Fine dispersion aluminum base bearing
Assignee: JPI Transportation Products Inc
•
Filing: 1973-05-04
•
Granted: 1978-01-17
•
Expires: 1993-05-04
Abstract
Abstract A mixture of metals composed predominantly of aluminum and the balance bearing phase materials are heated to a molten state, ejected through an orifice and atomized by impinging a stream of cold water against the molten metal to effect a rapid drop in temperature as well as solidifcation. A layer of the resulting pre-alloyed particles are roll compacted simultaneously with a sacrificial surface layer and a bottom bonding layer, both being composed of aluminum base particulate materials. The bottom layer is devoid of bearing phase materials. The tri-layer strip is sintered, roll clad onto a backing member and post-annealed, blanked and formed into a bearing which is bored to remove the sacrificial layer.
Inventors
- 👤 Robert J. Fedor
- 👤 Walter E. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 03:45
CPC Classifications
B; B22; B22F; B22F7/00; B22F7/02; C; C22; C22C; C22C1/00; C22C1/04; C22C1/0408; C22C1/0416; F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/06; F16C33/12; F16C33/121; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12021; Y10T428/12028; Y10T428/12063; Y10T428/1209
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
260 words
A sintered, coherent, multi-layer powder metal composite comprising a powder metal bonding layer, a powder metal bearing layer strongly bonded to said powder metal bonding layer by a sintered transition zone of compacted, intermingled powder particles of said bearing layer and said bonding layer, and a powder metal sacrificial layer bonded to said powder metal bearing layer by a sintered transition zone of compacted, intermingled powder particles of said bearing layer and said sacrificial layer, said powder metal bonding layer comprising more than 55 weight percent aluminum and the balance material selected from a first group of additives consisting of silicon, copper, manganese, magnesium, nickel, iron, zinc, chromium, zirconium, titanium and mixtures thereof; said powder metal bearing layer comprising from 55 to about 95 weight percent aluminum, from 5 to 25 weight percent bearing phase material selected from a second group of additives consisting of lead, tin, cadmium, bismuth, antimony and mixtures thereof, and from 0 to about 20 weight percent material selected from said first group of additives, at least all of said aluminum and said bearing phase material of said bearing layer being in pre-alloyed particle form with said bearing phase material dispersed in an intra-particle position relative to said aluminum; said powder metal sacrificial layer comprising intermixed aluminum particles and bearing phase particles, more than 50 weight percent of said particles comprising aluminum particles and the balance of said particles being selected from said first and second groups of additives, the bearing phase material of said sacrificial layer having an interstitial position relative to said aluminum particles.
Claim 2
Dependent Claim
260 words
A sintered, coherent, multi-layer powder metal composite comprising a powder metal bonding layer, a powder metal bearing layer strongly bonded to said powder metal bonding layer by a sintered transition zone of compacted, intermingled powder particles of said bearing layer and said bonding layer, and a powder metal sacrificial layer bonded to said powder metal bearing layer by a sintered transition zone of compacted, intermingled powder particles of said bearing layer and said sacrificial layer, said powder metal bonding layer comprising more than 55 weight percent aluminum and the balance material selected from a first group of additives consisting of silicon, copper, manganese, magnesium, nickel, iron, zinc, chromium, zirconium, titanium and mixtures thereof; said powder metal bearing layer comprising from 55 to about 95 weight percent aluminum, from 5 to 25 weight percent bearing phase material selected from a second group of additives consisting of lead, tin, cadmium, bismuth, antimony and mixtures thereof, and from 0 to about 20 weight percent material selected from said first group of additives, at least all of said aluminum and said bearing phase material of said bearing layer being in pre-alloyed particle form with said bearing phase material dispersed in an intra-particle position relative to said aluminum; said powder metal sacrificial layer comprising intermixed aluminum particles and bearing phase particles, more than 50 weight percent of said particles comprising aluminum particles and the balance of said particles being selected from said first and second groups of additives, the bearing phase material of said sacrificial layer having an interstitial position relative to said aluminum particles.
Claim 3
Dependent Claim
37 words
A fine dispersion aluminum base multi-layer bearing material comprising: a. the sintered coherent multi-layer composite of claim 1; and b. a steel backing layer directly bonded in face-to-face relationship to said bonding layer of said multi-layer composite.
Claim 4
Dependent Claim
22 words
A bearing strip according to claim 2, wherein said sacrificial layer consists essentially of 20% tin, 1% copper and the balance aluminum.
Claim 5
Dependent Claim
20 words
A bearing strip according to claim 2, wherein said sacrificial layer consists essentially of 20% lead and the balance aluminum.
Claim 6
Dependent Claim
22 words
A bearing strip according to claim 2, wherein said sacrificial layer consists essentially of 17% lead, 3% tin and the balance aluminum.
Claim 7
Dependent Claim
24 words
The fine dispersion aluminum base multi-layer bearing material of claim 2 wherein said powder metal bearing layer consists essentially of about 100% prealloyed particles.
Claim 8
Dependent Claim
24 words
The fine dispersion aluminum base multi-layer bearing material of claim 2 wherein said bearing phase material of said powder metal bearing layer comprises lead.
Claim 9
Dependent Claim
32 words
The fine dispersion aluminum base multi-layer bearing material of claim 2 wherein said powder metal bearing layer consists essentially of 8.5% lead, 1.5% tin, 4% silicon, 1% copper and the balance aluminum.
Claim 10
Dependent Claim
30 words
The fine dispersion aluminum base multi-layer bearing material of claim 2 wherein said powder metal bearing layer consists essentially of 17% lead, 3% tin, 1% copper and the balance aluminum.
Claim 11
Dependent Claim
28 words
The fine dispersion aluminum base multi-layer bearing material of claim 2 wherein said powder metal bearing layer consists essentially of 20% tin, 1% copper and the balance aluminum.
Claim 12
Dependent Claim
189 words
A fine dispersion aluminum base bearing strip comprising: a sintered, coherent powder metal bonding layer consisting essentially of more than 55 weight percent aluminum and the balance selected from a first group of additives consisting of silicon, copper, manganese, magnesium, nickel, iron, zinc, chromium, zirconium, titanium and mixtures thereof; and a sintered, coherent powder metal bearing layer on said bonding layer, said bearing layer consisting essentially of at least 55 weight percent aluminum and the balance selected from said first group of materials in an amount of 0 to about 20 weight percent and from a second group composed of bearing phase materials in the amount of about 5 to 25 weight percent, said second group consisting of lead, tin, cadmium, bismuth, antimony and mixtures thereof; at least all of said aluminum and said bearing phase material of said bearing layer being in pre-alloyed particle form to establish an intra-particle position relative to each other, said powder metal bonding layer and said powder metal bearing layer being bonded to each other by a sintered transition zone of compacted intermingled powder particles of said bearing layer and said bonding layer.
Claim 13
Dependent Claim
189 words
A fine dispersion aluminum base bearing strip comprising: a sintered, coherent powder metal bonding layer consisting essentially of more than 55 weight percent aluminum and the balance selected from a first group of additives consisting of silicon, copper, manganese, magnesium, nickel, iron, zinc, chromium, zirconium, titanium and mixtures thereof; and a sintered, coherent powder metal bearing layer on said bonding layer, said bearing layer consisting essentially of at least 55 weight percent aluminum and the balance selected from said first group of materials in an amount of 0 to about 20 weight percent and from a second group composed of bearing phase materials in the amount of about 5 to 25 weight percent, said second group consisting of lead, tin, cadmium, bismuth, antimony and mixtures thereof; at least all of said aluminum and said bearing phase material of said bearing layer being in pre-alloyed particle form to establish an intra-particle position relative to each other, said powder metal bonding layer and said powder metal bearing layer being bonded to each other by a sintered transition zone of compacted intermingled powder particles of said bearing layer and said bonding layer.
Claim 14
Dependent Claim
209 words
A fine dispersion aluminum base multi-layer bearing material comprising: a sintered, coherent, multi-layer powder metal composite comprising a powder metal bonding layer and a powder metal bearing layer strongly bonded to each other by a sintered transition zone of compacted, intermingled powder particles of said bearing layer and said bonding layer; and a steel backing layer directly bonded in face-to-face relationship to said bonding layer of said multi-layer composite; said powder metal bonding layer consisting essentially of more than 55 weight percent aluminum and the balance material selected from the group consisting of silicon, copper, manganese, magnesium, nickel, iron, zinc, chromium, zirconium, titanium and mixtures thereof; and a sintered, coherent powder metal bearing layer on said bonding layer consisting essentially of at least 55 weight percent aluminum and the balance selected from said first group of materials in an amount of 0 to about 20 weight percent and from a second group composed of bearing phase materials in the amount of about 5 to 25 weight percent, said second group consisting of lead, tin, cadmium, bismuth, antimony and mixtures thereof; at least all of said aluminum and said bearing phase material of said bearing layer being in pre-alloyed particle form to establish an intra-particle position relative to each other.
Claim 15
Dependent Claim
209 words
A fine dispersion aluminum base multi-layer bearing material comprising: a sintered, coherent, multi-layer powder metal composite comprising a powder metal bonding layer and a powder metal bearing layer strongly bonded to each other by a sintered transition zone of compacted, intermingled powder particles of said bearing layer and said bonding layer; and a steel backing layer directly bonded in face-to-face relationship to said bonding layer of said multi-layer composite; said powder metal bonding layer consisting essentially of more than 55 weight percent aluminum and the balance material selected from the group consisting of silicon, copper, manganese, magnesium, nickel, iron, zinc, chromium, zirconium, titanium and mixtures thereof; and a sintered, coherent powder metal bearing layer on said bonding layer consisting essentially of at least 55 weight percent aluminum and the balance selected from said first group of materials in an amount of 0 to about 20 weight percent and from a second group composed of bearing phase materials in the amount of about 5 to 25 weight percent, said second group consisting of lead, tin, cadmium, bismuth, antimony and mixtures thereof; at least all of said aluminum and said bearing phase material of said bearing layer being in pre-alloyed particle form to establish an intra-particle position relative to each other.
Claim 16
Dependent Claim
24 words
A fine dispersion aluminum base bearing according to claim 12 wherein said powder metal bearing layer consists essentially of about 100 percent pre-alloyed particles.
Claim 17
Dependent Claim
20 words
A bearing according to claim 12, wherein said bonding layer consists essentially of 6 percent silicon and the balance aluminum.
Claim 18
Dependent Claim
25 words
A bearing according to claim 12, wherein said bonding layer consists essentially of 0.8% silicon, 4.4% copper, 0.8% manganese, 0.4% magnesium and the balance aluminum.
Claim 19
Dependent Claim
25 words
A bearing according to claim 12, wherein said bearing layer consists essentially of 8.5% lead, 1.5% tin, 4% silicon, 1% copper and the balance aluminum.
Claim 20
Dependent Claim
23 words
A bearing according to claim 12, wherein said bearing layer consists essentially of 17% lead, 3% tin, 1% copper and the balance aluminum.
Claim 21
Dependent Claim
21 words
A bearing according to claim 12, wherein said bearing layer consists essentially of 20% tin, 1% copper and the balance aluminum.
Claim 22
Dependent Claim
37 words
A bearing according to claim 12, wherein said bonding layer consists essentially of 100% aluminum of commercial quality, and said bearing layer consists essentially of 8.5% lead, 1.5% tin, 4% silicon, 1% copper and the balance aluminum.
Claim 23
Dependent Claim
44 words
A bearing according to claim 12, wherein said bonding layer consists essentially of 0.8% silicon, 0.4% copper, 0.8% manganese, 0.4% magnesium and the balance aluminum; and said bearing layer consists essentially of 8.5% lead, 1.5% tin, 4% silicon, 1% copper and the balance aluminum.
Claim 24
Dependent Claim
24 words
The fine dispersion aluminum base multi-layer bearing material of claim 12 wherein said bearing phase material of said powder metal bearing layer comprises lead.
References Cited (Backward Citations)
US2341732A
Cited
US2426940A
Cited
US2815567A
Cited
GB773722A
Cited
US3104135A
Cited
US3146099A
Cited
US3221392A
Cited
US3094415A
Cited
US3161502A
Cited
US3386161A
Cited
US3432293A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-16 | 1981-07-18 | 1982-01-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-16 | 1985-07-18 | 1986-01-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-16 | 1989-07-18 | 1990-01-17 | $7700.00 | Window Closed / Lapsed |