 words
A process for fabricating a semiconductor device comprising the steps of: providing a semiconductor substrate having elevated regions and recessed regions therein, wherein a first planarization layer overlies the elevated regions; depositing a fill material to overlie the first planarization layer and the recessed regions; forming a second planarization layer to overlie the fill material; providing a chemical-mechanical-polishing apparatus having a polishing pad and means for variably applying a contact pressure between the polishing pad and the semiconductor substrate; polishing a first portion of the fill material, wherein the first portion is polished at a first contact pressure wherein the first contact pressure is created by the means for variably applying a contact pressure so that a polishing selectivity ratio between the fill material and the second planarization layer is N:1, N being a finite positive number; and polishing a second portion of the fill material at a second contact pressure wherein the second contact pressure is created by the means for variably applying a contact pressure so that a polishing selectivity ratio between the fill material and the second planarization layer is M:1, M being a finite positive number, wherein the first contact pressure is greater than the second contact pressure and wherein M is greater than N.
Claim 21
Dependent Claim
209 words
A process for fabricating a semiconductor device comprising the steps of: providing a semiconductor substrate having elevated regions and recessed regions therein, wherein a first planarization layer overlies the elevated regions; depositing a fill material to overlie the first planarization layer and the recessed regions; forming a second planarization layer to overlie the fill material; providing a chemical-mechanical-polishing apparatus having a polishing pad and means for variably applying a contact pressure between the polishing pad and the semiconductor substrate; polishing a first portion of the fill material, wherein the first portion is polished at a first contact pressure wherein the first contact pressure is created by the means for variably applying a contact pressure so that a polishing selectivity ratio between the fill material and the second planarization layer is N:1, N being a finite positive number; and polishing a second portion of the fill material at a second contact pressure wherein the second contact pressure is created by the means for variably applying a contact pressure so that a polishing selectivity ratio between the fill material and the second planarization layer is M:1, M being a finite positive number, wherein the first contact pressure is greater than the second contact pressure and wherein M is greater than N.
Claim 22
Dependent Claim
20 words
The process of claim 17, wherein the step of depositing a fill material comprises chemical vapor deposition of silicon dioxide.
Claim 23
Dependent Claim
34 words
The process of claim 17, wherein the step of forming a second planarization layer comprises depositing a layer selected from the group consisting of silicon nitride, boron nitride, silicon-rich silicon nitride, and boron oxynitride.
Claim 24
Dependent Claim
19 words
The method of claim 17 wherein N is substantially equal to 3 and M is substantially equal to 10.
References Cited (Backward Citations)
US4671851A
Cited
US4811522A
Cited
US4889586A
Cited
JPH02178926A
Cited
US5173439A
Cited
US5064683A
Cited
US5290396A
Cited
US5514245A
Cited
US5308438A
Cited
US5232875A
Cited
US5540811A
Cited
US5356513A
Cited
US5502007A
Cited
US5395801A
Cited
US5459096A
Cited
US5522965A
Cited
US5486265A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-09-08 | 2001-03-10 | 2001-09-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-09-08 | 2005-03-10 | 2005-09-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-09-08 | 2009-03-10 | 2009-09-09 | $7700.00 | Window Closed / Lapsed |