Stabilized diphenylmethane diisocyanate prepolymer
Assignee: Caschem Inc
•
Filing: 1977-09-26
•
Granted: 1978-11-14
•
Expires: 1997-09-26
Abstract
Abstract Liquid 4,4'diphenylmethane diisocyanate (MDI) prepolymers have been produced which remain fluid and do not crystallize at temperatures below 40° F. These prepolymers comprise the reaction product of a polyol, 4,4'diphenylmethane diisocyanate (MDI) and an aliphatic and/or cycloaliphatic diisocyanate. The polyol employed is selected from the group consisting of castor oil, polyoxypropylene glycol, polyhydric alcohol mono- and di-esters of hydroxyacids of at least 12 carbon atoms and mixtures thereof. The reaction product contains the polyol in amount from about 10% to about 40%, the 4,4'diphenylmethane diisocyanate in amount from about 50% to about 70% and the aliphatic or cycloaliphatic isocyanate in amount from about 10% to about 20%. The prepolymer should be prepared such that the NCO/OH ratio should fall within the range of about 3 to about 7.
Inventors
- 👤 Thaddeus F. Kroplinski
- 👤 Melvin Brauer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 22:37
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/721; C08G18/724; C08G18/08; C08G18/10
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
110 words
A prepolymer stable at temperatures below 40° F. comprising the product of the simultaneous reaction of a polyol, 4,4,'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of aliphatic diisocyanate, cycloaliphatic diisocyanate and mixtures thereof, said polyol selected from the group consisting of castor oil and polyoxypropylene glycol, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
Claim 2
Dependent Claim
110 words
A prepolymer stable at temperatures below 40° F. comprising the product of the simultaneous reaction of a polyol, 4,4,'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of aliphatic diisocyanate, cycloaliphatic diisocyanate and mixtures thereof, said polyol selected from the group consisting of castor oil and polyoxypropylene glycol, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
Claim 3
Dependent Claim
13 words
Prepolymer according to claim 1 in which the second diisocyanate is 3-isocyanatomethyl-3,5,5-trimethyl-cyclohexyl isocyanate.
Claim 4
Dependent Claim
13 words
Prepolymer according to claim 1 in which the second diisocyanate is 4,4'dicyclohexylmethane diisocyanate.
Claim 5
Dependent Claim
14 words
Prepolymer according to claim 1 in which the second diisocyanate is 1,6 hexamethylene diisocyanate.
Claim 6
Dependent Claim
16 words
Prepolymer according to claim 1 in which the second diisocyanate is the biuret of 1,6-hexamethylene diisocyanate.
Claim 7
Dependent Claim
14 words
Prepolymer according to claim 1 in which the second diisocyanate is trimethyl hexamethylene diisocyanate.
Claim 8
Dependent Claim
148 words
A process for producing a prepolymer which is stable at temperature below 40° F. which comprises admixing a polyol, 4,4'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of aliphatic diisocyanate and mixtures thereof, said polyol selected from the group consisting of castor oil and polyoxypropylene glycol, and heating said mixture to a temperature of about 100° F. to 200° F. and holding said mixture at that temperature for a period of about 1 to 8 hours to complete the reaction and cooling the prepolymer formed, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
Claim 9
Dependent Claim
148 words
A process for producing a prepolymer which is stable at temperature below 40° F. which comprises admixing a polyol, 4,4'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of aliphatic diisocyanate and mixtures thereof, said polyol selected from the group consisting of castor oil and polyoxypropylene glycol, and heating said mixture to a temperature of about 100° F. to 200° F. and holding said mixture at that temperature for a period of about 1 to 8 hours to complete the reaction and cooling the prepolymer formed, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
Claim 10
Dependent Claim
16 words
Process according to claim 7 in which the process is carried out under a nitrogen atmosphere.
Claim 11
Dependent Claim
118 words
A prepolymer stable at temperatures below 40° F. comprising the product of the simultaneous reaction of a polyol, 4,4'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate, 4,4'dicyclohexylmethane diisocyanate, 1,6 hexamethylene diisocyanate, biuret of 1,6 hexamethylene diisocyanate and trimethyl hexamethylene diisocyanate, said polyol selected from the group consisting of castor oil and polyoxypropylene glycol, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
Claim 12
Dependent Claim
118 words
A prepolymer stable at temperatures below 40° F. comprising the product of the simultaneous reaction of a polyol, 4,4'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate, 4,4'dicyclohexylmethane diisocyanate, 1,6 hexamethylene diisocyanate, biuret of 1,6 hexamethylene diisocyanate and trimethyl hexamethylene diisocyanate, said polyol selected from the group consisting of castor oil and polyoxypropylene glycol, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
Claim 13
Dependent Claim
161 words
A process for producing a prepolymer which is stable at temperatures below 40° F. which comprises admixing a polyol, 4,4'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate, 4,4'-discyclohexylmethane diisocyanate, 1,6 hexamethylene diisocyanate, biuret of 1,6 hexamethylene diisocyanate and trimethyl hexamethylene diisocyanate, said polyol selected from the group consisting of castor oil and polyoxypropylene glycol, said polyol present in amount from about 10% to about 40%, said 4,4' diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, and heating said mixture at a temperature of about 100° F. to about 200° F. and holding said mixture at that temperature for a period of about 1 to 8 hours to complete the reaction, and cooling the prepolymer formed, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
Claim 14
Dependent Claim
161 words
A process for producing a prepolymer which is stable at temperatures below 40° F. which comprises admixing a polyol, 4,4'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate, 4,4'-discyclohexylmethane diisocyanate, 1,6 hexamethylene diisocyanate, biuret of 1,6 hexamethylene diisocyanate and trimethyl hexamethylene diisocyanate, said polyol selected from the group consisting of castor oil and polyoxypropylene glycol, said polyol present in amount from about 10% to about 40%, said 4,4' diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, and heating said mixture at a temperature of about 100° F. to about 200° F. and holding said mixture at that temperature for a period of about 1 to 8 hours to complete the reaction, and cooling the prepolymer formed, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
Claim 15
Dependent Claim
125 words
A prepolymer stable at temperature below 40° F comprising the product of the simultaneous reaction of a polyol, 4,4'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of aliphatic diisocyanate, cycloaliphatic diisocyanate and mixtures thereof, said polyol selected from the group consisting of castor oil, polyoxypropylene glycol, polyhydric alcohol mono- and di-esters of hydroxyacids of at least 12 carbon atoms and mixtures thereof, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out a a NCO/OH ratio from about 3 to about 7.
Claim 16
Dependent Claim
125 words
A prepolymer stable at temperature below 40° F comprising the product of the simultaneous reaction of a polyol, 4,4'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of aliphatic diisocyanate, cycloaliphatic diisocyanate and mixtures thereof, said polyol selected from the group consisting of castor oil, polyoxypropylene glycol, polyhydric alcohol mono- and di-esters of hydroxyacids of at least 12 carbon atoms and mixtures thereof, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out a a NCO/OH ratio from about 3 to about 7.
Claim 17
Dependent Claim
13 words
Prepolymer according to claim 11 in which the second diisocyanate is 3-isocyanatomethyl-3,5,5-trimethyl-cyclohexyl isocyanate.
Claim 18
Dependent Claim
13 words
Prepolymer according to claim 11 in which the second diisocyanate is 4,4'dicyclohexylmethane diisocyanate.
Claim 19
Dependent Claim
14 words
Prepolymer according to claim 11 in which the second diisocyanate is 1,6 hexamethylene diisocyanate.
Claim 20
Dependent Claim
17 words
Prepolymer according to claim 11 in which the second diisocyanate is the biuret of 1,6 hexamethylene diisocyanate.
Claim 21
Dependent Claim
14 words
Prepolymer according to claim 11 in which the second diisocyanate is trimethyl hexamethylene diisocyanate.
Claim 22
Dependent Claim
167 words
A process for producing a prepolymer which is stable at temperatures below 40° F. which comprises admixing a polyol, 4,4' diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of aliphatic diisocyanate, cycloaliphatic diisocyanate and mixtures thereof, said polyol selected from the group consisting of castor oil, polyoxypropylene glycol, polyhydric alcohol mono- and di-esters of hydroxy acids of at least 12 carbon atoms and mixtures thereof, and heating said mixture to a temperature of about 100° F. to 200° F. and holding said mixture at that temperature for a period of about 1 to 8 hours to complete the reaction and cooling the prepolymer formed, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
Claim 23
Dependent Claim
167 words
A process for producing a prepolymer which is stable at temperatures below 40° F. which comprises admixing a polyol, 4,4' diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of aliphatic diisocyanate, cycloaliphatic diisocyanate and mixtures thereof, said polyol selected from the group consisting of castor oil, polyoxypropylene glycol, polyhydric alcohol mono- and di-esters of hydroxy acids of at least 12 carbon atoms and mixtures thereof, and heating said mixture to a temperature of about 100° F. to 200° F. and holding said mixture at that temperature for a period of about 1 to 8 hours to complete the reaction and cooling the prepolymer formed, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
Claim 24
Dependent Claim
130 words
A prepolymer stable at temperatures below 40° F. comprising the product of the simultaneous reaction of a polyol, 4,4'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate, 4,4'dicyclohexylmethane diisocyanate, 1,6 hexamethylene diisocyanate, biuret of 1,6 hexamethylene diisocyanate, and trimethyl hexamethylene diisocyanate, said polyol selected from the group consisting of castor oil, polyoxypropylene glycol, ethylene glycol monoricinoleate, propylene glycol monoricinoleate, propylene glycol 12-hydroxystearate and mixtures thereof, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
Claim 25
Dependent Claim
130 words
A prepolymer stable at temperatures below 40° F. comprising the product of the simultaneous reaction of a polyol, 4,4'diphenylmethane diisocyanate, and a second diisocyanate selected from the group consisting of 3-isocyanatomethyl-3,5,5-trimethylcyclohexyl isocyanate, 4,4'dicyclohexylmethane diisocyanate, 1,6 hexamethylene diisocyanate, biuret of 1,6 hexamethylene diisocyanate, and trimethyl hexamethylene diisocyanate, said polyol selected from the group consisting of castor oil, polyoxypropylene glycol, ethylene glycol monoricinoleate, propylene glycol monoricinoleate, propylene glycol 12-hydroxystearate and mixtures thereof, said polyol present in amount from about 10% to about 40%, said 4,4'diphenylmethane diisocyanate present in amount from about 50% to about 70% and said second diisocyanate present in amount from about 10% to about 20%, all of the percentages expressed on a weight basis, the reaction being carried out at a NCO/OH ratio from about 3 to about 7.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-13 | 1982-05-15 | 1982-11-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-13 | 1986-05-15 | 1986-11-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-13 | 1990-05-15 | 1990-11-14 | $7700.00 | Window Closed / Lapsed |