Process for producing high impact and weather resistant graft copolymers
Assignee: Resonac Corp
•
Filing: 1977-08-26
•
Granted: 1979-05-15
•
Expires: 1997-08-26
Abstract
Abstract High impact and weather resistant graft copolymers are produced by a two-stage process comprising (I) carrying out bulk or suspension polymerization of a mixture obtained by impregnating a substantially non-polar rubber-like polymer having iodine value of 2 to 40 with a mixture of an aromatic vinyl compound and a polar vinyl compound in the presence of a polymerization initiator to yield a graft copolymer, and (II) subjecting a mixture obtained by dispersing with partly dissolving (or impregnating) the graft copolymer in (or with) a mixture of an aromatic vinyl compound and a polar vinyl compound to bulk, suspension or bulk-suspension polymerization in the presence of a polymerization initiator.
Inventors
- 👤 Fusaji Shoji
- 👤 Susumu Era
- 👤 Hisashi Kogame
- 👤 Tatsuo Ito
- 👤 Koichi Kakefuda
- 👤 Kiyoyuki Suzue
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:19
CPC Classifications
C; C08; C08F; C08F255/00; C08F285/00
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
256 words
A two-step process for producing high impact and weather resistant graft copolymers which comprises: (I) in the first step, impregnating (A) 30 to 90% by weight of a substantially non-polar rubber-like polymer having an iodine value of from 2 to 40 and selected from the group consisting of ethylene-propylene type rubbers and butyl rubber with (B) 70 to 10% by weight of a vinyl compound mixture consisting of (B-1) 40 to 90% by weight of an aromatic vinyl compound, and (B-2) 60 to 10% by weight of a polar vinyl compound, and conducting bulk or suspension polymerization of the mixture obtained by the above-mentioned impregnation in the presence of (C) a polymerization initiator to produce a graft copolymer; and (II) in the second step, either dispersing with partly dissolving (D) the graft copolymer obtained in the step (I) in (E) a vinyl compound mixture consisting of (E-1) 40 to 90% by weight of an aromatic vinyl compound, and (E-2) 60 to 10% by weight of a polar vinyl compound or impregnating the component (D) with the component (E) and conducting bulk, suspension, or bulk-suspension polymerization of the mixture obtained by the above-mentioned dispersion or impregnation without using any organic solvent in the presence of (F) a polymerization initiator to produce the end product having 5 to 20% by weight of rubber component and 95 to 80% by weight of the total vinyl compounds, wherein the ratio of the aromatic vinyl compounds to the polar vinyl compounds is in the range of 60/40 to 90/10 by weight.
Claim 2
Dependent Claim
256 words
A two-step process for producing high impact and weather resistant graft copolymers which comprises: (I) in the first step, impregnating (A) 30 to 90% by weight of a substantially non-polar rubber-like polymer having an iodine value of from 2 to 40 and selected from the group consisting of ethylene-propylene type rubbers and butyl rubber with (B) 70 to 10% by weight of a vinyl compound mixture consisting of (B-1) 40 to 90% by weight of an aromatic vinyl compound, and (B-2) 60 to 10% by weight of a polar vinyl compound, and conducting bulk or suspension polymerization of the mixture obtained by the above-mentioned impregnation in the presence of (C) a polymerization initiator to produce a graft copolymer; and (II) in the second step, either dispersing with partly dissolving (D) the graft copolymer obtained in the step (I) in (E) a vinyl compound mixture consisting of (E-1) 40 to 90% by weight of an aromatic vinyl compound, and (E-2) 60 to 10% by weight of a polar vinyl compound or impregnating the component (D) with the component (E) and conducting bulk, suspension, or bulk-suspension polymerization of the mixture obtained by the above-mentioned dispersion or impregnation without using any organic solvent in the presence of (F) a polymerization initiator to produce the end product having 5 to 20% by weight of rubber component and 95 to 80% by weight of the total vinyl compounds, wherein the ratio of the aromatic vinyl compounds to the polar vinyl compounds is in the range of 60/40 to 90/10 by weight.
Claim 3
Dependent Claim
25 words
A process according to claim 1, wherein the component (A) is impregnated with the component (B) in the absence of water in the step (I).
Claim 4
Dependent Claim
40 words
A process according to claim 1, wherein, in the step (I), the component (A) is impregnated with the component (B) in the presence of water and the mixture is subjected to suspension polymerization in the presence of the component (C).
Claim 5
Dependent Claim
50 words
A process according to claim 1, wherein, in the step (I), the mixture obtained by grinding the component (A) in the presence of water by a crusher while or after impregnating the component (A) with the component (B) is subjected to suspension polymerization in the presence of the component (C).
Claim 6
Dependent Claim
14 words
A process according to claim 4, wherein the crusher is a convectional high mixer.
Claim 7
Dependent Claim
41 words
A process according to claim 1, wherein, in the step (II), the mixture obtained by dispersing with partly dissolving the component (D) in the component (E) is subjected to bulk, suspension or bulk-suspension polymerization in the presence of the component (F).
Claim 8
Dependent Claim
66 words
A process according to claim 6, wherein said dispersion with partial solution of the component (D) in the component (E) is accomplished by first dissolving the component (D) in a vinyl compound mixture consisting of 100 to 85% by weight of an aromatic vinyl compound and 0 to 15% by weight of a polar vinyl compound, and then adding the remaining vinyl compounds to the solution.
Claim 9
Dependent Claim
14 words
A process according to claim 6, wherein said mixture is subjected to suspension polymerization.
Claim 10
Dependent Claim
14 words
A process according to claim 6, wherein said mixture is subjected to bulk-suspension polymerization.
Claim 11
Dependent Claim
14 words
A process according to claim 6, wherein said mixture is subjected to bulk polymerization.
Claim 12
Dependent Claim
35 words
A process according to claim 1, wherein, in the step (II), the mixture obtained by impregnating the component (D) with the component (E) is subjected to suspension polymerization in the presence of the component (F).
Claim 13
Dependent Claim
25 words
A process according to claim 11, wherein the component (D) is impregnated with the component (E) in the absence of water in the step (II).
Claim 14
Dependent Claim
27 words
A process according to claim 11, wherein, in the step (II), the component (D) is first ground by a crusher and then impregnated with the component (E).
Claim 15
Dependent Claim
48 words
A process according to claim 11, wherein, in the step (II), the component (D) is impregnated with the component (E) under agitation in the presence of water in an amount of 50% by weight or more based on the total weight of said both components (D) and (E).
Claim 16
Dependent Claim
69 words
A process according to claim 11, wherein, in the step (II), the mixture obtained by grinding the component (D) by a crusher, while or after impregnating the component (D) with the component (E), in the presence of water in an amount of 50% by weight or more based on the total weight of said both components and is subjected to suspension polymerization in the presence of the component (F).
Claim 17
Dependent Claim
14 words
A process according to claim 15, wherein the crusher is a convectional high mixer.
Claim 18
Dependent Claim
102 words
A process according to claim 1, wherein in the step (I), the mixture obtained by impregnating the component (A) with the component (B) in the presence of water is subjected to suspension polymerization in the presence of the component (C), and then in the step (II), the mixture obtained by first dissolving the component (D) in a vinyl compound mixture consisting of 100 to 85% by weight of an aromatic vinyl compound and 0 to 15% by weight of a polar vinyl compound and then adding the remaining vinyl compounds is subjected to suspension polymerization in the presence of the component (F).
Claim 19
Dependent Claim
111 words
A process according to claim 1, wherein in the step (I), the mixture obtained by impregnating the component (A) with the component (B) in the presence of water is subjected to suspension polymerization in the presence of the component (C), and then in the step (II), the mixture obtained by grinding the component (D) by a convectional high mixer while or immediately after impregnating the component (D) with the component (E) under agitation in the presence of water in an amount of 50% by weight or more based on the total weight of said both components (D) and (E) is subjected to suspension polymerization in the presence of the component (F).
Claim 20
Dependent Claim
27 words
A process according to claim 1, wherein the graft copolymer obtained in the step (II) is loaded with 8 to 20% by weight of the rubber-like polymer.
Claim 21
Dependent Claim
27 words
A process according to claim 1, wherein the graft copolymer obtained in the step (I) is loaded with 40 to 70% by weight of the rubber-like polymer.
Claim 22
Dependent Claim
32 words
A process according to claim 1, wherein the aromatic vinyl compound/polar vinyl compound weight ratio in the graft copolymer obtained in the step (II) is in the range of 60/40 to 80/20.
Claim 23
Dependent Claim
28 words
A process according to claim 1, wherein the substantially non-polar rubber-like polymer with iodine value of 2 to 40 is an ethylene-propylene copolymer rubber or ethylene-propylene-non-conjugated-diene terpolymer rubber.
Claim 24
Dependent Claim
22 words
A process according to claim 22, wherein the ethylene-propylene-non-conjugated-diene terpolymer rubber has Mooney viscosity ML 1+4 (100° C.) of 60 to 90.
Claim 25
Dependent Claim
16 words
A process according to claim 23, wherein the ethylene-propylene-non-conjugated-diene terpolymer rubber is an ethylene-propylene-5-ethylidene-2-norbornene terpolymer rubber.
Claim 26
Dependent Claim
21 words
A process according to claim 1, wherein the aromatic vinyl compounds of the components (B) and (E) are styrene and/or α-methylstyrene.
Claim 27
Dependent Claim
22 words
A process according to claim 1, wherein the polar vinyl compounds of the components (B) and (E) are acrylonitrile and/or methyl methacrylate.
Claim 28
Dependent Claim
48 words
A process according to claim 1, wherein the rubber-like polymer (component (A)) is an ethylene-propylene-5-ethylidene-2-norbonrnene terpolymer rubber, and the aromatic vinyl compound of the components (B) and (E) is styrene and the polar vinyl compounds of the components (B) and (E) are acrylonitrile, or acrylonitrile and methyl methacrylate.
References Cited (Backward Citations)
US3671607A
Cited
US3855355A
Cited
GB1373089A
Cited
US3927142A
Cited
US3900529A
Cited
US3939225A
Cited
US4012462A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-05-14 | 1982-11-13 | 1983-05-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-05-14 | 1986-11-13 | 1987-05-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-05-14 | 1990-11-13 | 1991-05-15 | $7700.00 | Window Closed / Lapsed |