Assignee: RTX Corp
•
Filing: 1977-12-27
•
Granted: 1979-06-05
•
Expires: 1997-12-27
Abstract
Abstract A thermally conductive caulk particularly suited for use in a phosphoric acid fuel cell is made by mixing graphite into a stable aqueous dispersion of polytetrafluoroethylene and fluorinated ethylene propylene such that the solids floc to form a paste. The paste is applied to the part to be caulked and then dried and heat treated. Caulks made according to the present invention have good thermal conductivity and absorb very little phosphoric acid.
Inventors
- 👤 Ronald G. Martin
- 👤 Joseph Powers
- 👤 John C. Trocciola
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 10:26
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/20; C08J3/205; C08J3/21; C08J3/212; C08K; C08K3/00; C08K3/02; C08K3/04; H; H01; H01M; H01M8/00; H01M8/04; H01M8/04007; H01M8/04067; H01M8/04074; C08J2327/00; C08J2327/02; C08J2327/12; C08J2327/18; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
143 words
A process for making an electrically conductive and thermally conductive caulk comprising the steps of: forming a compound by (1) mixing together a stable aqueous dispersion of fluorinated ethylene propylene and a stable aqueous dispersion of PTFE to form a stable aqueous dispersion of fluorinated ethylene propylene and PTFE and (2) stirring into said dispersion of fluorinated ethylene propylene and PTFE an amount of particulate graphite at least sufficient to cause flocculation of all the fluorinated ethylene propylene and PTFE solids along with the graphite, the solids content of said compound comprising 50-70% by weight fluorinated ethylene propylene and PTFE combined and 30-50% graphite, the ratio of fluorinated ethylene propylene to PTFE being between 3:1 and 1:10; drying the compound by heating below the initial melting point of fluorinated ethylene propylene; and heating the dried compound to between 560° F. and 700° F.
Claim 2
Dependent Claim
143 words
A process for making an electrically conductive and thermally conductive caulk comprising the steps of: forming a compound by (1) mixing together a stable aqueous dispersion of fluorinated ethylene propylene and a stable aqueous dispersion of PTFE to form a stable aqueous dispersion of fluorinated ethylene propylene and PTFE and (2) stirring into said dispersion of fluorinated ethylene propylene and PTFE an amount of particulate graphite at least sufficient to cause flocculation of all the fluorinated ethylene propylene and PTFE solids along with the graphite, the solids content of said compound comprising 50-70% by weight fluorinated ethylene propylene and PTFE combined and 30-50% graphite, the ratio of fluorinated ethylene propylene to PTFE being between 3:1 and 1:10; drying the compound by heating below the initial melting point of fluorinated ethylene propylene; and heating the dried compound to between 560° F. and 700° F.
Claim 3
Dependent Claim
25 words
The process according to claim 1 wherein said solids content of said finished caulk is between 50% and 60% fluorinated ethylene propylene and PTFE combined.
Claim 4
Dependent Claim
20 words
The process according to claim 1 wherein the ratio of fluorinated ethylene propylene to PTFE is between 2:1 and 1:3.
Claim 5
Dependent Claim
25 words
The process according to claim 3 wherein said solids content of said finished caulk is between 50% and 60% fluorinated ethylene propylene and PTFE combined.
Claim 6
Dependent Claim
18 words
The process according to claim 4 wherein the ratio of fluorinated ethylene propylene to PTFE is about 1:1.
Claim 7
Dependent Claim
30 words
The process according to claim 4 wherein during the step of forming a compound a floccing agent is added to the stable aqueous dispersion of fluorinated ethylene propylene and PTFE.
Claim 8
Dependent Claim
36 words
The process according to claim 6 wherein said floccing agent is isopropanol, which is added in an amount equivalent to between 25% and 35% of the combined weight of fluorinated ethylene propylene, PTFE, graphite and isopropanol.
Claim 9
Dependent Claim
26 words
The process according to claim 4 wherein said heating of said dried caulk is done between 600° F. and 620° F. for at least one hour.
Claim 10
Dependent Claim
36 words
The process according to claim 3 wherein said caulk, when immersed in a bath of 400° F. 105% concentration phosphoric acid for 65 hours, will absorb no more than 6% of its own weight in acid.
Claim 11
Dependent Claim
33 words
The process according to claim 8 wherein said finished caulk has a coefficient of thermal conductivity of at least 0.6 BTU/ft·hr·°F. and absorbs no more than about 1% of its weight in acid.
Claim 12
Dependent Claim
26 words
The process according to claim 8 wherein said solids content is between 50% and 60% fluorinated ethylene propylene and PTFE combined, with a balance of graphite.
Claim 13
Dependent Claim
18 words
The process according to claim 11 wherein the ratio of fluorinated ethylene propylene to PTFE is about 1:1.
Claim 14
Dependent Claim
140 words
A thermally and electrically conductive and acid resistant caulk made by mixing sufficient particulate graphite into a stable aqueous dispersion of fluorinated ethylene propylene and PTFE to cause flocculation of all the fluorinated ethylene propylene and PTFE solids along with the graphite, drying the floc so formed and heating the dried floc to at least 560° F. and no greater than 700° F. for at least 0.5 hour, said caulk comprising 50-70% by weight fluorinated ethylene propylene and PTFE combined and 30-50% graphite, the ratio of fluorinated ethylene propylene to PTFE solids being between 3:1 and 1:10, and said caulk having a coefficient of thermal conductivity of at least 0.6 BTU/ft·hr·°F, and when immersed in a bath of 400° F. 105% concentration phosphoric acid for 65 hours it absorbs no more than about 3% of its own weight in acid.
Claim 15
Dependent Claim
140 words
A thermally and electrically conductive and acid resistant caulk made by mixing sufficient particulate graphite into a stable aqueous dispersion of fluorinated ethylene propylene and PTFE to cause flocculation of all the fluorinated ethylene propylene and PTFE solids along with the graphite, drying the floc so formed and heating the dried floc to at least 560° F. and no greater than 700° F. for at least 0.5 hour, said caulk comprising 50-70% by weight fluorinated ethylene propylene and PTFE combined and 30-50% graphite, the ratio of fluorinated ethylene propylene to PTFE solids being between 3:1 and 1:10, and said caulk having a coefficient of thermal conductivity of at least 0.6 BTU/ft·hr·°F, and when immersed in a bath of 400° F. 105% concentration phosphoric acid for 65 hours it absorbs no more than about 3% of its own weight in acid.
Claim 16
Dependent Claim
33 words
The caulk according to claim 13 wherein said caulk comprises 50-60% fluorinated ethylene propylene and PTFE combined and 40-50% graphite, and absorbs no more than about 1% of its own weight in acid.
Claim 17
Dependent Claim
19 words
The caulk according to claim 14 wherein the ratio of fluorinated ethylene propylene to PTFE solids is about 1:1.
Claim 18
Dependent Claim
17 words
The caulk according to claim 15 wherein the coefficient of thermal conductivity is at least 0.8 BTU/ft·hr·°F.
References Cited (Backward Citations)
US2782180A
Cited
US2782179A
Cited
US3801374A
Cited
UST884008I4
Cited
US3684755A
Cited
US3772249A
Cited
US4038244A
Cited
JPS5058158A
Cited
JPS5128136A
Cited
US3964930A
Cited
US4053443A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-06-04 | 1982-12-04 | 1983-06-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-06-04 | 1986-12-04 | 1987-06-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-06-04 | 1990-12-04 | 1991-06-05 | $7700.00 | Window Closed / Lapsed |