US4101450A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Catalyst for production of acetic acid
Assignee: Celanese Corp
•
Filing: 1977-05-09
•
Granted: 1978-07-18
•
Expires: 1997-05-09
Abstract
Abstract This invention provides a novel rhodium-ruthenium catalyst composition which is adapted for highly selective conversion of synthesis gas to acetic acid and related oxygenated two-carbon hydrocarbon derivatives.
Inventors
- 👤 H. Shinn Hwang
- 👤 Paul D. Taylor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:08
CPC Classifications
C; C07; C07C; C07C29/00; C07C29/15; C07C29/151; C07C29/153; C07C29/156; C07C29/157; C07C29/158; B; B01; B01J; B01J23/00; B01J23/38; B01J23/40; B01J23/46; B01J23/464; C07C51/00; C07C51/10; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/52; Y10; Y10S; Y10S502/00; Y10S502/52
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
155 words
A method for the preparation and pretreatment of a catalyst composition which is highly selective for the production of oxygenated C 2 -hydrocarbon derivatives from synthesis gas which comprises (1) co-impregnating a carrier substrate with an aqueous solution of soluble rhodium and ruthenium compounds, and subjecting the co-impregnated carrier substrate to drying conditions to remove substantially all of the water content, wherein the resultant catalyst composition consists essentially of between about 0.1 and 10 weight percent rhodium metal and between about 0.01 and 2 weight percent ruthenium metal, based on the total catalyst composition weight; (2) calcining and reducing the catalyst composition by contacting said catalyst composition with hydrogen at a temperature between about 200° C and 500° C; and (3) subsequently heating the catalyst composition in a static atmosphere of carbon monoxide and hydrogen at a temperature between about 150° C and 350° C for a time period between about 0.2 and 20 hours.
Claim 2
Independent Claim
155 words
A method for the preparation and pretreatment of a catalyst composition which is highly selective for the production of oxygenated C 2 -hydrocarbon derivatives from synthesis gas which comprises (1) co-impregnating a carrier substrate with an aqueous solution of soluble rhodium and ruthenium compounds, and subjecting the co-impregnated carrier substrate to drying conditions to remove substantially all of the water content, wherein the resultant catalyst composition consists essentially of between about 0.1 and 10 weight percent rhodium metal and between about 0.01 and 2 weight percent ruthenium metal, based on the total catalyst composition weight; (2) calcining and reducing the catalyst composition by contacting said catalyst composition with hydrogen at a temperature between about 200° C and 500° C; and (3) subsequently heating the catalyst composition in a static atmosphere of carbon monoxide and hydrogen at a temperature between about 150° C and 350° C for a time period between about 0.2 and 20 hours.
Claim 3
Dependent Claim
27 words
A method in accordance with claim 1 wherein the step (2) calcining and reducing procedure is conducted for a time period between about 0.5 and 3.0 hours.
Claim 4
Dependent Claim
46 words
A method in accordance with claim 1 wherein the molar ratio of carbon monoxide to hydrogen in the static atmosphere in step (3) is in the range between about 0.5 and 10, and the pressure of the static atmosphere is between about 50 and 5000 psi.
Claim 5
Dependent Claim
15 words
A rhodium-ruthenium catalyst composition prepared and pretreated in accordance with the method of claim 1.
Claim 6
Dependent Claim
16 words
A rhodium-ruthenium catalyst composition in accordance with claim 4 wherein the carrier substrate is silica gel.
References Cited (Backward Citations)
US2083824A
Cited
US2880241A
Cited
US3055840A
Cited
US3176038A
Cited
US3318913A
Cited
US3909456A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-17 | 1982-01-16 | 1982-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-17 | 1986-01-16 | 1986-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-17 | 1990-01-16 | 1990-07-18 | $7700.00 | Window Closed / Lapsed |