US4098748A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Plasticized polyvinyl chloride resin composition containing molybdenum flame retardant and antimony compound smoke suppressant agent
Assignee: Cyprus Amax Minerals Co
•
Filing: 1976-08-16
•
Granted: 1978-07-04
•
Expires: 1996-08-16
Abstract
Abstract A flame resistant and smoke suppressed plasticized polyvinyl chloride polymer containing from about 20 to about 100 parts per hundred resin (phr) of a plasticizer comprising an ester-type primary plasticizer in combination with a controlled amount of a chlorinated paraffin or organic phosphate ester secondary plasticizer and an effective amount of a flame retardant and smoke suppressant agent comprising inorganic molybdenum compounds, such as molybdenum oxides and metal molybdates. In accordance with a preferred embodiment, the flame retardant and smoke suppressant agent further includes a controlled effective amount of antimony oxide in combination with the molybdenum compound imparting synergistic flame retardancy and smoke suppressing characteristics to the plasticized polyvinyl chloride resin formulation.
Inventors
- 👤 Fred W. Moore
- 👤 George A. Tsigdinos
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 21:46
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/18; C08K3/24; C08K13/00; C08K13/02; C08K3/20; C08K3/22; C08K5/00; C08K5/02; C08K5/04; C08K5/10; C08K5/49; C08K5/51; C08K5/52
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
151 words
A flame resistant and smoke suppressed plasticized polyvinyl chloride polymer composition consisting essentially of a polyvinyl chloride polymer, from about 20 phr to about 100 phr of a plasticizing agent comprising a mixture of a primary ester-type plasticizer and a secondary plasticizer selected from the group consisting of halogenated paraffins and organic phosphate esters, said secondary plasticizer present in an amount of from about 15 to about 50% of the total plasticizing agent present, and a flame retardant and smoke suppressant agent comprising a mixture of a molybdenum compound selected from the group consisting of molybdenum oxide and molybdate salts and an antimony compound selected from the group consisting of antimony oxide, sodium antimonate and potassium antimonate present in an amount of from about 1 phr up to about 8 phr, said antimony compound present in an amount of from 0.5 parts up to 2 parts per part molybdenum compound present.
Claim 2
Dependent Claim
151 words
A flame resistant and smoke suppressed plasticized polyvinyl chloride polymer composition consisting essentially of a polyvinyl chloride polymer, from about 20 phr to about 100 phr of a plasticizing agent comprising a mixture of a primary ester-type plasticizer and a secondary plasticizer selected from the group consisting of halogenated paraffins and organic phosphate esters, said secondary plasticizer present in an amount of from about 15 to about 50% of the total plasticizing agent present, and a flame retardant and smoke suppressant agent comprising a mixture of a molybdenum compound selected from the group consisting of molybdenum oxide and molybdate salts and an antimony compound selected from the group consisting of antimony oxide, sodium antimonate and potassium antimonate present in an amount of from about 1 phr up to about 8 phr, said antimony compound present in an amount of from 0.5 parts up to 2 parts per part molybdenum compound present.
Claim 3
Dependent Claim
31 words
The polymer composition as defined in claim 1, wherein said secondary plasticizer comprises a chlorinated paraffin present in an amount up to 30% by weight of the total plasticizing agent present.
Claim 4
Dependent Claim
46 words
The polymer composition as defined in claim 1, wherein said secondary plasticizer comprises a chlorinated paraffin containing from about 30 up to 70% by weight chlorine and present in an amount of from about 15 up to 30% by weight of the total plasticizing agent present.
Claim 5
Dependent Claim
31 words
The polymer composition as defined in claim 1, wherein said secondary plasticizer comprises organic phosphate esters present in an amount up to 50% by weight of the total plasticizing agent present.
Claim 6
Dependent Claim
29 words
The polymer composition as defined in claim 1, wherein said flame retardant and smoke suppressant agent is present in an amount of about 2 phr to about 4 phr.
Claim 7
Dependent Claim
41 words
The polymer composition as defined in claim 1, wherein said flame retardant and smoke suppressant agent is present in the form of particles of an average size less than about 20 mesh which are distributed substantially uniformly throughout said polymer composition.
Claim 8
Dependent Claim
42 words
The polymer composition as defined in claim 1, wherein said flame retardant and smoke suppressant agent is present in the form of particles of an average particle size less than about 10 microns which are distributed substantially uniformly throughout said polymer composition.
Claim 9
Dependent Claim
15 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises molybdenum trioxide.
Claim 10
Dependent Claim
15 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises molybdenum dioxide.
Claim 11
Dependent Claim
17 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises an ammonium molybdate salt.
Claim 12
Dependent Claim
17 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises a calcium molybdate salt.
Claim 13
Dependent Claim
17 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises a sodium molybdate salt.
Claim 14
Dependent Claim
17 words
The polymer composition as defined in claim 1, wherein said molybdenum compound comprises a zinc molybdate salt.
Claim 15
Dependent Claim
32 words
The polymer composition as defined in claim 1, wherein at least a portion of said molybdenum compound is present in the form of a coating on the surfaces of an extender filler.
Claim 16
Dependent Claim
28 words
The polymer composition as defined in claim 14, in which the coated said extender filler contains from about 1 to about 20% by weight of said molybdenum compound.
Claim 17
Dependent Claim
32 words
The polymer composition as defined in claim 1, wherein at least a portion of said antimony compound is present in the form of a coating on the surfaces of an extender filler.
References Cited (Backward Citations)
US2888414A
Cited
US3121067A
Cited
US3014000A
Cited
US3892667A
Cited
US3741893A
Cited
US3870679A
Cited
US3869420A
Cited
US3900441A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-03 | 1982-01-02 | 1982-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-03 | 1986-01-02 | 1986-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-03 | 1990-01-02 | 1990-07-04 | $7700.00 | Window Closed / Lapsed |