Elastomer coated carbon filament reinforcing yarn or cord, method and article
Assignee: Toray Industries Inc
•
Filing: 1976-03-04
•
Granted: 1977-08-30
•
Expires: 1996-03-04
Abstract
Abstract Multi-filament reinforcing carbon yarn coated with a resorcinol-formaldehyde-latex (RFL) composition for use in reinforced rubber articles such as tires. The reinforcing yarn is prepared from a multi-filament carbon yarn having a limited denier of about 500-4,000, having a twist factor of the yarn of about 0-250, and having individual filaments which have a denier of 1.4-2.0. The reinforcing yarn is impregnated with RFL, so that the amount of coated RFL is at least about 10 weight percent based on the yarn. Treatment of the carbon filament yarn with an epoxy resin, prior to being subjected to impregnation with RFL, is also disclosed.
Inventors
- 👤 Masamichi Toki
- 👤 Noriaki Kusatsu
- 👤 Yoshio Kohno
- 👤 Kenji Matsugasako
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:31
CPC Classifications
D; D02; D02G; D02G3/00; D02G3/02; D02G3/16; B; B60; B60C; B60C9/00; B60C9/0028; C; C08; C08J; C08J5/00; C08J5/04; C08J5/06; D02G3/22; D02G3/40; D02G3/404; D02G3/44; D02G3/48; C08J2321/00; D10; D10B; D10B2101/00; D10B2101/10; D10B2101/12; Y; Y10; Y10S; Y10S57/00; Y10S57/902; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
137 words
A multi-filament reinforcing carbon yarn having tenacity of at least about 7 grams per denier, said reinforcing yarn being encapsulated by a resorcinol-formaldehyde-latex composition, in which the amount by weight of the resorcinol-formaldehyde-latex composition encapsulating said multi-filament yarn is equivalent at least to about 10% by weight of the multi-filament yarn, said multi-filament yarn having a denier in the range of from about 500 to 4,000 and a twist factor in the range of from 0 to about 250, wherein the twist factor is the twist in turns per 10 cm in the multi-filament yarn multiplied by the square root of the denier of the multi-filament yarn, said multi-filament yarn further comprising individual filaments having a denier in the range of from about 0.4 to 2.0 and a tenacity of at least about 10 grams per denier.
Claim 2
Dependent Claim
137 words
A multi-filament reinforcing carbon yarn having tenacity of at least about 7 grams per denier, said reinforcing yarn being encapsulated by a resorcinol-formaldehyde-latex composition, in which the amount by weight of the resorcinol-formaldehyde-latex composition encapsulating said multi-filament yarn is equivalent at least to about 10% by weight of the multi-filament yarn, said multi-filament yarn having a denier in the range of from about 500 to 4,000 and a twist factor in the range of from 0 to about 250, wherein the twist factor is the twist in turns per 10 cm in the multi-filament yarn multiplied by the square root of the denier of the multi-filament yarn, said multi-filament yarn further comprising individual filaments having a denier in the range of from about 0.4 to 2.0 and a tenacity of at least about 10 grams per denier.
Claim 3
Dependent Claim
47 words
A yarn according to claim 1, in which the multi-filament yarn is encapsulated by an epoxy resin, and in which the equivalent amount of the epoxy resin encapsulating the multi-filament yarn is in the range of from about 0.5% to 10% by weight of the multi-filament yarn.
Claim 4
Dependent Claim
17 words
A yarn according to claim 2 in which the epoxy resin is a water soluble epoxy resin.
Claim 5
Dependent Claim
21 words
A yarn according to claim 1 in which the amount by weight of the resorcinol-formaldehyde-latex composition is at least about 40%.
Claim 6
Dependent Claim
160 words
A carbon filament reinforcing cord which comprises at least two strands of yarn twisted together, at least one of said strands being prepared from a multi-filament reinforcing carbon yarn, said multi-filament reinforcing carbon yarn having tenacity of at least about 7 grams per denier, and encapsulated by a resorcinol-formaldehyde-latex composition, the amount by weight of the resorcinol-formaldehyde-latex composition encapsulating the multi-filament yarn being equivalent at least to about 10% by weight of the multi-filament yarn, said multi-filament yarn having a denier in the range of from about 500 to 4,000 and a twist factor in the range of from 0 to about 250, wherein said twist factor is the twist in turns per 10 cm in the multi-filament yarn multiplied by the square root of the denier of said multi-filament yarn, individual filaments of said multi-filament yarn having a denier in the range of from about 0.4 to 2.0 and a tenacity of at least about 10 grams per denier.
Claim 7
Dependent Claim
160 words
A carbon filament reinforcing cord which comprises at least two strands of yarn twisted together, at least one of said strands being prepared from a multi-filament reinforcing carbon yarn, said multi-filament reinforcing carbon yarn having tenacity of at least about 7 grams per denier, and encapsulated by a resorcinol-formaldehyde-latex composition, the amount by weight of the resorcinol-formaldehyde-latex composition encapsulating the multi-filament yarn being equivalent at least to about 10% by weight of the multi-filament yarn, said multi-filament yarn having a denier in the range of from about 500 to 4,000 and a twist factor in the range of from 0 to about 250, wherein said twist factor is the twist in turns per 10 cm in the multi-filament yarn multiplied by the square root of the denier of said multi-filament yarn, individual filaments of said multi-filament yarn having a denier in the range of from about 0.4 to 2.0 and a tenacity of at least about 10 grams per denier.
Claim 8
Dependent Claim
205 words
A reinforcing cord which comprises at least two strands twisted together, an individual strand being prepared from a multi-filament reinforcing carbon yarn, said multi-filament reinforcing carbon yarn having a tenacity of at least about 7 grams per denier and coated with a resorcinol-formaldehyde-latex composition, the amount by weight of said resorcinol-formaldehyde-latex composition being equivalent at least to about 10% by weight of said multi-filament reinforcing carbon yarn, said multi-filament reinforcing carbon yarn having a denier in the range of from about 500 to about 4,000, and a twist factor in the range of from 0 to about 250, wherein said twist factor is the twist in turns per 10 cm in the multi-filament reinforcing carbon yarn multiplied by the square root of the denier of said yarn, individual filaments of said yarn having a denier in the range of from about 0.4 to 2.0 and a tenacity of at least about 10 grams per denier, and wherein the twist factor of the cord is in the range of from about 100 to about 800, wherein said twist factor of said cord is defined as the twist in turns per 10 cm in said cord multiplied by the square root of the denier of said cord.
Claim 9
Dependent Claim
205 words
A reinforcing cord which comprises at least two strands twisted together, an individual strand being prepared from a multi-filament reinforcing carbon yarn, said multi-filament reinforcing carbon yarn having a tenacity of at least about 7 grams per denier and coated with a resorcinol-formaldehyde-latex composition, the amount by weight of said resorcinol-formaldehyde-latex composition being equivalent at least to about 10% by weight of said multi-filament reinforcing carbon yarn, said multi-filament reinforcing carbon yarn having a denier in the range of from about 500 to about 4,000, and a twist factor in the range of from 0 to about 250, wherein said twist factor is the twist in turns per 10 cm in the multi-filament reinforcing carbon yarn multiplied by the square root of the denier of said yarn, individual filaments of said yarn having a denier in the range of from about 0.4 to 2.0 and a tenacity of at least about 10 grams per denier, and wherein the twist factor of the cord is in the range of from about 100 to about 800, wherein said twist factor of said cord is defined as the twist in turns per 10 cm in said cord multiplied by the square root of the denier of said cord.
Claim 10
Dependent Claim
150 words
A multi-filament carbon yarn for preparing a reinforcing yarn, having a plurality of individual filaments having a tenacity of at least about 10 grams per denier, the multi-filament yarn having a denier in the range of from about 500 to about 4,000, said filaments having a denier per filament in the range of from about 0.4 to 2.0, said multi-filament yarn having a twist factor in the range of from 0 to about 250 where the twist factor is defined as the twist in turns per 10 cm length of the multi-filament yarn multiplied by the square root of the denier of the multi-filament yarn, the individual filaments being coated with an epoxy resin and the multi-filament yarn being encapsulated by the epoxy resin, the equivalent amount of the epoxy resin encapsulating the multi-filament yarn being in the range of from 0.5% to 10% by weight of the multi-filament yarn.
Claim 11
Dependent Claim
150 words
A multi-filament carbon yarn for preparing a reinforcing yarn, having a plurality of individual filaments having a tenacity of at least about 10 grams per denier, the multi-filament yarn having a denier in the range of from about 500 to about 4,000, said filaments having a denier per filament in the range of from about 0.4 to 2.0, said multi-filament yarn having a twist factor in the range of from 0 to about 250 where the twist factor is defined as the twist in turns per 10 cm length of the multi-filament yarn multiplied by the square root of the denier of the multi-filament yarn, the individual filaments being coated with an epoxy resin and the multi-filament yarn being encapsulated by the epoxy resin, the equivalent amount of the epoxy resin encapsulating the multi-filament yarn being in the range of from 0.5% to 10% by weight of the multi-filament yarn.
Claim 12
Independent Claim
146 words
A method for manufacture of carbon multi-filament reinforcing yarn having a tenacity of at least about 7 grams per denier, which method comprises: a. impregnating a multi-filament carbon yarn with a liquid medium containing a resorcinol-formaldehyde-latex composition, b. adjusting the amount of pick-up of the liquid so that after subsequently being dried, the amount by weight of the resorcinol-formaldehyde-latex composition encapsulating the multi-filament yarn becomes equivalent to at least about 10% by weight of the multi-filament yarn, and c. drying the product to encapsulate the multi-filament yarn with the solidified resorcinol-formaldehyde-latex composition, the multi-filament carbon yarn having a denier in the range of from about 500 to about 4,000, a twist factor in the range of from 0 to about 250, an individual filament tenacity of at least about 10 grams per denier and a denier per filament in the range of from 0.4 to 2.0.
Claim 13
Independent Claim
146 words
A method for manufacture of carbon multi-filament reinforcing yarn having a tenacity of at least about 7 grams per denier, which method comprises: a. impregnating a multi-filament carbon yarn with a liquid medium containing a resorcinol-formaldehyde-latex composition, b. adjusting the amount of pick-up of the liquid so that after subsequently being dried, the amount by weight of the resorcinol-formaldehyde-latex composition encapsulating the multi-filament yarn becomes equivalent to at least about 10% by weight of the multi-filament yarn, and c. drying the product to encapsulate the multi-filament yarn with the solidified resorcinol-formaldehyde-latex composition, the multi-filament carbon yarn having a denier in the range of from about 500 to about 4,000, a twist factor in the range of from 0 to about 250, an individual filament tenacity of at least about 10 grams per denier and a denier per filament in the range of from 0.4 to 2.0.
Claim 14
Dependent Claim
88 words
A method according to claim 8 in which prior to being subjected to said impregnation the multi-filament carbon yarn is subjected to the following steps: a. impregnating the yarn with a liquid medium containing an epoxy resin, b. adjusting the amount of pick-up of the liquid so that after subsequently being dried, the amount by weight of the epoxy resin encapsulating the yarn becomes equivalent to about 0.5% to 10% by weight of the yarn and c. drying the yarn to encapsulate the yarn with the epoxy resin.
Claim 15
Dependent Claim
32 words
A method according to claim 9 in which the amount by weight of the epoxy resin is in the range of from 1% to 6% based upon the weight of the yarn.
Claim 16
Dependent Claim
32 words
A method according to claim 9 in which the amount by weight of the resorcinol-formaldehyde-latex composition is in the range of from 10% to 50%, based upon the weight of the yarn.
Claim 17
Dependent Claim
14 words
A method according to claim 9 in which the epoxy resin is water soluble.
Claim 18
Dependent Claim
28 words
A method according to claim 12 in which the amount by weight of the resorcinol-formaldehyde-latex composition is at least about 40%, based upon the weight of the yarn.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-29 | 1981-02-28 | 1981-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-29 | 1985-02-28 | 1985-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-29 | 1989-02-28 | 1989-08-30 | $7700.00 | Window Closed / Lapsed |