Dual cure cathodic electrocoating composition
Assignee: Lilly Industries Inc
•
Filing: 1977-03-28
•
Granted: 1978-01-03
•
Expires: 1997-03-28
Abstract
Abstract An electrocoating composition containing a polymer having pendant tertiary amine groups, a polymer containing pendant mercaptan groups, a bis-maleimide cross-linking agent, and a photosensitizer can be electrodeposited onto a cathode substrate disposed within an aqueous electrocoating bath. The amine groups and the mercaptan groups are protonated with acid to render the polymers water dispersible prior to electrodeposition and are adapted to become deprotonated upon electrodeposition. Full cure of the electrodeposited coating on the cathode substrate is obtained by the combination of heat curing and ultraviolet radiation curing. In a specific embodiment of the present invention, a single polymer contains both the pendant tertiary amine groups and pendant mercaptan groups.
Inventors
- 👤 Vincent D. McGinniss
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 23:54
CPC Classifications
C; C09; C09D; C09D151/00; C09D151/003; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; C08G18/83; C08G18/833; C08G59/00; C08G59/18; C08G59/40; C08G59/4007; C08G59/4014; C08G59/4042; C08K; C08K5/00; C08K5/16; C08K5/20; C08L; C08L63/00; C09D175/00; C09D175/04; C09D5/00; C09D5/44; C09D5/4473; C09D5/4488; Y; Y10; Y10S; Y10S524/00; Y10S524/901; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31529; Y10T428/31678
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
188 words
A cathodic electrocoating composition dispersed in an aqueous electrocoating bath for electrodeposition onto a cathode substrate disposed within said bath for forming a curable electrodeposited coating on said cathode substrate comprising: a. a water-dispersed electrocoating polymer having at least about 1% by weight pendant mercaptan groups; b. a water-dispersed electrocoating polymer having at least about 1% by weight pendant tertiary amine groups, each said amine group being attached to an alpha carbon of said polymer; c. at least about 5% bis-maleimide cross-linking agent by weight of said polymers; and, d. at least about 0.5% ultraviolet photosensitizer by weight of said polymers; said pendant amine groups and said pendant mercaptan groups together comprising at least about 5% by weight of said polymers, said electrodeposited coating of said electrocoating composition adapted to cure by heating said electrodeposited coating on said cathode substrate to cross-link said mercaptan groups with said bis-maleimide to partially cure said coating followed by irradiating with ultraviolet radiation said partially cured coating to cross-link said alpha carbon of said polymer having said pendant amine groups with said bis-maleimide to fully cure said coating on said cathode substrate.
Claim 2
Dependent Claim
188 words
A cathodic electrocoating composition dispersed in an aqueous electrocoating bath for electrodeposition onto a cathode substrate disposed within said bath for forming a curable electrodeposited coating on said cathode substrate comprising: a. a water-dispersed electrocoating polymer having at least about 1% by weight pendant mercaptan groups; b. a water-dispersed electrocoating polymer having at least about 1% by weight pendant tertiary amine groups, each said amine group being attached to an alpha carbon of said polymer; c. at least about 5% bis-maleimide cross-linking agent by weight of said polymers; and, d. at least about 0.5% ultraviolet photosensitizer by weight of said polymers; said pendant amine groups and said pendant mercaptan groups together comprising at least about 5% by weight of said polymers, said electrodeposited coating of said electrocoating composition adapted to cure by heating said electrodeposited coating on said cathode substrate to cross-link said mercaptan groups with said bis-maleimide to partially cure said coating followed by irradiating with ultraviolet radiation said partially cured coating to cross-link said alpha carbon of said polymer having said pendant amine groups with said bis-maleimide to fully cure said coating on said cathode substrate.
Claim 3
Dependent Claim
25 words
The electrocoating composition of claim 1 wherein said polymer having pendant mercaptan groups and said polymer having pendant tertiary amine groups are the same polymer.
Claim 4
Dependent Claim
33 words
The electrocoating composition of claim 1 wherein said bis-maleimide is represented by the following general structure: ##STR2## where R is alkyl, aryl, alkyl-aryl, or polymers having a molecular weight up to about 3,000.
Claim 5
Dependent Claim
34 words
The electrocoating composition of claim 1 wherein the proportion of said pendant mercaptan groups is at least about 1% by weight less than the proportion of said bis-maleimide cross-linking agent in said electrocoating composition.
Claim 6
Dependent Claim
30 words
The electrocoating composition of claim 1 wherein said polymer containing pendant mercaptan group contains between about 1% and about 4% by weight of said polymer of said pendant mercaptan groups.
Claim 7
Dependent Claim
36 words
The electrocoating composition of claim 2 wherein said polymer having both pendant mercaptan groups and pendant tertiary amine groups contains beteen about 1% and about 4% by weight of said polymer of said pendant mercaptan groups.
Claim 8
Dependent Claim
22 words
The electrocoating composition of claim 1 wherein said electrocoating composition additionally contains an ethylenically unsaturated compound having a multiplicity of ethylenic unsaturation.
Claim 9
Dependent Claim
22 words
The electocoating composition of claim 2 wherein said electrocoating composition additionally contains an ethylenically unsaturated compound having a multiplicity of ethylenic unsaturation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-02 | 1981-07-04 | 1982-01-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-02 | 1985-07-04 | 1986-01-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-02 | 1989-07-04 | 1990-01-03 | $7700.00 | Window Closed / Lapsed |