Hydrometallurgical treatment of nickel and copper bearing intermediates
Assignee: Viridian Inc Canada
•
Filing: 1975-05-23
•
Granted: 1976-08-17
•
Expires: 1995-05-23
Abstract
Abstract According to the process described, non-ferrous metal values, particularly nickel, copper and/or cobalt, are extracted from metallurgical intermediates, such as matte and speiss, by reacting the material under oxidizing conditions at a pH of about 4.5 to 6.5 with an ammonia free aqueous solution containing ammonium sulphate, sodium sulphate and/or nickel sulphate. The reaction-products of this operation are then mixed with sulphuric acid under ambient conditions to decrease the pH to about 3-4.5 and to dissolve the non-ferrous metals in the solution which is then separated from the undissolved residue. The process is particularly useful in treating intermediates containing precious metals in that the precious metals are substantially completely recovered in concentrated form in the undissolved residue.
Inventors
- 👤 Sjaak Johan Van Der Meulen
- 👤 Bauke Weizenbach
- 👤 Vladimir N. Mackiw
- 👤 Theodore Andrew Kinjerski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 23:01
CPC Classifications
C; C22; C22B; C22B15/00; C22B15/0063; C22B15/0065; C22B15/0067; C22B15/0071; C22B15/0078; C22B15/0084; C22B15/0089; C22B15/0093; C22B23/00; C22B23/04; C22B23/0407; C22B23/0415; C22B23/043; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
238 words
A method of treating metal bearing intermediate materials which contain (a) one or more metals selected from the group consisting of nickel, cobalt and copper, (b) sulphide sulphur in an amount less than that required to combine stoichiometrically with said metals as sulphates and, optionally, (c) one or more precious metals selected from the group consisting of palladium, platinum, silver and gold, said method comprising the steps of: forming a slurry of finely divided particles of said materials in a substantially ammonia-free aqueous solution containing from about 25 to about 300 grams per liter of at least one sulphate salt selected from the group consisting of ammonium sulphate, sodium sulphate and nickel sulphate; adjusting the pH of said slurry to a level within the range of 4.5 - 6.5 and reacting said adjusted slurry at a temperature within the range of about 80° to about 180°C. under a positive partial pressure of oxygen with a free oxygen-containing gas; continuing said reaction to convert said group (a) metals to hydroxides; cooling the thus-reacted slurry to below about 100°C. and reducing the pressure to atmospheric; adding sulphuric acid to said cooled slurry in an amount sufficient to decrease the pH thereof to a value within the range of about 3 to about 4.5 and agitating said acid-treated slurry to dissolve said group (a) metal hydroxides in the solution, and separating solution containing dissolved group (a) metals from said acid-treated slurry.
Claim 2
Independent Claim
238 words
A method of treating metal bearing intermediate materials which contain (a) one or more metals selected from the group consisting of nickel, cobalt and copper, (b) sulphide sulphur in an amount less than that required to combine stoichiometrically with said metals as sulphates and, optionally, (c) one or more precious metals selected from the group consisting of palladium, platinum, silver and gold, said method comprising the steps of: forming a slurry of finely divided particles of said materials in a substantially ammonia-free aqueous solution containing from about 25 to about 300 grams per liter of at least one sulphate salt selected from the group consisting of ammonium sulphate, sodium sulphate and nickel sulphate; adjusting the pH of said slurry to a level within the range of 4.5 - 6.5 and reacting said adjusted slurry at a temperature within the range of about 80° to about 180°C. under a positive partial pressure of oxygen with a free oxygen-containing gas; continuing said reaction to convert said group (a) metals to hydroxides; cooling the thus-reacted slurry to below about 100°C. and reducing the pressure to atmospheric; adding sulphuric acid to said cooled slurry in an amount sufficient to decrease the pH thereof to a value within the range of about 3 to about 4.5 and agitating said acid-treated slurry to dissolve said group (a) metal hydroxides in the solution, and separating solution containing dissolved group (a) metals from said acid-treated slurry.
Claim 3
Dependent Claim
23 words
The process according to claim 1 wherein the sulphate salt concentration of the aqueous slurrying solution is about 50 to about 100 g.p.l.
Claim 4
Dependent Claim
13 words
The process according to claim 1 wherein the sulphate salt is ammonium sulphate.
Claim 5
Dependent Claim
32 words
The process according to claim 1, wherein the slurry is reacted at an oxygen overpressure between about 20 and about 100 p.s.i. and at a temperature between about 120°C. and about 150°C.
Claim 6
Dependent Claim
36 words
The process according to claim 1, wherein said materials contain at least one group (c) metal and said metal is recovered in concentrated form with the undissolved residue from the group (a) metal hydroxides dissolution step.
References Cited (Backward Citations)
US3798304A
Cited
US3684489A
Cited
US3744994A
Cited
US3793432A
Cited
US3869360A
Cited
US3909248A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-08-17 | 1980-02-16 | 1980-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-08-17 | 1984-02-16 | 1984-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-08-17 | 1988-02-16 | 1988-08-17 | $7700.00 | Window Closed / Lapsed |