Process for making paper
Assignee: Sumitomo Chemical Co Ltd
•
Filing: 1997-09-25
•
Granted: 1999-02-02
•
Expires: 2017-09-25
Abstract
Abstract This invention relates to a process for papermaking which comprises forming a sheet in the presence of a neutral sizing agent and optionally a filler using as a paper quality improver a cationic polymer which is prepared by copolymerizing an acrylamide compound of the formula:CH2=C(R1)CONH2wherein R1 is hydrogen atom or methyl group, and an inorganic or organic acid salt of a diallylamine compound of the formula:[CH2=C(R2)CH2]2N-R3wherein R2 is hydrogen atom or methyl group, R3 is hydrogen atom or an alkyl having 1 to 6 carbon atoms, in the presence or absence of a vinyl monomer copolymerizable with said acrylamide compound and/or said diallylamine compound salt. When the above paper quality improver is used, the yield per each additive particularly in case of neutral or alkaline papermaking is excellent and hence the sizing properties are sufficiently given, and there can be obtained a paper having sufficiently improved paper strength.
Inventors
- 👤 Shigenao Kawakami
- 👤 Nobuyuki Matsuda
- 👤 Hiroshi Horiuchi
- 👤 Norio Kondo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 06:26
CPC Classifications
D; D21; D21H; D21H17/00; D21H17/20; D21H17/33; D21H17/34; D21H17/37; D21H17/375; D21H21/00; D21H21/06; D21H21/10; D21H21/14; D21H21/16
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
208 words
A process for papermaking which consists essentially of mixing an aqueous pulp slurry with a neutral sizing agent and a cationic polymer as a paper quality improver, and forming the mixed slurry into a paper sheet at a pH of 6 to 10, said cationic polymer showing Brookfield viscosity of at most about 73 ps at 25° C. in an aqueous solution containing 15% by weight of the polymer, and being prepared by copolymerizing the components consisting essentially of (a) an acrylamide compound of the formula: CH.sub.2 ═C(R.sub.1)CONH.sub.2 wherein R 1 is a hydrogen atom or methyl group; and (b) an inorganic or organic acid salt of a secondary or tertiary diallylamine compound of the formula: (CH.sub.2 ═C(R.sub.2)CH.sub.2).sub.2 N--R.sub.3 wherein R 2 is a hydrogen atom or methyl group, and R 3 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, wherein said component (a) is present in an amount of 50 to 97% by mole and said component (b) is present in an amount of 3 to 50% by mole, and wherein the cationic polymer is present in an amount of 0.01 to 2% by weight when calculated as solid polymer based on the weight of the paper in a dry state.
Claim 2
Dependent Claim
208 words
A process for papermaking which consists essentially of mixing an aqueous pulp slurry with a neutral sizing agent and a cationic polymer as a paper quality improver, and forming the mixed slurry into a paper sheet at a pH of 6 to 10, said cationic polymer showing Brookfield viscosity of at most about 73 ps at 25° C. in an aqueous solution containing 15% by weight of the polymer, and being prepared by copolymerizing the components consisting essentially of (a) an acrylamide compound of the formula: CH.sub.2 ═C(R.sub.1)CONH.sub.2 wherein R 1 is a hydrogen atom or methyl group; and (b) an inorganic or organic acid salt of a secondary or tertiary diallylamine compound of the formula: (CH.sub.2 ═C(R.sub.2)CH.sub.2).sub.2 N--R.sub.3 wherein R 2 is a hydrogen atom or methyl group, and R 3 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms, wherein said component (a) is present in an amount of 50 to 97% by mole and said component (b) is present in an amount of 3 to 50% by mole, and wherein the cationic polymer is present in an amount of 0.01 to 2% by weight when calculated as solid polymer based on the weight of the paper in a dry state.
Claim 3
Dependent Claim
16 words
The process of claim 1, wherein said aqueous pulp slurry is mixed additionally with a filler.
Claim 4
Dependent Claim
11 words
The process of claim 1, wherein said component (a) is acrylamide.
Claim 5
Dependent Claim
11 words
The process of claim 1, wherein said component (a) is methacrylamide.
Claim 6
Dependent Claim
27 words
The process of claim 1, wherein said component (b) is a salt of a member selected from the group consisting of diallylamine, diallylmethylamine, diallylethylamine, diallylbutylamine and dimethallylamine.
Claim 7
Dependent Claim
13 words
The process of claim 1, wherein said component (b) is a diallylamine salt.
Claim 8
Dependent Claim
38 words
The process of claim 1, wherein said cationic polymer is prepared by copolymerizing said components (a) and (b) in water or in a mixed solvent of water and a water-soluble solvent in the presence of a polymerization initiator.
Claim 9
Dependent Claim
37 words
The process of claim 1, wherein said cationic polymer is prepared by copolymerizing said components (a) and (b) at a temperature of 10° to 100° C. for 1 to 10 hours under an atmosphere of inert gas.
Claim 10
Dependent Claim
24 words
The process of claim 1, wherein said cationic polymer is present in an amount of 0.01 to 2% by weight in said paper sheet.
Claim 11
Dependent Claim
22 words
The process of claim 1, wherein said neutral sizing agent is selected from the group consisting of alkylketene dimers and alkenylsuccinic anhydrides.
Claim 12
Dependent Claim
20 words
The process of claim 1, wherein the cationic polymer is present in an amount of 0.05 to 1% by weight.
Claim 13
Dependent Claim
234 words
A process for papermaking which consists essentially of mixing an aqueous pulp slurry with a neutral sizing agent and a cationic polymer as a paper quality improver, and forming the mixed slurry into a paper sheet at a pH of 6 to 10, said cationic polymer showing Brookfield viscosity of at most about 73 ps at 25° C. in an aqueous solution containing 15% by weight of the polymer, and being prepared by copolymerizing the components consisting essentially of (a) an acrylamide compound of the formula: CH.sub.2 ═C(R.sub.1)CONH.sub.2 wherein R 1 is a hydrogen atom or methyl group; (b) an inorganic or organic acid salt of a secondary or tertiary diallylamine compound of the formula: (CH.sub.2 ═C(R.sub.2)CH.sub.2).sub.2 N--R.sub.3 wherein R 2 is a hydrogen atom or methyl group, and R 3 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms; and (c) a vinyl monomer copolymerizable with said component (a) and/or (b), wherein said component (a) is present in an amount of 50 to 97% by mole, said component (b) is present in an amount of 3 to 50% by mole, and said component (c) is present in an amount of not more than 30% by mole, and wherein the cationic polymer is present in an amount of 0.01 to 2% by weight when calculated as solid polymer based on the weight of the paper in a dry state.
Claim 14
Dependent Claim
234 words
A process for papermaking which consists essentially of mixing an aqueous pulp slurry with a neutral sizing agent and a cationic polymer as a paper quality improver, and forming the mixed slurry into a paper sheet at a pH of 6 to 10, said cationic polymer showing Brookfield viscosity of at most about 73 ps at 25° C. in an aqueous solution containing 15% by weight of the polymer, and being prepared by copolymerizing the components consisting essentially of (a) an acrylamide compound of the formula: CH.sub.2 ═C(R.sub.1)CONH.sub.2 wherein R 1 is a hydrogen atom or methyl group; (b) an inorganic or organic acid salt of a secondary or tertiary diallylamine compound of the formula: (CH.sub.2 ═C(R.sub.2)CH.sub.2).sub.2 N--R.sub.3 wherein R 2 is a hydrogen atom or methyl group, and R 3 is a hydrogen atom or an alkyl group having 1 to 6 carbon atoms; and (c) a vinyl monomer copolymerizable with said component (a) and/or (b), wherein said component (a) is present in an amount of 50 to 97% by mole, said component (b) is present in an amount of 3 to 50% by mole, and said component (c) is present in an amount of not more than 30% by mole, and wherein the cationic polymer is present in an amount of 0.01 to 2% by weight when calculated as solid polymer based on the weight of the paper in a dry state.
Claim 15
Dependent Claim
16 words
The process of claim 12, wherein said aqueous pulp slurry is mixed additionally with a filler.
Claim 16
Dependent Claim
83 words
The process of claim 12, wherein said component (c) is a nonionic vinyl monomer selected from the group consisting of methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, acrylonitrile, methacrylonitrile, styrene, hydroxyethyl acrylate, hydroxyethyl methacrylate and vinyl acetate; a cationic vinyl monomer selected from the group consisting of dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, diethylaminoethyl acrylate, diethylaminoethyl methacrylate, dimethylaminopropylacrylamide, dimethylaminopropylmethacrylamide, diallyldimethylammonium chloride, vinylpyridine and vinylpyrrolidone; or an anionic vinyl monomer selected from the group consisting of acrylic acid, methacrylic acid, vinylsulfonic acid and maleic acid.
Claim 17
Dependent Claim
40 words
The process of claim 12, wherein said cationic polymer is prepared by copolymerizing said components (a), (b) and (c) in water or in a mixed solvent of water and a water soluble solvent in the presence of a polymerization initiator.
Claim 18
Dependent Claim
38 words
The process of claim 12, wherein said cationic polymer is prepared by copolymerizing said components (a), (b) and (c) at a temperature of 10° to 100° C. for 1 to 10 hours under an atmosphere of inert gas.
Claim 19
Dependent Claim
24 words
The process of claim 12, wherein said cationic polymer is present in an amount of 0.01 to 2% by weight in said paper sheet.
Claim 20
Dependent Claim
22 words
The process of claim 12, wherein said neutral sizing agent is selected from the group consisting of alkylketene dimers and alkenylsuccinic anhydrides.
Claim 21
Dependent Claim
20 words
The process of claim 12, wherein the cationic polymer is present in an amount of 0.05 to 1% by weight.
References Cited (Backward Citations)
US3234076A
Cited
US4017431A
Cited
US4295931A
Cited
FR2393011A1
Cited
US4606773A
Cited
JPH07212521A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-02-01 | 2002-08-03 | 2003-02-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-02-01 | 2006-08-03 | 2007-02-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-02-01 | 2010-08-03 | 2011-02-02 | $7700.00 | Window Closed / Lapsed |