Abstract
Abstract The invention relates to the preparation of graft copolymers from silicones. The method comprises subjecting an article such as a contact lens previously moulded from silicone resins to an UV irradiation step with radiations of wave-length from 1800 to 4000 angstroms, in the presence of oxygen, and in a subsequent step contacting said article with an unsaturated monomer compound at a temperature sufficient to ensure the grafting of said compound on the silicone resin.
Inventors
- 👤 Georges H. Wajs
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 10:31
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J7/16; C08J7/18; B; B29; B29D; B29D11/00; B29D11/00009; B29D11/00038; B29D11/00125; B29D11/00134; B29D11/00865; G; G02; G02B; G02B1/00; G02B1/04; G02B1/041; G02B1/043; C08J2383/00; C08J2383/04
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
119 words
A method for preparing graft polyorganosiloxanes comprising an irradiating step, wherein an article previously moulded from a polyorgaosiloxane is subjected to a non ionizing UV radiation having a wave-length within the range from 1800 to 4000 Angtroms in the presence of oxygen, the article being exposed to a power intensity of said radiation of about 100 to 1000 mw/cm 2 for a time period of about 5 seconds to 30 minutes and a subsequent grafting step wherein said article is contacted with a monomer selected from compounds having a pyrrolidone ring wherein the nitrogen atom of the heterocyclic ring carries as a substituent a hydrocarbon radical including an ethylenically unsaturated group, whereby said monomer is grafted onto the polyorganosiloxane.
Claim 2
Independent Claim
119 words
A method for preparing graft polyorganosiloxanes comprising an irradiating step, wherein an article previously moulded from a polyorgaosiloxane is subjected to a non ionizing UV radiation having a wave-length within the range from 1800 to 4000 Angtroms in the presence of oxygen, the article being exposed to a power intensity of said radiation of about 100 to 1000 mw/cm 2 for a time period of about 5 seconds to 30 minutes and a subsequent grafting step wherein said article is contacted with a monomer selected from compounds having a pyrrolidone ring wherein the nitrogen atom of the heterocyclic ring carries as a substituent a hydrocarbon radical including an ethylenically unsaturated group, whereby said monomer is grafted onto the polyorganosiloxane.
Claim 3
Dependent Claim
16 words
A method according to claim 1, wherein said monomer is selected from monomers having hydrophilic properties.
Claim 4
Dependent Claim
86 words
A method as defined in claim 1 wherein said graft polyorganosiloxanes are ophthalmologically acceptable, whereby using said radiation having a wave-length of about 2,000 to 3,000 Angstroms, the article is exposed to a power intensity of said radiation of about 100 to 1000 mW/cm 2 for a time period of about 5 seconds to 30 minutes, wherein said oxygen is present in the form of atmospheric air, wherein said unsaturated compound has hydrophilic properties, and wherein said grafting takes place in the substantial absence of oxygen.
Claim 5
Dependent Claim
11 words
A method according to claim 1, wherein said monomer is vinylpyrrolidone.
Claim 6
Dependent Claim
57 words
A method according to claim 1, wherein said polyorgaosiloxane is a cured composition as obtained from mixtures comprising siloxanic polymers the chains of which are terminated by vinyl groups and in which all silicon atoms are linked to two substituent aromatic or saturated aliphatic hydrocarbon radicals and further comprising an hydrogeno-organopolysiloxane comprising Si-H bonds in its formula.
Claim 7
Dependent Claim
30 words
A method according to claim 5, wherein the substituent radicals on each of said silicon atoms are two identical or different alkyl radicals having from 1 to 4 carbon atoms.
Claim 8
Dependent Claim
31 words
A method according to claim 1, wherein the dose of UV radiation received by the article processed corresponds to an energy within the range from 1 to 100 cal/cm 2 .
Claim 9
Dependent Claim
27 words
A method according to claim 1, wherein said polyorganosiloxane is admixed with an agent efficient to limit the length of the chains formed in the grafting reaction.
Claim 10
Dependent Claim
26 words
A method according to claim 1, further comprising, subsequent to the grafting step a cross-linking step wherein the article is further exposed to an UV radiation.
Claim 11
Dependent Claim
43 words
A method according to claim 1, wherein the grafting reaction is effected by contacting the polyorganosiloxane with said monomer in the absence of oxygen at a temperature from 20° C. to 250° C., for a time period from 5 minutes to 8 hours.
Claim 12
Dependent Claim
17 words
A method according to claim 1, wherein said moulded article has the shape of a contact lens.
Claim 13
Independent Claim
121 words
A method for preparing a contact lens adapted to be worn on the cornea comprising moulding a polyorganosiloxane composition into a substrate a generally concave-convex shape, irradiating said substrate in the presence of oxygen with a non ionizing UV radiation having a wave length within the range from 1800 to 4000 Angstroms in the presence of oxygen, and contacting said irradiating substrate with a hydrophillic monomer selected from compounds having a pyrrolidone ring wherein the nitrogen atom of the heterocyclic ring carries as a substituent a hydrocarbon radical including an ethylenically unsaturated group to form a graft copolymer of about 75 to 99% by weight of said polyorganosiloxane composition and about 1 to 25% by weight of said monomer grafted thereto.
Claim 14
Independent Claim
121 words
A method for preparing a contact lens adapted to be worn on the cornea comprising moulding a polyorganosiloxane composition into a substrate a generally concave-convex shape, irradiating said substrate in the presence of oxygen with a non ionizing UV radiation having a wave length within the range from 1800 to 4000 Angstroms in the presence of oxygen, and contacting said irradiating substrate with a hydrophillic monomer selected from compounds having a pyrrolidone ring wherein the nitrogen atom of the heterocyclic ring carries as a substituent a hydrocarbon radical including an ethylenically unsaturated group to form a graft copolymer of about 75 to 99% by weight of said polyorganosiloxane composition and about 1 to 25% by weight of said monomer grafted thereto.
Claim 15
Dependent Claim
72 words
A method according to claim 12, further comprising further irradiating said graft copolymers to cross-link said monomer units, said further irradiating being of sufficient intensity and duration to cause a sufficient amount of cross-linking of said monomer units to substantially reduce the risk of rupture of a precorneal lachrymal film, while said graft copolymer remains capable of being rendered transparent and has the optical properties necessary to function as a contact lens.
Claim 16
Dependent Claim
17 words
Articles and contact lenses made of a graft polyorganosiloxane produced by the method according to claim 1.
References Cited (Backward Citations)
US3959102A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-10-21 | 1984-04-21 | 1984-10-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-10-21 | 1988-04-21 | 1988-10-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-10-21 | 1992-04-21 | 1992-10-21 | $7700.00 | Window Closed / Lapsed |