Metallic bonding method
Assignee: Associated Engineering Ltd
•
Filing: 1975-10-28
•
Granted: 1977-09-06
•
Expires: 1995-10-28
Abstract
Abstract Bonded metallic structures comprising at least two pieces each of a metallic aluminous substance selected from the group consisting of aluminium and aluminium alloys are formed by bonding the pieces together by eutectic diffusion bonding using a metallic interlayer material which is applied between the surfaces to be joined, which forms a less stable oxide than that formed by the aluminous substance and which is preferably selected from the group consisting of copper and copper-rich alloys including at least about 95% copper.
Inventors
- 👤 Dennis Cockburn Brown
- 👤 Reginald Murray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 09:23
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/001; B23K35/002; B23K20/00; B23K20/22; B23K20/233; B23K20/2336; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12736; Y10T428/12764
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
164 words
A method of bonding together at least two pieces of aluminium alloy by eutectic diffusion bonding using, between the surfaces to be joined, an interlayer selected from the group consisting of copper and copper-rich alloys including at least about 95% copper and in which said pieces are heated and said surfaces to be joined are pressed together to form a metallurgical bond therebetween, characterized in that at least one of said pieces is of high silicon aluminum alloy and at least one other of said pieces is of an aluminium alloy having a melting point not lower than that of said high silicon aluminum alloy and in that said one piece of high silicon aluminum alloy and said other piece of aluminium alloy are heated to a temperature in the range of about 515° to about 530° C, whereby to form between the joined surfaces a metallurgical bond consisting of a complex alloy of at least said high silicon aluminum alloy and said interlayer.
Claim 2
Independent Claim
164 words
A method of bonding together at least two pieces of aluminium alloy by eutectic diffusion bonding using, between the surfaces to be joined, an interlayer selected from the group consisting of copper and copper-rich alloys including at least about 95% copper and in which said pieces are heated and said surfaces to be joined are pressed together to form a metallurgical bond therebetween, characterized in that at least one of said pieces is of high silicon aluminum alloy and at least one other of said pieces is of an aluminium alloy having a melting point not lower than that of said high silicon aluminum alloy and in that said one piece of high silicon aluminum alloy and said other piece of aluminium alloy are heated to a temperature in the range of about 515° to about 530° C, whereby to form between the joined surfaces a metallurgical bond consisting of a complex alloy of at least said high silicon aluminum alloy and said interlayer.
Claim 3
Dependent Claim
26 words
A method as claimed in claim 1, wherein the surfaces to be joined are provided withe a surface finish of 20 to 50 micro inches CLA.
Claim 4
Dependent Claim
25 words
A method as claimed in claim 1, wherein the surfaces to be joined are pressed together by the action of co-operating screw-threads on said surfaces.
Claim 5
Dependent Claim
33 words
A method as claimed in claim 1 and including the step of pre-shaping at least two of said pieces to be bonded to produce a bonded structure having at least one internal cavity.
Claim 6
Dependent Claim
33 words
A method as claimed in claim 1 and including the step of pre-shaping at least two of said pieces to be bonded to produce a bonded structure in the form of a piston.
Claim 7
Dependent Claim
20 words
A method as claimed in claim 5, wherein the said another of said pieces is of high silicon aluminum alloy.
Claim 8
Dependent Claim
19 words
A method as claimed in claim 5, wherein the said another of said pieces is of LM 14 alloy.
Claim 9
Dependent Claim
37 words
A method as claimed in claim 5, including the step of pre-forming co-operating screw-threads on the surfaces to be joined and wherein the surfaces to be joined are pressed together by the action of said co-operating screw-threads.
Claim 10
Dependent Claim
44 words
A method as claimed in claim 1 and including the step of pre-shaping at least two of said pieces to be bonded to produce a bonded structure in the form of a piston and with the bonded pieces defining a cavity within the piston.
Claim 11
Dependent Claim
17 words
A method as claimed in claim 1, wherein the said another of said pieces is HE30 alloy.
Claim 12
Dependent Claim
37 words
A method as claimed in claim 1 and including the steps of pre-shaping two of said pieces to form two plates, preforming grooving in one of said plates and bonding said plates together to close the grooving.
Claim 13
Dependent Claim
116 words
A bonded structure comprising at least two pieces of aluminium alloy having between their joined surfaces a metallurgical bond formed by eutectic diffusion bonding using between the surfaces to be joined an interlayer selected from the group consisting of copper and copper rich alloys including at least about 95% copper, characterized in that at least one of said pieces is of high silicon aluminum alloy and at least one other of said pieces is of an aluminium alloy having a melting point not lower than that of said high silicon aluminum alloy and in that said metallurgical bond is formed of a complex alloy consisting at least of said high silicon aluminum alloy and said interlayer.
Claim 14
Dependent Claim
116 words
A bonded structure comprising at least two pieces of aluminium alloy having between their joined surfaces a metallurgical bond formed by eutectic diffusion bonding using between the surfaces to be joined an interlayer selected from the group consisting of copper and copper rich alloys including at least about 95% copper, characterized in that at least one of said pieces is of high silicon aluminum alloy and at least one other of said pieces is of an aluminium alloy having a melting point not lower than that of said high silicon aluminum alloy and in that said metallurgical bond is formed of a complex alloy consisting at least of said high silicon aluminum alloy and said interlayer.
Claim 15
Dependent Claim
15 words
A bonded structure as claimed in claim 12, and in the form of a piston.
Claim 16
Dependent Claim
19 words
A bonded structure as claimed in claim 13, wherein the bonded pieces together define a cavity within the piston.
Claim 17
Dependent Claim
21 words
A bonded structure as claimed in claim 13, wherein the said another of said pieces is of high silicon aluminum alloy.
Claim 18
Dependent Claim
19 words
A bonded structure as claimed in claim 13, wherein said another of said pieces is of LM 14 alloy.
Claim 19
Dependent Claim
19 words
A bonded structure as claimed in claim 13, wherein the bonded pieces have co-operating screw-threads on their joined surfaces.
Claim 20
Dependent Claim
16 words
A bonded structure as claimed in claim 12, and in the form of a heat exchanger.
Claim 21
Dependent Claim
17 words
A bonded structure as claimed in claim 18, wherein the heat exchanger is of the plate type.
Claim 22
Dependent Claim
19 words
A bonded structure as claimed in claim 12, wherein the bonded pieces comprises corrugated radiator fins and half tubes.
Claim 23
Dependent Claim
36 words
A bonded structure as claimed in claim 12, wherein the bonded pieces comprise two plates of which one has means defining grooving therein and the other is bonded to the grooved plate to close the grooving.
Claim 24
Dependent Claim
19 words
A bonded structure as claimed in claim 12, wherein the bonded pieces have co-operating screw-threads on their joined surfaces.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-09-05 | 1981-03-07 | 1981-09-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-09-05 | 1985-03-07 | 1985-09-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-09-05 | 1989-03-07 | 1989-09-06 | $7700.00 | Window Closed / Lapsed |