Hardenable epoxy resin compositions and process for making the same
Assignee: Novartis Corp
•
Filing: 1975-08-15
•
Granted: 1978-02-28
•
Expires: 1995-08-15
Abstract
Abstract A curable composition comprising a mixture of an epoxy resin and a hardener can be prepared by dissolving the resin and curing agent in a low boiling solvent and flashing off the solvent at temperatures in excess of 400° F, the evaporating solvent cooling the composition and minimizing precure of the resin. Reinforced composites can be prepared by passing a supporting material such as a continuous web strand or roving through the resin solution and thereafter heating at temperatures above 400° F to remove the solvent without appreciably precuring the resin. The curable epoxy compositions can be used for molding, laminating and the like.
Inventors
- 👤 Robert Flynn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 21:23
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/20; C08J3/205; C08J3/21; C08J2363/00; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2971; Y10T428/31504; Y10T428/31511; Y10T428/31525
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
91 words
A method for making a reinforced epoxy composition which comprises dissolving an 1,2-epoxy resin containing two or more epoxy groups, and a conventional curing agent therefor in a nonreactive solvent boiling at from 30° to about 100° C, passing a reinforcing substrate through the solution and exposing the impregnated substrate to a temperature of from 400° to 950° F to evaporate the solvent, the conditions of temperature and time of exposure being so adjusted and controlled that the resulting composite has a retained solvent level below 0.5% and is substantially uncured.
Claim 2
Independent Claim
91 words
A method for making a reinforced epoxy composition which comprises dissolving an 1,2-epoxy resin containing two or more epoxy groups, and a conventional curing agent therefor in a nonreactive solvent boiling at from 30° to about 100° C, passing a reinforcing substrate through the solution and exposing the impregnated substrate to a temperature of from 400° to 950° F to evaporate the solvent, the conditions of temperature and time of exposure being so adjusted and controlled that the resulting composite has a retained solvent level below 0.5% and is substantially uncured.
Claim 3
Dependent Claim
21 words
A method according to claim 1 in which the resin solution comprises 25 to 60% of resin and associated curing materials.
Claim 4
Dependent Claim
20 words
A method according to claim 1 in which the resulting composite contains from 20 to 60% by weight of binder.
Claim 5
Dependent Claim
17 words
A method according to claim 1 in which the impregnated substrate is dried under substantially isothermal conditions.
Claim 6
Dependent Claim
22 words
A method according to claim 1 in which the reinforcing substrate is in the form of a roving, strand, filament or web.
Claim 7
Dependent Claim
20 words
A method according to claim 1 in which the resulting composite has a retained epoxy value of above about 75%.
Claim 8
Dependent Claim
92 words
A method according to claim 1 in which a reinforcing substrate comprising glass or graphite roving, strand, filament or web is passed through a solution comprising 20 to 60% of epoxy resin and associated curing materials dissolved in a solvent boiling at from 40° to 80° C and thereafter passed at the same rate through a drying tower or tunnel maintained at a substantially isothermal temperature of 400° to 950° F to provide a reinforced composite having a retained solvent level below about 0.5% and a retained epoxy value above about 75%.
Claim 9
Dependent Claim
28 words
A method according to claim 7 in which the reinforcement is in the form of a roving and the resulting reinforced composite is chopped to form chopped prepreg.
Claim 10
Dependent Claim
10 words
The product obtained according to the process of claim 1.
Claim 11
Dependent Claim
10 words
The product obtained according to the process of claim 5.
Claim 12
Dependent Claim
10 words
The product obtained according to the process of claim 8.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-02-27 | 1981-08-29 | 1982-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-02-27 | 1985-08-29 | 1986-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-02-27 | 1989-08-29 | 1990-02-28 | $7700.00 | Window Closed / Lapsed |