Polymer concrete compositions and cured products thereof
Assignee: Rohm and Haas Co
•
Filing: 1978-12-12
•
Granted: 1980-04-08
•
Expires: 1998-12-12
Abstract
Abstract This application concerns compositions comprising a mixture of air-drying dicyclopentenyl acrylate or methacrylate binder and a granular or particulate aggregate material, which may comprise a hydraulic cement, and is adapted to be formed by casting, extruding, or molding in any fashion into any desired shape and air-drying and resulting shaped article, thereby producing an integral, solid article of unitary mass and structure. The dicyclopentenyl (meth)acrylate may be used as an impregnant, polymerizable in situ, for already formed articles of porous nature, e.g., concrete, wood, pressed boards, and powdered pressed metal, such as aluminum, iron, steel, etc., to reduce the permeability at their surfaces and provides hard, continuous, hydrophobic, wear-resistant, and weather-resistant surfaces thereon.
Inventors
- 👤 William D. Emmons
- 👤 Peter R. Sperry
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 09:42
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B24/00; C04B24/04; C04B24/045; C04B24/24; C04B24/26; C04B24/2641; C04B26/00; C04B26/02; C04B26/04; C04B26/06; C04B41/45; C04B41/46; C04B41/48; C04B41/483; C04B41/60; C04B41/61; C04B41/62; C04B41/63; C08; C08L; C08L97/00; C08L97/02; B; B27; B27K; B27K3/00; B27K3/02; B27K3/15; C08L33/00; C08L33/04; C08L33/06
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
98 words
A composition suitable for use as a polymer concrete comprising (a) a granular aggregate having a void fraction of less than 0.37, (b) a liquid selected from dicyclopentenyl acrylate, dicyclopentenyl methacrylate, mixtures thereof, and mixtures of at least one of said (meth)acrylates with up to 40% by weight of another non-volatile monomer, such as a higher alkyl or alkenyl acrylate or methacrylate, and (c) a siccative or drier, the proportion of component (b) being such as to make the composition of workable consistency, and the amount of (c) being from 0.0005 to 2% by weight of component (b).
Claim 2
Dependent Claim
98 words
A composition suitable for use as a polymer concrete comprising (a) a granular aggregate having a void fraction of less than 0.37, (b) a liquid selected from dicyclopentenyl acrylate, dicyclopentenyl methacrylate, mixtures thereof, and mixtures of at least one of said (meth)acrylates with up to 40% by weight of another non-volatile monomer, such as a higher alkyl or alkenyl acrylate or methacrylate, and (c) a siccative or drier, the proportion of component (b) being such as to make the composition of workable consistency, and the amount of (c) being from 0.0005 to 2% by weight of component (b).
Claim 3
Dependent Claim
41 words
A composition according to claim 1 wherein the aggregate material (a) of the composition comprises (1) a hydraulic cement and (2) other aggregate material, the relative proportions between (1) and (2) being from 1:100 to 10:1, preferably from 1:20 to 3:1.
Claim 4
Dependent Claim
28 words
A product obtained from the casting or molding of the composition of claim 1 or 2 in or on a form and air-curing the cast or molded mass.
Claim 5
Dependent Claim
12 words
A composition according to claim 1 or 2 which is essentially anhydrous.
Claim 6
Dependent Claim
14 words
A composition according to claim 2 which also contains a small amount of water.
Claim 7
Dependent Claim
21 words
A product obtained by casting or molding, and subsequently air-curing the cast or molded mass, a composition according to claim 4.
Claim 8
Dependent Claim
21 words
A product obtained by casting or molding, and subsequently air-curing the cast or molded mass, a composition according to claim 5.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-08 | 1983-10-08 | 1984-04-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-08 | 1987-10-08 | 1988-04-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-08 | 1991-10-08 | 1992-04-08 | $7700.00 | Window Closed / Lapsed |