Process for the continuous casting of liquid polymerizable compositions
Assignee: Sumitomo Chemical Co Ltd
•
Filing: 1975-12-23
•
Granted: 1978-05-16
•
Expires: 1995-12-23
Abstract
Abstract A process and apparatus for the continuous casting of a liquid polymerizable composition comprising feeding the liquid polymerizable composition together with a pair of continuous gaskets into a spacing between a pair of moving endless belts arranged such that the lower run of the upper belt is disposed above the upper run of the lower belt and said runs are driven concurrently in the same direction at substantially the same speed, said gaskets being fed such that they circumscribe both side end portions of the spacing to form a cavity, while moving together with the moving belts and keeping in contact with the opposing surfaces of the belts. Passing the composition through a portion of the path of the belts to partially polymerize said composition to such a viscosity that a common logarithm of its viscosity in terms of poise at the temperature of polymerization is within the range of 2 to 5, then passing a portion of the path thereof arranged so as to be curved at least once to bring its degree of polymerization within the range of 40 to 60 weight per cent, and thereafter passing the composition through a straight portion of the path for complete polymerization, said path for polymerization being arranged such the lower and upper runs of the respective belts are brought closer together to follow shrinkage of the composition upon polymerization. Finally the resultant polymerized plate product with a good preciseness in thickness in the widthwise direction and with favorable surface qualities is removed, from the discharge end of the belts.
Inventors
- 👤 Yasuyuki Kato
- 👤 Masahiko Moritani
- 👤 Seiichi Suzuki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 19:14
CPC Classifications
B; B29; B29C; B29C39/00; B29C39/14; B29C39/16; B29C39/003; B29C39/006
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
271 words
A process for continuously casting a liquid polymerizable composition which comprises feeding the liquid polymerizable composition, together with a pair of continuous gaskets, into a spacing defined between the lower run of the upper belt and the upper run of the lower belt both of which are arranged such that the pair of the endless belts are driven concurrently in the same direction at substantially the same speed, said gaskets being arranged so as to circumscribe the spacing serving as a pair of seals to confine a cavity whilst moving concurrently with the belts in contact with the opposing surfaces of the belts, passing the composition through a portion of the path of the belts where said composition is partially polymerized to such a viscosity that a common logarithm of its viscosity in terms of poise at the temperature of polymerization is within a range of 2 to 5, passing the resultant composition through a portion of the path thereof which is arranged so as to be curved at least once until the composition reaches a degree of polymerization within a range of about 40 to 60 weight percent based on the total weight of the composition, and thereafter passing through a straight portion of the path thereof for complete polymerization, while heat is applied to substantially the entire path thereof, said path for polymerization being arranged such that the lower and upper runs of the respective belts are brought closer together to follow shrinkage of the composition during the course of the polymerization, and removing the polymerized plate from the end portion of the belts at the discharge side thereof.
Claim 2
Dependent Claim
271 words
A process for continuously casting a liquid polymerizable composition which comprises feeding the liquid polymerizable composition, together with a pair of continuous gaskets, into a spacing defined between the lower run of the upper belt and the upper run of the lower belt both of which are arranged such that the pair of the endless belts are driven concurrently in the same direction at substantially the same speed, said gaskets being arranged so as to circumscribe the spacing serving as a pair of seals to confine a cavity whilst moving concurrently with the belts in contact with the opposing surfaces of the belts, passing the composition through a portion of the path of the belts where said composition is partially polymerized to such a viscosity that a common logarithm of its viscosity in terms of poise at the temperature of polymerization is within a range of 2 to 5, passing the resultant composition through a portion of the path thereof which is arranged so as to be curved at least once until the composition reaches a degree of polymerization within a range of about 40 to 60 weight percent based on the total weight of the composition, and thereafter passing through a straight portion of the path thereof for complete polymerization, while heat is applied to substantially the entire path thereof, said path for polymerization being arranged such that the lower and upper runs of the respective belts are brought closer together to follow shrinkage of the composition during the course of the polymerization, and removing the polymerized plate from the end portion of the belts at the discharge side thereof.
Claim 3
Dependent Claim
39 words
A process according to claim 1 wherein the composition is partially polymerized to provide a composition having such a viscosity that the common logarithm of its viscosity in terms of poise is in the range of 2.7 to 4.
Claim 4
Dependent Claim
87 words
A process according to claim 1 wherein the liquid polymerizable composition comprises at least one polymerizable, unsaturated monomer which is a methacrylate, styrene or a derivative thereof having at least one halogen atom and/or alkyl group substituent or a mixture thereof with a monomer containing at least one unsaturation copolymerizable with the monomers and which is an acrylate, acrylonitrile or a derivative thereof or a poly-functionally unsaturated monomer having at least two unsaturations and which is glycol dimethacrylate, diallyl methacrylate, diallyl phthalate, diethylene glycol or bisally carbonate.
Claim 5
Dependent Claim
14 words
A process according to claim 3 wherein the liquid polymerizable composition comprises methyl methacrylate.
Claim 6
Dependent Claim
36 words
A process according to claim 1 wherein a polymerization initiator is included in the polymerizable composition in the amount of from 0.005 to 5 percent by weight based upon the weight of the liquid polymerizable composition.
Claim 7
Dependent Claim
66 words
A process according to claim 5 wherein the polymerization initiator is at least one azo compound which is azobisisobutyronitrile, azobisdimethylvaleronitrile, or azobiscyclohexanenitrile, or at least one peroxide which is benzoyl peroxide, lauroyl peroxide, acetyl peroxide, caproyl peroxide, 2,4-dichlorobenzoyl peroxide, isopropyl peroxy dicarbonate, isobutyl peroxide, acetyl cyclohexylsulfonyl peroxide or bis(4-tert.-butylcyclohexyl)peroxydicarbonate or a mixture of an initiator of the former type with an initiator of the latter type.
Claim 8
Dependent Claim
24 words
A process according to claim 1 wherein the polymerization is carried out at a temperature in the range of from 50° to 150° C.
Claim 9
Dependent Claim
78 words
The method of claim 1, wherein the moving belts are conveyed through a curved path at least once at a radius of curvature determined by the following equation: R = K × S × T where R is the radius of curvature (in meters); S is an initial tension strength applied to the belt (in kilograms per square mm); T is the thickness of the belt (in mm); and K is a constant from about 2 to 100.
References Cited (Backward Citations)
US3383448A
Cited
US3376371A
Cited
US3872197A
Cited
US3600490A
Cited
US3852387A
Cited
US3894826A
Cited
US3978178A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-15 | 1981-11-14 | 1982-05-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-15 | 1985-11-14 | 1986-05-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-15 | 1989-11-14 | 1990-05-16 | $7700.00 | Window Closed / Lapsed |