High strength oxidation resistant nickel base alloys
Assignee: Olin Corp
•
Filing: 1976-04-01
•
Granted: 1977-04-26
•
Expires: 1996-04-01
Abstract
Abstract High strength oxidation resistant nickel base alloys are disclosed, said alloys consisting essentially of from 2 to 6% aluminum, 1 to 6% chromium, 0.5 to 4% silicon, 5 to 20% cobalt, 0.03 to 0.30% carbon, 0.005 to 0.25% magnesium, balance nickel. The alloys may optionally include 0.002 to 0.05% boron, 0.002 to 0.05% zirconium, up to 15% iron, up to 1% manganese and up to 1% of an element selected from the group consisting of Rare Earth elements. The alloys exhibit a high resistance to oxidation deterioration and good mechanical properties at elevated temperatures.
Inventors
- 👤 Mathur Raghavan
- 👤 Eugene Shapiro
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 09:12
CPC Classifications
C; C22; C22C; C22C19/00; C22C19/03; C22C19/05; C22C19/058
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
72 words
A nickel base alloy having high resistance to oxidation at elevated temperatures, good hot workability, good creep resistance, good high temperature mechanical properties and high creep rupture strength, said alloy consisting essentially of from 2 to 6% by weight aluminum, 1 to 6% by weight chromium, 0.5 to 4% by weight silicon, 5 to 20% by weight cobalt, 0.03 to 0.30% by weight carbon, 0.005 to 0.25% by weight magnesium, balance nickel.
Claim 2
Dependent Claim
72 words
A nickel base alloy having high resistance to oxidation at elevated temperatures, good hot workability, good creep resistance, good high temperature mechanical properties and high creep rupture strength, said alloy consisting essentially of from 2 to 6% by weight aluminum, 1 to 6% by weight chromium, 0.5 to 4% by weight silicon, 5 to 20% by weight cobalt, 0.03 to 0.30% by weight carbon, 0.005 to 0.25% by weight magnesium, balance nickel.
Claim 3
Dependent Claim
20 words
An alloy according to claim 1 including 0.002 to 0.05% by weight boron and 0.002 to 0.05% by weight zirconium.
Claim 4
Dependent Claim
13 words
An alloy according to claim 2 including up to 15% by weight iron.
Claim 5
Dependent Claim
13 words
An alloy according to claim 2 including up to 1% by weight manganese.
Claim 6
Dependent Claim
24 words
An alloy according to claim 2 including up to 1% by weight of an element selected from the group consisting of Rare Earth elements.
Claim 7
Dependent Claim
22 words
An alloy according to claim 1 wherein said alloy consists of a duplex gamma matrix plus a gamma prime precipitate phase system.
Claim 8
Dependent Claim
23 words
An alloy according to claim 1 wherein said alloy contains a dispersed chromium carbide phase preferably at the grain boundaries of the alloy.
Claim 9
Dependent Claim
51 words
An alloy according to claim 1 wherein said alloy consists essentially of from 3.3 to 4.5% by weight aluminum, 4 to 5% by weight chromium, 1.5 to 2.5% by weight silicon, 8 to 20% by weight cobalt, 0.08 to 0.20% by weight carbon, 0.01 to 0.15% by weight magnesium, balance nickel.
Claim 10
Dependent Claim
29 words
An alloy according to claim 2 wherein said boron and said zirconium are present in the alloy in the range of 0.002 to 0.015% by weight for each element.
Claim 11
Independent Claim
160 words
A method of preparing a wrought nickel base alloy comprising: A. providing a nickel base alloy consisting essentially of from 2 to 6% by weight aluminum, 1 to 6% by weight chromium, 0.5 to 4% by weight silicon, 5 to 20% by weight cobalt, 0.03 to 0.30% by weight carbon, 0.005 to 0.25% by weight magnesium, balance nickel; B. hot rolling said alloy at a temperature of at least 1600° F; C. cold rolling said alloy to a desired gage with intermediate annealing to provide a substantially recrystallized structure in the alloy system and to minimize the formation and growth of the gamma prime phase in the gamma matrix of the alloy upon cooling to room temperature; D. subjecting said alloy to a solution treatment to effect the dissolution of the gamma prime and carbide phases in the gamma matrix of the alloy system; and E. aging said alloy at 1300° to 1700° F for 30 minutes to 16 hours.
Claim 12
Independent Claim
160 words
A method of preparing a wrought nickel base alloy comprising: A. providing a nickel base alloy consisting essentially of from 2 to 6% by weight aluminum, 1 to 6% by weight chromium, 0.5 to 4% by weight silicon, 5 to 20% by weight cobalt, 0.03 to 0.30% by weight carbon, 0.005 to 0.25% by weight magnesium, balance nickel; B. hot rolling said alloy at a temperature of at least 1600° F; C. cold rolling said alloy to a desired gage with intermediate annealing to provide a substantially recrystallized structure in the alloy system and to minimize the formation and growth of the gamma prime phase in the gamma matrix of the alloy upon cooling to room temperature; D. subjecting said alloy to a solution treatment to effect the dissolution of the gamma prime and carbide phases in the gamma matrix of the alloy system; and E. aging said alloy at 1300° to 1700° F for 30 minutes to 16 hours.
Claim 13
Dependent Claim
29 words
A method according to claim 10 wherein prior to hot rolling the alloy is homogenized at a temperature from 1600° to 2200° F for 30 minutes to 24 hours.
Claim 14
Dependent Claim
29 words
A method according to claim 10 wherein said hot rollin is accomplished in a plurality of passes, with the material being reheated at least once during said hot rolling.
References Cited (Backward Citations)
US3810754A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-25 | 1980-10-25 | 1981-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-25 | 1984-10-25 | 1985-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-25 | 1988-10-25 | 1989-04-26 | $7700.00 | Window Closed / Lapsed |