Abstract
Abstract A method for the diminution of high temperature oxidation in an iron alloyontaining chromium consisting of at least partially enclosing the alloy and a volatile inorganic boron compound, heating the boron compound and allowing the volatile constituent of the boron compound to contact at least one surface of the alloy.
Inventors
- 👤 Geoffrey Oliver Lloyd
- 👤 John Ernest Rhoades-Brown
- 👤 Stuart Richard John Saunders
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 07:24
CPC Classifications
C; C23; C23F; C23F11/00; C23F11/02; C21; C21D; C21D1/00; C21D1/74; C21D1/76; C23C; C23C14/00; C23C14/06
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
128 words
A method for the diminution of high temperature oxidation in an iron alloy containing from 5% to 20% by weight of chromium comprising, at least partially enclosing in a oxygen-containing atmosphere said alloy and a volatile inorganic boron compound physically separate from said alloy and selected from the group consisting of borosilicate glasses, sodium metaborate, sodium tetraborate, boric acid, and boric oxide, treating said boron compound to a temperature sufficient to volatilize at least a component of said volatile inorganic boron compound and contacting said volatilized component with at least one surface of said alloy at a temperature within the range of 400° C to 900° C, whereby a boron-containing oxide film is formed on the said at least one surface which protects said surface from further oxidation.
Claim 2
Independent Claim
128 words
A method for the diminution of high temperature oxidation in an iron alloy containing from 5% to 20% by weight of chromium comprising, at least partially enclosing in a oxygen-containing atmosphere said alloy and a volatile inorganic boron compound physically separate from said alloy and selected from the group consisting of borosilicate glasses, sodium metaborate, sodium tetraborate, boric acid, and boric oxide, treating said boron compound to a temperature sufficient to volatilize at least a component of said volatile inorganic boron compound and contacting said volatilized component with at least one surface of said alloy at a temperature within the range of 400° C to 900° C, whereby a boron-containing oxide film is formed on the said at least one surface which protects said surface from further oxidation.
Claim 3
Dependent Claim
30 words
A method according to claim 1 wherein the alloy and the volatile inorganic boron compound are heated together to a temperature in the range about 400° to about 900° C.
Claim 4
Dependent Claim
16 words
A method according to claim 1 wherein the volatile inorganic boron compound is a borosilicate glass.
Claim 5
Independent Claim
117 words
A method for the diminution of high temperature oxidation of iron alloys containing from 5% to 20% by weight of chromium forming part of an at least partially enclosed assembled apparatus and heated to at least 400° C by enclosing within said apparatus a volatile inorganic boron compound selected from the group consisting of borosilicate-glasses, sodium metaborate, sodium tetraborate, boric acid and boric oxide physically separate from said alloy, and at least intermittently heating said volatile inorganic boron compound to a temperature sufficient to volatilize at least a component thereof and contacting said component with an exposed surface of said alloy, whereby a boron-containing oxide film is formed on said surface which protects it from further oxidation.
Claim 6
Independent Claim
117 words
A method for the diminution of high temperature oxidation of iron alloys containing from 5% to 20% by weight of chromium forming part of an at least partially enclosed assembled apparatus and heated to at least 400° C by enclosing within said apparatus a volatile inorganic boron compound selected from the group consisting of borosilicate-glasses, sodium metaborate, sodium tetraborate, boric acid and boric oxide physically separate from said alloy, and at least intermittently heating said volatile inorganic boron compound to a temperature sufficient to volatilize at least a component thereof and contacting said component with an exposed surface of said alloy, whereby a boron-containing oxide film is formed on said surface which protects it from further oxidation.
Claim 7
Dependent Claim
24 words
A method according to claim 1 wherein the inorganic boron compound is heated by a supplementary heater to a higher temperature than the alloy.
Claim 8
Dependent Claim
27 words
A method according to claim 4 wherein the alloy and the volatile boron compound are both heated to a temperature in the range 400° to 900° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-04-25 | 1980-10-25 | 1981-04-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-04-25 | 1984-10-25 | 1985-04-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-04-25 | 1988-10-25 | 1989-04-26 | $7700.00 | Window Closed / Lapsed |