Method for preparing shaped articles of a fluorinated elastomer
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1976-05-28
•
Granted: 1978-06-13
•
Expires: 1996-05-28
Abstract
Abstract A fluorinated elastomer is blended with a poly(vinylidene fluoride) resin at a temperature between the temperature of 70 DEG C below the melting temperature of the resin and the decomposition temperature of the same resin to form a resin blend capable of giving shaped articles having superior mechanical strengths. The resin blend is suitable for preparing heat-shrinkable articles like heat-shrinkable tubes by heating with expansion by internal pressure at an elevated temperature higher than the melting temperature of the resin, followed by cooling without release of the pressure to room temperature where the pressure is released. Such heat-shrinkable tubes can readily become shrunken by re-heating.
Inventors
- 👤 Kiyoshi Yokokawa
- 👤 Noboru Shimamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:18
CPC Classifications
C; C08; C08J; C08J3/00; C08J5/00; C08J2327/00; C08J2327/02; C08J2327/12; Y; Y10; Y10S; Y10S264/00; Y10S264/71
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
134 words
A method for preparing a heat-shrinkable article from a resin blend of a fluorinated elastomer and a poly(vinylidene fluoride) resin which comprises the steps of (a) mixing from 50 to 200 parts by weight of the poly(vinylidene fluoride) resin with 100 parts by weight of the fluorinated elastomer at a temperature between the melting temperature of the poly(vinylidene fluoride) resin and the decomposition temperature of the same resin to form the resin blend, (b) adding a curing catalyst to the thus formed resin blend, (c) shaping the resin blend into an article, (d) heating the article under forced deformation at a temperature not lower than the melting temperature of the resin to effect curing, and (e) cooling the article as such to a temperature below 100° C at which the deforming force is released.
Claim 2
Independent Claim
134 words
A method for preparing a heat-shrinkable article from a resin blend of a fluorinated elastomer and a poly(vinylidene fluoride) resin which comprises the steps of (a) mixing from 50 to 200 parts by weight of the poly(vinylidene fluoride) resin with 100 parts by weight of the fluorinated elastomer at a temperature between the melting temperature of the poly(vinylidene fluoride) resin and the decomposition temperature of the same resin to form the resin blend, (b) adding a curing catalyst to the thus formed resin blend, (c) shaping the resin blend into an article, (d) heating the article under forced deformation at a temperature not lower than the melting temperature of the resin to effect curing, and (e) cooling the article as such to a temperature below 100° C at which the deforming force is released.
Claim 3
Dependent Claim
31 words
The method as claimed in claim 1, wherein step (a) is preceded by the mixing of said resin and said elastomer at a temperature below the melting temperature of said resin.
Claim 4
Dependent Claim
19 words
The method as claimed in claim 1, wherein step (b) is carried out at a temperature below 120° C.
Claim 5
Dependent Claim
25 words
The method as claimed in claim 1, wherein the resin blend prepared in step (a) is filtered through a mesh screen prior to step (b).
Claim 6
Dependent Claim
13 words
The method as claimed in claim 1, wherein said curing catalyst is N,N'-dicinnamylidene-1,6-hexanediamine.
Claim 7
Dependent Claim
32 words
The method as claimed in claim 1, wherein said curing catalyst is added in an amount from 0.5 to 10 parts by weight per 100 parts by weight of said fluorinated elastomer.
Claim 8
Dependent Claim
29 words
The method as claimed in claim 1, wherein the shaped article is cured by heating in an atmosphere of air at a temperature ranging from 70° to 200° C.
Claim 9
Dependent Claim
30 words
The method as claimed in claim 7, wherein the cured shaped article is further subjected to heat-treatment at a temperature from 180° to 250° C for 4 to 48 hours.
Claim 10
Dependent Claim
33 words
The method of claim 1 wherein the elastomer is selected from the group consisting of copolymers of vinylidene fluoride-hexafluoropropylene, vinylidene fluoride-hexafluoropropylene-tetrafluoroethylene, tetrafluoroethylene-propylene, and vinylidene fluoride-trifluorochloroethylene alone or in mixtures of two or more.
References Cited (Backward Citations)
US3597372A
Cited
US3417176A
Cited
US3560595A
Cited
US3452126A
Cited
US3769371A
Cited
US3701702A
Cited
US3899807A
Cited
US3864228A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-12 | 1981-12-12 | 1982-06-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-12 | 1985-12-12 | 1986-06-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-12 | 1989-12-12 | 1990-06-13 | $7700.00 | Window Closed / Lapsed |