Method of producing silicon useful for semiconductor component manufacture
Assignee: Siemens AG
•
Filing: 1977-05-19
•
Granted: 1978-06-27
•
Expires: 1997-05-19
Abstract
Abstract Technical-grade silicon is purified to produce silicon having less than 1 ppm of electrically effective impurities therein, particularly boron and phosphorus, by treating molten technical silicon with a hydrogen containing gas in the presence of water so as to remove such impurities from the molten silicon.
Inventors
- 👤 Konrad Reuschel
- 👤 Norbert Schink
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:06
CPC Classifications
C; C01; C01B; C01B33/00; C01B33/02; C01B33/037; Y; Y10; Y10S; Y10S423/00; Y10S423/09; Y10S423/12
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
171 words
A method of producing silicon having a boron and phosphorous content of less than 1 ppm so that such silicon can be utilized for manufacture of silicon components, comprising: confining technical-grade silicon in a reaction chamber heated to a temperature in the range of 1420° to 1480° C. so as to produce a silicon melt within said chamber, said technical-grade silicon having an amount of boron and phosphorous therein greater than 1 ppm; and providing a stream of hydrogen-containing gas having at least 0.1% water vapor, at least 1% hydrogen and an inert gas therein and controllably passing said stream through said silicon melt within the reaction chamber so that an amount of phosphorous escapes from such silicon melt as gaseous phosphorus hydrogen compound and is removed from said melt via exhaust gases from said reaction chamber and an amount of boron escapes from such silicon melt as boron oxide and is removed from said melt in a slag that forms on top of said silicon melt, which slag is removed.
Claim 2
Independent Claim
171 words
A method of producing silicon having a boron and phosphorous content of less than 1 ppm so that such silicon can be utilized for manufacture of silicon components, comprising: confining technical-grade silicon in a reaction chamber heated to a temperature in the range of 1420° to 1480° C. so as to produce a silicon melt within said chamber, said technical-grade silicon having an amount of boron and phosphorous therein greater than 1 ppm; and providing a stream of hydrogen-containing gas having at least 0.1% water vapor, at least 1% hydrogen and an inert gas therein and controllably passing said stream through said silicon melt within the reaction chamber so that an amount of phosphorous escapes from such silicon melt as gaseous phosphorus hydrogen compound and is removed from said melt via exhaust gases from said reaction chamber and an amount of boron escapes from such silicon melt as boron oxide and is removed from said melt in a slag that forms on top of said silicon melt, which slag is removed.
Claim 3
Dependent Claim
71 words
A method as defined in claim 1 wherein said stream of hydrogen-containing gas includes not more than 0.1% of ammonium hydroxide therein so that when such gas stream is controllably passed through said silicon melt an amount of boron escapes from such silicon melt as boron oxide and boron nitride and is removed from said melt in a slag that forms on top of said silicon melt, which slag is removed.
Claim 4
Dependent Claim
23 words
A method as defined in claim 1 wherein said reaction chamber is maintained under a pressure ranging from about 100 to 300 Torr.
Claim 5
Dependent Claim
44 words
A method as defined in claim 1 wherein said stream of hydrogen-containing gas is passed through said silicon melt at a controlled flow velocity proportional to a flow velocity of 1 to 10 liters per second per a 20 kilogram mass of silicon melt.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-26 | 1981-12-26 | 1982-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-26 | 1985-12-26 | 1986-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-26 | 1989-12-26 | 1990-06-27 | $7700.00 | Window Closed / Lapsed |