Production of maleic anhydride from four-carbon hydrocarbons using catalysts prepared by hydrothermal techniques

Claim 2

In a process for the production of maleic anhydride by the oxidation of n-butene, n-butene, 1,3-butadiene or mixture thereof with molecular oxygen in the vapor phase at a reaction temperature of 250° C. to 600° C. in the presence of a catalyst comprising the mixed oxides of vanadium and phosphorus, the improvement wherein the catalyst is prepared by (a) forming an aqueous oxide slurry of a vanadium compound containing pentavalent vanadium and a mineral acid-free, inorganic reducing agent capable of reducing said pentavalent vanadium to a valence state below +5, wherein said reducing agent is a member selected from the group consisting of ammonia, hydrazine, hydrazine hydrate, a finely divided metal or colloidal metal; (b) admixing a phosphorus compound containing pentavalent phosphorus with said aqueous slurry of step (a); (c) heating said aqueous slurry of step (b) at a temperature of at least 120° C. under autogenous pressure so that substantial evaporation of the water in said slurry is prevented; (d) removing the water from the slurry of step (c) to form a dried catalyst; and (e) calcining the dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas.

Claim 3

The process of claim 1 wherein n-butane is reacted.

Claim 4

The process of claim 1 wherein an n-butene is reacted.

Claim 5

The process of claim 1 wherein the phosphorus to vanadium atom ratio is 0.1:10 to 10:0.1.

Claim 6

The process of claim 1 wherein the phosphorus to vanadium atom ratio is 0.5:3 to 3:0.5.

Claim 7

The process of claim 1 wherein the compound containing pentavalent vanadium is vanadium pentoxide.

Claim 8

The process of claim 1 wherein the compound containing pentavalent phosphorus is phosphoric acid.

Claim 9

The process of claim 1 wherein the aqueous slurry of step (c) is heated at a temperature of 120° C. to 300° C.

Claim 10

The process of claim 1 wherein the aqueous slurry of step (c) is heated under autogenous pressure of 15 to 1300 p.s.i.g.

Claim 11

The process of claim 1 wherein the aqueous slurry of step (c) is heated at a temperature of 130° C. to 240° C. under autogenous pressure of 20 to 500 p.s.i.g.

Claim 12

The process of claim 1 wherein the catalyst is prepared in the absence of a hydrogen halide, or an organic reducing agent.

Claim 13

The process of claim 11 wherein the organic reducing agent is an organic acid, aldehyde or secondary alcohol.

Claim 14

The process of claim 1 wherein said finely divided metal or colloidal metal is selected from the group consisting of molybdenum, tungsten, magnesium, aluminum or nickel.

Claim 15

The process of claim 1 wherein compounds containing respective optional promoter elements of uranium, tantalum, cerium, chromium, manganese, cobalt, copper, antimony, iron, bismuth, tungsten, molybdenum, alkaline earth metal, an alkali metal, hafnium, zirconium, thorium and sulfur may be added during the preparation of the catalyst immediately before the addition of the phosphorus compound or after the addition of the phosphorus compound.

Claim 16

In a process for the production of maleic anhydride by the oxidation of n-butane, n-butene, 1,3-butadiene or mixture thereof with molecular oxygen in the vapor phase at a reaction temperature of 250° C. to 600° C. in the presence of a catalyst comprising mixed oxides of vanadium and phosphorus, the improvement wherein the catalyst is prepared by (a) forming an aqueous oxide slurry of a vanadium compound containing pentavalent vanadium and a mineral acid-free, inorganic reducing agent capable of reducing said pentavalent vanadium to a valence state below +5, wherein said reducing agent is selected from the group consisting of hydrazine and finely divided metals; (b) admixing a phosphorus compound containing pentavalent phosphorus with said aqueous slurry of step (a); (c) heating said aqueous slurry of step (b) at a temperature of at least 120° C. under autogenous pressure so that substantial evaporation of the water in said slurry is presented; (d) removing the water from the slurry of step (c) to form a dried catalyst; and (e) calcining the dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas.

Claim 17

In a process for the production of maleic anhydride by the oxidation of n-butane, n-butene, 1,3-butadiene or mixture thereof with molecular oxygen in the vapor phase at a reaction temperature of 250° C. to 600° C. in the presence of a catalyst comprising mixed oxides of vanadium and phosphorus, the improvement wherein the catalyst is prepared by (a) forming an aqueous oxide slurry of a vanadium compound containing pentavalent vanadium and a mineral acid-free, inorganic reducing agent capable of reducing said pentavalent vanadium to a valence state below +5, wherein said reducing agent is selected from the group consisting of hydrazine and finely divided metals; (b) admixing a phosphorus compound containing pentavalent phosphorus with said aqueous slurry of step (a); (c) heating said aqueous slurry of step (b) at a temperature of at least 120° C. under autogenous pressure so that substantial evaporation of the water in said slurry is presented; (d) removing the water from the slurry of step (c) to form a dried catalyst; and (e) calcining the dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas.

Claim 18

The process of claim 15 wherein the finely divided metal is tungsten.

Claim 19

The process of claim 15 wherein said finely divided metal is selected from the group consisting of molybdenum, tungsten, magnesium, aluminum or nickel.

Claim 20

The process of claim 15 wherein n-butane is reacted.

Claim 21

In a process for producing maleic anhydride from n-butane, n-butene, 1,3-butadiene or mixture thereof with molecular oxygen in the vapor phase at a reaction temperature of 250° C. to 600° C. in the presence of a catalyst comprising the mixed oxides of vanadium and phosphorus, the improvement wherein the catalyst is prepared by (a) refluxing an aqueous oxide slurry containing vanadium pentoxide and a mineral acid-free, inorganic reducing agent capable of reducing the vanadium in the vanadium pentoxide to a valence state below +5 to obtain an aqueous slurry containing reduced vanadium, wherein said reducing agent is a member selected from the group consisting of ammonia, hydrazine, hydrazine hydrate, a finely divided metal or colloidal metal; (b) admixing phosphoric acid with said aqueous slurry containing reduced vanadium; (c) autoclaving the aqueous slurry of step (b) at a temperature of 120° C. to 250° C. under autogenous pressure of 15 to 1300 p.s.i.g. so as to retain substantially all of the water content in the slurry; (d) removing the water from the slurry of step (c) to form a dried catalyst; and (e) calcining said dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas.

Claim 22

In a process for producing maleic anhydride from n-butane, n-butene, 1,3-butadiene or mixture thereof with molecular oxygen in the vapor phase at a reaction temperature of 250° C. to 600° C. in the presence of a catalyst comprising the mixed oxides of vanadium and phosphorus, the improvement wherein the catalyst is prepared by (a) refluxing an aqueous oxide slurry containing vanadium pentoxide and a mineral acid-free, inorganic reducing agent capable of reducing the vanadium in the vanadium pentoxide to a valence state below +5 to obtain an aqueous slurry containing reduced vanadium, wherein said reducing agent is a member selected from the group consisting of ammonia, hydrazine, hydrazine hydrate, a finely divided metal or colloidal metal; (b) admixing phosphoric acid with said aqueous slurry containing reduced vanadium; (c) autoclaving the aqueous slurry of step (b) at a temperature of 120° C. to 250° C. under autogenous pressure of 15 to 1300 p.s.i.g. so as to retain substantially all of the water content in the slurry; (d) removing the water from the slurry of step (c) to form a dried catalyst; and (e) calcining said dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas.

Claim 23

The process of claim 19 wherein said finely divided metal or colloidal metal is selected from the group consisting of molybdenum, tungsten, magnesium, aluminum or nickel.

Claim 24

The process of claim 19 wherein n-butane is reacted.

Claim 25

In a process for producing maleic anhydride from n-butane, n-butene, 1,3-butadiene or mixture thereof with molecular oxygen in the vapor phase at a reaction temperature of 250° C. to 600° C. in the presence of a catalyst comprising mixed oxides of vanadium and phosphorus, the improvement wherein the catalyst is prepared by (a) refluxing an aqueous oxide slurry containing vanadium pentoxide and a mineral acid-free, inorganic reducing agent capable of reducing the vanadium in the vanadium pentoxide to a valence state below +5 to obtain an aqueous slurry containing reduced vanadium, wherein said reducing agent is a finely divided metal; (b) admixing phosphoric acid with said aqueous slurry containing reduced vanadium; (c) autoclaving the aqueous slurry of step (b) at a temperature of 120° C. to 250° C. under autogenous pressure of 15 to 1,300 p.s.i.g. so as to retain substantially all of the water content in the slurry; (d) removing the water from the slurry of step (c) to form a dried catalyst; and (e) calcining said dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas.

Claim 26

In a process for producing maleic anhydride from n-butane, n-butene, 1,3-butadiene or mixture thereof with molecular oxygen in the vapor phase at a reaction temperature of 250° C. to 600° C. in the presence of a catalyst comprising mixed oxides of vanadium and phosphorus, the improvement wherein the catalyst is prepared by (a) refluxing an aqueous oxide slurry containing vanadium pentoxide and a mineral acid-free, inorganic reducing agent capable of reducing the vanadium in the vanadium pentoxide to a valence state below +5 to obtain an aqueous slurry containing reduced vanadium, wherein said reducing agent is a finely divided metal; (b) admixing phosphoric acid with said aqueous slurry containing reduced vanadium; (c) autoclaving the aqueous slurry of step (b) at a temperature of 120° C. to 250° C. under autogenous pressure of 15 to 1,300 p.s.i.g. so as to retain substantially all of the water content in the slurry; (d) removing the water from the slurry of step (c) to form a dried catalyst; and (e) calcining said dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas.

Claim 27

The process of claim 22 wherein the finely divided metal is tungsten.

Claim 28

In a process for the preparation of maleic anhydride by the oxidation of n-butane with molecular oxygen in the vapor phase at a reaction temperature of 250° C. to 600° C. in the presence of a catalyst comprising vanadium, phosphorus, uranium and oxygen, the improvement wherein said catalyst is prepared by (a) forming an aqueous slurry of a vanadium compound containing pentavalent vanadium and a mineral acid-free, inorganic reducing agent capable of reducing said pentavalent vanadium to a valence state below +5; (b) admixing a phosphorus compound containing pentavalent phosphorus with said aqueous slurry of step (a); (c) heating said aqueous slurry of step (b) at a temperature of 120° C. undder autogenous pressure so that substantial evaporation of the water in said slurry is prevented; (d) removing the water from the slurry of step (c) to form a dried catalyst; (e) calcining the dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas, and (f) adding a uranium compound immediately before the addition of the phosphorus compound or after the addition of the phosphorus compound.

Claim 29

In a process for the preparation of maleic anhydride by the oxidation of n-butane with molecular oxygen in the vapor phase at a reaction temperature of 250° C. to 600° C. in the presence of a catalyst comprising vanadium, phosphorus, uranium and oxygen, the improvement wherein said catalyst is prepared by (a) forming an aqueous slurry of a vanadium compound containing pentavalent vanadium and a mineral acid-free, inorganic reducing agent capable of reducing said pentavalent vanadium to a valence state below +5; (b) admixing a phosphorus compound containing pentavalent phosphorus with said aqueous slurry of step (a); (c) heating said aqueous slurry of step (b) at a temperature of 120° C. undder autogenous pressure so that substantial evaporation of the water in said slurry is prevented; (d) removing the water from the slurry of step (c) to form a dried catalyst; (e) calcining the dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas, and (f) adding a uranium compound immediately before the addition of the phosphorus compound or after the addition of the phosphorus compound.

Claim 30

In a process for the preparation of maleic anhydride by the oxidation of n-butane, n-butene, 1,3-butadiene or mixture thereof with molecular oxygen in the vapor phase at a reaction temperaure of 250° C. to 600° C. in the presence of a catalyst comprising vanadium, phosphorus, uranium, and oxygen, the improvement wherein said catalyst is prepared by (a) forming an aqueous slurry of a vanadium compound containing pentavalent vanadium and a mineral acid-free, inorganic reducing agent capable of reducing said pentavalent vanadium to a valence state below +5, wherein said reducing agent is a member selected from the group consisting of ammonia, hydrazine, hydrazine hydrate, or a finely divided metal or a colloidal metal; (b) admixing a phosphorus compound containing pentavalent phosphorus with said aqueous slurry of step (a); (c) heating said aqueous slurry of step (b) at a temperature of 120° C. under autogenous pressure so that substantial evaporation of the water in said slurry is prevented; (d) removing the water from the slurry of step (c) to form a dried catalyst; (e) calcining the dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas; and (f) adding a uranium compound immediately before the addition of the phosphorus compound or after the addition of the phosphorus compound.

Claim 31

In a process for the preparation of maleic anhydride by the oxidation of n-butane, n-butene, 1,3-butadiene or mixture thereof with molecular oxygen in the vapor phase at a reaction temperaure of 250° C. to 600° C. in the presence of a catalyst comprising vanadium, phosphorus, uranium, and oxygen, the improvement wherein said catalyst is prepared by (a) forming an aqueous slurry of a vanadium compound containing pentavalent vanadium and a mineral acid-free, inorganic reducing agent capable of reducing said pentavalent vanadium to a valence state below +5, wherein said reducing agent is a member selected from the group consisting of ammonia, hydrazine, hydrazine hydrate, or a finely divided metal or a colloidal metal; (b) admixing a phosphorus compound containing pentavalent phosphorus with said aqueous slurry of step (a); (c) heating said aqueous slurry of step (b) at a temperature of 120° C. under autogenous pressure so that substantial evaporation of the water in said slurry is prevented; (d) removing the water from the slurry of step (c) to form a dried catalyst; (e) calcining the dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas; and (f) adding a uranium compound immediately before the addition of the phosphorus compound or after the addition of the phosphorus compound.

Claim 32

The process of claim 25 wherein the catalyst prepared is described by the formula V.sub.a P.sub.b U.sub.c O.sub.x wherein a and b are 1 to 10; c is 0.01 to 5; x is the number of oxygens required to satisfy the valence requirements of the other elements present; and wherein said catalyst optionally contains at least one element selected from the group consisting of tantalum, cerium, chromium, manganese, cobalt, copper, antimony, iron, bismuth, tungsten, molybdenum, sulfur alkaline earth metal, an alkali metal, hafnium, zirconium, and thorium.

Claim 33

The process of claim 25 wherein an n-butene is reacted.

Claim 34

The process of claim 26 wherein at least one optional promoter is present in the catalyst in an atomic range of 0.01 to 1.

Claim 35

The process of claim 26 wherein a and b are 0.5 to 3.

Claim 36

The process of claim 26 wherein c is 0.1 to 0.5.

Claim 37

The process of claim 26 wherein the optional promoter is selected from the group consisting of Ta, Ce, Mn, Co, Sb, Fe, Bi, W and Mo.

Claim 38

The process of claim 25 wherein said finely divided metal or colloidal metal is selected from the group consisting of molybdenum, tungsten, magnesium, aluminum or nickel.

Claim 39

In a process for the preparation of maleic anhydride by the oxidation of n-butane, n-butene, 1,3-butadiene or mixture thereof with molecular oxygen in the vapor phase at a reaction temperature of 250° C. to 600° C. in the presence of a catalyst comprising vanadium, phosphorus, uranium and oxygen, the improvement wherein said catalyst is prepared by (a) forming an aqueous slurry of a vanadium compound containing pentavalent vanadium and a mineral acid-free, inorganic reducing agent capable of reducing said pentavalent vanadium to a valence state below +5, wherein the reducing agent is selected from the group consisting of hydrazine and finely divided metals; (b) admixing a phosphorus compound containing pentavalent phosphorus with said aqueous slurry of step (a); (c) heating said aqueous slurry of step (b) at a temperature of 120° C. under autogenous pressure so that substantial evaporation of the water in said slurry is prevented; (d) removing the water from the slurry of step (c) to form a dried catalyst; (e) calcining the dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas; and (f) adding a uranium compound immediately before the addition of the phosphorus compound or after the addition of the phosphorus compound.

Claim 40

In a process for the preparation of maleic anhydride by the oxidation of n-butane, n-butene, 1,3-butadiene or mixture thereof with molecular oxygen in the vapor phase at a reaction temperature of 250° C. to 600° C. in the presence of a catalyst comprising vanadium, phosphorus, uranium and oxygen, the improvement wherein said catalyst is prepared by (a) forming an aqueous slurry of a vanadium compound containing pentavalent vanadium and a mineral acid-free, inorganic reducing agent capable of reducing said pentavalent vanadium to a valence state below +5, wherein the reducing agent is selected from the group consisting of hydrazine and finely divided metals; (b) admixing a phosphorus compound containing pentavalent phosphorus with said aqueous slurry of step (a); (c) heating said aqueous slurry of step (b) at a temperature of 120° C. under autogenous pressure so that substantial evaporation of the water in said slurry is prevented; (d) removing the water from the slurry of step (c) to form a dried catalyst; (e) calcining the dried catalyst at a temperature of 250° C. to 600° C. in the presence of an oxygen-containing gas; and (f) adding a uranium compound immediately before the addition of the phosphorus compound or after the addition of the phosphorus compound.

Claim 41

The process of claim 33 wherein the finely divided metal is tungsten in an atomic range of 0.01 to 5.