Method of making laminar material having a base of bonded wood particles
Assignee: Feldmuehle Anlagen und Produktion GmbH
•
Filing: 1976-05-12
•
Granted: 1977-08-30
•
Expires: 1996-05-12
Abstract
Abstract A laminar board having a base of bonded wood particles carrying a decorat facing is produced by sequentially moving a carrier web through a loading zone and a press zone. The carrier web consists essentially of paper impregnated with a synthetic resin composition and having a permeability to water vapor of at least 1000 g/m 2 /day. A layer of loose wood particles intimately mixed with a bonding agent is superimposed on the carrier web in the loading zone, and the resulting layered material is subjected in the press zone to a temperature and pressure sufficient to bond the loose particles to each other by the bonding agent in a dense structure and simultaneously to bond the particles to the carrier web by the bonding agent and/or the synthetic resin composition.
Inventors
- 👤 Hans Joachim Enzinger
- 👤 Hans Fechner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:43
CPC Classifications
B; B32; B32B; B32B21/00; B32B21/02; B27; B27N; B27N3/00; B27N3/06; B27N3/08; B27N3/10; B27N3/26; B30; B30B; B30B15/00; B30B15/30; B30B15/302; B30B15/308; B30B5/00; B30B5/04; B30B5/06; B32B21/04; B32B21/06; B32B21/10; B32B5/00; B32B5/02; B32B5/024; B32B5/026; B32B2260/00; B32B2260/02; B32B2260/028; B32B2260/04; B32B2260/046; B32B2317/00; B32B2317/16; Y; Y10; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249994
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
160 words
A process of producing a laminar material in continuous lengths which comprises: a. sequentially and continuously moving a paper web through a loading zone and through a press zone, 1. said web consisting essentially of fibrous material impregnated with a synthetic resin composition, being free from sizing and filler, and having a permeability to water vapor of at least 1000 grams per square meter per day; b. superimposing on said web in said loading zone loose wood particles intimately mixed with a bonding agent for said particles to form a layer on said web; and c. subjecting the web and the superimposed layer during said moving through said press zone to a temperature greater than 100° C and to a pressure sufficient to bond said loose particles to each other by said bonding agent in a dense structure and simultaneously to bond said particles to said web by at least one of said bonding agent and said synthetic resin composition.
Claim 2
Dependent Claim
160 words
A process of producing a laminar material in continuous lengths which comprises: a. sequentially and continuously moving a paper web through a loading zone and through a press zone, 1. said web consisting essentially of fibrous material impregnated with a synthetic resin composition, being free from sizing and filler, and having a permeability to water vapor of at least 1000 grams per square meter per day; b. superimposing on said web in said loading zone loose wood particles intimately mixed with a bonding agent for said particles to form a layer on said web; and c. subjecting the web and the superimposed layer during said moving through said press zone to a temperature greater than 100° C and to a pressure sufficient to bond said loose particles to each other by said bonding agent in a dense structure and simultaneously to bond said particles to said web by at least one of said bonding agent and said synthetic resin composition.
Claim 3
Dependent Claim
82 words
A process as set forth in claim 1, wherein said web and the superimposed layer are confined between surfaces impermeable to water vapor while being subjected to said temperature and said pressure, and said web is relieved of said pressure at said temperature by release from one of said surfaces, the water content of said impregnated fibrous material being sufficient to cause partial failure of the bond between said particles and said web after said relieving in the absence of said permability.
Claim 4
Dependent Claim
45 words
A process as set forth in claim 2, wherein said fibrous material includes at least 30% wood fibers and has a dry weight of 50 - 120 g/m 2 , the dry weight of said synthetic resin composition being 60 - 130 g/m 2 .
Claim 5
Dependent Claim
62 words
A process as set forth in claim 3, wherein said web is prepared prior to said moving by saturating said paper with an aqueous solution of a urea-formaldehyde precondensate and of a hardener for said precondensate, and drying the saturated paper to a residual moisture content of 6 to 10 percent at a temperature sufficiently low to prevent curing of said precondensate.
Claim 6
Dependent Claim
21 words
A process as set forth in claim 4, wherein said paper prior to said saturating is imprinted with a decorative pattern.
Claim 7
Dependent Claim
26 words
A process as set forth in claim 3, wherein said carrier web is prepared prior to said moving by impregnating said paper with a melamine-formaldehyde precondensate.
Claim 8
Dependent Claim
56 words
A process as set forth in claim 2, wherein said web and said superimposed layer are moved in said press zone through a nip between a heated drum rotating about the axis thereof and a cylinder, and are subjected in said nip to a pressure of 220 to 280 kg/cm of axial length of said drum.
Claim 9
Dependent Claim
33 words
A process as set forth in claim 2, wherein said temperature is between 120° and 230° C, and said web and said layer are subjected to said temperature for 30 - 90 seconds.
Claim 10
Dependent Claim
41 words
A process as set forth in claim 2, wherein the synthetic resin in said composition is a thermosetting resin in the A stage or B stage, and said temperature and pressure are sufficient to convert said resin to the C stage.
Claim 11
Dependent Claim
34 words
A process set forth in claim 9, wherein said bonding agent includes a curing agent for said resin, said temperature and pressure being sufficient to cause migration of the curing agent into said paper.
References Cited (Backward Citations)
US3078510A
Cited
US3301726A
Cited
US3300361A
Cited
US3607489A
Cited
US3905847A
Cited
US3737351A
Cited
US3874962A
Cited
US3933558A
Cited
US3968308A
Cited
US3930110A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-08-29 | 1981-02-28 | 1981-08-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-08-29 | 1985-02-28 | 1985-08-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-08-29 | 1989-02-28 | 1989-08-30 | $7700.00 | Window Closed / Lapsed |