Surface coating for insulative materials, method of obtaining it and its application to shielding insulative cases
Assignee: Tecmachine SA
•
Filing: 1997-09-19
•
Granted: 2000-03-28
•
Expires: 2017-09-19
Abstract
Abstract A surface coating on an insulative material substrate, assuring protection against electromagnetic interference in corrosive environments, comprises two stacked metallic layers. The first layer, in contact with the substrate, is a layer of nickel-based alloy containing about 2% to 20% by weight of an element from group V B from the Periodic Table of the Elements. The second, surface layer is a layer of silver or one or its alloys. Applications include insulative material cases for electrical or electronic components including a shield consisting of a surface coating of this kind.
Inventors
- 👤 Christophe Heau
- 👤 Paul Berger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 05:09
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/20; C23C14/205; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12556; Y10T428/12569; Y10T428/12771; Y10T428/12861; Y10T428/12896; Y10T428/12944
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
85 words
A surface coating on an insulative material substrate, adapted to a protection against electromagnetic interference in corrosive environments, comprising two stacked metal layers, the first, in contact with said substrate, being a layer of nickel-based alloy containing about 80% to 98% by weight of nickel, and between about 2% and 20% by weight of at least one metal from group V B of the Periodic Table of the Elements, the second, surface layer being a layer based on metallic silver or one of its alloys.
Claim 2
Dependent Claim
85 words
A surface coating on an insulative material substrate, adapted to a protection against electromagnetic interference in corrosive environments, comprising two stacked metal layers, the first, in contact with said substrate, being a layer of nickel-based alloy containing about 80% to 98% by weight of nickel, and between about 2% and 20% by weight of at least one metal from group V B of the Periodic Table of the Elements, the second, surface layer being a layer based on metallic silver or one of its alloys.
Claim 3
Dependent Claim
35 words
The surface coating claimed in claim 1 wherein the concentration in the nickel-based alloy of said element from Group VB from the Periodic Table of the Element is between about 5% and 10% by weight.
Claim 4
Dependent Claim
22 words
The surface coating claimed in claim 1 wherein said element from Group VB of the Periodic Table of the Elements is vanadium.
Claim 5
Dependent Claim
22 words
The surface coating claimed in claim 1 wherein the thickness of said nickel-based alloy layer is between 0.02 μm and 1 μm.
Claim 6
Dependent Claim
32 words
The surface coating claimed in claim 1 wherein said surface layer is of metallic silver and the thickness of said layer based on metallic silver is between 0.2 μm and 2 μm.
Claim 7
Dependent Claim
52 words
The surface coating claimed in claim 1 wherein said surface layer is a silver-based alloy and the thickness of said silver alloy-based layer is between n×0.2 μm and n×2 μm where "n" is the value of the ratio between the resistivity of said silver-based alloy and the resistivity of the metallic silver.
Claim 8
Dependent Claim
19 words
The surface coating claimed in claim 1 wherein said insulative material is chosen from polymer materials and composite materials.
Claim 9
Dependent Claim
17 words
The surface coating claimed in claim 7 wherein said composite material comprises a polymer and reinforcing fibers.
Claim 10
Dependent Claim
24 words
The surface coating claimed in claim 1 wherein said nickel-based alloy layers and said silver-based surface layer are applied by a vacuum deposition technology.
Claim 11
Dependent Claim
15 words
The surface coating claimed in claim 9 wherein said vacuum deposition technology is cathode sputtering.
Claim 12
Dependent Claim
32 words
A shielded insulative material case for electrical or electronic components wherein the shield is a surface coating as claimed in claims 1, 2, 3, 4, 5, 6, 7, 8, 9 or 10.
Claim 13
Dependent Claim
123 words
A surface coating on an insulative material substrate, adapted to assure protection against electromagnetic interference in corrosive environments, comprising two stacked metal layers, the first, in contact with said substrate, being a layer of nickel-based alloy containing 80% to 98% by weight of nickel, said nickel based alloy containing between about 2% and 20% by weight of at least one metal from group V B of the Periodic Table of the Elements the second, surface layer being a layer based on metallic silver or one of its alloys, the surface resistivity of said surface coating capable of remaining stable when said surface coating is subjected for 48 hours to an accelerated corrosion test, carried out in accordance with French standard NF C 20-711.
Claim 14
Dependent Claim
123 words
A surface coating on an insulative material substrate, adapted to assure protection against electromagnetic interference in corrosive environments, comprising two stacked metal layers, the first, in contact with said substrate, being a layer of nickel-based alloy containing 80% to 98% by weight of nickel, said nickel based alloy containing between about 2% and 20% by weight of at least one metal from group V B of the Periodic Table of the Elements the second, surface layer being a layer based on metallic silver or one of its alloys, the surface resistivity of said surface coating capable of remaining stable when said surface coating is subjected for 48 hours to an accelerated corrosion test, carried out in accordance with French standard NF C 20-711.
Claim 15
Dependent Claim
36 words
The surface coating claimed in claim 12 wherein the concentration in the nickel-based alloy of said element from group V B from the Periodic Table of the Elements is between about 5% and 10% by weight.
Claim 16
Dependent Claim
22 words
The surface coating claimed in claim 12 wherein said element from group VB from the Periodic Table of the Elements is vanadium.
Claim 17
Dependent Claim
22 words
The surface coating claimed in claim 12 wherein the thickness of said nickel-based alloy layer is between 0.02 μm and 1 μm.
Claim 18
Dependent Claim
32 words
The surface coating claimed in claim 12 wherein said surface layer is of metallic silver and the thickness of said layer based on metallic silver is between 0.2 μm and 2 μm.
Claim 19
Dependent Claim
16 words
The surface coating claimed in claim 12 wherein said resistivity is between 35 and 260 mΩ.
References Cited (Backward Citations)
EP0140032A1
Cited
DE4322512A1
Cited
GB2270421A
Cited
WO1994018003A1
Cited
WO1994021099A1
Cited
DE4443530A1
Cited
US5585139A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-03-28 | 2003-09-27 | 2004-03-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-03-28 | 2007-09-27 | 2008-03-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-03-28 | 2011-09-27 | 2012-03-28 | $7700.00 | Window Closed / Lapsed |