US4016589A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Semiconductor device
Assignee: Omron Corp
•
Filing: 1974-03-26
•
Granted: 1977-04-05
•
Expires: 1994-03-26
Abstract
Abstract A semiconductor composite having a rectifying characteristic is provided by first forming an insulating film of a semiconductor compound such as SiO 2 on a semiconductor substrate of N-type Si to a uniform thickness of 27A to 500A, for example, and then further depositing thereon a tin oxide film. The intermediate insulating film between the SnO 2 film and the semiconductor substrate decreases the reverse leakage current, raises the reverse breakdown voltage and makes uniform the reverse breakdown voltage. The semiconductor composite of the present invention, as subjected to a predetermined value of light energy, shows an excellent switching characteristic with respect to a voltage applied to the composite in a reverse direction. Also the semiconductor composite of the present invention, as supplied with a certain value of reverse bias voltage or with no bias, shows an excellent switching characteristic with respect to light energy applied to the composite.
Inventors
- 👤 Shigeru Tanimura
- 👤 Nobuaki Miura
- 👤 Osamu Asano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 03:24
CPC Classifications
H; H10; H10F; H10F10/00; H10F10/10; H10F10/18; H10F99/00; H10D; H10D1/00; H10D1/60; H10D1/62; H10D1/66; H10D99/00; H10F39/00; H10F39/10; H10F39/103; Y; Y02; Y02E; Y02E10/00; Y02E10/50
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
206 words
A photosensitive semiconductor device comprising: a composite including: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, an insulating layer deposited in substantially uniform thickness on said semiconductor substrate, the material layer being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , and said insulating layer being in the range of from 27A to 500A in thickness, a tin oxide layer deposited on said insulating layer, metal electrodes deposited on said tin oxide layer and the substrate, said composite having a barrier with rectifying and photoelectric characteristics between said substrate and said tin oxide layer, means connected to said electrodes for applying a reverse bias voltage across the composite less than the reverse breakdown voltage thereof, said composite being adapted for receiving radiation energy at said barrier, and means connected to said electrodes for withdrawing a photosensitive electrical output from between said tin oxide layer and said substrate, whereby said device exhibits a radiation energy response characteristic which is a function of the level of said applied reverse bias voltage and is substantially increased for a thickness of said insulating layer within said range relatively to a thickness outside of said range.
Claim 2
Dependent Claim
206 words
A photosensitive semiconductor device comprising: a composite including: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, an insulating layer deposited in substantially uniform thickness on said semiconductor substrate, the material layer being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , and said insulating layer being in the range of from 27A to 500A in thickness, a tin oxide layer deposited on said insulating layer, metal electrodes deposited on said tin oxide layer and the substrate, said composite having a barrier with rectifying and photoelectric characteristics between said substrate and said tin oxide layer, means connected to said electrodes for applying a reverse bias voltage across the composite less than the reverse breakdown voltage thereof, said composite being adapted for receiving radiation energy at said barrier, and means connected to said electrodes for withdrawing a photosensitive electrical output from between said tin oxide layer and said substrate, whereby said device exhibits a radiation energy response characteristic which is a function of the level of said applied reverse bias voltage and is substantially increased for a thickness of said insulating layer within said range relatively to a thickness outside of said range.
Claim 3
Dependent Claim
13 words
The semiconductor composite according to claim 1, in which said semiconductor is Si.
Claim 4
Dependent Claim
15 words
The semiconductor composite according to claim 1, in which said semiconductor is N-type conductivity Si.
Claim 5
Dependent Claim
16 words
The semiconductor composite according to claim 1, in which said insulating material is SiO 2 .
Claim 6
Dependent Claim
23 words
The semiconductor composite according to claim 4, in which the thickness of the SiO 2 layer is chosen to be 27A to 300A.
Claim 7
Dependent Claim
23 words
The semiconductor composite according to claim 4 in which the thickness of the SiO 2 layer is chosen to be 27A to 100A.
Claim 8
Dependent Claim
25 words
The semiconductor composite according to claim 1, in which said tin oxide layer is of a thickness to transmit radiation energy therethrough to said barrier.
Claim 9
Dependent Claim
30 words
The semiconductor device according to claim 7 wherein said reverse bias voltage applying means comprises a means for controlling the level of the reverse bias voltage applied to said composite.
Claim 10
Dependent Claim
30 words
The semiconductor device according to claim 8 in which said device is disposed to permit a constant level of radiation energy to be applied to the barrier of said device.
Claim 11
Dependent Claim
21 words
The semiconductor device according to claim 7 in which a constant level of reverse bias voltage is applied to the composite.
Claim 12
Dependent Claim
16 words
The semiconductor device according to claim 7 in which said reverse bias voltage is zero volts.
Claim 13
Dependent Claim
108 words
A semiconductor composite according to claim 1, in which said semiconductor substrate has a main surface including a first portion bounded by a second portion, and wherein a second insulating layer of a substantially uniform thickness greater than the thickness of said first mentioned insulating layer is provided on said second portion of the main surface of said substrate, having an opening therein defining said first portion of said main surface, said first mentioned insulating layer is deposited on said first portion of said main surface of said substrate defined by said second insulating layer, and said tin oxide film is deposited on said first mentioned insulating layer.
Claim 14
Dependent Claim
22 words
The semiconductor device according to claim 12 in which said tin oxide layer is of a thickness to transmit radiation energy therethrough.
Claim 15
Dependent Claim
45 words
The semiconductor device according to claim 13 wherein said reverse bias voltage applying means comprises a voltage source for supplying a bias voltage between said tin oxide layer and said semiconductor substrate in a reverse direction with respect to the rectifying characteristic of the device.
Claim 16
Dependent Claim
198 words
A voltage responsive semiconductor switching device comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge, and GaAs, an insulating layer deposited on said semiconductor substrate, the material of said insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , and said insulating layer being in the range of from about 27A to 500A in thickness, a transparent tin oxide layer deposited on said insulating layer, said semiconductor device having a barrier with rectifying and photoelectric characteristics between said substrate and said tin oxide layer, said barrier having a predetermined reverse breakdown voltage, said device being adapted to receive bias radiation energy at said barrier of said device, means for applying a reverse voltage across the device less than the reverse breakdown voltage of said device, and means for withdrawing an electrical output from between said tin oxide layer and said substrate, whereby said device exhibits a voltage response characteristic which is a function of bias radiation energy received at said barrier and is substantially increased for said thickness of said insulating layer within said range relative to thicknesses thereof outside of said range.
Claim 17
Dependent Claim
198 words
A voltage responsive semiconductor switching device comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge, and GaAs, an insulating layer deposited on said semiconductor substrate, the material of said insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , and said insulating layer being in the range of from about 27A to 500A in thickness, a transparent tin oxide layer deposited on said insulating layer, said semiconductor device having a barrier with rectifying and photoelectric characteristics between said substrate and said tin oxide layer, said barrier having a predetermined reverse breakdown voltage, said device being adapted to receive bias radiation energy at said barrier of said device, means for applying a reverse voltage across the device less than the reverse breakdown voltage of said device, and means for withdrawing an electrical output from between said tin oxide layer and said substrate, whereby said device exhibits a voltage response characteristic which is a function of bias radiation energy received at said barrier and is substantially increased for said thickness of said insulating layer within said range relative to thicknesses thereof outside of said range.
Claim 18
Dependent Claim
195 words
A photosensitive semiconductor device comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, an insulating layer deposited on said semiconductor substrate, the material of said insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , and said insulating layer being in the range of from 27A to 500A in thickness, a tin oxide layer deposited on said insulating layer, said semiconductor device having a barrier with a rectifying and photosensitive characteristic between said substrate and said tin oxide layer, said barrier having a predetermined reverse breakdown voltage, means for applying a reverse bais voltage across the device less than the reverse breakdown voltage of said device, said device being adapted to receive radiation energy at said barrier of said device, and means for withdrawing a photosensitive electrical output from between said tin oxide layer and said substrate, said device exhibiting a radiation energy response characteristic which is a function of said applied reverse bias voltage and is substantially increased for a thickness of said insulating layer within said range thereof relative to a thickness outside of said range.
Claim 19
Dependent Claim
195 words
A photosensitive semiconductor device comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, an insulating layer deposited on said semiconductor substrate, the material of said insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , and said insulating layer being in the range of from 27A to 500A in thickness, a tin oxide layer deposited on said insulating layer, said semiconductor device having a barrier with a rectifying and photosensitive characteristic between said substrate and said tin oxide layer, said barrier having a predetermined reverse breakdown voltage, means for applying a reverse bais voltage across the device less than the reverse breakdown voltage of said device, said device being adapted to receive radiation energy at said barrier of said device, and means for withdrawing a photosensitive electrical output from between said tin oxide layer and said substrate, said device exhibiting a radiation energy response characteristic which is a function of said applied reverse bias voltage and is substantially increased for a thickness of said insulating layer within said range thereof relative to a thickness outside of said range.
Claim 20
Dependent Claim
196 words
In a semiconductor composite device comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, said substrate having any incidentally formed oxide removed, an insulating layer on said substrate, a tin oxide layer deposited on said insulating layer said semiconductor composite device having a barrier with rectifying and photosensitive characteristics between said substrate and said tin oxide layer, and being adapted to receive radiation energy at said barrier of said barrier, means for applying a reverse bias voltage across the device less than reverse breakdown voltage, and means for withdrawing a photosensitive electrical output from between said tin oxide layer and said substrate, the improvement which comprises: said insulating layer being formed on said semiconductor substrate in a uniform thickness in the range of from 27A to 500A, and the material thereon being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , said device having a radiation energy response which is a function of said applied reverse bias voltage and which is increased for said uniform insulating layer in said range of thickness relative to an insulating layer outside of said range.
Claim 21
Dependent Claim
196 words
In a semiconductor composite device comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, said substrate having any incidentally formed oxide removed, an insulating layer on said substrate, a tin oxide layer deposited on said insulating layer said semiconductor composite device having a barrier with rectifying and photosensitive characteristics between said substrate and said tin oxide layer, and being adapted to receive radiation energy at said barrier of said barrier, means for applying a reverse bias voltage across the device less than reverse breakdown voltage, and means for withdrawing a photosensitive electrical output from between said tin oxide layer and said substrate, the improvement which comprises: said insulating layer being formed on said semiconductor substrate in a uniform thickness in the range of from 27A to 500A, and the material thereon being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , said device having a radiation energy response which is a function of said applied reverse bias voltage and which is increased for said uniform insulating layer in said range of thickness relative to an insulating layer outside of said range.
Claim 22
Dependent Claim
73 words
The composite device of claim 17 wherein the surface of said substrate has at most an even layer of naturally formed semiconductor oxide thereon, and onto which said insulating layer is deposited, any uneven naturally formed semiconductor oxide thereon being removed by washing said substrate with an etching solution to remove any said uneven naturally formed semiconductor oxide thereon and said insulating layer is positively formed by thermal reaction with an oxidizing gas.
Claim 23
Dependent Claim
40 words
The composite device of claim 18 wherein said insulating layer is formed by heating a Si substrate in a reaction zone for at least 5 minutes at 400° C or more thereby to form SiO 2 as said insulating layer.
Claim 24
Dependent Claim
134 words
In a semiconductor composite comprising an N-type Si semiconductor substrate, an insulating layer on said substrate, and a tin oxide layer deposited on said insulating layer and forming rectifying and photosensitive barrier between said tin oxide layer and said substrate, a metal electrode deposited on a portion of said tin oxide layer, and means for withdrawing an electrical signal from said composite representative of radiation energy received by said barrier and reverse bias voltage applied to said composite, the improvement which comprises: said insulating layer between said substrate and said tin oxide layer comprising an SiO 2 layer having substantially uniform characteristics and thickness, being at least about 27A in thickness, and being substantially uniformly formed by heating said substrate in an oxidizing gas under conditions to obtain said substantially uniform characteristics and thickness.
Claim 25
Dependent Claim
134 words
In a semiconductor composite comprising an N-type Si semiconductor substrate, an insulating layer on said substrate, and a tin oxide layer deposited on said insulating layer and forming rectifying and photosensitive barrier between said tin oxide layer and said substrate, a metal electrode deposited on a portion of said tin oxide layer, and means for withdrawing an electrical signal from said composite representative of radiation energy received by said barrier and reverse bias voltage applied to said composite, the improvement which comprises: said insulating layer between said substrate and said tin oxide layer comprising an SiO 2 layer having substantially uniform characteristics and thickness, being at least about 27A in thickness, and being substantially uniformly formed by heating said substrate in an oxidizing gas under conditions to obtain said substantially uniform characteristics and thickness.
Claim 26
Dependent Claim
16 words
The composite of claim 20 wherein the SiO 2 layer is about 27A to 300A thick.
Claim 27
Dependent Claim
162 words
A photosensitive semiconductor composite comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, said substrate comprising at least one main surface having substantially no naturally formed oxide of the semiconductor thereon, an insulating layer deposited on said main surface of said semiconductor substrate, the material of said insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 , and GeO 2 and said insulating layer being in the range of from about 27A to 500A in thickness, a transparent tin oxide layer deposited on said insulating layer, said composite having a barrier between said substrate and said tin oxide layer with rectifying and photoelectric characteristics and having a predetermined reverse breakdown voltage, said composite exhibiting a photosensitive response characteristic to radiation received at said barrier through said transparent tin oxide layer in accordance with a reverse bias voltage, less than the predetermined reverse breakdown voltage, applied across said barrier.
Claim 28
Dependent Claim
162 words
A photosensitive semiconductor composite comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, said substrate comprising at least one main surface having substantially no naturally formed oxide of the semiconductor thereon, an insulating layer deposited on said main surface of said semiconductor substrate, the material of said insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 , and GeO 2 and said insulating layer being in the range of from about 27A to 500A in thickness, a transparent tin oxide layer deposited on said insulating layer, said composite having a barrier between said substrate and said tin oxide layer with rectifying and photoelectric characteristics and having a predetermined reverse breakdown voltage, said composite exhibiting a photosensitive response characteristic to radiation received at said barrier through said transparent tin oxide layer in accordance with a reverse bias voltage, less than the predetermined reverse breakdown voltage, applied across said barrier.
Claim 29
Dependent Claim
25 words
A semiconductor composite as recited in claim 22 in which said insulating layer is in the range of from about 27A to 100A in thickness.
Claim 30
Dependent Claim
168 words
A voltage responsive semiconductor composite comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, said substrate comprising at least one main surface having substantially no naturally formed oxide of the semiconductor thereon, an insulating layer deposited on said main surface of said semiconductor substrate, the material of said insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 , and GeO 2 and said insulating layer being in the range of from about 27A to 500A in thickness, a transparent tin oxide layer deposited on said insulating layer, said composite having a barrier between said substrate and said tin oxide layer with rectifying and photoelectric characteristics and having a predetermined reverse breakdown voltage, said composite exhibiting a voltage responsive characteristic to a reverse voltage applied across said barrier, less than the predetermined reverse breakdown voltage, which is a function of the level of radiation energy received at said barrier through said transparent tin oxide layer.
Claim 31
Dependent Claim
168 words
A voltage responsive semiconductor composite comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, said substrate comprising at least one main surface having substantially no naturally formed oxide of the semiconductor thereon, an insulating layer deposited on said main surface of said semiconductor substrate, the material of said insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 , and GeO 2 and said insulating layer being in the range of from about 27A to 500A in thickness, a transparent tin oxide layer deposited on said insulating layer, said composite having a barrier between said substrate and said tin oxide layer with rectifying and photoelectric characteristics and having a predetermined reverse breakdown voltage, said composite exhibiting a voltage responsive characteristic to a reverse voltage applied across said barrier, less than the predetermined reverse breakdown voltage, which is a function of the level of radiation energy received at said barrier through said transparent tin oxide layer.
Claim 32
Dependent Claim
25 words
A semiconductor composite as recited in claim 24 in which said insulating layer is in the range of from about 27A to 100A in thickness.
Claim 33
Dependent Claim
145 words
A voltage responsive semiconductor composite comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, said substrate comprising at least one main surface pretreated to reduce any naturally formed oxide of the semiconductor thereon to substantially uniform thickness, an insulating layer deposited on said main surface of said semiconductor substrate over any naturally formed oxide thereon to form a substantially uniform thickness of an insulating layer in the range of from about 27A to 500A in thickness, the materil of the deposited insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , said composite exhibiting a photosensitive response characteristic to radiation received at said barrier through said transparent tin oxide layer in accordance with a reverse bias voltage, less than the predetermined reverse breakdown voltage, applied across said barrier.
Claim 34
Dependent Claim
145 words
A voltage responsive semiconductor composite comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, said substrate comprising at least one main surface pretreated to reduce any naturally formed oxide of the semiconductor thereon to substantially uniform thickness, an insulating layer deposited on said main surface of said semiconductor substrate over any naturally formed oxide thereon to form a substantially uniform thickness of an insulating layer in the range of from about 27A to 500A in thickness, the materil of the deposited insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , said composite exhibiting a photosensitive response characteristic to radiation received at said barrier through said transparent tin oxide layer in accordance with a reverse bias voltage, less than the predetermined reverse breakdown voltage, applied across said barrier.
Claim 35
Dependent Claim
25 words
A semiconductor composite as recited in claim 26 in which said insulating layer is in the range of from about 27A to 100A in thickness.
Claim 36
Dependent Claim
150 words
A voltage responsive semiconductor composite comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, said substrate comprising at least one main surface pretreated to reduce any naturally formed oxide of the semiconductor thereon to substantially uniform thickness, an insulating layer deposited on said main surface of said semiconductor substrate over any naturally formed oxide thereon to form a substantially uniform thickness of an insulating layer in the range of from about 27A to 500A in thickness, the material of the deposited insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , said composite exhibiting a voltage responsive characteristic to a reverse voltage applied across said barrier, less than the predetermined reverse breakdown voltage, which is a function of the level of radiation energy received at said barrier through said transparent tin oxide layer.
Claim 37
Dependent Claim
150 words
A voltage responsive semiconductor composite comprising: a substrate of a semiconductor selected from the group consisting of Si, Ge and GaAs, said substrate comprising at least one main surface pretreated to reduce any naturally formed oxide of the semiconductor thereon to substantially uniform thickness, an insulating layer deposited on said main surface of said semiconductor substrate over any naturally formed oxide thereon to form a substantially uniform thickness of an insulating layer in the range of from about 27A to 500A in thickness, the material of the deposited insulating layer being selected from the group consisting of SiO 2 , Si 3 N 4 and GeO 2 , said composite exhibiting a voltage responsive characteristic to a reverse voltage applied across said barrier, less than the predetermined reverse breakdown voltage, which is a function of the level of radiation energy received at said barrier through said transparent tin oxide layer.
Claim 38
Dependent Claim
25 words
A semiconductor composite as recited in claim 28 in which said insulating layer is in the range of from about 27A to 100A in thickness.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-04 | 1980-10-04 | 1981-04-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-04 | 1984-10-04 | 1985-04-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-04 | 1988-10-04 | 1989-04-05 | $7700.00 | Window Closed / Lapsed |