Cross-linker for flexible and semi-flexible polyurethane foams
Assignee: Dow Chemical Co
•
Filing: 1977-01-06
•
Granted: 1978-09-19
•
Expires: 1997-01-06
Abstract
Abstract Novel flexible and semi-flexible polyurethane foams having good hardness properties and superior resistance to permanent set are disclosed. The novel foams are produced by reacting an organic polyisocyanate with a polyether polyol and employing as a cross-linker an effective amount of a polymethylene polyphenylamine having a functionality of from about 2.2 to about 2.7 having a specific isomeric distribution. The cross-linker is easy to handle and is compatible with urethane foam systems.
Inventors
- 👤 William Alvis Kennedy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 21:53
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/65; C08G18/66; C08G18/6666; C08G18/667; C08G18/6681; C08G18/6685; C08G18/08; C08G18/10; C08G18/30; C08G18/32; C08G18/3225; C08G18/3237; C08G18/3243; C08G2110/00; C08G2110/0008; C08G2110/0016
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
99 words
A polyurethane foam composition consisting essentially of: a polyether polyol which has been reacted with an organic polyisocyanate in the presence of blowing agent and from about 0.8 parts to about 2.5 parts by weight per 100 parts by weight of said polyether polyol of a polymethylene polyphenyl amine mixture having an average functionality of from about 2.2 to about 2.9 wherein the methylene dianiline portion of said amine mixture has an isomeric distribution of from about 10 to 70 weight percent 2,4'-isomer, from about 1 to 20 weight percent 2,2'-isomer, with the remaining methylene dianiline being the 4,4'-isomer.
Claim 2
Dependent Claim
99 words
A polyurethane foam composition consisting essentially of: a polyether polyol which has been reacted with an organic polyisocyanate in the presence of blowing agent and from about 0.8 parts to about 2.5 parts by weight per 100 parts by weight of said polyether polyol of a polymethylene polyphenyl amine mixture having an average functionality of from about 2.2 to about 2.9 wherein the methylene dianiline portion of said amine mixture has an isomeric distribution of from about 10 to 70 weight percent 2,4'-isomer, from about 1 to 20 weight percent 2,2'-isomer, with the remaining methylene dianiline being the 4,4'-isomer.
Claim 3
Dependent Claim
30 words
The polyurethane foam composition of claim 1 wherein the ratio of isocyanate groups to the sum of the hydroxyl groups, and amine groups is from about 0.9 to about 1.1.
Claim 4
Dependent Claim
33 words
The polyurethane composition of claim 2 wherein said polymethylene polyphenyl amine mixture is present in an amount from about 1.0 to about 2.0 parts by weight per 100 parts of said olyether polyol.
Claim 5
Dependent Claim
39 words
The polyurethane composition of claim 1 wherein the polyether polyol has an average molecular weight of from about 3,500 to about 8,000 and is selected from a group consisting of polyether diols, polether triols, polyether tetrols, and mixtures thereof.
Claim 6
Dependent Claim
166 words
A polyurethane foam composition prepared by admixing and reacting a polymethylene polyphenyl isocyanate with a polyether polyol having a molecular weight from 3,500 to 8,000 in the presence of a fluorocarbon blowing agent, an effective amount of water, an effective amount of tertiary amine catalyst, an effective amount of an organo-metallic catalyst, and a cross linking agent consisting essentially of a polymethylene polyphenyl amine mixture having an average functionality of from about 2.2 to about 2.4 wherein the methylene dianiline portion of said amine mixture has an isomeric distribution of from about 15 to 30 weight percent 2,4'-isomer, from about 1 to 5 weight percent 2,2'-isomer, with the remaining methylene dianiline being substantially the 4,4'-isomer wherein the ratio of isocyanate group to the sum of the hydroxyl group and the amine groups is from about 0.9 to about 1.1 and wherein said polymethylene polyphenyl amine mixture is present in amounts from about 1.0 to about 2.0 parts by weight per 100 parts of said polyether polyol.
Claim 7
Dependent Claim
166 words
A polyurethane foam composition prepared by admixing and reacting a polymethylene polyphenyl isocyanate with a polyether polyol having a molecular weight from 3,500 to 8,000 in the presence of a fluorocarbon blowing agent, an effective amount of water, an effective amount of tertiary amine catalyst, an effective amount of an organo-metallic catalyst, and a cross linking agent consisting essentially of a polymethylene polyphenyl amine mixture having an average functionality of from about 2.2 to about 2.4 wherein the methylene dianiline portion of said amine mixture has an isomeric distribution of from about 15 to 30 weight percent 2,4'-isomer, from about 1 to 5 weight percent 2,2'-isomer, with the remaining methylene dianiline being substantially the 4,4'-isomer wherein the ratio of isocyanate group to the sum of the hydroxyl group and the amine groups is from about 0.9 to about 1.1 and wherein said polymethylene polyphenyl amine mixture is present in amounts from about 1.0 to about 2.0 parts by weight per 100 parts of said polyether polyol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-18 | 1982-03-20 | 1982-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-18 | 1986-03-20 | 1986-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-18 | 1990-03-20 | 1990-09-19 | $7700.00 | Window Closed / Lapsed |