Corrugating adhesive compositions containing thermoplastic polymer, thermosetting resin, and starch
Assignee: Ingredion Inc
•
Filing: 1975-12-10
•
Granted: 1977-04-19
•
Expires: 1995-12-10
Abstract
Abstract Improved adhesive compositions useful in the manufacturing of corrugated boards are disclosed; said compositions being comprised of a mixture of: (a) a crosslinkable water dispersible polymer, (b) an ungelatinized starch, (c) a urea-formaldehyde resin, (d) an acidic metal salt, and (e) water.
Inventors
- 👤 Paul R. Demko
- 👤 Frank J. Washabaugh
- 👤 Robert H. Williams
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:57
CPC Classifications
C; C09; C09J; C09J133/00; C09J133/04; C09J133/06; C09J133/062; C08; C08K; C08K3/00; C08K3/18; C08K3/24; C08L; C08L31/00; C08L31/02; C08L31/04; C08L33/00; C08L33/04; C08L33/06; C09J103/00; C09J103/02; C09J131/00; C09J131/02; C09J131/04; C09J161/00; C09J161/20; C08L2666/00; C08L2666/02; C08L2666/04; C08L2666/54; C08L3/00; C08L3/02; C08L61/00; C08L61/20; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24628; Y10T428/24669; Y10T428/24694
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
219 words
A corrugating adhesive composition capable of yielding dry films which are characterized by their outstanding water resistance and thermal stability; said adhesive composition comprising a mixture of (a) a crosslinkable polymer in aqueous emulsion form selected from the group consisting of vinyl acetate homopolymers, copolymers of vinyl acetate with one or more ethylenically unsaturated copolymerizable comonomers, and copolymers of C 1 -C 8 alkyl esters of acrylic and methacrylic acids with one or more ethylenically unsaturated copolymerizable comonomers; (b) an ungelatinized starch which is present in amount ranging from 0.5 to 6.0 times the amount of the resinous content of said polymer, (c) a thermosetting resin selected from the group consisting of dimethylol ethylene urea, dimethylol methoxy ethyl carbamate, dimethylol isobutyl carbamate, dimethylol hydroxyethyl triazone, methylated methylol melamine, melamine-formaldehyde, and urea-formaldehyde; said thermosetting resin being present in an amount ranging from about 0.1 to about 5.0% by weight, of the total composition, (d) an acidic metal salt curing agent selected from the group consisting of chromium nitrate, chromium perchlorate, zirconium nitrate, aluminum chloride, zirconium oxychloride, aluminum sulfate and aluminum nitrate; said acidic metal salt curing agent being present in an amount ranging from about 0.1 to about 2.0%, by weight, of the total composition, and (e) water; said composition having a viscosity of from about 100 to 2500 cps.
Claim 2
Dependent Claim
219 words
A corrugating adhesive composition capable of yielding dry films which are characterized by their outstanding water resistance and thermal stability; said adhesive composition comprising a mixture of (a) a crosslinkable polymer in aqueous emulsion form selected from the group consisting of vinyl acetate homopolymers, copolymers of vinyl acetate with one or more ethylenically unsaturated copolymerizable comonomers, and copolymers of C 1 -C 8 alkyl esters of acrylic and methacrylic acids with one or more ethylenically unsaturated copolymerizable comonomers; (b) an ungelatinized starch which is present in amount ranging from 0.5 to 6.0 times the amount of the resinous content of said polymer, (c) a thermosetting resin selected from the group consisting of dimethylol ethylene urea, dimethylol methoxy ethyl carbamate, dimethylol isobutyl carbamate, dimethylol hydroxyethyl triazone, methylated methylol melamine, melamine-formaldehyde, and urea-formaldehyde; said thermosetting resin being present in an amount ranging from about 0.1 to about 5.0% by weight, of the total composition, (d) an acidic metal salt curing agent selected from the group consisting of chromium nitrate, chromium perchlorate, zirconium nitrate, aluminum chloride, zirconium oxychloride, aluminum sulfate and aluminum nitrate; said acidic metal salt curing agent being present in an amount ranging from about 0.1 to about 2.0%, by weight, of the total composition, and (e) water; said composition having a viscosity of from about 100 to 2500 cps.
Claim 3
Dependent Claim
127 words
The adhesive composition of claim 1 wherein said crosslinkable polymer is polyvinyl acetate or copolymer of vinyl acetate with one or more copolymerizable comonomers selected from the group consisting of (1) alpha-beta unsaturated mono and dicarboxylic acids containing from 3 - 6 carton atoms, (2) alkyl esters of acrylic and methacrylic acids wherein the alkyl group contains from 1 to 8 carbon atoms, (3) mono- or dialkyl esters of alpha, beta unsaturated dicarboxylic acids wherein said acids contain from 3 to 6 carbon atoms, and the alkyl groups contain from 1 to 8 carbon atoms, (4) vinyl halides, and (5) amides of acrylic and methacrylic acids and their N-alkylol derivatives; said vinyl acetate being present in an amount of at least 50%, by weight, of the copolymer.
Claim 4
Dependent Claim
77 words
The adhesive composition of claim 1 wherein said crosslinkable polymer is a copolymer of an alkyl (C 1 -C 8 ) ester of acrylic or methacrylic acid with one or more copolymerizable comonomers selected from the group consisting of amides of acrylic or methacrylic acid; N-alkylol amides of acrylic or methacrylic acid, cyanoethylacrylamide; and acrylonitrile; said alkyl ester of acrylic or methacrylic acid being present in an amount of at least 60%, by weight, of the copolymer.
Claim 5
Dependent Claim
142 words
An adhesive composition comprising a copolymer of vinyl acetate and N-methylol acrylamide having at least 50%, by weight, of vinyl acetate; from 1.0 to 4.0 times the weight of the resinous content of said copolymer of ungelatinized corn starch; from about 0.1 to about 5.0%, by weight, of the total composition of a thermosetting resin selected from the group consisting of dimethylol ethylene urea, dimethylol hydroxyethyl triazone, dimethylol methoxy ethyl carbamate, dimethylol isobutyl carbamate, methylated methylol melamine, melamine-formaldehyde, and urea-formaldehyde, from about 0.1 to about 2.0%, by weight, of the total composition of an acidic metal salt curing agent selected from the group consisting of chromium nitrate, chromium perchlorate, zirconium nitrate, aluminum nitrate, zirconium oxychloride, aluminum sulfate and aluminum chloride; and water; said copolymer being in aqueous emulsion form and said composition having a viscosity of from about 200 to 1400 cps.
Claim 6
Dependent Claim
142 words
An adhesive composition comprising a copolymer of vinyl acetate and N-methylol acrylamide having at least 50%, by weight, of vinyl acetate; from 1.0 to 4.0 times the weight of the resinous content of said copolymer of ungelatinized corn starch; from about 0.1 to about 5.0%, by weight, of the total composition of a thermosetting resin selected from the group consisting of dimethylol ethylene urea, dimethylol hydroxyethyl triazone, dimethylol methoxy ethyl carbamate, dimethylol isobutyl carbamate, methylated methylol melamine, melamine-formaldehyde, and urea-formaldehyde, from about 0.1 to about 2.0%, by weight, of the total composition of an acidic metal salt curing agent selected from the group consisting of chromium nitrate, chromium perchlorate, zirconium nitrate, aluminum nitrate, zirconium oxychloride, aluminum sulfate and aluminum chloride; and water; said copolymer being in aqueous emulsion form and said composition having a viscosity of from about 200 to 1400 cps.
Claim 7
Dependent Claim
14 words
The adhesive composition of claim 4 wherein said copolymer is replaced with polyvinyl acetate.
Claim 8
Dependent Claim
17 words
The adhesive composition of claim 4 wherein said corn starch is replaced with an ungelatinized waxy maize.
Claim 9
Dependent Claim
41 words
The adhesive composition of claim 4 wherein said copolymer is replaced with a copolymer of butyl acrylate, vinyl acetate and N-isobutoxy methylol acrylamide; said butyl acrylate being present in an amount of at least 60%, by weight, of the total copolymer.
Claim 10
Dependent Claim
39 words
The adhesive composition of claim 4 wherein said copolymer is replaced with a copolymer of butyl acrylate, acrylonitrile, and N-methylol acrylamide; said butyl acrylate being present in an amount of at least 60%, by weight, of the total copolymer.
Claim 11
Dependent Claim
12 words
A corrugated paperboard product prepared employing the adhesive composition of claim 1.
Claim 12
Dependent Claim
12 words
A corrugated paperboard product prepared employing the adhesive composition of claim 5.
Claim 13
Dependent Claim
12 words
A corrugated paperboard product prepared employing the adhesive composition of claim 7.
Claim 14
Dependent Claim
12 words
A corrugated paperboard product prepared employing the adhesive composition of claim 8.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-18 | 1980-10-18 | 1981-04-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-18 | 1984-10-18 | 1985-04-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-18 | 1988-10-18 | 1989-04-19 | $7700.00 | Window Closed / Lapsed |