Glass fiber sizing agent
Assignee: Kao Corp
•
Filing: 1976-12-10
•
Granted: 1978-01-10
•
Expires: 1996-12-10
Abstract
Abstract A glass fiber sizing agent comprising, as a sizing component, an oil-in-water emulsion of a saturated polyester which is formed by emulsifying in water, a saturated polyester obtained by reacting, under heating, (a) an aromatic or saturated aliphatic dicarboxylic acid or lower alkyl ester thereof, (b) a diol component containing at least 40 mole %, based on the total diol component, of an adduct of 2 to 10 moles of an alkylene oxide to 2,2-bis(4-hydroxyphenyl)propane, and (c) 5 to 30 parts by weight, per 100 parts by weight of the sum of the starting components (a) and (b), of an emulsifier selected from the group consisting of an adduct of 10 to 200 moles of ethylene oxide to castor oil, an adduct of 10 to 200 moles of ethylene oxide to hardened castor oil and a polyethylene glycol having an average molecular weight of 1000 to 6000.
Inventors
- 👤 Shigeru Takamori
- 👤 Yoshinao Kono
- 👤 Hirotaka Takemoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:14
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/66; C08G63/668; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/26; C03C25/32; C03C25/323; C08K; C08K5/00; C08K5/04; C08K5/09; C08K5/16; C08K5/20; C08K5/54; C08K9/00; C08K9/08; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
147 words
A composition useful for sizing glass fibers, comprising an oil-in-water emulsion obtained by emulsifying in water a saturated film-forming polyester prepared by reacting, under polyester-forming conditions, (a) an aromatic or saturated aliphatic dicarboxylic acid or lower alkyl ester thereof, (b) a diol component consisting of from 40 to 100 mole % of an adduct of 2 to 10 moles of an alkylene oxide to 2,2-bis(4-hydroxyphenyl)propane and from zero to 60 mole % of a different polyester-forming polyol, and (c) from 5 to 30 parts by weight, per 100 parts by weight of the sum of (a) and (b), of an emulsifier selected from the group consisting of an adduct of 10 to 200 moles of ethylene oxide to castor oil, an adduct of 10 to 200 moles of ethylene oxide to hardened castor oil and polyethylene glycol having an average molecular weight of from 1000 to 6000.
Claim 2
Dependent Claim
147 words
A composition useful for sizing glass fibers, comprising an oil-in-water emulsion obtained by emulsifying in water a saturated film-forming polyester prepared by reacting, under polyester-forming conditions, (a) an aromatic or saturated aliphatic dicarboxylic acid or lower alkyl ester thereof, (b) a diol component consisting of from 40 to 100 mole % of an adduct of 2 to 10 moles of an alkylene oxide to 2,2-bis(4-hydroxyphenyl)propane and from zero to 60 mole % of a different polyester-forming polyol, and (c) from 5 to 30 parts by weight, per 100 parts by weight of the sum of (a) and (b), of an emulsifier selected from the group consisting of an adduct of 10 to 200 moles of ethylene oxide to castor oil, an adduct of 10 to 200 moles of ethylene oxide to hardened castor oil and polyethylene glycol having an average molecular weight of from 1000 to 6000.
Claim 3
Dependent Claim
62 words
A composition as claimed in claim 1 in which said aromatic dicarboxylic acid is selected from the group consisting of phthalic acid, isophthalic acid, terephthalic acid, phthalic anhydride, naphthalene dicarboxylic acid and lower alkyl esters thereof and said saturated aliphatic dicarboxylic acid is selected from the group consisting of succinic acid, adipic acid, hexahydrophthalic acid, sebacic acid and lower alkyl esters thereof.
Claim 4
Dependent Claim
44 words
A composition as claimed in claim 1 in which said different polyester-forming polyol is selected from the group consisting of ethylene glycol, propylene glycol, diethylene glycol, triethylene glycol, dipropylene glycol, neopentyl glycol, hydrogenated bisphenol A, 1,3-butanediol, 1,4-butanediol, glycerin, trimethylol propane, pentaerythritol and mixtures thereof.
Claim 5
Dependent Claim
29 words
A composition as claimed in claim 1 containing from 1 to 30 parts by weight of a lubricant for glass fibers, per 100 parts by weight of said polyester.
Claim 6
Dependent Claim
30 words
A composition as claimed in claim 4 containing from 1 to 40 parts by weight of a coupling agent for glass fibers, per 100 parts by weight of said polyester.
Claim 7
Dependent Claim
18 words
A glass fiber reinforcing material coated with a composition as claimed in claim 1 as a sizing composition.
Claim 8
Dependent Claim
24 words
A glass fiber reinforced plastic article comprising glass fiber reinforcing material as claimed in claim 6 in a matrix of an unsaturated polyester resin.
References Cited (Backward Citations)
US3262809A
Cited
US3310512A
Cited
US3763064A
Cited
US3920596A
Cited
US3923708A
Cited
US4009132A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-09 | 1981-07-11 | 1982-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-09 | 1985-07-11 | 1986-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-09 | 1989-07-11 | 1990-01-10 | $7700.00 | Window Closed / Lapsed |