Abstract A barium-lithium-alumina-borate glass frit includes the following by weight on an oxide basis: 10.5-16.7% BaO; 10-11% Li2O; 2-3% Al2O3; and 70-77% B2O3. The frit can be fired, i.e., fused from powdered form to solid sealing glass, at low temperatures, e.g., about 530 DEG C. Firing can take place in an atmosphere which is inert, oxidizing, or reducing. After firing for a sufficient time, e.g., 3 hours, the sealing glass becomes fully devitrified. The devitrified sealing glass has an expansion coefficient substantially the same as that of window glass, i.e., about 90 x 10-7/ DEG C. The devitrified sealing glass can be reheated to temperatures in excess of 530 DEG C without deterioration or strains developing in a sealed joint.
A devitrifiable glass frit consisting essentially by weight on an oxide basis of about 10-20% BaO, 10-11% Li 2 O, 2-7% Al 2 O 3 , and 66-77% B 2 O 3 .
Claim 2
Dependent Claim
33 words
A devitrifiable glass frit consisting essentially by weight on an oxide basis of about 10-20% BaO, 10-11% Li 2 O, 2-7% Al 2 O 3 , and 66-77% B 2 O 3 .
Claim 3
Dependent Claim
38 words
A glass frit in accordance with claim 1 which consists essentially by weight on an oxide basis of about 10.5-16.7% BaO, 10-11% Li 2 O, 2-3% Al 2 O 3 , and 70-77% B 2 O 3 .
Claim 4
Dependent Claim
51 words
A composite article comprising at least two preformed glass bodies with sealing material disposed therebetween, said sealing material comprising a devitrified glass consisting essentially by weight on an oxide basis of about 10-20% BaO, 10-11% Li 2 O, 2-7% Al 2 O 3 , and 66-77% B 2 O 3 .
Claim 5
Dependent Claim
51 words
A composite article comprising at least two preformed glass bodies with sealing material disposed therebetween, said sealing material comprising a devitrified glass consisting essentially by weight on an oxide basis of about 10-20% BaO, 10-11% Li 2 O, 2-7% Al 2 O 3 , and 66-77% B 2 O 3 .
Claim 6
Dependent Claim
42 words
A composite article in accordance with claim 3 in which said sealing material consists essentially by weight on an oxide basis of about 10.5-16.7% BaO, 10-11% Li 2 O, 2-3% Al 2 O 3 , and 70-77% B 2 O 3 .
Claim 7
Dependent Claim
17 words
A composite article in accordance with claim 4 in which said two preformed bodies comprise window glass.
Claim 8
Dependent Claim
27 words
A composite article in accordance with claim 5 in which said devitrified glass has a temperature coefficient of expansion of about 90 × 10 -7 /° C.
Claim 9
Dependent Claim
22 words
A composite article in accordance with claim 6 in which said devitrified glass is about 70 to about 75 volume percent crystalline.