Process for preparing magnetic iron oxide and magnetic iron oxide produced thereby
Assignee: Fujifilm Holdings Corp
•
Filing: 1975-06-12
•
Granted: 1980-04-29
•
Expires: 1995-06-12
Abstract
Abstract A magnetic iron oxide having a large coercive force and an improved squareness ratio prepared by coating the surface of needle-like particles of magnetic iron oxide with a cobalt compound, placing the coated iron oxide particles in a unidirectionally oriented magnetic field thereby orienting the particles in the direction of the magnetic field, and heat-treating the needle-like particles in this state with the application of an external magnetic field, or heat-treating the needle-like particles in a magnetized state.
Inventors
- 👤 Koji Sasazawa
- 👤 Shigeo Komine
- 👤 Tatsuji Kitamoto
- 👤 Goro Akashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 07:04
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/706; G11B5/70626; G11B5/70642; G11B5/70652; G11B5/70668; G11B5/70673; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
137 words
A process for preparing magnetic iron oxide, which comprises, (a) coating the surface of needle-like particles of magnetic iron oxide with a cobalt compound, said iron oxide having the formula FeO x wherein x is from about 1.36 to 1.49, (b) placing the coated iron oxide particles in a unidirectionally oriented magnetic field of at least about 300 Oe, thereby to orient most of the needle-like particles in the direction of said magnetic field, (c) heat-treating said needle-like particles at a temperature of from about 200° to 800° C., in an atmosphere of inert gas, and (d) conducting said heat treating while said needle-like particles are in a magnetized state or, if said needle-like particles are not in a magnetized state, then conducting said heat treating while simultaneously applying an external magnetic field to said needle-like particles.
Claim 2
Dependent Claim
137 words
A process for preparing magnetic iron oxide, which comprises, (a) coating the surface of needle-like particles of magnetic iron oxide with a cobalt compound, said iron oxide having the formula FeO x wherein x is from about 1.36 to 1.49, (b) placing the coated iron oxide particles in a unidirectionally oriented magnetic field of at least about 300 Oe, thereby to orient most of the needle-like particles in the direction of said magnetic field, (c) heat-treating said needle-like particles at a temperature of from about 200° to 800° C., in an atmosphere of inert gas, and (d) conducting said heat treating while said needle-like particles are in a magnetized state or, if said needle-like particles are not in a magnetized state, then conducting said heat treating while simultaneously applying an external magnetic field to said needle-like particles.
Claim 3
Dependent Claim
34 words
The process of claim 1 wherein said needle-like magnetic iron oxide particles contain from about 0.5 to about 10 atomic percent of Co based upon the total atomic percent of said iron oxide particles.
Claim 4
Dependent Claim
19 words
The process of claim 1, wherein said inert gas is N 2 , He, Ne, Ar, Kr or Xe.
Claim 5
Dependent Claim
14 words
The process of claim 3, wherein the heat-treating temperature is 200° to 800° C.
Claim 6
Dependent Claim
17 words
The process of claim 1, wherein the heat-treating temperature is from about 300 ° to 400° C.
Claim 7
Dependent Claim
16 words
The process of claim 4, wherein the heat-treating temperature is from about 300° to 400° C.
Claim 8
Dependent Claim
37 words
The process of claim 1, wherein said cobalt compound is selected from the group consisting of cobalt oxides, cobalt-containing oxides, cobalt inorganic acid salts, cobalt organic acid salts, cobalt hydroxides, cobalt-containing hydroxides, metallic cobalt and cobalt alloys.
Claim 9
Dependent Claim
15 words
The process of claim 1, wherein said cobalt compound is cobalt oxide or cobalt hydroxide.
Claim 10
Dependent Claim
21 words
The process of claim 1, wherein said needle-like iron oxide particles have an average particle length of 0.2 to 2 μm.
Claim 11
Dependent Claim
16 words
A magnetic recording material comprising the magnetic iron oxide prepared by the process of claim 1.
References Cited (Backward Citations)
US3573980A
Cited
US3770500A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-04-29 | 1983-10-29 | 1984-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-04-29 | 1987-10-29 | 1988-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-04-29 | 1991-10-29 | 1992-04-29 | $7700.00 | Window Closed / Lapsed |