ABS polymer and process for its preparation
Assignee: Huntsman Chemical Corp
•
Filing: 1975-05-07
•
Granted: 1977-12-20
•
Expires: 1995-05-07
Abstract
Abstract ABS polymers having improved physical properties are prepared by graft polymerizing, in an aqueous medium, and in the presence of a suspending agent, styrene and acryonitrile onto a butadiene polymer in the form of a latex using certain peroxy ester catalysts.
Inventors
- 👤 Stelvio Papetti
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 23:40
CPC Classifications
C; C08; C08F; C08F279/00; C08F279/02; C08F279/04
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
117 words
A method for graft polymerizing a mixture containing monovinyl aromatic monomer and a nitrile monomer which is acrylonitrile or methacrylonitrile onto a rubbery polymer in the form of a latex, said rubbery polymer being selected from the group consisting of polybutadiene, butadiene-styrene copolymer, butadiene acrylonitrile copolymer or mixtures thereof, said method consisting essentially of effecting the polymerization in an aqueous medium in the presence of an effective suspending agent, and, as the essential catalytic agent, about 0.05-0.8%, based on the total weight of monomer present, of at least one compound having the formula: ##STR3## wherein R is an alkyl radical having 1-8 carbon atoms and R' is a tertiary alkyl group containing up to 8 carbon atoms.
Claim 2
Independent Claim
117 words
A method for graft polymerizing a mixture containing monovinyl aromatic monomer and a nitrile monomer which is acrylonitrile or methacrylonitrile onto a rubbery polymer in the form of a latex, said rubbery polymer being selected from the group consisting of polybutadiene, butadiene-styrene copolymer, butadiene acrylonitrile copolymer or mixtures thereof, said method consisting essentially of effecting the polymerization in an aqueous medium in the presence of an effective suspending agent, and, as the essential catalytic agent, about 0.05-0.8%, based on the total weight of monomer present, of at least one compound having the formula: ##STR3## wherein R is an alkyl radical having 1-8 carbon atoms and R' is a tertiary alkyl group containing up to 8 carbon atoms.
Claim 3
Dependent Claim
28 words
A process according to claim 1 wherein said catalytic acid agent is present in an amount of about 0.1 to 0.3%, based on the total weight of monomer.
Claim 4
Dependent Claim
12 words
A process according to claim 1 wherein said rubbery polymer is polybutadiene.
Claim 5
Dependent Claim
16 words
A process according to claim 1 wherein said polymerization reaction is conducted in an inert atmosphere.
Claim 6
Dependent Claim
21 words
A process according to claim 1 wherein said polymerization reaction is carried out at a pressure of about 14.50 lbs. psig.
Claim 7
Dependent Claim
13 words
A process according to claim 1 wherein R' is a tertiary butyl radical.
Claim 8
Dependent Claim
19 words
A process according to claim 6 wherein R' is the t-butyl radical and R is a tertiary alkyl compound.
Claim 9
Dependent Claim
13 words
A process according to claim 7 wherein R is a tertiary butyl group.
Claim 10
Dependent Claim
107 words
A process, according to claim 1, for preparing improved ABS polymers consisting essentially of graft copolymerizing, onto a polybutadiene backbone in a latex form, a monomeric material comprised of styrene and acrylonitrile, said process being conducted in an aqueous medium in the presence of an effective suspending agent which is polyvinyl alcohol and which is present in an amount of about 0.2-0.5%, based on the weight of water present in the reaction mixture and 0.1-0.3%, based on the weight of the monomer, of a catalyst selected from the group consisting of tertiary butyl peroxy isobutyrate, tertiary butyl peroxy octoate, tertiary butyl peroxy pivalate, and mixtures of these.
Claim 11
Dependent Claim
68 words
The process of claim 9 wherein the polymerization is conducted in two steps consisting essentially of a first stage polymerization conducted at about 40°-90° C in the presence of a catalyst having a 2 hour half-life temperature of about 40°-100° C, and a second stage conducted at about 70°-130° C in the presence of a high temperature catalyst having a 2 hour half-life temperature of about 80°-130° C.
Claim 12
Independent Claim
89 words
A method of making an ABS type polymer which consists essentially of: 1. adding to an aqueous medium contained in a closed reaction vessel, (a) a rubbery polymer which is in latex form and which is polybutadiene, butadiene-styrene copolymer, butadiene-acrylonitrile copolymer and mixtures thereof, (b) styrene, (c) acrylonitrile, (d) a suspending agent, (e) about 0.05 - 0.8%, of at least one catalyst having the formula: ##STR4## wherein R is an alkyl group having 1-8 carbon atoms and R' is a tertiary alkyl group having up to 8 carbon atoms;
Claim 13
Independent Claim
89 words
A method of making an ABS type polymer which consists essentially of: 1. adding to an aqueous medium contained in a closed reaction vessel, (a) a rubbery polymer which is in latex form and which is polybutadiene, butadiene-styrene copolymer, butadiene-acrylonitrile copolymer and mixtures thereof, (b) styrene, (c) acrylonitrile, (d) a suspending agent, (e) about 0.05 - 0.8%, of at least one catalyst having the formula: ##STR4## wherein R is an alkyl group having 1-8 carbon atoms and R' is a tertiary alkyl group having up to 8 carbon atoms;
Claim 14
Dependent Claim
17 words
polymerizing the contents of said reaction vessel at a temperature of about 50°-150° C, with continuous agitation.
Claim 15
Dependent Claim
17 words
polymerizing the contents of said reaction vessel at a temperature of about 50°-150° C, with continuous agitation.
Claim 16
Dependent Claim
32 words
The process of claim 11 wherein said suspending agent is polyvinyl alcohol and is present in an amount of about 0.2-0.5%, based on the weight of water present in the reaction mixture.
Claim 17
Dependent Claim
52 words
A process according to claim 11 wherein said catalyst is a member of the group consisting of tertiary butyl peroxy isobutyrate, tertiary butyl peroxy octoate, tertiary butyl peroxy pivalate and mixtures of these and wherein said catalyst is present in an amount of about 0.1-0.3%, based on the total weight of monomer.
Claim 18
Dependent Claim
126 words
A process, according to claim 11, for preparing an ABS polymer consisting essentially of: 1. adding to an aqueous medium contained in a closed reaction vessel: a. about 3 to 60 parts of polybutadiene in latex form; b. about 97 to 40 parts of a mixture comprised of about 20 to 40 parts of acrylonitrile and 80 to 60 parts of styrene; c. 0.2-0.5%, based on the total weight of water in said reaction mixture, of a suspending agent; d. 0.05 to 0.5% of a catalyst having a 2 hour half-life temperature of about 50° to 100° C and having the formula: ##STR5## wherein R is an alkyl group containing 1-8 carbon atoms and R' is a tertiary alkyl group containing up to 8 carbon atoms;
Claim 19
Dependent Claim
31 words
heating the contents of said reaction vessel to about 50° to 100° C, and maintaining it in this range for about 4-8 hours; and 3. recovering product from the reaction vessel.
Claim 20
Dependent Claim
31 words
heating the contents of said reaction vessel to about 50° to 100° C, and maintaining it in this range for about 4-8 hours; and 3. recovering product from the reaction vessel.
Claim 21
Dependent Claim
28 words
A process according to claim 14 wherein a portion of the catalyst is added initially and the remainder is added in one or more increments during the polymerization.
Claim 22
Independent Claim
91 words
A method for marking ABS type polymers by polymerizing an aqueous reaction medium consisting essentially of a monovinyl aromatic monomer, acrylonitrile, or methacrylonitrile, a rubbery polymer which is employed in latex form and which is polybutadiene, butadiene-styrene copolymer, or butadiene-acrylonitrile compolymer or mixtures thereof, an effective suspending agent, and about 0.05-0.8%, based on the total weight of the monomer present, of a catalyst of the formula: ##STR6## wherein R is an alkyl radical of 1-8 carbon atoms and R' is a tertiary alkyl group of up to about 8 carbon atoms.
Claim 23
Independent Claim
91 words
A method for marking ABS type polymers by polymerizing an aqueous reaction medium consisting essentially of a monovinyl aromatic monomer, acrylonitrile, or methacrylonitrile, a rubbery polymer which is employed in latex form and which is polybutadiene, butadiene-styrene copolymer, or butadiene-acrylonitrile compolymer or mixtures thereof, an effective suspending agent, and about 0.05-0.8%, based on the total weight of the monomer present, of a catalyst of the formula: ##STR6## wherein R is an alkyl radical of 1-8 carbon atoms and R' is a tertiary alkyl group of up to about 8 carbon atoms.
Claim 24
Dependent Claim
44 words
The process of claim 16 wherein the monovinyl aromatic polymer is styrene, the rubbery polymer is polybutadiene, and the catalyst is a member of the group consisting of tertiary butyl peroxy isobutyrate, tertiary butyl peroxy octoate, tertiary butyl peroxy pivalate or mixtures of these.
Claim 25
Dependent Claim
68 words
The process of claim 16 wherein the polymerization is conducted in two stages consisting essentially of a first stage polymerization conducted at about 40°-90° C in the presence of a catalyst having a 2 hour half-life temperature of about 40°-100° C, and a second stage conducted at about 70°-130° C in the presence of a high temperature catalyst having a 2 hour half-life temperature of about 80°-130° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-12-19 | 1981-06-20 | 1981-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-12-19 | 1985-06-20 | 1985-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-12-19 | 1989-06-20 | 1989-12-20 | $7700.00 | Window Closed / Lapsed |