Friction bearing and method of making such a bearing
Assignee: Erma-Werke Waffen- und Maschinenfabrik GmbH
•
Filing: 1977-05-02
•
Granted: 1979-02-06
•
Expires: 1997-05-02
Abstract
Abstract Spherical friction or sliding bearings are produced by first making a laminate from a layer of a thermosetting resin and a layer of material having a low friction coefficient. The thermosetting resin is used to impregnate a first web or fabric. The low friction coefficient material may be provided in the form of a further webbing or fabric, for instance, made of polytetrafluoroethylene. The thermosetting material may, for example, be a phenolic resin which is at this point of manufacture in its A-state and hence tacky. In order to permit the immediate further processing of the laminate with the thermosetting resin still in its tacky A-state, a dry adhesive film which neutralizes the tackiness, is applied to the laminate in sandwich formation which is then cut into pieces or strips of suitable size. The sandwich strips are then placed into a mold and pre-shaped and precision cut at room temperatures while the resin is still in its A-state. The pre-shaped low friction coefficient laminate is then assembled with the outer and inner bearing members and heated under pressure to such an extent that the thermosetting resin changes substantially from its A-state to its C-state while rapidly passing through the B-state.
Inventors
- 👤 Dieter Krauss
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 13:52
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/20; F16C33/201; F16C11/00; F16C11/04; F16C11/06; F16C11/0619; F16C11/0623; F16C11/0628; F16C11/0633; F16C33/203; F16C33/205; F16C33/208; F16C2208/00; F16C2208/20; F16C2208/30; F16C2208/32; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49636; Y10T29/49643; Y10T29/49647; Y10T29/49648; Y10T29/49657; Y10T29/49661; Y10T29/49668; Y10T29/4967
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
218 words
A method of making friction bearings comprising the following steps in sequence, preparing a laminate antifriction material by applying a thermosetting material in its A-state to one surface of a low friction coefficient webbing to form a coated webbing which initially retains the thermosetting material in its A-state, said webbing preventing said thermosetting material from penetrating through the webbing, then sandwiching under pressure said thermosetting material between said first mentioned webbing and a dry adhesive film, whereby said A-stage thermosetting material is protected by said low friction coefficient webbing on the one side and by said dry adhesive film on the other side, contacting the sandwiched, laminate antifriction material with tool means for pre-shaping said sandwiched, laminate antifriction material while said thermosetting material is still substantially in its A-state, by applying pressure to the antifriction laminate material through said tool means and by simultaneously applying heat to said antifriction laminate material also through said tool means, assemblying the pressure and heat pre-shaped antifriction laminate material with parts of a bearing and applying pressure and heat to the assembled bearing while simultaneously final shaping said antifriction laminate material, whereby said thermosetting material changes substantially from its A-state to its C-state by rapidly passing through its B-state and wherein the tackiness of said A-state is neutralized by said sandwich formation.
Claim 2
Independent Claim
218 words
A method of making friction bearings comprising the following steps in sequence, preparing a laminate antifriction material by applying a thermosetting material in its A-state to one surface of a low friction coefficient webbing to form a coated webbing which initially retains the thermosetting material in its A-state, said webbing preventing said thermosetting material from penetrating through the webbing, then sandwiching under pressure said thermosetting material between said first mentioned webbing and a dry adhesive film, whereby said A-stage thermosetting material is protected by said low friction coefficient webbing on the one side and by said dry adhesive film on the other side, contacting the sandwiched, laminate antifriction material with tool means for pre-shaping said sandwiched, laminate antifriction material while said thermosetting material is still substantially in its A-state, by applying pressure to the antifriction laminate material through said tool means and by simultaneously applying heat to said antifriction laminate material also through said tool means, assemblying the pressure and heat pre-shaped antifriction laminate material with parts of a bearing and applying pressure and heat to the assembled bearing while simultaneously final shaping said antifriction laminate material, whereby said thermosetting material changes substantially from its A-state to its C-state by rapidly passing through its B-state and wherein the tackiness of said A-state is neutralized by said sandwich formation.
Claim 3
Dependent Claim
24 words
The method of claim 1, comprising using as said antifriction material a webbing of polytetrafluoroethylene, and using as said thermosetting material a phenolic resin.
Claim 4
Dependent Claim
59 words
The method of claim 1, wherein said preshaping is performed at temperatures from 80° C. to 120° C., and at pressures ranging from 10 kg/cm 2 to 50 kg/cm 2 ; and wherein said assembled bearing is subjected to temperatures ranging from 180° C. to 200° C. and pressures ranging from 5 kg/cm 2 to 25 kg/cm 2 .
Claim 5
Dependent Claim
14 words
The method of claim 1, wherein said dry adhesive film comprises a phenolic resin.
Claim 6
Dependent Claim
18 words
The method of claim 4, wherein said phenolic resin of said dry adhesive film is in its B-state.
Claim 7
Dependent Claim
46 words
The method of claim 1, wherein said parts of a bearing comprise an outer bearing ring or shell and pressing said pre-shaped laminate antifriction material against the outer bearing ring or shell by means of an inner mold corresponding to the inner bearing ring or shell.
Claim 8
Dependent Claim
18 words
The method of claim 1, further comprising reinforcing said low friction coefficient webbing with metal or glass fibers.
Claim 9
Dependent Claim
16 words
The method of claim 1, wherein said dry adhesive film comprises a phenol-butyl rubber adhesive film.
Claim 10
Dependent Claim
13 words
A spherical friction bearing when produced according to the method of claim 1.
Claim 11
Independent Claim
212 words
A method of making friction bearings comprising the following steps in sequence, preparing a laminate antifriction material by impregnating a webbing (1) with a thermosetting material in its A-state, to form an impregnated webbing which initially retains said thermosetting material in its A-state, then sandwiching under pressure said impregnated webbing with the thermosetting A-state material therein, between a further webbing having a low friction coefficient and a dry adhesive film, whereby said A-stage thermosetting material is protected by said low friction coefficient webbing on the one side and by said dry adhesive film on the other side, contacting the sandwiched, laminate antifriction material with tool means for pre-shaping said sandwiched, laminate antifriction material while said thermosetting material is still substantially in its A-state, by applying pressure to the antifriction laminate material through said tool means and by simultaneously applying heat to said antifriction laminate material also through said tool means, assemblying the pressure and heat pre-shaped antifriction laminate material with parts of a bearing and applying pressure and heat to the assembled bearing while simultaneously final shaping said antifriction laminate material, whereby said thermosetting material changes substantially from its A-state to its C-state by rapidly passing through its B-state and wherein the tackiness of said A-state is neutralized by said sandwich formation.
Claim 12
Independent Claim
212 words
A method of making friction bearings comprising the following steps in sequence, preparing a laminate antifriction material by impregnating a webbing (1) with a thermosetting material in its A-state, to form an impregnated webbing which initially retains said thermosetting material in its A-state, then sandwiching under pressure said impregnated webbing with the thermosetting A-state material therein, between a further webbing having a low friction coefficient and a dry adhesive film, whereby said A-stage thermosetting material is protected by said low friction coefficient webbing on the one side and by said dry adhesive film on the other side, contacting the sandwiched, laminate antifriction material with tool means for pre-shaping said sandwiched, laminate antifriction material while said thermosetting material is still substantially in its A-state, by applying pressure to the antifriction laminate material through said tool means and by simultaneously applying heat to said antifriction laminate material also through said tool means, assemblying the pressure and heat pre-shaped antifriction laminate material with parts of a bearing and applying pressure and heat to the assembled bearing while simultaneously final shaping said antifriction laminate material, whereby said thermosetting material changes substantially from its A-state to its C-state by rapidly passing through its B-state and wherein the tackiness of said A-state is neutralized by said sandwich formation.
Claim 13
Dependent Claim
40 words
The method of claim 10, comprising using as said first mentioned, impregnated webbing a glass fiber webbing, using as said further webbing having a low friction coefficient a webbing of polytetrafluoroethylene, and using as said thermosetting material a phenolic resin.
Claim 14
Dependent Claim
59 words
The method of claim 10, wherein said preshaping is performed at temperatures from 80° C. to 120° C., and at pressures ranging from 10 kg/cm 2 to 50 kg/cm 2 ; and wherein said assembled bearing is subjected to temperatures ranging from 180° C. to 200° C. and pressures ranging from 5 kg/cm 2 to 25 kg/cm 2 .
Claim 15
Dependent Claim
14 words
The method of claim 10, wherein said dry adhesive film comprises a phenolic resin.
Claim 16
Dependent Claim
18 words
The method of claim 13, wherein said phenolic resin of said dry adhesive film is in its B-state.
Claim 17
Dependent Claim
46 words
The method of claim 10, wherein said parts of a bearing comprise an outer bearing ring or shell and pressing said pre-shaped laminate antifriction material against the outer bearing ring or shell by means of an inner mold corresponding to the inner bearing ring or shell.
Claim 18
Dependent Claim
18 words
The method of claim 10, further comprising reinforcing said low friction coefficient webbing with metal or glass fibers.
Claim 19
Dependent Claim
16 words
The method of claim 10, wherein said dry adhesive film comprises a phenol-butyl rubber adhesive film.
Claim 20
Dependent Claim
13 words
A spherical friction bearing when produced according to the method of claim 10.
References Cited (Backward Citations)
US2838436A
Cited
US3202749A
Cited
US3231963A
Cited
US3238602A
Cited
US3522975A
Cited
US3507022A
Cited
US3582166A
Cited
US3594049A
Cited
US3900408A
Cited
US3873168A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-05 | 1982-08-07 | 1983-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-05 | 1986-08-07 | 1987-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-05 | 1990-08-07 | 1991-02-06 | $7700.00 | Window Closed / Lapsed |