Patent US3935168A successfully refreshed from Google Patents.
US3935168A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for preparing polyesters from terephthalic acid in the presence of phosphonium compounds
Assignee: Imperial Chemical Industries Ltd
•
Filing: 1973-12-12
•
Granted: 1976-01-27
•
Expires: 1993-12-12
Abstract
Abstract Preparation of fibre-or film-forming polyester or copolyester wherein terephthalic acid or mixture with a second dicarboxylic acid is reacted with glycol and polycondensed with a phosphonium compound having at least one aryl constituent.
Inventors
- 👤 Robert Benson Rashbrook
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 13:45
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/78; C08G63/82; C08G63/87
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
159 words
A process for the preparation of a fiber or film forming polyester or copolyester wherein terephthalic acid or a mixture of terephthalic acid with up to 25 molecules per 100 molecules of a second dicarboxylic acid is reacted with at least one glycol selected from the group consisting of HO(CH 2 ) n OH where n is greater than 1 and not greater than 10 and 1:4-hydroxymethylcyclohexane at elevated temperature and the resultant ester or mixture of esters is polycondensed in the presence of a polycondensation catalyst selected from the group consisting of soluble antimony compounds and soluble germanium compounds, at temperatures above said elevated temperature until a high molecular weight polyester or copolyester is formed, characterized in that during the reaction there is present a compound of the formula: ##EQU3## in amount not less than 0.001 percent by weight based on the terephthalic acid and not greater than about 0.5 percent by weight based on the terephthalic acid.
Claim 2
Dependent Claim
159 words
A process for the preparation of a fiber or film forming polyester or copolyester wherein terephthalic acid or a mixture of terephthalic acid with up to 25 molecules per 100 molecules of a second dicarboxylic acid is reacted with at least one glycol selected from the group consisting of HO(CH 2 ) n OH where n is greater than 1 and not greater than 10 and 1:4-hydroxymethylcyclohexane at elevated temperature and the resultant ester or mixture of esters is polycondensed in the presence of a polycondensation catalyst selected from the group consisting of soluble antimony compounds and soluble germanium compounds, at temperatures above said elevated temperature until a high molecular weight polyester or copolyester is formed, characterized in that during the reaction there is present a compound of the formula: ##EQU3## in amount not less than 0.001 percent by weight based on the terephthalic acid and not greater than about 0.5 percent by weight based on the terephthalic acid.
Claim 3
Dependent Claim
152 words
A process for the preparation of fiber or film forming polyester from terephthalic acid and a glycol selected from the group consisting of HO(CH 2 ) n OH where n is greater than 1 and not greater than 10 and 1:4-hydroxymethylcyclohexane, comprising conducting the esterification and polycondensation reactions in the presence of from 5 to 25 molecules per 100 molecules of terephthalic acid of a second dicarboxylic acid selected from the group consisting of isophthalic acid and sebacic acid and a compound of the formula: ##EQU4## in amounts not less than 0.001 percent by weight based on the terephthalic acid and not greater than about 0.5 percent by weight based on the terephthalic acid, said esterification being conducted at elevated temperature and said polycondensation being conducted in the presence of a polycondensation catalyst selected from the group consisting of soluble antimony compounds and soluble germanium compounds at temperatures above said elevated temperature.
Claim 4
Dependent Claim
152 words
A process for the preparation of fiber or film forming polyester from terephthalic acid and a glycol selected from the group consisting of HO(CH 2 ) n OH where n is greater than 1 and not greater than 10 and 1:4-hydroxymethylcyclohexane, comprising conducting the esterification and polycondensation reactions in the presence of from 5 to 25 molecules per 100 molecules of terephthalic acid of a second dicarboxylic acid selected from the group consisting of isophthalic acid and sebacic acid and a compound of the formula: ##EQU4## in amounts not less than 0.001 percent by weight based on the terephthalic acid and not greater than about 0.5 percent by weight based on the terephthalic acid, said esterification being conducted at elevated temperature and said polycondensation being conducted in the presence of a polycondensation catalyst selected from the group consisting of soluble antimony compounds and soluble germanium compounds at temperatures above said elevated temperature.
Claim 5
Dependent Claim
12 words
A process according to claim 1 wherein said glycol is ethylene glycol.
Claim 6
Dependent Claim
12 words
A process according to claim 2 wherein said glycol is ethylene glycol.
References Cited (Backward Citations)
US3427287A
Cited
JPS4210622Y1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-01-26 | 1979-07-28 | 1980-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-01-26 | 1983-07-28 | 1984-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-01-26 | 1987-07-28 | 1988-01-27 | $7700.00 | Window Closed / Lapsed |