Heat-coagulable latex binders and process for the preparation thereof
Assignee: Ingredion Inc
•
Filing: 1978-04-17
•
Granted: 1979-11-27
•
Expires: 1998-04-17
Abstract
Abstract An improved latex binder for nonwoven webs comprising an acrylate- and/or vinyl acetate-based copolymer containing 0.1-10% by weight of 2-hydroxyethyl or 2-hydroxypropyl acrylate or methacrylate is prepared by employing in combination with the copolymer 0.2-10% by weight, on latex solids, of anionic surfactant and 0.3-15% by weight, on latex solids, of nonionic surfactant in selected relative proportions and by adding to the copolymer 1-40% by weight, on latex solids, of a water-soluble salt. The resultant binder is characterized by being stable to coagulation at room temperature but coagulable at a temperature between 40° and 85° C. In the preparation of nonwoven fiber material, a nonwoven web is impregnated with the copolymer latex binder, heated to a temperature of within 40° and 85° C. sufficient to coagulate the binder within the web and thus prevent migration, and finally dried to form a chemically bonded, nonwoven fiber material in sheet form.
Inventors
- 👤 Ronald J. Caimi
- 👤 Walter F. Schlauch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:30
CPC Classifications
C; C08; C08F; C08F218/00; C08F218/02; C08F218/04; C08F218/08; C08F220/00; C08F220/02; C08F220/10; C08F220/12; C08F220/16; C08F220/18; C08F220/1802; D; D04; D04H; D04H1/00; D04H1/40; D04H1/58; D04H1/587; D04H1/64
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
143 words
In a process for preparing copolymer latex binders of the type wherein the copolymer latex is formed by emulsion polymerization of acrylate or vinyl acetate monomers or mixtures thereof and from 0.1 to 10% by weight of 2-hydroxyethyl or 2-hydroxypropyl acrylate or methacrylate monomers, the improvement which comprises employing in combination with said copolymer a surfactant system consisting of 0.2-10% by weight, based on latex solids, of an anionic surfactant and 0.3-15% by weight, on latex solids, of a nonionic surfactant, wherein the ratio of anionic to nonionic surfactant is between 1:1.5 and 1:3, and adding to said copolymer latex after polymerization from 1 to 40% by weight, based on latex solids, of a water-soluble salt, the resulting latex binder being characterized by its stability to coagulation at room temperature and its ability to coagulate at a temperature between 40° and 85° C.
Claim 2
Dependent Claim
143 words
In a process for preparing copolymer latex binders of the type wherein the copolymer latex is formed by emulsion polymerization of acrylate or vinyl acetate monomers or mixtures thereof and from 0.1 to 10% by weight of 2-hydroxyethyl or 2-hydroxypropyl acrylate or methacrylate monomers, the improvement which comprises employing in combination with said copolymer a surfactant system consisting of 0.2-10% by weight, based on latex solids, of an anionic surfactant and 0.3-15% by weight, on latex solids, of a nonionic surfactant, wherein the ratio of anionic to nonionic surfactant is between 1:1.5 and 1:3, and adding to said copolymer latex after polymerization from 1 to 40% by weight, based on latex solids, of a water-soluble salt, the resulting latex binder being characterized by its stability to coagulation at room temperature and its ability to coagulate at a temperature between 40° and 85° C.
Claim 3
Dependent Claim
13 words
The process of claim 1 wherein said water-soluble salt is a chloride salt.
Claim 4
Dependent Claim
15 words
The process of claim 2 wherein said water-soluble salt is sodium chloride or ammonium chloride.
Claim 5
Dependent Claim
17 words
The process of claim 1 wherein said copolymer contains mers derived from 2-hydroxyethyl acrylate or 2-hydroxypropyl acrylate.
Claim 6
Dependent Claim
41 words
The process of claim 1 wherein said copolymer latex is formed with a mixture of acrylate and vinyl acetate monomers and said acrylate monomers are selected from the group consisting of ethyl acrylate, butyl acrylate, methyl methacrylate, and 2-ethylhexyl acrylate monomers.
Claim 7
Dependent Claim
26 words
The process of claim 1 wherein said water-soluble salt is added to said latex binder in an amount of 2-5% by weight, based on latex solids.
Claim 8
Dependent Claim
35 words
The process of claim 1 wherein the total amount of anionic and nonionic surfactants in said latex binder is 1-6% by weight, on latex solids, and the ratio of anionic to nonionic surfactant is 1:2.
Claim 9
Dependent Claim
194 words
A process for preparing chemically bonded, nonwoven fiber material consisting essentially of the steps of: A. preparing a copolymer latex binder by forming a copolymer latex by emulsion polymerization of acrylate or vinyl acetate monomers or mixtures thereof and from 0.1 to 10% by weight of 2-hydroxyethyl or 2-hydroxypropyl acrylate or methacrylate monomers, employing in combination with said copolymer a surfactant system consisting of 0.2-10% by weight, based on latex solids, of an anionic surfactant and 0.3-15% by weight, on latex solids, of a nonionic surfactant, wherein the ratio of anionic to nonionic surfactant is between 1:1.5 and 1:3, and adding to said copolymer latex after polymerization from 1 to 40% by weight, based on latex solids, of a water-soluble salt, the resulting latex binder being characterized by its stability to coagulation at room temperature and its ability to coagulate at a temperature between 40° and 85° C.; B. impregnating a nonwoven web with said copolymer latex binder; C. heating said impregnated web to a temperature within the range of about 40° to 85° C. sufficient to coagulate the latex binder within the web; and D. drying the resultant chemically bonded, nonwoven fiber material.
Claim 10
Dependent Claim
194 words
A process for preparing chemically bonded, nonwoven fiber material consisting essentially of the steps of: A. preparing a copolymer latex binder by forming a copolymer latex by emulsion polymerization of acrylate or vinyl acetate monomers or mixtures thereof and from 0.1 to 10% by weight of 2-hydroxyethyl or 2-hydroxypropyl acrylate or methacrylate monomers, employing in combination with said copolymer a surfactant system consisting of 0.2-10% by weight, based on latex solids, of an anionic surfactant and 0.3-15% by weight, on latex solids, of a nonionic surfactant, wherein the ratio of anionic to nonionic surfactant is between 1:1.5 and 1:3, and adding to said copolymer latex after polymerization from 1 to 40% by weight, based on latex solids, of a water-soluble salt, the resulting latex binder being characterized by its stability to coagulation at room temperature and its ability to coagulate at a temperature between 40° and 85° C.; B. impregnating a nonwoven web with said copolymer latex binder; C. heating said impregnated web to a temperature within the range of about 40° to 85° C. sufficient to coagulate the latex binder within the web; and D. drying the resultant chemically bonded, nonwoven fiber material.
Claim 11
Dependent Claim
23 words
The process of claim 1 or 8 wherein said copolymer contains from 0.1 to 4% by weight of the mers derived from N-methylolacrylamide.
Claim 12
Dependent Claim
47 words
The process of claim 1 wherein said water-soluble salt is selected from the group consisting of sodium chloride, potassium chloride, sodium bromide, sodium acetate, sodium sulfate, ammonium sulfate, ammonium chloride, magnesium chloride, calcium chloride, calcium nitrate, aluminum sulfate, aluminum chloride, aluminum acetate, zinc chloride, and zinc sulfate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-11-26 | 1983-05-28 | 1983-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-11-26 | 1987-05-28 | 1987-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-11-26 | 1991-05-28 | 1991-11-27 | $7700.00 | Window Closed / Lapsed |