Compatibilization of hydroxyl-containing fillers and thermoplastic polymers
Assignee: Champion International Corp
•
Filing: 1975-12-23
•
Granted: 1978-01-31
•
Expires: 1995-12-23
Abstract
Abstract Hydroxyl-containing filler reinforced thermoplastic polymers, such as polyolefins, are disclosed having improved physical properties such as impact strength, break strength and flexural modulus. The filler is compatibilized with a thermoplastic polymer containing labile atoms by mixing the two together in the presence of a coupling agent, such as maleic anhydride and a free radical initiator such as a peroxide catalyst. In a preferred embodiment, clay is coated with polyethylene by mixing the two in the presence of a peroxide catalyst and maleic anhydride and the coated filler is then compounded with additional polyethylene. In another preferred embodiment, a filler is coated with a polyolefin having a high melt index and the coated filler is then compounded with a polyolefin having a lower melt index. Also disclosed are various means for molding the compatibilized composites of this invention.
Inventors
- 👤 Norman G. Gaylord
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 08:15
CPC Classifications
C; C09; C09C; C09C3/00; C09C3/10; C08; C08F; C08F255/00; C08F292/00; C08K; C08K9/00; C08K9/04; C08K9/08; C01; C01P; C01P2004/00; C01P2004/10; C01P2004/60; C01P2004/62; C01P2004/80; C01P2006/00; C01P2006/90
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
108 words
A process for compatibilizing a hydroxyl group containing inorgaic filler with a thermoplastic polymer having labile atoms which provide sites for the formation of free radicals which comprises mixing said filler and said thermoplastic polymer in the presence of an ethylenically unsaturated carboxylic acid or anhydride and a free radical catalyst under conditions which will generate free radicals on the thermoplastic polymer and which will permit the acid or anhydride to react simultaneously with the thermoplastic polymer and the hydroxyl group containing filler, whereby said acid or anhydride reacts with and couples said thermoplastic polymer and said hydroxyl group containing filler to provide a filled thermoplastic polymer composition.
Claim 2
Dependent Claim
108 words
A process for compatibilizing a hydroxyl group containing inorgaic filler with a thermoplastic polymer having labile atoms which provide sites for the formation of free radicals which comprises mixing said filler and said thermoplastic polymer in the presence of an ethylenically unsaturated carboxylic acid or anhydride and a free radical catalyst under conditions which will generate free radicals on the thermoplastic polymer and which will permit the acid or anhydride to react simultaneously with the thermoplastic polymer and the hydroxyl group containing filler, whereby said acid or anhydride reacts with and couples said thermoplastic polymer and said hydroxyl group containing filler to provide a filled thermoplastic polymer composition.
Claim 3
Dependent Claim
24 words
A process as defined in claim 1 wherein said free radical catalyst is a peroxide compound which will initiate the homopolymerization of maleic anhydride.
Claim 4
Dependent Claim
34 words
A process as defined in claim 1 wherein said free radical catalyst is a peroxide compound which has a half-life of up to about 30 minutes at the temperature at which said mixing occurs.
Claim 5
Dependent Claim
14 words
A process as defined in claim 1 wherein said thermoplastic polymer is a polyolefin.
Claim 6
Dependent Claim
21 words
A process as defined in claim 4 wherein said ethylenically unsaturated carboxylic acid or anhydride is maleic anhydride or maleic acid.
Claim 7
Dependent Claim
13 words
A process according to claim 5 wherein said polyolefin is high density polyethylene.
Claim 8
Dependent Claim
12 words
A process as defined in claim 5 wherein said filler is clay.
Claim 9
Dependent Claim
39 words
A process as defined in claim 5 wherein said filler material and said polyolefin are mixed with from about 2 to 30% by weight of maleic anydride and from about 0.5 to 10% by weight of a peroxide catalyst.
Claim 10
Dependent Claim
33 words
A process as defined in claim 5 wherein said filler and said thermoplastic polymer are mixed together before being mixed with said ethylenically unsaturated carboxylic acid or anhydride and said free radical catalyst.
Claim 11
Dependent Claim
15 words
A process as defined in claim 5 wherein said hydroxyl group containing filler is glass.
Claim 12
Dependent Claim
16 words
A process as defined in claim 5 wherein said hydroxyl group containing filler is calcium carbonate.
Claim 13
Dependent Claim
22 words
A process as defined in claim 1 wherein said thermoplastic polymer is polystyrene or a copolymer of styrene and another vinyl monomer.
Claim 14
Dependent Claim
19 words
A process as defined in claim 1 wherein said thermoplastic polymer is a copolymer of ethylene and vinyl acetate.
Claim 15
Dependent Claim
14 words
A process as defined in claim 1 wherein said thermoplastic polymer is a polyamide.
Claim 16
Dependent Claim
15 words
A process as defined in claim 1 wherein said thermoplastic polymer is an epoxy resin.
Claim 17
Dependent Claim
102 words
A process for preparing a compatibilized, filled polyolefin composition comprising coating hydroxyl group containing filler particles with a coating of a polyolefin by mixing said particles and said polyolefin in the presence of maleic anhydride or poly(maleic anhydride) and a free radical catalyst under conditions which will generate free radicals on the polyolefin and and which will permit the maleic anhydride or poly(maleic anhydride) to react simultaneously with the polyolefin and hydroxyl group containing filler particles, whereby said polyolefin coating is coupled to said filler, and said polyolefin coated filler particles are thereafter dispersed in a polyolefin matrix, said composition being thermoplastic.
Claim 18
Dependent Claim
102 words
A process for preparing a compatibilized, filled polyolefin composition comprising coating hydroxyl group containing filler particles with a coating of a polyolefin by mixing said particles and said polyolefin in the presence of maleic anhydride or poly(maleic anhydride) and a free radical catalyst under conditions which will generate free radicals on the polyolefin and and which will permit the maleic anhydride or poly(maleic anhydride) to react simultaneously with the polyolefin and hydroxyl group containing filler particles, whereby said polyolefin coating is coupled to said filler, and said polyolefin coated filler particles are thereafter dispersed in a polyolefin matrix, said composition being thermoplastic.
Claim 19
Dependent Claim
32 words
A process as defined in claim 16 wherein said filler and thermoplastic polymer are mixed together before being mixed with said ethylenically unsaturated carboxylic acid or anhydride and said free radical catalyst.
Claim 20
Dependent Claim
24 words
A process as defined in claim 16 wherein said free radical catalyst is a peroxide compound which will initiate the homopolymerization of maleic anhydride.
Claim 21
Dependent Claim
35 words
A process as defined in claim 16 wherein said free radical catalyst is a peroxide compound which has a half life of up to about 30 minutes at the temperature at which said mixing occurs.
Claim 22
Dependent Claim
24 words
A process as defined in claim 19 wherein maleic anhydride is formed in situ by heating maleic acid to a temperature above 100° C.
Claim 23
Dependent Claim
13 words
A process as defined in claim 16 wherein said filler material is clay.
Claim 24
Dependent Claim
13 words
A process according to claim 16 wherein said polyolefin is high density polyethylene.
Claim 25
Dependent Claim
39 words
A process as defined in claim 16 wherein said filler material and said polyolefin are mixed with from about 2 to 30% by weight of maleic anhydride and from about 0.5 to 10% by weight of a peroxide catalyst.
Claim 26
Dependent Claim
20 words
A process as defined in claim 16 wherein said coating polyolefin and said matrix polyolefin are the same chemical species.
Claim 27
Dependent Claim
22 words
A process as defined in claim 24 wherein said matrix polyolefin has a lower melt index than that of said encapsulating polymer.
Claim 28
Dependent Claim
20 words
A process as described in claim 25 wherein said encapsulating polyolefin has a melt index of from 5 to 50.
Claim 29
Dependent Claim
26 words
A process as described in claim 21 wherein said polyolefin coated filler particles comprise about 30 to 80% by weight of clay, the remainder being polyolefin.
Claim 30
Dependent Claim
37 words
A process as described in claim 21 wherein said polyolefin coated filler particles are mixed with sufficient matrix polyolefin to yield a final composition containing from 5 to 70% by weight of clay, the remainder being polyolefin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-30 | 1981-08-01 | 1982-01-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-30 | 1985-08-01 | 1986-01-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-30 | 1989-08-01 | 1990-01-31 | $7700.00 | Window Closed / Lapsed |